• Korean Journal of Materials Research
• /
• v.10 no.12
• /
• pp.793-798
• /
• 2000

The age-hardening behavior of unreinforced 6061 Al alloy and SiCp/6061 Al alloy composites reinforced with different size of SiC particle (average diameter ; 0.7$\mu\textrm{m}$ and 7.0$\mu\textrm{m}$) was investigated by hardness measurement, calorimetric technique and transmission electron microscopy. At 17$0^{\circ}C$ isothermal aging treatment, the peak aging time of 0.7$\mu\textrm{m}$SiCp/6061Al alloy composite and 7.0$\mu\textrm{m}$SiCp/6061Al alloy composite is shorter than that of unreinforced 6061Al alloy, and the aging of 7.0$\mu\textrm{m}$SiCp/6061Al alloy composite is accelerated more than that of 0.7$\mu\textrm{m}$SiCp/6061Al alloy composite. This acceleration is due to the increase of dislocation density by the compositeness with SiCp and the SiC particle size. In the peak aged condition, the major strengthening phase of these materials is intermediate $\beta$ phase(Mg$_2$Si), and the activation energy for the formation of $\beta$ phase is considerably decreased by the compositeness with SiCp and the increasing of SiC Particle site.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.05a
• /
• pp.208-210
• /
• 2009

5성분계 Ti-Al-Si-C-N 코팅막은 하이브리드 코팅 시스템을 사용하여 실리콘 (Si) 웨이퍼와 SUS 304 기판위에 합성되었다. 본 연구에서는 Si 첨가에 의해 Ti-Al-Si-C-N 코팅막의 미세구조와 기계적 특성의 변화를 체계적으로 조사하였다. Si 함량이 증가됨에 따라 Ti-Al-Si-C-N 코팅막의 미세구조는 주상정에서 나노복합체를 가지는 미세구조로 변화하였다. 나노복합체의 고유한 특성에 의하여 미소경도는 약 56GPa로 증가하였고, Si가 증가함에 따라 평균 마찰계수도 크게 줄어들었다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.12 no.2
• /
• pp.80-86
• /
• 2002

$Al_{2}O_{3}/SiC$ nanocomposites were made by infiltrating partially sintered alumina bodies with polycarbosilane (PCS) solutions, which is a SiC polymer precursor, with pressureless sintering. The SiC content, densification, phases, strength, and microstructure were investigated with the processing parameters such as PCS solution concentration and heat treatment condition for PCS pyrolysis and sintering. The results were compared with those for pure alumina and nanocomposite samples made by the existing polymer precursor route (i.e. the PCS addition process). The SiC contents of up to 1.5 vol% were obtained by the PCS infiltration. PCS pyrolysis, followed by air heat treatment, was needed before sintering to avoid a cracking problem and to attain a densification as high as 98 % of theoretical. The nanocomposites exhibited significantly higher strength than pure alumina and those prepared by the PCS addition process despite larger grain size. Besides $\alpha-Al_{2}O_{3}/SiC$ and $\beta-SiC$ phases, mullite was present a little in the nanocomposites, which resulted from the reaction of $SiO_{2}$ in the pyrolysis product of PCS with the $Al_{2}O_{3}$ matrix during sintering. The nanocomposites had intagranular particles believed to be SiC, which is a typical feature of $Al_{2}O_{3}/SiC$ nanocomposites.

• Journal of Korea Foundry Society
• /
• v.10 no.1
• /
• pp.43-49
• /
• 1990

The influences of Cu and Mg addition on wear properties of SiC particulate reinforced Al-Si metal(alloy) matrix composites were investigated. Metal matrix composites were prepared by combination of compocasting and hot pressing techniques. The main results obtained are as follows : 1) The composite with Mg addition exhibits letter wear resistance than that with Cu addition. It is considered that Mg addition improved wettability of matal matrix composite by the strong segregation to the SiC / Al matrix interface. 2) After homogenization treatment, it was found that the interfacial segregation of Mg was predominant, while that of Cu was not detected. 3) The SiC / Al-11Si eutectic composite exhibits better wear resistance than the SiC / Al-6Si hypoeutectic composite does. 4) It seems that the increase in the amount of Mg addition affects on the uniform dispersion of SiC particulates, on the refinement of microstructure and on age hardening and these effects cause wear resistance improvement of composites.

• Journal of the Korean Ceramic Society
• /
• v.35 no.1
• /
• pp.1-4
• /
• 1998

SiC whisker reinforced Al2O3-SiC composite was fabricated by reaction synthesis method whish is cost ef-fective and allows good dispersion of whiskers. Fracture strength at room temperature showed the highest value with 150$0^{\circ}C$ reaction temperature because a lot of SiC whiskers was formed. Fracture strength at 135$0^{\circ}C$ did not show big differences with reaction temperature due to agglomeration of whiskers and formation of sil-icon oxynitride during hot MO(modulus of rupture) test probably promoting grain boundary sliding.

