• 한국결정성장학회지
• /
• 제26권4호
• /
• pp.155-158
• /
• 2016

전자소자내의 방열특성은 제품의 신뢰성을 결정하는 우주 중요한 인자중의 하나이다. 본 연구에서는 Al과 graphite 분말을 기계적 합금법(mechanical alloying)을 이용하여 Al/graphite 복합체 분말을 합성하고, 합성된 분말을 열처리한 시편에 대한 물리적 특성을 분석하였다. 열처리가 완료된 Al/graphite 샘플에서 열처리 온도 및 시간이 증가할수록 $Al_4C_3$ 이차상의 비율이 증가함을 확인하였다. 또한 Al/graphite 샘플의 열전도도는 순수 Al 분말 샘플에 비해 현저히 낮았으나, 열처리 온도와 시간에 비례하여 증가하는 것을 확인하였다.

• 한국세라믹학회지
• /
• 제49권4호
• /
• pp.369-374
• /
• 2012

Based on the structure feature of a tree, a cylindrical $Ti_2AlC$/graphite layered composite has been fabricated through heat treating a graphite column and six close-matched thin wall $Ti_2AlC$ cylinders bonded with the $Ti_2AlC$ powders at $1300^{\circ}C$ and low oxygen partial pressure. SEM examination reveals that the bond interlayers between cylinders or that between cylinder and column are not fully dense without any crack formation. During the compressive test, the strain of the $Ti_2AlC$/graphite layered composite is about twice higher than that of the monolithic $Ti_2AlC$ ceramic, and the compressive strength of the layered composite is 348 MPa. The layered composite show the noncatastrophic fracture behaviors due to the debonding and shelling off of the layers, which are different from the monolithic $Ti_2AlC$ ceramic. The mechanism of the improved deformation capacity and noncatastrophic failure modes are attributed to the presence of the central soft graphite column and cracks deflection by the bond interlayers.

• 한국전기전자재료학회논문지
• /
• 제25권6호
• /
• pp.462-466
• /
• 2012

In this paper, heat-releasing composite sheets made of AlN, graphite, Al powder and acryl binder as thermoset were prepared using tape casting method. The crystal structure, morphology, thermal conductivity of heat-releasing composite sheet were measured by using X-ray diffractometer, field emission-scanning electron microscopy and laser flash instrument. It was found thermal conductivity of sheet was decided by solid content, composition including AlN, graphite, Al in heat-releasing composite sheets. As a result, 4.56 W/mK of thermal conductivity could be obtained by using LFA 447.

• 한국주조공학회지
• /
• 제21권2호
• /
• pp.119-126
• /
• 2001

Al/15%Gr. composite have been manufactured by mixing, compacting, and extruding aluminium powder and graphite powder. Then, Al-6%Si/x%Gr., Al-12%Si/x%Gr., and Al-18%Si/x%Gr.(x: 0, 2, 4, 6, 8) composites have been manufactured by remelting the extruded materials(Al/15%Gr.), Al-33.3%Si alloy, and Al ingot, etc. We conducted experiments to chracterize the microstructure, and damping properties and hardness. The result of microstructure experiment on Al-x%Si/y%Gr. composites reveals the good dispersion of graphite. As to Al-Si/y%Gr. composites, the more the graphite contents, the less the tensile strength. And the tensile strength varied according to contents of Si: with its highest value in Al-18%Si/y%Gr. composites and lowest in Al-6%Si/y%Gr. composites. As to Al-x%Si/y%Gr. composites, the more the contents of graphite, the more the vibration damping properties. And we can get the highest vibration damping rate in Al-12%Si/y%Gr. composites which matrix structure is an eutectic component.

• The Korean Journal of Ceramics
• /
• 제3권1호
• /
• pp.47-51
• /
• 1997

The dense sintered bodies of Si/SiC composite with various Si contents could be fabricated by changing the green density in the forming process. The Si/SiC/graphite composites with various graphite contents could be also fabricated by changing a graphite content in the starting composition. Their mechanical and tribological properties were characterized and wear mechanism was also studided. The hardness and strength of the Si/SiC and the Si/SiC/graphite were decreased with increasing the contents of free Si and graphite, respectively. However, the friction coefficient and specific wear rate had no specific relations to their hardness and strength. Adhesion of free Si was a main factor to determine a wear resistance of the Si/SiC composite. In the case of the Si/SiC/graphite, solid lubricationl and liquid reservoir of the graphite particles played the main role of the reduction of the friction force. In the torque test to estimate the possibility of practical of practical applications, the value of torque between the Al2O3 disk and Si/SiC/graphite disk was 1/6 lower compared with two $Al_2O_3$ disks on the basis of 100,000 cycles.

