• Journal of Powder Materials
• /
• v.29 no.5
• /
• pp.363-369
• /
• 2022

AlSi10Mg alloys are being actively studied through additive manufacturing for application in the automobile and aerospace industries because of their excellent mechanical properties. To obtain a consistently high quality product through additive manufacturing, studying the flowability and spreadability of the metal powder is necessary. AlSi10Mg powder easily forms an oxide film on the powder surface and has hydrophilic properties, making it vulnerable to moisture. Therefore, in this study, AlSi10Mg powder was hydrophobically modified through silane surface treatment to improve the flowability and spreadability by reducing the effects of moisture. The improved flowability according to the number of silane surface treatments was confirmed using a Carney flowmeter. In addition, to confirm the effects of improved spreadability, the powder prior to surface treatment and that subjected to surface treatment four times were measured and compared using s self-designed recoating tester. The results of this study confirmed the improved flowability and spreadability based on the modified metal powder from hydrophilic to hydrophobic for obtaining a high-quality additive manufacturing product.

• Corrosion Science and Technology
• /
• v.23 no.2
• /
• pp.104-112
• /
• 2024

Al-Zn-Mg-Si alloy coatings have been developed to inhibit corrosion of cold rolled steel sheets, and an understanding of the alloy system helps prevent coating defects. We used a Bridgman furnace to characterise the nature and formation mechanisms of the phases present in the quaternary system with 0.4 wt% Fe. In the directional solidification experiments we imposed steep temperature gradients and varied the pull rate. After the samples were quenched in the furnace, detailed characterization of the samples was carried out by electron microscopy (SEM/EDS). From the dT/dt vs T plots of the cooling curves of the alloys, the solidification path was determined to be $Liquid{\longrightarrow[80]^{544-558}}{\alpha}-Al{\longrightarrow[80]^{453-459}}Al/Mg_2Si{\longrightarrow[80]^{371-374}}Al/Zn{\longrightarrow[80]^{331-333}}Zn/mgZn_2$. The formation mechanisms of the Mg and Zn containing phases and their morphology was discussed together with the effects of the cooling rate. Key findings include the lengthening of the mushy zone in directionally solidified samples remelted against a positive temperature gradient, as well as an enrichening of the α-Al phase by Zn through remelting. Mg₂Si and other Si based phases were observed to adopt a much finer faceted microstructure in favour of a script-like microstructure when exposed to the higher cooling rate of coolant quenching.

• Journal of Korea Foundry Society
• /
• v.41 no.1
• /
• pp.3-10
• /
• 2021

In the compound casting between the aluminum alloy and the cast iron, the iron component may be dissolved from the cast iron during the process and mixed into the aluminum melt, thereby forming various iron-containing intermetallic compounds and significantly deteriorating the tensile properties of the aluminum alloy. On the other hand, unlike Fe, which is added as an impurity, Cu is added to improve the mechanical properties of the aluminum alloy. In this study, the change in microstructure and tensile properties of aluminum alloys due to the addition of Fe and Cu was investigated. A large amount of iron-containing compounds such as coarse Al₅FeSi phases were formed when the iron content was 1% or more, and the tensile properties were significantly reduced. In the case of the aluminum alloy to which Cu was added, an Al₂Cu phase was additionally formed and the tensile strength was clearly improved.

• Journal of Powder Materials
• /
• v.15 no.2
• /
• pp.142-147
• /
• 2008

The hypereutectic Al-20 wt%Si powders including some amount of Cu, Fe, Mg, Mn were prepared by a gas atomization process. In order to get highly densified Al-Si bulk specimens, the as-atomized and sieved powders were extruded at $500^{\circ}C$, Microstructure and tensile properties of the extruded Al-Si alloys were investigated in this study. Relative density of the extruded samples was over 98%. Ultimate tensile strength (UTS) in stress-strain curves of the extruded powders increased after T6 heat treatments. Elongation of the samples was also increased from 1.4% to 3.2%. The fracture surfaces of the tested pieces showed a fine microstructure and the average grain size was about $1{\mu}m$.

• Transactions of Materials Processing
• /
• v.14 no.6 s.78
• /
• pp.502-508
• /
• 2005

Hypereutectic Al-Si alloys have been regarded attractive for automotive and aerospace application, due to high specific strength, good wear resistance, high thermal stability, low thermal expansion coefficient and good creep resistance. Spray casting of hypereutectic Al-Si alloy has been reported to provide distinct advantages over ingot metallurgy (IM) or rapid solidification/powder metallurgy (RS/PM) process in terms of microstructure refinement. In this study, hypereutectic Al-25Si-2.0Cu-1.0Mg alloy was prepared by OSPREY spray casting process. The change of strain rate sensitivity and Creep transition were analyzed by using the load relaxation test and constant creep test. High temperature deformation behavior of the hypereutectic Al-Si alloy has been investigated by applying the internal variable theory proposed by Chang et al. Especially, the creep resistance of spray casted hypereutectic Al-Si alloy can be enhanced considerably by the accumulation of prestrain.

• Journal of Welding and Joining
• /
• v.22 no.5
• /
• pp.65-72
• /
• 2004

The tendency and degree of hot cracking of high strength 5083, 6N01 and 7N01 Al alloy welds by using DCSP-GTAW through modified Varestraint test and autogenous butt welding were investigated. In hot cracking test, 6N01 alloy showed the highest susceptibility to hot cracking in the weld metal and HAZ. Cracking susceptibilities generally increased with increase of solidification temperature range of the base metal and bead penetration-to-width ratio of the weld metal. The cracks in welds of the alloys vertically formed to solid-liquid interface and propagated along with columnar grain boundaries. The fracture facets of cracks showed the typical morphology of solidification crack observed as dendritic structures. Especially, in 6N01 alloy, liquation cracks which were due to elements of Si, Fe and Mg also observed in HAZ near fusion boundary. In butt welding of different Al alloys, the bead crack was mainly occurred in the welds of 6N01, 7N01 and other Al alloys together with 6N01 or 7N01. In the butt welds of 7N01, it was found that the component of Cu had an effect on the higher susceptibility to the hot cracking.

