• 대한치과보철학회지
• /
• 제45권5호
• /
• pp.675-686
• /
• 2007

Statement of problem: Titanium nitride(TiN) coatings are the most general and popular coating method and used to improve the properties of metallic surface for industrial purposes. When TiN coating applied to the abutment screw, frictional resistance would be reduced, as a results, the greater preload and prevention of the screw loosening could be expected. Purpose: The purpose of this study was to investigate mechanical properties of TiN coated film of various coating thickness on the titanium alloy surface and to evaluate proper coating thickness. Material and method: 95 Titanium alloy (Ti-6Al-4V) discs of 15 mm in diameter and 3 mm in thickness were prepared for TiN coating and divided into 7 groups in this study. Acceding to coating deposition time (CDT) with TiN by using Arc ion plating, were divided into 7 groups : Group A (CDT 30min), Group B (CDT 60min), Group C (CDT 90min), Group D (CDT 120min), Group E (CDT 150min), Group F(CDT 180min) and Group G (no CDT) as a control group. TiN coating surface was observed with Atomic Force Microscope(AFM), field emission scanning electron microscopy(FE-SEM) and examined with scratch tester, wear tester. Result: 1. Coating thickness fir each coated group was increased in proportion to coating deposition time. 2. Surface of all coated groups except Group A was homogeneous and smooth. However, surface of none coated Group G had scratch. 3. Adhesion strength for each coated group was increased in proportion to coating deposition time. 4. Wear resistance for each coated group was increased in proportion to coating deposition time. 5. Surface roughness in Group A, B, C was increased in proportion to coating deposition time. But, surface roughness in Group D, E, F was showed decreased tendency in proportion to coating deposition time. Conclusion: According to coating deposition time, mechanical properties of TiN coated film were changed. It was considered that 120 minutes coating deposition time ($1.32{\mu}m$ in coating thickness) is necessary.

• 한국재료학회지
• /
• 제3권2호
• /
• pp.131-139
• /
• 1993

극저탄소 알루미늄 킬드강내에 합금원소로 첨가된 Al, Ti, Nb, B등은 열처리 공정중 질화물이나 탄화물로 석출되어 강의 재결정집합조직을 변화시킴으로써 강판재의 디입드로잉 특성에 결정적인 영향을 미친다. 본 연구에서는 Ti및 Nb를 단독으로 또는 동시에 첨가한 데 이어, B, P, Si 및 Mn등을 추가로 첨가한 극저탄소 고강도 강판의 집삽조직에 미치는 질화물, 탄화물과 같은 미세 석출물의 영향을 TEM, SEM, 광학현미경분석에 의하여 조사하였다. Nb 및 Ti를 동시에 첨가한 강에서는 미세한 N$b_2$C 및 T$i_2$AIN가 주로 석출되는 반면, Nb를 단독으로 첨가한 강에서는 미세한 AIN 및 조대한 BN이 석출되고,Ti를 단독으로 첨가한 강에서는 비교적 조대한 T${i_4}{N_3}$및 조대한 ${N_10}{N_22}$/T$i_68$이 석출되는 것으로 관찰되었다. 또한 이러한 탄질화물들의 석출에 의하여 세 강이 서로 다른 결정입도를 나타내는데, 결정입도는 Nb 및 Ti동시첨가강과 Nb단독첨가강이 서로 비슷하고, Ti단독첨가강이 가장 큰 것으로 나타났다.

