• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.15 no.6
• /
• pp.229-233
• /
• 2005

Novel process was tried to obtain micro-porous ceramic body containing continuous pore channel. $MgAl_2O_4/MgO$ eutectic fibers and rods have been grown successfully by the micro-pulling-down method, and the microstructures and optical characterizations of grown crystals were performed. $MgAl_2O_4/MgO$ eutectic fibers of $0.3{\sim}1mm$ in diameter and about 500 mm in length, and the rods having 5 mm in diameter with approximately 60 mm in length have been grown with the $6{\sim}120mm/hr$ of growth speed. The eutectic fibers showed homogeneous microstructure in which MgO fiber aligned to the growth direction in the $MgAl_2O_4$ (spinel) matrix. The grown crystals looked semitransparency under naked eyes. Optical and orientational characterizations were performed. The second phase of MgO (periclase) was easily removed by selective etching with hydrochloric acid, and then porous bodies were obtained.

• Journal of the Korean Society for Heat Treatment
• /
• v.24 no.2
• /
• pp.82-86
• /
• 2011

The influences of Bi addition on morphological modification of $Mg_2Si$ phase and mechanical properties were investigated in Mg-7%Al-0.5%Si casting alloy. It was found that the addition of 0.3%Bi changed the $Mg_2Si$ morphology from coarse Chinese script type to polygonal type, and significantly decreased the size to ~5 ${\mu}m$ or less with the increase of number density. The modification of $Mg_2Si$ phase by the addition of Bi resulted in the improvement of tensile properties of the Mg-Al-Si alloy at RT and $175^{\circ}C$.

• Journal of the Korean Society for Precision Engineering
• /
• v.20 no.12
• /
• pp.48-54
• /
• 2003

Alumium alloys casting are gaining increased acceptance in the automotive and electronic industeries and squeeze casting is the most efficient method of manufacturing such mass produced parts. This study has been investigated the microstructures and mechanical properties of Al-7.0Si-0.4Mg (AC4C) alloy fabricated by squeeze casting process for development of Fuel system Parts (Fuel rail). The microstructure of squeeze casted specimen were composed of eutectic structure Alumimim solid solution and $Mg_2$Si precipitates. The tensile strength of as-solid solution treatment Al-7.0Si-0.4Mg ahoy revealed 298.5MPa. It was found that Al-7.0Si-0.4Mg alloy have good corrosion resistance in electrochemical polarization test.

• International Journal of Korean Welding Society
• /
• v.2 no.2
• /
• pp.42-46
• /
• 2002

The solidification cracking susceptibilities of Al-Mg-Si alloy laser welds were assessed using the self-restraint tapered specimen crack test. The cracking susceptibility of 6061 and 6082 Al-Mg-Si alloy laser welds was substantially reduced when the filler wire containing high Si such as Al-12 wt.% Si (4047A) was used. The amount of eutectic was observed to affect the solidification cracking of Al-Mg-Si alloy laser welds. Abundant eutectic seems to heal the cracking and reduces the cracking susceptibility, while an initial increase in eutectic liquid leads to the increased cracking tendency.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2000.04a
• /
• pp.109-115
• /
• 2000

In the present study, (10%$Al_2O_3$+5%Si)/AZ91 Mg hybrid composite was fabricated using the squeeze casting method. During squeeze casting, molten Mg was infiltrated into the preform of 10%$Al_2O_3$+5%Si and reaction product of $Mg_2Si$ intermetallic compound was formed by the reaction between molten Mg and Si powder. Microstructure has been observed and mechanical properties were evaluated for the reaction squeeze cast (RSC) hybrid composite. It was found that Si powder totally reacted with molten Mg to form $Mg_2Si$. Reinforcement ($Al_2O_3$) and the reaction product ($Mg_2Si$) are fairly uniformly distributed in Mg matrix for the squeeze cast hybrid composite. Mechanical properties were improved with hybridization of reinforcements, namely higher hardness and enhanced wear resistance comparing squeeze cast (15%$Al_2O_3$)/AZ91 Mg composite.

• Korean Journal of Soil Science and Fertilizer
• /
• v.41 no.6
• /
• pp.369-373
• /
• 2008

Special concern has been given to the elevated arsenic content in soils because of its high mobility and toxicity. Layered double hydroxide (LDH) which has a high anionic exchange capacity is another potential anion adsorbent for toxic anions such as arsenic, chromate and selenium etc. The uptake of arsenate from aqueous solutions by the calcined Mg-Al LDH has been investigated. The sorption capacity was about 530 mmol/kg. Sorption isotherm was defined as L-type in which arsenate was removed by LDH through anion uptake reaction. Arsenate sorption by the calcined Mg-Al LDH was occurred by reconstruction of LDH's framework. Competitive adsorption revealed that Mg-Al LDH had higher selectivity for arsenate than for sulfate. These results strongly suggest that calcined Mg-Al LDH has a promising potential for efficient removal of toxic metal oxides like arsenates from aqueous environments.