• Nuclear Engineering and Technology
• /
• v.53 no.10
• /
• pp.3398-3405
• /
• 2021

This study observed the effect of neutron irradiation and ageing on the microstructure, hardness, and corrosion resistance of SAV-1 (Al-Mg-Si) alloy. The investigated material was irradiated with neutrons to fluences of 10²¹-10²⁶ n/m² in the WWR-K research reactor and kept in dry storage. Long-term irradiation led to an increase in hardness of the alloy and a deterioration of pitting corrosion resistance. Post-irradiation ageing for 1 h at 100-300 ℃ resulted in a decrease in microhardness of the irradiated SAV-1. The effect of post-irradiation ageing on pitting corrosion was made clear through the formation of Guinier-Preston zones and secondary precipitates in the Al matrix. Ageing at 250 ℃ corresponded to the development of stable microstructure and the highest corrosion resistance for the irradiated samples. Mg₂Si, Si, and needle-shaped β" precipitates were formed in SAV-1 alloy that was irradiated with low fluences. β" and clusters of rod-shaped B-type precipitates were observed in highly irradiated samples. The precipitates were similar to those seen in non-irradiated pseudo-binary Al-Mg₂Si alloys with Si excess.

• Journal of Korea Foundry Society
• /
• v.37 no.6
• /
• pp.207-216
• /
• 2017

This study investigated the effects of the addition of Zn, Ca, and SiC on the microstructure and mechanical properties of Mg-Al alloys. The tensile properties of homogenized Mg-xAl (x = 6, 7, 8, and 9 wt.%) alloys increased with increasing Zn content by the solid-solution strengthening effect. However, when the added Zn content exceeded the solubility limit, the strength and ductility of the alloys decreased greatly owing to premature fracture caused by undissolved coarse particles or local melting. Among the Mg-xAl-yZn alloys tested in this study, the AZ74 alloy showed the best tensile properties. However, from the viewpoints of the thermal stability, castability, and tensile properties, the AZ92 alloy was deemed to be the most suitable cast alloy. Moreover, the addition of a small amount (0.17 wt.%) of SiC reduced the average grain size of the AZ91 alloy significantly, from $430{\mu}m$ to $73{\mu}m$. As a result, both the strength and the elongation of the AZ91 alloy increased considerably by the grain-boundary hardening effect and the suppression of twinning behavior, respectively. On the other hand, the addition of Ca (0.5-1.5 wt.%) and a combined addition of Ca (0.5-1.5 wt.%) and SiC (0.17 wt.%) increased the average grain size of the AZ91 alloy, which resulted in a decrease in its tensile properties. The SiC-added AZ92 alloy exhibited excellent tensile properties (YS 125 MPa, UTS 282 MPa, and EL 12.3%), which were much higher than those of commercial AZ91 alloy (YS 93 MPa, UTS 192 MPa, and EL 7.0%). The fluidity of the SiC-added AZ92 alloy was slightly lower than that of the AZ91 alloy because of the expansion of the solid-liquid coexistence region in the former. However, the SiC-added AZ92 alloy showed better hot-tearing resistance than the AZ91 alloy owing to its refined grain structure.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1993.04a
• /
• pp.54-58
• /
• 1993

Cu, Si, Mg, Ca, Cd, Sn, Pb등이 첨가되는 Al계 bearing 합금은 베어링 특성이 우수하여 최근 자동차드의 엔진 부품용 베어링소재로 많이 사용되어지고 있다. 합금원소 Si는 합금의 경도를 향상시키며 Si-rich한 경한 입자를 생성시켜 소착저항력(antiseizure)을 향상시키며 또한 합금의 주조성도 향상시켜 내마모성이 요구되는 Al계 베어링 합금에 주합금원소로 첨가된다. 본 연구에서는 강제죠반법과 급냉응고법을 이용하여 Al-Pb-Gu계와 Al-Si-Gu-Pb계 베어링합금을 제조하였다. 베어링합금이 급냉응고법으로 제조되었기 때문에 합금의 기지에는 Cu가 과포된 상태로 존재하여 석출경화에 앞서 행하여지는 용체화처리와 같은 효과가 얻어졌다. 본 실험에서는 Cu가 과포화된 기지를 갖는 주조상태의 시료를 시효열처리하여 석출경화된 베어링합금을 얻어서 석출경화에 의한 기지강화가 베어링합금의 내마모성질에 어떠한 효과를 가져오는지 규명하였다.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.12
• /
• pp.25-31
• /
• 2018

Selective Laser Melting is one of the representative 3D printing techniques for handling metal materials. The main factors influencing the characteristics of structures fabricated by the SLM method include the build-up angle of structures, laser power, laser scan speed, and scan spacing. In this study, the tensile properties of AlSi10Mg alloys were investigated by considering the build-up angle of tensile test specimens, laser scanning speed and scan spacing as variables. The yield stress, tensile strength, and elongation were considered as tensile properties. From the test results, it was confirmed that the yield stress values were lowered in the order of 0, 45, and 90 based on the manufacturing direction of the tensile specimen. The maximum yield stress value was obtained at 1870 mm / min based on the laser scan speed. The yield stress size decreased with decreasing scan speed. Based on the laser scan spacing, as the value increases, the yield stress increases, but the variation is smaller than the other test criteria. The tendency of the tensile strength and elongation variation depending on the test conditions was difficult to understand.