• 한국분말재료학회지
• /
• 제16권3호
• /
• pp.209-216
• /
• 2009

A composite of rapidly solidified Al-6061 alloy powder with graphite particle reinforcements was prepared by ball milling and subsequent hot extrusion. The microstructure and mechanical properties of these composites were investigated as a function of milling time. With increasing milling time, the gas atomized initially and spherical powders became elongated with a maximum aspect ratio after milling for 30 h. Then, refinement and spheroidization were achieved by further milling to 70 h with a homogeneous and fine dispersion of graphite particles forming between the matrix alloy layers. The best compression and wear properties were obtained in the powder milled for 70 h, associated with the increased fine and homogeneous distribution of graphite particles in the aluminum alloy matrix.

• 한국표면공학회지
• /
• 제50권3호
• /
• pp.198-205
• /
• 2017

Thermal dissipation was investigated for poly methyl methacrylate (PMMA) composite films containing graphite and multi wall carbon nanotube(CNT) powders as filler materials. After mixing PMMA with fillers, solvent, and dispersant, the pastes were prepared by passing through a three roll mill for three times. The prepared pastes were coated $15{\sim}40{\mu}m$ thick on a side of 0.4 mm thick aluminium alloy plate and dried for 30 min at $150^{\circ}C$ in an oven. The content of fillers in dried films was varied as 1, 2, and 5 weight % maintaining the ratio of graphite and CNT as 1:1. Raman spectra from three different samples exhibited D, G and 2D peaks, as commonly observed in graphite and multi wall CNT. Among those peaks, D peak was prominent, which manifested the presence of defects in carbon materials. Thermal emissivity values of three samples were measured as 0.916, 0.934, and 0.930 with increasing filler content, which were the highest ever reported for the similar composite films. The thermal conductivities of three films were measured as 0.461, 0.523, and $0.852W/m{\cdot}K$, respectively. After placing bare Al plate and film coated samples over an opening of a polystyrene box maintained for 1 h at $92^{\circ}C$, the temperatures inside and outside of the box were measured. Outside temperatures were lower by $5.4^{\circ}C$ in the case of film coated plates than the bare one, and inside temperatures of the former were lower by $3.6^{\circ}C$ than the latter. It can be interpreted that the PMMA composite film coated Al plates dissipate heat quicker than the bare Al plate.

• 한국분말재료학회지
• /
• 제7권2호
• /
• pp.71-77
• /
• 2000

A process has been successfully used to manufacture 6061/Graphite composite material and the Graphite particles are distributed uniformly within the Al alloy matrix. The 6061 powders was mixed with natural Graphite particles in a ball milling blender and cold compacted specimens were extruded into rods 15mm in diameter at 450$^{\circ}C$. The results showed that tensile properties of the composites with Graphite content have been reduced. The emergence of fine microstructures appeared to be related to the graphite volume. Heat-treated composites were found to possess good mechanical properties as compared with those of non heated composites. A model was used that the tensile strength of the composites would be estimated from the theoretical calculation and experimental data.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2004년도 추계학술발표대회 논문집
• /
• pp.35-38
• /
• 2004

Graphite nanofiber (GNF) and carbon nanotube (CNT) are novel fiber reinforcing materials which have outstanding physical and mechanical properties. Aluminum matrix composites reinforced graphite nanofiber were fabricated by conventional powder metallurgy (PM) method. The composites were prepared through ultrasonication, ball milling, and hot isostatic pressing. A uniform distribution of GNF in aluminum matrix could be obtained. To measure the mechanical properties of GNF-Al composites testings were done in indentation and compression. The compressive strength was enhanced according to reinforcing graphite nanofiber while the hardness was decreased. This study makes the high performance composites for future applications.

• Corrosion Science and Technology
• /
• 제12권1호
• /
• pp.12-26
• /
• 2013

This work focused on galvanic corrosion of carbon steel bolted GECM/Al plates by long-term test in tap water and NaCl solutions. Test product was carbon steel bolted between cross packed GECM and painted aluminium. Tests for the product and coupled parts determined corrosion rate in tap water and NaCl solutions. Also, using a potentiostat and salt water sprayer, galvanic test was done. In galvanic test on carbon steel bolted GECM/Al plates, corrosion of carbon steel bolt was faster in series of tap water>1% NaCl solution>3.5% NaCl solution. In galvanic couple between aluminium and carbon steel bolt, their corrosion rates were higher than those of single specimen. In galvanic couple between GECM, aluminium, and carbon steel bolt, corrosion behaviors of carbon steel bolt and aluminium were changed due to different corrosion mechanism in tap water and chloride solution.