• Journal of Korea Foundry Society
• /
• v.31 no.1
• /
• pp.18-25
• /
• 2011

Effect of Fe and Mn contents on the tensile properties has been studied in Al-9wt%Si-0.3wt%Mg alloy. As Fe content of Al-9wt%Si-0.3wt%Mg-0.5wt%Mn alloy increased from 0.15wt% to 0.45wt%, tensile strength of as-cast alloy decreased from 192 MPa to 174 MPa, and elongation of the alloy also decreased from 4.8% to 4.2%. Decrease of these properties can be explained as the formation of plate shape, ${\beta}-Al_5FeSi$ phase with high Fe/Mn ratio of the alloy. However when Mn content of Al-9wt%Si-0.3wt%Mg-0.45wt%Fe alloy increased from 0.3wt% to 0.5wt%, tensile strength of T6 aged alloy increased from 265 MPa to 275 MPa, and elongation of the alloy increased from 2.3% to 3.6%. These improvements attribute to chinese script, ${\alpha}-Al_{15}(Mn,Fe)_3Si_2$ phase shape-modified from ${\beta}-Al_5FeSi$ phase with low Fe/Mn ratio of the alloy.

• Korean Journal of Materials Research
• /
• v.30 no.3
• /
• pp.111-116
• /
• 2020

Two different casting speeds of 60 and 80mm/min are adopted to determine the effect of casting speed on the microstructure and mechanical properties of Al-Mg-Si/Al hybrid material prepared by duo-casting. The obtained hybrid material has a uniform and straight macro-interface between the pure Al side and the Al-Mg-Si alloy side at both casting speeds. When the casting speed is increased to 80mm/min, the size of primary α phases in Al-Mg-Si alloy decreases, without change of shape. Although the Al-Mg-Si alloy produced at higher casting speed of 80mm/min shows much higher ultimate tensile strength (UTS) and 0.2 % proof stress and lower elongation, along with higher bending strength compared to the case of the 60mm/min in casting speed, the tensile properties and bending strength of the hybrid material, which are similar to those of pure Al, are the same regardless of the increase of casting speed. Despite the different casting speeds, deformation and fracturing in hybrid materials are observed only on the pure Al side. This indicates that the macro-interface is well-bonded, allowing it to endure tensile and bending deformation in all hybrid materials.

• Journal of the Korean institute of surface engineering
• /
• v.40 no.5
• /
• pp.241-244
• /
• 2007

$MgF_2$/Cr/$MgF_2$, $MgF_2$/Cu/$MgF_2$ and $MgF_2$/Al/$MgF_2$ multi-layered thin films were fabricated by evaporation system. $MgF_2$ and Cr(Cu, And Al) was selected as a low refractive index material and mid reflector layer, respectively. Optical properties including color effect were systematically studied in terms of different film layer by using spectrophotometer. Experimental results were compared to the simulation result. The films consistings of $MgF_2$/Cr/$MgF_2$, $MgF_2$/Cu/$MgF_2$, $MgF_2$/Al/$MgF_2$ multi-layered thin films showed wavelength range of $430{\sim}780nm$, typically color range between greenish yellow and orange at view angle of $45^{\circ}$. It was confirmed that this experimental result was well matched with simulation result.

• Journal of the Korean Ceramic Society
• /
• v.22 no.6
• /
• pp.29-36
• /
• 1985

This study was carried out to research on the optimum condition of $MgAl_2O_4$ spinel synthesis and the chara-ceteristics of its sintered bodies. In this study the used materials-MgO $Al_2O_3$-were prepared from the extragrade chemicals $Mg(OH)_2 Al(OH)_3$ respectively. The tendency to spinel synthesis and sintering condition were discussed about additives of SEM and the characteristics of sintered bodies were measured by TMA etc, The results were as follows ; 1. The addion of $TiO_2$ promoted more effectively the sinterbility than that of $MnO_2$. 2. Residual $\alpha$-$Al_2O_3$ and MgO in theorectical composition samples were disappeared at 1$600^{\circ}C$ 3. When added MnO2 residual $\alpha$-$Al_2O_3$ and MgO were disappeared at 150$0^{\circ}C$ and 1$600^{\circ}C$ respectively. 4, . When added $TiO_2$ residual $\alpha$-$Al_2O_3$ and MgO were disappeared at 150$0^{\circ}C$ and 134$0^{\circ}C$ respectively.