• 한국주조공학회지
• /
• 제31권5호
• /
• pp.284-287
• /
• 2011

본 연구는 Mg-Al 합금에 첨가된 희토류 금속(rare earth metal, RE)과 스트론튬(Sr)이 상온 및 고온 기계적 특성에 미치는 영향을 비교하고, 그 결과를 미세조직의 변화와 연관지어 분석하는 것이 목적이다. 이를 위해 4종의 Mg-6%Al-(3-X)%REX% Sr 합금(X = 0~3)을 마련하여 RE를 Sr으로 대체하면서 상온 및 고온 인장 특성, 크립 저항성을 평가하였다. RE가 Sr으로 대체됨에 따라, 층상구조의(${\alpha}$ + $Al_4Sr$)상이 ${\alpha}$ 덴드라이트 사이에 생성되면서 침상의 $Al_4RE$상이 점차 소멸하였으며 Mg-6%Al-3%Sr 합금에서는(${\alpha}$ + $Al_4Sr$과 블록형태의 Mg-Al-Sr상이 관찰되었다. Sr 함량이 증가할수록 항복강도와 크립저항성은 지속적으로 향상되는 경향을 나타내었다.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2003년도 추계학술대회논문집
• /
• pp.172-175
• /
• 2003

Thermomechanical behavior of Al-Mg-Si alloys have been studied to investigate the effect of microstructural features such as pre-existing substructure and distribution of particles on the deformation characteristics. The controlled compression tests have been carried out to get the basic information on how the alloy responds to temperature, strain amount and strain rate. Then hot forging of Al-Mg-Si alloys has been carried out and analyzed by the comparison with the compression tests. Microstructural features after forging have been discussed in terms of the thermomechanical response of Al-Mg-Si alloys. As already well mentioned, we have found that the deformation of Al-Mg-Si at the elevated temperature brought the recovered structure on most conditions. In a certain time, however, abnormally large grains have been found as a result of deformation assisted grain growth, which means that hot forging of Al-Mg-Si alloys could lead to a undesirable microstructural variation and the consequent mechanical properties such as fatigue strength.

• 한국정밀공학회지
• /
• 제19권10호
• /
• pp.77-83
• /
• 2002

Magnesium alloys casting are gaining increased acceptance in the automotive and electronic industeries and die casting is the most efficient method of manufacturing such mass produced parts. This study has been investigated the microstructures and mechanical properties of Mg-9Al-lZn alloy fabricated by die casting process for development of air bag case. The microstructure of die casted specimen were composed of pro-eutectic magnesium solid solution and $\beta$(Mg17Al12) precipitates. The tensile strength of as-fabricated Mg-9Al-lZn alloy revealed 231.4MPa. It was found that Mg-9Al-lZn alloy have good corrosion resistance in electrochemical polarization test.

• 소성∙가공
• /
• 제13권1호
• /
• pp.27-32
• /
• 2004

Thermomechanical behavior of Al-Mg-Si alloys was studied to investigate the effect of microstructural features such as pre-existing substructure and distribution of particles on the deformation characteristics. The controlled compression tests were carried out to get the information on how the alloy responds to temperature, strain amount and strain rate. Then hot forging of Al-Mg-Si alloys carried out and analyzed by the comparison with the compression tests. Microstructural features after forging were discussed in terms of the thermomechanical response of Al-Mg-Si alloys. As already well mentioned, we found that the deformation of Al-Mg-Si at the elevated temperature brought the recovered structure on most conditions. In a certain time, however, abnormally large grains were found as a result of deformation assisted grain growth, which means that hot forging of Al-Mg-Si alloys could lead to a undesirable microstructural variation and the consequent mechanical properties such as fatigue strength.