• 대한금속재료학회지
• /
• 제47권2호
• /
• pp.129-137
• /
• 2009

Corrosion behaviors of TiN coated dental casting alloys have been researched by using various electrochemical methods. Three casting alloys (Alloy 1: 63Co-27Cr-5.5Mo, Alloy 2: 63Ni-16Cr-5Mo, Alloy 3: 63Co-30Cr-5Mo) were prepared for fabricating partial denture frameworks with various casting methods; centrifugal casting(CF), high frequency induction casting(HFI) and vacuum pressure casting(VP). The specimens were coated with TiN film by RF-magnetron sputtering method. The corrosion behaviors were investigated using potentiostat (EG&G Co, 263A. USA) in 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. The corrosion morphologies were analyzed using FE-SEM and EDX. Alloy 1 and Alloy 2 showed the ${\alpha}-Co$ and ${\varepsilon}-Co$ phase on the matrix, and it was disappeared in case of TiN coated Alloy 1 and 2. In the Alloy 3, $Ni_2Cr$ second phases were appeared at matrix. Corrosion potentials of TiN coated alloy were higher than that of non-coated alloy, but current density at passive region of TiN coated alloy was lower than that of non-coated alloy. Pitting corrosion resistances were increased in the order of centrifugal casting, high frequency induction casting and vacuum pressure casting method from cyclic potentiodynamic polarization test.

• 한국식품저장유통학회지
• /
• 제14권4호
• /
• pp.414-418
• /
• 2007

더덕 함량을 10, 15 및 20% (w/v)로 달리하여 50% (v/v) 주정에 담아 밀봉한 후 상온에서 180일간 침출시킨 다음 더덕 침출주의 이화학적 및 관능적 특성에 미치는 영향을 조사하였다. 더덕 함량을 달리하여 상온에서 180일간 침출시킨 결과 총당은 더덕 함량이 많을수록 많은 양의 총당이 용출되는 경향을 보이고 있었으며 맛을 결정하는 환원당도 총당과 유사한 경향을 보이고 있었다. 한편 더덕의 유효성분인 total polyphenol의 경우 더덕 함량이 많을수록 차이는 뚜렷하였으나 원료 더덕 중에 함유된 total polyphenol에 비해 적은 양이 용출되고 있었다. 관능적인 기호도의 측도인 노란색의 경우 더덕 함량이 20% (w/v)인 침출주에서 가장 높은 값을 보이고 있었고 crude saponin은 비교적 완만히 용출되는 경향을 보이고 있었으나 침출 100일경이 지나면서 급격히 용출되는 경향을 보이고 있었다. 더덕 침출주의 주세법 기준 항목인 불휘발성분의 경우 더덕 20% (w/v) 함유 침출주만이 침출 160일이 지나야 법적 기준치인 2.0% (w/v) 이상을 만족하는 것으로 나타나 더덕 침출주를 제조하기 위해서는 더덕 2.0% (w/v) 이상 필요하고 침출시간도 상온에서 160일 이상 요구되는 것으로 나타났다. 관능적인 기호도에서는 더덕 20% (w/v)이상 함유된 침출주에서 맛, 향, 색 및 전체적인 기호도에서 우수한 것으로 나타났다. 이상의 결과로부터 더덕 침출주를 제조하기 위해 더덕 함량을 20% (w/v) 이상 함유하여야 불휘발성분의 법적 기준인 2.0% (w/v)를 만족하는 것으로 나타나 앞으로 품질이 우수한 더덕 침출주를 제조하기 위해 더덕 함량, 침출시간 및 온도 등의 침출방법을 결정하는 연구가 필요한 것으로 나타났다.a}$,24S)-stigmast-5-en-3-ol (${\gamma}-sitosterol$)은 감귤이나 버섯 균사체에서 보고되지 않은 성분들이 검출되었다.M 영상 역시 oxide island 들이 형성에 기인된 어떤 "Strawberry" 구조를 보여주었으나 정확하게 $Al_2O_3$ overlayer가 형성되었는지는 규명할 수 없었다. 결론적으로, 800 K와 1000 K에서 $Ni_3Al(111)$ 합금표면위의 산소 상호작용결과 어떤 aluminum oxide overlayer의 island들이 성장됨을 확인할 수 있었다.q/g$이 검출되었다. 고방사능 폐수지의 평균 $^{14}C/^3H$비는 28로 저방사능 폐수지의 0.70에 비해 높게 나타났으며, $^{14}C$ 및 $^3H$의 농도는 서로 비례하는 경향을 보였다.보완대책이 필요하다는 사실을 이 성적을 통하여 비로소 확인할 수 있었다.가정교과교육학 문항내용의 포괄성을 살펴보면 다음과 같다. 가정과교육과정 문항내용은 제7차 교육과정 문서상에 표면적으로 제시된 내용에 한정되어 있어 구체적인 개선방안으로 교육과정의 철학적 이론적 배경, 다양한 교육과정 원리를 활용하는 문항내용 등과 같이 좀 더 이론적이고 원론적인 내용으로의 확대를 제안하였다. 가정과교수학습법 문항내용은 특정 교수학습모형에 관련된 지식을 묻는 내용으로 주로 출제되었다. 이에 구체적인 개선방안으로 특정 교수학습모형의 이론적 토대가 되고 전체적인 교수설계를 하기 위한 기본 바탕이 될 수 있는 교수학습이론에 관한 내용, 또한 현재가정과교육에 있어서 유용한 교수학습법이라고 입증되고 있는 실천적 추론 가정과 수업에 관한

