• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.19-20
• /
• 2007

At first the $Ba_{0.5}Sr_{0.5}TiO_3$-MgO powder with $B_2O_3-Li_2CO_3$ were made by the Sol-Gel method. The thick films of BST-MgO with $B_2O_3-Li_2CO_3$ were fabricated on the $Al_2O_3$ substrates coated with Pt by the screen printing method. The structural and dielectric properties of the BST-MgO thick film with $B_2O_3-Li_2CO_3$, addition were investigated. The structure of the BST-MgO with $B_2O_3-Li_2CO_3$ thick films were dense and homogeneous with no pores. The dielectric constant was increased and dielectric loss was decreased with increasing the sintering temperature.

• Korean Journal of Materials Research
• /
• v.2 no.2
• /
• pp.157-160
• /
• 1992

Unusual surface impurity levels of PREPed Ti-51at%Al powders were analyzed using Auger spectroscopy and they were compared with these obtained from bulk starting electrode. Oxygen and carbon contents were varied very much with particle size. Powder surfaces were believed to be mainly covered by a complex compound containing Ti, Al, O, and C. The decrease in contents of oxygen and carbon of powders were attributed to the certain refining reaction of transfer type DC Ar plasma during the powder production.

• Proceedings of the KIEE Conference
• /
• 2007.07a
• /
• pp.1261-1262
• /
• 2007

At first the $Ba_{0.5}Sr_{0.5}TiO_{3}$-MgO powder with $B_{2}O_{3}-Li_{2}CO_{3}$ were made by the Sol-Gel method. And then the thick films of BST-MgO with $B_{2}O_{3}-Li_{2}CO_{3}$ were fabricated on the $Al_{2}O_{3}$ substrates coated with Pt by the screen printing method. The structural and dielectric properties of the BST-MgO thick film with $B_{2}O_{3}-Li_{2}CO_{3}$ addition were investigated. The structure of the BST-MgO with $B_{2}O_{3}-Li_{2}CO_{3}$ thick films were dense and homogeneous with no pores. The dielectric constant and dielectric loss were increased with decreasing the $B_{2}O_{3}-Li_{2}CO_{3}$ addition ratio.

• Journal of Welding and Joining
• /
• v.18 no.5
• /
• pp.98-104
• /
• 2000

Aluminum alloys are being employed in automobile parts as strive to reduce overall vehicle weight to meet demands for improved fuel economy and reduction in vehicle emissions. Al-based composites reinforced with ceramic ($Al_2O_3,\;SiC,\;TiC\;and\;B_4C$) applications in a variety of components in automotive engines, such as liners, where the tribological properties of the material are important. In this study, Al-base composites reinforced with TiC particle powders has been developed for producing plasma spray coatings. The composite plasma spray powders were prepared Al-13Si-3Mg(wt%) alloy with TiC(40, 60 and 80wt%) particles ($0.2~5{\mu}textrm{m}$) by drum type ball milling. The composite powders ($36~76{\mu}textrm{m}$) were sprayed with plasma torch. Plasma sprayed coatings were heat-treated at $500^{\circ}C$ for 3 hours. The wear resistances of the plasma sprayed coatings were found to decrease with increasing TiC content and improved with heat treatment. AlSiMg-40% TiC heat-treated coatings were showed the best wear resistance in this study.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2000.04a
• /
• pp.11-11
• /
• 2000

Large-size ceramic/metal bulk FGMs have been fabricated on a recently developed and the world's largest Spark Plasma Sintering(SPS) systems, As a part of the development program for practical production processes and machines for FGMs by SPS, the processes, mechanical properties, dimensional size and shape effects, and production machine systems were investigated. In the past, $ZrO_{2}$/TiAI, $ZrO_{2}$/Ni, $Al_{2}O_{3}$/Ti, WC/Co, WC/Co/Steel, A1/P, Polymide, Cu/Polymide, nano-composites, porous and other combinations of bulk FGMs have already been processed using SPS. However, most of the specimen sizes were small, in a range of 20 to 30mm in diameter. Recently disk-shape sintered compacts with diameters of 100 and 150 mm, and thickness of approximately 15 and 17 mm, $ZrO_{2}$(3Y)/ stainless steel FGMs were homogenous consolidated in a shorter sintering time, while maintaining high quality and repeatability by utilizing a temperature gradient sintering method. The SPS heating up and holding time totaled less than one hour. Therefore, the SPS process in expected to find increased use in the fabrication of large-size FGMs as a new industrial processing technology. This paper introduces SPS systems, the processing principles, features and the characteristies of ceramic/metal bulk FGM.

