• Journal of the Korean Society for Heat Treatment
• /
• v.12 no.1
• /
• pp.1-8
• /
• 1999

This study has investigated the effect of aging treatment on the microstructure and mechanical properties of Mg-6Al-xZn(x = 1.5, 2.5) alloys fabricated by the squeeze casting process. The microstructures of as-squeeze cast were composed of pro-eutectic ${\alpha}$, super saturated ${\alpha}$ and ${\beta}(Mg_{17}Al_{12})$ compound. Aged at both $200^{\circ}C$ and $240^{\circ}C$, Mg-6Al-xZn alloys showed the peak hardness due to the formation of ${\beta}(Mg_{17}Al_{12})$ precipitates. The discontinuous precipitates of the lamella type are predominant at $200^{\circ}C$ aging treatment, while the finely dispersed continuous precipitates were dominant at $240^{\circ}C$ aging treatment. Mg-6Al-xZn alloys fabricated by the squeeze casting process had the better combination of tensile strength and elongation compared to the conventionally cast alloys. As zinc contents increased, the tensile strength was increased by the solid solution strengthening effect of zinc.

• Korean Journal of Materials Research
• /
• v.17 no.12
• /
• pp.648-653
• /
• 2007

Plasma electrolytic oxidation (PEO) treatment was performed on cast Mg-6 wt%Al alloy solution-treated at 693K for 16h and aged at 498K. The surface roughness, thickness, micro-hardness, wear and corrosion properties of coatings on solution-treated and aged Mg-6 wt%Al alloy were investigated. The coatings on aged Mg-6 wt%Al alloy had thinner layer and lower micro-hardness and wear resistance than the solution-treated Mg-6 wt%Al alloy. As the aging time increased, the thickness of coatings decreased while the surface roughness was almost no changed. In addition, the micro-hardness and wear property of coatings decreased with increasing the aging time unlike the uncoated Mg-6 wt%Al alloy showing the peak micro-hardness and the best wear property after aging for 16 h. However, the coatings on Mg-6 wt%Al alloy peak-aged for 16h revealed the best corrosion resistance in 3.5% NaCl solution, which was explained based on the microstructural characteristics.

• Journal of Korea Foundry Society
• /
• v.21 no.2
• /
• pp.127-134
• /
• 2001

Misch metal (rare earth element, Ce, La, Nd, Pr) which has large influence on high-temperature stability and toughness was added to the Al-5%Ni-5%Mg alloy, and squeeze casting was used for Al-5%Ni-5%Mg-(Mm) alloys. The effect of applied pressure and misch metal additions on mechanical properties in Al-5%Ni-5%Mg alloy by direct squeeze casting has been investigated. The applied pressure were 0 MPa(gravity casting), 25, 50 and 75 MPa. Squeeze-cast Al-5%Ni-5%Mg-(Mm) alloys had better mechanical properties than those of non-pressurized cast alloys because of the increased cooling rate by the application of pressure during solidification. By the addition of misch metal in Al-5%Ni-5%Mg alloy, better combination of strength and elongation was obtained. The addition of 0.3%Mm in Al-5%Ni-5%Mg alloy improved the heat resistant property due to the formation of fine eutectic phases.

• Korean Journal of Materials Research
• /
• v.6 no.10
• /
• pp.1043.1-1048
• /
• 1996

알루미나 매트릭스 복합재료를 AIZnMg(7075)-합금의 직접적인 용융산화를 통하여 제조하였다. 충전재료는 17$\mu\textrm{m}$ 크기의 모서리가 둥근 연마재용 SiC 입자를 사용하였다. 산화촉진재 SiO2를 사용한 경우와 사용하지 않은 경우를 비교하였다. 매트릭스 형성 매카니즘과 반응거동을 온도와 SiO2사용량을 중심으로 연구하였으며, 얻어진 AI2O3/SiC/금속 복합재료의 미세구조를 관찰하였다.

• Journal of Korea Foundry Society
• /
• v.34 no.6
• /
• pp.187-193
• /
• 2014

In the present work, the effect of adding Ce on the corrosion behavior of Mg-4Al-2Sn-1Ca alloy was investigated. The studied alloys were fabricated by gravity casting method and a potentiodynamic polarization, A.C. impedance and hydrogen evolution tests were carried out in a 3.5% NaCl solution with pH 7.2 at room temperature to measure the corrosion properties of Mg-4Al-2Sn-1Ca-xCe alloys. The microstructure of the Mg-4Al-2Sn-1Ca alloy was composed of ${\alpha}$-Mg, Mg17Al12, Mg2Sn and CaMgSn phase. Also, a $Al_{11}Ce_3$ phase was newly formed by the addition of Ce. With an increase of the Ce contents, the microstructure became refined and the corrosion resistance improved.