• 박물관보존과학
• /
• 제30권
• /
• pp.23-46
• /
• 2023

동아대학교 석당박물관 소장 지자총통은 조선 중기에 사용하던 전장유통식 중화기무기로 천자총통 다음으로 큰 화기류이다. 지자총통의 표면에는 표면 이물질들로 인해 고유의 색상이 가려져 있는 상태로, 보존처리가 필요한 상황으로 판단되었다. 안정적인 보존처리를 위해 감마선(γ선), X선 비파괴 투과조사, 내시경카메라 관찰을 실시하여 내부 구조와 보존상태를 파악하였고, p-XRF 성분분석, SEM-EDS 성분분석, XRD 분석 등을 활용하여 지자총통의 재질 성분과 표면 오염물 등에 관한 성분분석을 진행하였다. 휴대용현미경 관찰과 정밀 3D스캔으로 지자총통 표면 명문의 상태, 새김형태 등을 확인하였다. 감마선, X선 비파괴 투과조사 결과, 지자총통 내부에 다량의 기포가 관찰되었으며, 육안관찰로 확인되는 표면의 채플릿은 비파괴투과조사 결과로는 확인되지 않았다. p-XRF 성분분석 결과 지자총통은 구리(Cu), 주석(Sn), 납(Pb) 합금으로 만들어진 청동으로 확인되었으며, SEM-EDS를 활용한 표면 이물질 성분분석 결과, 백색이물질은 칼슘(Ca), 황(S), 티타늄(Ti)이 주성분으로 확인되었다. 티타늄은 백색수정액의 주성분인 이산화티타늄(TiO₂)으로 추정되었으며, 적색이물질은 바륨(Ba)이 주성분으로 확인되어 페인트의 체질안료인 황산바륨(BaSO₄)으로 추정되었다. 티타늄과 바륨을 주성분으로 하는 백색과 적색 오염물은 근래에 이르러 표면에 묻은 것으로 추정된다. 황색이물질은 알루미늄(Al), 규소(Si)로 확인되어 토양성분에서 유래한 것으로 추정했다. 백색이물질의 XRD 성분분석결과 황화칼슘(CaS)으로 확인되었고, SEM-EDS와 XRD 성분분석결과로 백색이물질은 석고(CaS)로 확인하였다. 성분분석의 결과를 토대로 표면 이물질 제거, 안정화처리, 강화처리를 진행하였다. 보존처리를 진행하던 중에 휴대용 현미경과 정밀 3D스캔을 통해 알려지지 않았던 명문 우(右), 병(兵), 상(上), 이(二)를 발견하였다. 또한, 명문의 새김방법과 깊이, 너비 등을 측정하였다. 우병상(右兵上)은 창원 합포성 내 위쪽이며, 이(二)는 두 번째 돈대로 파악할 수 있다.