• Journal of the Microelectronics and Packaging Society
• /
• v.10 no.4
• /
• pp.47-52
• /
• 2003

A new type of Bi based glass frit was developed for Ag paste in PDP applications and its properties are compared with the commercially used Pb based glass frit. After optimization of the properties of Bi based frits for PDP application such as the softening temperature and the coefficient of thermal expansion (C.T.E), the screen printed electrodes prepared with the Bi based fit contained Ag paste were characterized. In $Bi_2O_3-B_2O_3-Al_2O_3$ glass system with the more than 50% of $Bi_2O_3$, the softening temperature, the thermal expansion coefficient and the line resistivity was 400∼$480^{\circ}C$, 7.31∼$10.02\times 10^{-6}/^{\circ}C$> and 4.1∼4.8$\Omega$ respectively. Properties of the Bi based frits are comparable with the Pb based frits. A printability and an uniformity of the Bi based frits were excellent in screen printed Ag eletrode. The Bi based frit system is an excellent candidate material for Pb free and Alkali free frit in PDP applications.

• Korean Chemical Engineering Research
• /
• v.57 no.1
• /
• pp.111-117
• /
• 2019

This study proposed the fabrication and deposition of high purity crystalline $core-TiO_2/shell-Al_2O_3$ nanoparticles. Morphological properties of $core-TiO_2$ and coated $shell-Al_2O_3$ were confirmed by transmission electron microscope (TEM) and transmission electron microscope - energy dispersive spectroscopy (TEM-EDS). The electrical properties of the prepared $core-TiO_2/shell-Al_2O_3$ nanoparticles were evaluated by applying them to a working electrode of a Dye-Sensitized Solar Cell (DSSC). The particle size, growth rate and the main crystal structure of $core-TiO_2$ were analyzed through dynamic light scattering system (DLS), scanning electron microscope (SEM) and X-ray diffraction (XRD). The $core-TiO_2$, which has a particle size of 17.1 nm, a thin film thickness of $20.1{\mu}m$ and a main crystal structure of anatase, shows higher electrical efficiency than the conventional paste-based dye-sensitized solar cell (DSSC). In addition, the energy conversion efficiency (6.28%) of the dye-sensitized solar cell (DSSC) using the $core-TiO_2/shell-Al_2O_3$ nanoparticles selectively controlled to the working electrode is 26.1% higher than the energy conversion efficiency (4.99%) of the dye-sensitized solar cell (DSSC) using the conventional paste method.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.27 no.6
• /
• pp.130-137
• /
• 2023

By using XRF (X-ray fluorescence), this study investigates the variation of chemical properties in cement pastes at elevated temperatures. High-temperature conditions were prepared by using an electric furnace, planning a total of 11 target temperatures ranging from room temperature to 1000 ℃. A standard library of geo-quant basic was applied for the analysis of 12 elements in cement paste, including Ca, Si, Al, Fe, S, Mg, Ti, Sr, P, Mn, Zn and K. The results revealed that, as the temperature increased, the proportion of each element in the cement paste also increased. With the exception of a few elements present in extremely low amounts in the cement pastes, the variation in the composition ratio of most elements exhibited a strong correlation with temperature, with an R-squared value exceeding 0.98. In this study, cement pastes exposed to normal and high-temperature environments were compared. The authors established that the reasons for the different results in this comparison can be explained from the same perspective as when comparing raw cement with cement paste. Furthermore, this study discussed the potentially most dominant parameter when investigating the properties of cement paste using XRF.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.364.1-364.1
• /
• 2014

고효율 태양전지로 가기 위해서는 태양전지의 후면 패시베이션은 중요한 역할을 한다. 후면 패시베이션 막으로 사용되는 $Al_2O_3$ 막은 $Al_2O_3/Si$ 계면에서 높은 화학적 패시베이션과 Negative Fixed Charge를 가지고 있어 적합한 Barrier막으로 여겨진다. 하지만 이후에 전면 Metal paste의 소성 공정에 의해 $800^{\circ}C$이상 온도를 올려주게 됨에 따라 $Al_2O_3$ 막 내부에 결합되어 있던 수소들이 방출되어 blister가 생성되고 막 질은 떨어지게 된다. 우리는 blister가 생성되는 것을 방지하기 위한 방법으로 PECVD 장비로 SiNx를 증착하는 공정 중에 $N_2O$ 가스를 첨가하여 SiON 막을 증착하였다. SiON막은 $N_2O$가스량을 조절하여 막의 특성을 변화시키고 변화에 따라 소성시 막에 미치는 영향에 대하여 조사하였다. 공정을 위해 $156{\times}156mm2$, $200{\mu}m$, $0.5-3.0{\Omega}{\cdot}cm$ and p-type 단결정 실리콘 웨이퍼를 사용하였고, $Al_2O_3$ 막을 올리기 전에 RCA Cleaning 실행하였다. ALD 장비를 통해 $Al_2O_3$ 막을 10nm 증착하였고 RF-PECVD 장비로 SiNx막과 SiON막을 80nm 증착하였다. 소성로에서 $850^{\circ}C$ ($680^{\circ}C$) 5초동안 소성하고 QSSPC를 통해 유효 반송자 수명을 알아보았다.