• Journal of Korea Foundry Society
• /
• v.32 no.5
• /
• pp.219-224
• /
• 2012

The effects of Mg and Si contents on the microstructure and mechanical properties in Al-Mg alloy (ALDC6) were investigated. The results showed that phase fraction and size of $Mg_2Si$ and $Al_{15}(Fe,Mn)_3Si_2$ phase in the microstructure of Al-Mg alloy were increased as the Mg and Si contents were raised from 2.5 to 3.5 wt%. With Si content of 1.5 wt%, freezing range of the alloy was significantly reduced and solidification became more complex during the final stage of solidification. While there was no significant influence of Mg contents on mechanical properties, Si contents up to 1.5 wt%, strongly affected the mechanical properties. Especially elongation was reduced by about a half with more than 1.0 wt%Si in the alloy. The bending and impact strength were decreased with increased amount of Si in the alloy, as well. The lowered mechanical properties are because of the growth of particle shaped coarse $Mg_2Si$ phase and precipitation of the needle like $\beta$-AlFeSi in the microstructure at the last region to solidify due to presence of excess amount of Si in the alloy.

• Journal of Korea Foundry Society
• /
• v.27 no.3
• /
• pp.126-130
• /
• 2007

Oxidation behavior of CaO added Mg and Mg-5Al alloys was investigated. At $500^{\circ}C$, oxidation rate of pure Mg was abruptly increased, while that of CaO added Mg was remarkably reduced with increasing CaO content. As a result of surface analysis by AES, there was the thin oxide layer mixed with MgO and CaO in CaO added Mg. Oxidation behavior of CaO added Mg was similar to that of Ca added Mg. Oxidation rate of 0.6CaO added Mg-5Al alloy was much lower than that of Mg-5Al alloy at $500^{\circ}C$ and both alloys showed the linear weight change at $400^{\circ}C$.

• Journal of the Korean Society of Marine Environment & Safety
• /
• v.18 no.6
• /
• pp.569-576
• /
• 2012

In general, aluminum alloys forms the passive film($Al_2O_3$, $Al_2O_3{\cdot}3H_2O$) in neutral solution. However, the passive film created on the surface will be destroyed by chloride ions contained in sea water so the corrosion will occur. In this study, in order to solve the problem of corrosion under a seawater environment, potentiostatic protection techniques were applied to Al-4.5%Mg-0.6%Mn aluminum alloy in seawater. At polarization experiments, active state were observed at anodic polarization and concentration polarization by reduction of dissolves oxygen and activation polarization were found at anodic polarization. As a results of potentiostatic experiment, calcareous deposit were created much more as applying time increase from the turning point of the concentration polarization and activation polarization and crevice corrosion was partially observed between calcareous deposit and surface of base metal. Overall potentiostatic anodic polarization experiment was difficult to apply potentiostatic corrosion protection technology by occurrence of active state, whereas potentiostatic cathodic polarization experiment examined optimum corrosion protection condition of -1.1 V~-0.75 V within the range of concentration polarization considered various applying time.

• Transactions of Materials Processing
• /
• v.8 no.6
• /
• pp.620-625
• /
• 1999

A finite element analysis is performed to predict the recrystallized volume fraction and the mean grain size in hot compression of Al-5wt%Mg alloy. In the analysis, a modeling equation of flow stress is assumed as a function of strain, strain rate, and temperature. And the influence of above varibles on flow stress is quantified by using Zener-Hollomon Parameter. In the modeling equation, effects of strain hardening and dynamic recrystallization on microstructure of Al-5wt%Mg alloy are investigated. The predicted results of recrystallized volume fraction and mean grain size are in good agreement with those of microstructures obtained from hot compression tests.

• Journal of Korea Foundry Society
• /
• v.33 no.2
• /
• pp.55-62
• /
• 2013

Effect of Fe and Mn contents on the castability of Al-4wt%Mg-0.9wt%Si system alloy has been studied. According to the analysis of cooling curve for Al-4wt%Mg-0.9wt%Si-0.3wt%Fe-0.3/0.5wt%Mn alloy, ${\alpha}-Al_{15}(Fe,Mn)_3Si_2$ and ${\beta}-Al_5FeSi$ phases crystallized above eutectic temperature of $Mg_2Si$. Therefore, these phases affected both the fluidity and shrinkage behaviors of the alloy during solidification. As Fe and Mn contents of Al-4wt%Mg-0.9wt%Si system alloy increased from 0.1 wt% to 0.4 wt% and from 0.3 wt% to 0.5 wt% respectively, the fluidity of the alloy decreased by 26% and 33%. When Fe content of the alloy increased from 0.1 wt% to 0.4 wt%, 23% decrease of macro shrinkage and 19% increase of micro shrinkage appeared. Similarly, Mn content of the alloy increased from 0.3 wt% to 0.5 wt%, 11% decrease of macro shrinkage and 14% increase of micro shrinkage appeared. Judging from the castability of the alloy, Al-4wt%Mg-0.9wt%Si alloy with low content of Fe and Mn, 0.1 wt% Fe and 0.3 wt% Mn, is recommendable.