• 한국세라믹학회지
• /
• 제50권6호
• /
• pp.510-517
• /
• 2013

In this study, the properties of blue inorganic nano-pigments with a spinel structure were systematically investigated. We report the preparation of a blue ceramic nano-pigment and the Co and Ni substitutional effects on the blue color. $MgAl_2O_4$ was selected as the crystalline host network for the synthesis of cobalt and nickel-based blue ceramic nano-pigments. Various compositions of $Co_xMg_{1-x}Al_2O_4$ and $Ni_xMg_{1-x}Al_2O_4$ ($0{\leq}x{\leq}1$) powders were prepared using apolymerized complex method. The obtained powder was preheated at $400^{\circ}C$ for 5 h and then calcined at $1000^{\circ}C$ for 5 h. XRD patterns of the (Co,Mg)$Al_2O_4$ and (Ni,Mg)$Al_2O_4$ samples showed a single phase of the spinel structure in all compositions. TEM results indicated nano-sized pigments for (Co,Mg)$Al_2O_4$ and (Ni,Mg)$Al_2O_4$ with a particle size ranging from 20 to 50 nm. The characteristics of the color tones of (Co,Mg)$Al_2O_4$ and (Ni,Mg)$Al_2O_4$ were analyzed by CIE $L^*a^*b^*$ measurements. In addition, the thermal stability and the binding characteristics of (Co,Mg)$Al_2O_4$, (Ni,Mg)$Al_2O_4$ are discussed in terms of the TG-DSC and FT-IR results, respectively.

• Metals and materials international
• /
• 제24권6호
• /
• pp.1241-1248
• /
• 2018

The reactive wetting behaviors of molten Zn-Al-Mg alloys on MnO- and amorphous (a-) $SiO_2$-covered steel sheets were investigated by the sessile drop method, as a function of the Al and Mg contents in the alloys. The sessile drop tests were carried out at $460^{\circ}C$ and the variation in the contact angles (${\theta}_c$) of alloys containing 0.2-2.5 wt% Al and 0-3.0 wt% Mg was monitored for 20 s. For all the alloys, the MnO-covered steel substrate exhibited reactive wetting whereas the $a-SiO_2$-covered steel exhibited nonreactive, nonwetting (${\theta}_c>90^{\circ}$) behavior. The MnO layer was rapidly removed by Al and Mg contained in the alloys. The wetting of the MnO-covered steel sheet significantly improved upon increasing the Mg content but decreased upon increasing the Al content, indicating that the surface tension of the alloy droplet is the main factor controlling its wettability. Although the reactions of Al and Mg in molten alloys with the $a-SiO_2$ layer were found to be sluggish, the wettability of Zn-Al-Mg alloys on the $a-SiO_2$ layer improved upon increasing the Al and Mg contents. These results suggest that the wetting of advanced high-strength steel sheets, the surface oxide layer of which consists of a mixture of MnO and $SiO_2$, with Zn-Al-Mg alloys could be most effectively improved by increasing the Mg content of the alloys.

• International Journal of Korean Welding Society
• /
• 제1권1호
• /
• pp.63-70
• /
• 2001

The solidification cracking susceptibilities of Al-Mg alloy laser welds were assessed using self-restraint tapered specimen crack test. The dependence of cracking susceptibility of Al-Mg alloy laser welds on Mg contents was observed to be similar to that of arc welds in the same materials. The cracking susceptibility of Al-Mg alloy laser welds increased as Mg content increased up to 1.6-1.9 wt.% and then it decreased as Mg content increased further. The peak cracking susceptibility occurred at around 1.6 to 1.9 wt.% Mg for both autogenous and wire feed welds. It was also observed that the cracking susceptibility decreased as the grain size of Al-Mg alloy laser welds decreased, when Mg content was in the range higher than 1.9 wt.%.