• Journal of Korea Foundry Society
• /
• v.14 no.3
• /
• pp.274-284
• /
• 1994

SiC fibers were coated with Cu, Ag and Ni metallic thin films by magnetron sputtering in order to improve wetting properties between Al matrix and SiC fiber. The wetting behavior of metal coated SiC fiber by pure Al has been studied at $670^{\circ}C{\sim}900^{\circ}C$ range for $10{\sim}90min$. under vacuum atmosphere. Besides, the effect of coated film thickness on the wettability has been investigated. The wetting behavior and interfacial reaction between Al and SiC fibers were analysed with optical microscope and SEM (scanning electron microscope). The wetting behavior of the as-received SiC fiber with Al melt was not uniform, indicated by the contact angles from less than $90^{\circ} to more Al melt was appeared in the initial stage of reation. It was considered that the metallic thin film played an important role in reducing the interfacial free energy and breaking down the aluminum oxide film by eutectic reaction with Al melt. However the wettability of Ni coated SiC fiber was not improved as much as that of Cu or Ag coated SiC fiber. The improvement of wettability by coating thickness is clearly showed in $1{\mu}m$ coated SiC fiber compared with $0.25{\mu}m$ coated SiC.

• Journal of the Korean Ceramic Society
• /
• v.54 no.4
• /
• pp.340-348
• /
• 2017

$SiC_f/SiC$ composites were joined using a $60{\mu}m-thick$ $Ti_3AlC_2$ or $Ti_3SiC_2$ MAX phase tape. The filler tape was inserted between the $SiC_f/SiC$ composites containing a 12 wt.% $Al_2O_3-Y_2O_3$ sintering additive. The joining was performed to a butt-joint configuration at $1600^{\circ}C$ or $1750^{\circ}C$ in an Ar atmosphere by applying 3.5 MPa using a hot press. Microstructural and phase analyses at the joining interface confirmed the decomposition of $Ti_3AlC_2$ and $Ti_3SiC_2$, indicating the joining by solid-state diffusion. The results showed sound joining interface without the presence of cracks. Joining strengths higher than 150 MPa could be obtained for the joints using $Ti_3AlC_2$ or $Ti_3SiC_2$ at $1750^{\circ}C$, while those for joined at $1600^{\circ}C$ decreased to 100 MPa approximately without the deformation of the joining bodies. The thickness of initial filler tape was reduced significantly after joining because of the decomposition and migration of MAX phase owing to the plasticity at high temperatures.

• Journal of the Korean Ceramic Society
• /
• v.37 no.4
• /
• pp.368-375
• /
• 2000

Fracture toughness of particulate composites of Al2O3/SiC, Al2O3/ZrO2 and Al2O3/ZrO2/SiC was analysed theoretically. According to the suggested particle bridging model for obtaining the R-curve height, the crack extension resistance for the long crack was linearly proportional to the residual calmping stress at the interface between the second phase and the matrix. It was also a function of the particle size and the content. It was confirmed that the rising R-curve behavior of Al2O3 containing 30 vol% SiC particles of 3${\mu}{\textrm}{m}$ was owing to the strong crack bridging by SiC particles. For Al2O3/ZrO2/SiC composites, the tensional stress from the 3${\mu}{\textrm}{m}$ SiC particles was large enough to activate the spontaneous transformation of the ZrO2. The crack extension resistance due to the particle bridging mechanism did not seem to be affected much by the coupled toughening, but its resultant toughness increase could be significantly smaller due to the dependency on the matrix toughness.

• Journal of Korea Foundry Society
• /
• v.20 no.4
• /
• pp.254-259
• /
• 2000

Metal matrix composites(MMCs) reinforced with hard particles have many potential application in aerospace structures, auto parts, semiconductor package, heat resistant panels, wear resistant materials and so on. In this work, the effect of SiC partioel sizes(50 and 100 ${\mu}m$) and additional elements such as Si, Cu and Ti on the microstructure and the wear property of $Al-5Mg-X(Si,Cu,Ti)/SiC_p$ composites produced by pressureless infiltration method have been investigated using optical microscopy, scanning eletron microcopy(SEM) with EDS(energy dispersive spectrometry), hardness test, X-ray diffractometer(XRD) and wear test. In present study, the sound $Al-5Mg-X(Si,Cu,Ti)/SiC_p$(50 and 100 ${\mu}m$) composites were fabricated by pressureless infiltration method. The $Al-5Mg-0.3Si-O.1Cu-O.1Ti/SiC_p$ composite with $50 {\mu}m$ size of SiC particle has higher hardness and better wear property than any other composite with $100{\mu}m$ size of SiC particle produced by pressureless infiltration method. The hardness and wear property of $Al-5Mg/SiC_p$(50 and 100 ${\mu}m$) composites were enhanced by the addition of Si, Cu and Ti in Al-5%Mg matrix alloy.

• Journal of the Korean Ceramic Society
• /
• v.24 no.1
• /
• pp.23-32
• /
• 1987

Synthesis of high purity ultrafine Si3N4 and ${\beta}$-Sialon powders was investigated via the simultaneous reduction and nitriding of amorphous SiO2, SiO2-Al2O3 system prepaerd by hydrolysis of alkoxides, using carbonablack as a reducing agent. In Si(OC2H5)4-C2H5 OH-H2 O-NH4OH system, hydrolysis rate increased with increasing reaction temperature and pH. Pure ${\alpha}$-Si3N4 was formed at 1350$^{\circ}C$ for 5 hrs in N2 atmosphere. In Si(OC2H5)4-Al(OC3H7)3-C6H6-H2 O-NH4OH system, weight loss increased as Si/Al ratio decreased. Single phase ${\beta}$-Sialon consisted of Si/Al=2 was formed at 1350$^{\circ}C$ in N2 and minor phases of ${\alpha}$-Si3N4, AIN, and X-phase were existed besides theSialon phase at other Si/Al ratios. The Si3N4 and Sialon powders synthesized from alkoxides consisted of uniform find particles of 0.05-0.2$\mu\textrm{m}$ in diameter, respectively.