• Journal of Applied Reliability
• /
• v.6 no.3
• /
• pp.205-212
• /
• 2006

The purpose of this article is about the accelerated product-reliability-test method of the changing colors of mobile products, which are majorly from the frequent touching of sweating fingers. Such problems of changing colors of mobile products have found mostly In metallic paint containing aluminum paste pigments. Also we found that the color of Al Paste is changed by human sweat. Therefore, the accelerated experimental method has been tested as follow: applying the various concentration of lactic acid, which is the changing color components from human sweat, and deeping the testing sample under temperature of $60^{\circ}C$ in dilutelactic acid with water. From the series of tests, the most optimum concentration of lacticacid has been obtained in 10wt% and the sample is observed to be almost same effect as natural changing of colors by human touching after the test. It has been also confirmed from the cross-sectional analysis. In detail, the testing sample has changed its color in 48hr by changing color effect of Alpaste with 10 wt% of lactic acid, and the digit of $\Delta$ E has measured 10.9 after the test.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.5 no.4
• /
• pp.121-129
• /
• 2001

The semi-adiabatic temperature rise and the losses of temperature of cement paste, mortar and concrete were measured by an apparatus of semi-adiabatic temperature. Heat of hydration was measured by a conduction calorimeter and adiabatic temperature rise of concrete was measured by an adiabatic calorimeter. The derived equation which can assume the adiabatic temperature was proposed by measuring the semi-adiabatic temperature of concrete. The maximum adiabatic temperature rise of concrete obtained by the derived equation of adiabatic temperature, $T_{ad}(t)=T_{sad}(t)+T_{dis}(t)$, showed $55^{\circ}C$ approximately and it had good relation with the other one obtained by the heat of hydration of cement paste and with maximum value which was measured by the adiabatic calorimeter. The adiabatic temperature rise obtained by derived equation was a different information in comparison with the value obtained by adiabatic temperature rise equations by Hell and et. al. in early age, but it showed similar tendencies with the other one according to elapsed time. Adiabatic temperature rise of lich mix concrete with highly cement content was predicted. The adiabatic temperature rise of cement paste and mortar obtained by derived equation from us showed comparatively matching results to compared with that of obtained by adiabatic temperature equation from concrete standard specification.

• Journal of the Korean Ceramic Society
• /
• v.50 no.4
• /
• pp.280-287
• /
• 2013

Plate-type phosphor is a promising substitute in overcoming the issues related to the powder phosphor paste mixed with resin. In this research, $Ca-{\alpha}-SiAlON:Eu^{2+}$ plate phosphor ($Ca_xSi_{12-(m+n)}Al_{m+n}O_nN_{16-n}:Eu_y$) was investigated for the varied compositions (m,n) of the host crystal with the fixed Eu content (y). Densification was promoted for the compositions with increasing 'm' values for the m=2n relationship. Dictated by the Eu concentration inside the phosphor crystal, photoluminescence intensity was stronger in ${\alpha}2$ specimen (m = 3.0, n = 1.5) containing the second phases when compared to ${\alpha}1$ specimen (m = 1.5, n = 0.75) comprising a single-phase ${\alpha}$-SiAlON. The concentration of Eu in the non-emitting amorphous interfacial glass phase was 2~4 times of the designed Eu concentration inside the ${\alpha}$-SiAlON crystal.

• Journal of the Korean Ceramic Society
• /
• v.51 no.4
• /
• pp.344-349
• /
• 2014

$RuO_2$-based high frequency thick-film resistor paste was printed at the speed of 10, 100, 300 mm/sec on the AlN substrate, and then sintered at between 750 and $900^{\circ}C$. The sintered thick films were characterized in terms of printing and sintering conditions. With increasing printing speed, the thickness and roughness of sintered film increased. The resistance of the thick film resistor was reduced by increasing the printing speed from 10 to 100 mm/sec, but did not significantly change at 300 mm/sec speed. With increasing sintering temperature, the surface roughness and thickness of sintered resistor film decreased. The reduction rate was large in case of fast printed resistor. The resistance of the resistor increased up to $800^{\circ}C$ with sintering temperature, but again decreased at the higher sintering temperature.

• Journal of the Microelectronics and Packaging Society
• /
• v.4 no.2
• /
• pp.55-62
• /
• 1997

P2O3-PbO-SiO2-Al2O3계 조성을 이용하여 저온에서 소결이 가증하며 열팽창계수와 유전율이 낮은 회로기판용 glass ceramics를 제조하고자 하였다. 155$0^{\circ}C$에서 2시간 동안 용 융하여 제조한 모유리의열팽창 거동을 확인하기 위하여 TMA로 열분석을 실시하였으며 이 유리를 분말화하여 80$0^{\circ}C$에서 열처리 하였다. 이때 cristobalite 형성억제제로 Ga2O3를 사용 하였으며 Ga2O3 첨가량에 따른 억제 영향을 XRD를 통행 확인하였다. Ga2O3를 첨가한 유리 분말로 pellet을 제조하여 열처리를 하였고 소결시편의 표면을 SEM을 통해 관찰하였다. 열 처리한 pellet에 silver paste를 screen printing하여 유전율을 측정하였으며 조성에 따른 유 전율의 변화를 확인하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.335-335
• /
• 2010

$SiO_2$, $B_2O_3$, $Al_2O_3$, CaO, MgO, $Na_2O$, $ZrO_2$, $Bi_2O_3$를 이용하여 성질이 다른 두 종류의 무연계 프릿트를 제조하여 특성을 표준화 하였고, 이들 무연계 프릿트를 이용하여 Ag계 도체 및 $RuO_2$계 저항페이스트롤 제조하여 특성에 미치는 프릿트 조성의 영향을 연구하였다. $B_2O_3$를 첨가하여 퍼짐특성이 큰 프릿트의 경우 더 우수한 페이스트 특성을 나타내었다.