• Journal of the Korean Ceramic Society
• /
• v.39 no.8
• /
• pp.721-727
• /
• 2002

In order to overcome trade-off among compositions, process and properties of the glasses with high PbO-base composition for PDP Rib, we studied glass crystallization and crystallization kinetics by Differential Thermal Analysis(DTA). Glass powder was obtained through melting/cooling/grinding, with 3 wt%TiO2 addition for the crystal nucleation and growth in $62PbO-19B_2O_3-10SiO_2-9(Al_2O_3-K_2O-BaO-ZnO)$(in wt%) composition glass. This powder was heat-treated for 1 to 10 h at $445^{\circ}C$ for nucleation. DTA measurements were performed to obtain the crystallization peak with $5∼25^{\circ}C/min$ heating rates. DTA crystallization peak temperature increased with increasing the heating rate and decreased with increasing the heating time. Because the Avrami parameter (n) was approximately 1, the surface crystallization occurred. The maximum nucleation time was 2 h.

• Journal of Powder Materials
• /
• v.3 no.2
• /
• pp.97-103
• /
• 1996

The densification of the compacts of pure Co, Fe+50%.Co and Fe+25% Co sintered under H$_2$ gas or in vacuum was investigated. The effects of AL, Nb, Ti, and V additions on the densification were also studied. The sintered compact of Co was fully-dense when the density of the compact was lower than $Dg^c$. However, above $Dg^{c}$, it was never fully-dense regardless of sintering atmosphere, temperature, and time. The densification of sintered compacts of Fe-50% Co and Fe-25% Co were always incomplete. While the addition of AL made all compacts fully-dense, the addition of Ti was effective for the compacts of Co and Fe-25% Co. V was effective only for the Fe-25% Co. These results tell us that the particle size of Co powder, the amount of Fe, and the amount of additives forming stable oxides play on important role for the complete densification. Therefore it is desirable to reduce or eliminate the equilibrium pressure of H$_{2}$O or CO in isolated pores to obtain a fully-dense sintered compact.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.27 no.1
• /
• pp.22-27
• /
• 2017

$TiO_2$ films, thickness of $1{\sim}30{\mu}m$ were deposited on glass substrate at room temperature by room temperature granule spray in vacuum. The starting powder was calcinated at $600^{\circ}C$ for 4 h using $Al_2O_3$ crucible in the furnace. The particle size of the $TiO_2$, $1.5{\mu}m$ was measured by a particle size analyzer. The effect of different process parameters such as number of pass, gas flow rate and feeder voltage was studied. As the number of passes increased, the film thickness increased proportionally due to adequate kinetic energy conserved. The effect of three different flow rates (i.e. 15, 25, and 35 LPM) on deposited film was investigated. As gas flow rate increased, the film thickness increased up to 25 LPM and then decreased. Higher feeder voltage with low flow rate of 15 LPM resulted in unsufficient coating thickness due to insufficient kinetic energy. Microstructure of $TiO_2$ films was investigated by scanning electron microscope and high resolution tramission electron microscope.

• Journal of the Korean Ceramic Society
• /
• v.22 no.6
• /
• pp.71-79
• /
• 1985

In order to fabricate the translucent electrooptic ceramics which are comparable to PLZT, $PNZT^*$ has been prepared from aqueous solutions of their itrate and chlorides. In the quarternary $Pb^{1-x} Nd_x(Zr_{0.63} Ti_{0.37})^{1-\frac{x}{4}O_3$, (PNZT) $(0.02\le x\ge 0.12)$ system cold-pressed PNZT slugs were sintered in $O_2$ in pt-crucible for 45 min. at 118$0^{\circ}C$ and were then heat-treated in air for 60 hrs. at 120$0^{\circ}C$ in Al2O3 crucibles containing $PbZrO_3$ powder to control the atmosphere. Mean particle size of calcined PNZT powders was 0.1~0.15${\mu}{\textrm}{m}$. It was found that the maximum value of optical transmission has been revealed at 6~8 at. % $Nd_2O_3$ added body and that their dielectric constant has been decreased as the frequency increased. Curic temperature has been varied inversely with $Nd^{3+}$ ion content up to 8 at. % and become constant above this value. $^*Pb_{1-x}Nd_x(Zr_{0.63} Ti_{0.37})_{1-2/4}O_3$

• Journal of the Korean Ceramic Society
• /
• v.29 no.7
• /
• pp.517-524
• /
• 1992

For the present study two alumina bodies were prepared. The sinter-aid alumina body(SAA) was made by conventional sinter-process using sintering additives of TiO2 & MgO/CaO and the reaction-bonded alumina (RBA) made from Al-Al2O3 mixed powder. A comparison was made between those two bodies and this investigation seeks to evaluate their microstructure, physical properties and material's reliability as well as their fracture behaviour. In spite of its considerable microstructural densification accompanied by sintering shrinkage, SAA is largely inferior to RBA in fracture strength. However, SAA shows a somewhat higher m-value than RBA in respect to the material's reliability, the Weibull modulus(m). RBA, which has high fracture strength, shows much longer lifetime under static loading than SAA. Though, as with m of fracture strength, the reliability(mt) of lifetime prediction in RBA is less high than of SAA.