• 한국주조공학회지
• /
• 제33권3호
• /
• pp.103-112
• /
• 2013

Effect of Fe and Mn contents on the tensile properties of Al-4 wt%Mg-0.9 wt%Si alloy system has been studied. Common phases of Al-4 wt%Mg-0.9 wt%Si alloy system were ${\alpha}$-Al, $Mg_2Si$, ${\alpha}-Al_{12}(Fe,Mn)_3Si$ and ${\beta}-Al_5FeSi$. As Fe content of Al-4 wt%Mg-0.9 wt%Si alloy system increased from 0.15 wt% to above 0.3 wt%, ${\beta}-Al_5FeSi$ compound appeared. When Mn content of the alloy increased from 0.3 wt% to 0.5 wt%, morphology of plate shaped ${\beta}-Al_5FeSi$ compound changed to chinese script ${\alpha}-Al_{12}(Fe,Mn)_3Si$. As Fe content of Al-4 wt%Mg-0.9 wt%Si-0.3 wt%Mn alloy increased from 0.15 wt% to 0.4 wt%, tensile strength of the as-cast alloy decreased from 191 MPa to 183 MPa and, elongation of the alloy also decreased from 8.0% to 6.2%. Decrease of these properties can be explained as the formation of plate shape, ${\beta}-Al_5FeSi$ phase with low Mn/Fe ratio of the alloy. However, when Mn content of Al-4 wt%Mg-0.9 wt%Si-0.3 wt%Fe alloy increased from 0.3 wt% to 0.5 wt%, tensile strength of as-cast alloy increased from 181 MPa to 194 MPa and, elongation of the alloy increased from 6.8% to 7.0%. These improvements attribute to the morphology change from ${\beta}-Al_5FeSi$ phase to chinese script, ${\alpha}-Al_{15}(Fe,Mn)_3Si_2$ phase shape-modified from with high Mn/Fe ratio of the alloy.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2006년도 6th International Meeting on Information Display
• /
• pp.877-881
• /
• 2006

We obtained sputtering yields for the MgO, $MgAl_2O_4$ and $MgAl_2O_4/MgO$ films using the FIB system. $MgAl_2O_4/MgO$ protective layers have been found to have less $24^{\sim}^30%$ sputtering yield values from 0.24 atoms/ion up to 0.36 atoms/ion than MgO layers with the values from 0.36 atoms/ion up to 0.45 atoms/ion for irradiated $Ga^+$ ion beam whose energies ranged from 10 keV to 14 keV. And $MgAl_2O_4$ layers have been found to have lowest sputtering yield values from 0.88 up to 0.11. It is also found that $MgAl_2O_4/MgO$ and MgO have secondary electron emission $coefficient({\gamma})$ values from 0.09 up to 0.12 for $Ne^+$ ion whose energies ranged from 50 eV to 200 eV.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2012년도 춘계학술발표회 논문집
• /
• pp.275-275
• /
• 2012

실용금속 중 가장 경량이고, 치수 안정성, 절삭성 등이 우수한 Mg과 각종 산업의 구조물, 전기전자 부품 등의 분야에서 방식용 코팅 제품으로 많이 사용되고 있는 Zn를 혼합박막으로 Zn-Mg 박막을 제작하였다. 또한 여기서는 모재와 Zn-Mg 박막 사이에 결합력 강화를 위하여 Al중간층을 삽입하고 (Zn-Mg)/Al 박막을 제작하였다. 이와 같이 혼합박막을 제작하는 것은 Zn, Mg, Al 등과 같은 단일박막의 밀착성과 내식성의 한계를 극복-향상시키기 위한 것이었다. 한편, 이와 유사한 혼합박막에 많이 사용되고 있는 희생양극의 성분적인 측면이나 구조적인 분석에 있어서는 연구의 진척이 많이 이루어지고 있지만, 밀착성과 내식성의 상관관계의 규명에 있어서는 기초 단계이다. 따라서 본 연구에서는 여러 가지 증착 조건에 따라 제작한 막에 대한 표면 몰포로지, 결정배향성, 밀착성과 내식성에 미치는 영향을 분석하여 이들의 상관관계를 규명함은 물론 Al 중간층의 유무에 따른 서로간의 특성을 분석하였다. 분석결과에 의하면 Zn, Mg, Al 단일박막과 Zn-Mg 혼합박막에 비해 Al 중간층을 삽입한 (Zn-Mg)/Al이 내식성은 물론 밀착성이 우수하게 나타났다.