• Korean Journal of Materials Research
• /
• v.7 no.2
• /
• pp.145-151
• /
• 1997

Remelting of $A-Si/SiC_{p}$ composites followed by isothermal holding and solidification, leads ro the settling of Sic particles to the bottom of the mold. With the isothermal holding time for molten $A-Si/SiC_{p}$ composites. the particle free zone increases rapidly up to approximately first 30 minutes of the holding time. Experimental resulls of the particle settling confirm that the larger SIC particles sink faster tlun the sniiller particles. An increase in volume fraction of Sic particles decreases the setrling velocity of the particles.

• The Korean Journal of Ceramics
• /
• v.3 no.1
• /
• pp.47-51
• /
• 1997

The dense sintered bodies of Si/SiC composite with various Si contents could be fabricated by changing the green density in the forming process. The Si/SiC/graphite composites with various graphite contents could be also fabricated by changing a graphite content in the starting composition. Their mechanical and tribological properties were characterized and wear mechanism was also studided. The hardness and strength of the Si/SiC and the Si/SiC/graphite were decreased with increasing the contents of free Si and graphite, respectively. However, the friction coefficient and specific wear rate had no specific relations to their hardness and strength. Adhesion of free Si was a main factor to determine a wear resistance of the Si/SiC composite. In the case of the Si/SiC/graphite, solid lubricationl and liquid reservoir of the graphite particles played the main role of the reduction of the friction force. In the torque test to estimate the possibility of practical of practical applications, the value of torque between the Al2O3 disk and Si/SiC/graphite disk was 1/6 lower compared with two $Al_2O_3$ disks on the basis of 100,000 cycles.

• Journal of Korea Foundry Society
• /
• v.22 no.1
• /
• pp.42-48
• /
• 2002

Effects of coating treatment of metallic Cu, Ni-P film on $SiC_p$, for $SiC_p$/iron aluminide composites were studied. Porous hybrid preforms were fabricated by reactive sintering after mixing the coated $SiC_p$, Fe and Al powders. Then the final composites were manufactured by squeeze casting after pouring AC4C Al alloy melts in preforms. The change of reactive temperature, density, microstructure of the preforms and microstructure of the composites were investigated. The exprimental results were summarized as follows. The thickness of Cu and Ni-P metallic layer formed on $SiC_p$ by electroless plating method were about $0.5{\mu}m$ and coated uniformly. There was no remakable change in the ignition temperature with variation of the mixing ratio of Fe and Al powder while in the case of coated $SiC_p$ it was lower about $20^{\circ}C$ than in the non-coated $SiC_p$. The maximum reaction temperature increased with increasing Al contents, but decreased with increasing $SiC_p$ contents. Expansion ratio of preform after reactive sintering increased with amount of Cu coated $SiC_p$. In the case of Fe-70at.%Al, the expansion ratio was about 7% up to 8wt.% of $SiC_p$, addition but further addition of $SiC_p$, increased the ratio significantly. And in the case of Fe-50 and 60at.%Al, it was about 20% up to 16wt.% of $SiC_p$ addition and about 28% in 24wt.% of $SiC_p$, addition. The microstructures of compounds showed that the grains became finer as amount of $SiC_p$, and mixing ratio of iron powder increased and the shape of compounds was changed gradually from irregular to spheroidal.

• Journal of Korea Foundry Society
• /
• v.18 no.4
• /
• pp.373-382
• /
• 1998

Particulate reinforced aluminum alloys produced by indirect squeeze casting are difficult to shape by cutting or milling. Therefore near net shape forming of complex shapes is of high economic and technical interest. The complex shape products of $SiC_p/6061$ Al composites are fabricated by the melt-stirring and indirect squeeze casting process. The mold temperatures are $200^{\circ}C$ and $300^{\circ}C$ and applied pressures are 70, 100, and 130 MPa. The volume fractions of the reinforcements are in the range of 5 vol% to 15 vol%. The reinforcement dispersion state are observed using on optical microscope. By employing observed results systematically a correlation is demonstrated among the microstructure, particles behavior, mechanical properties and processing parameters for an optimum melt-stirring(compocasting) and indirect squeeze casting process of MMCs. A procedure to establish the optimum squeeze casting of Al-MMCs is proposed.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.18 no.2
• /
• pp.103-111
• /
• 1998

A nondestructive ultrasonic technique is presented for estimating the reinforcement volume fractions of particulate composites. The proposed technique employs a theoretical model which accounts for composite microstructures, together with a measurement of ultrasonic velocity to determine the reinforcement volume fractions. The approach is used for a wide range of SiC particulate reinforced Al matrix ($SiC_p/Al$) composites. The method is considered to be reliable in determining the reinforcement volume fractions. The technique could be adopted in a production unit for the quality assessment of the metal matrix particulate composite extrusions.

• Applied Microscopy
• /
• v.29 no.3
• /
• pp.281-289
• /
• 1999

The stirred and thixoformed $SiC_p/AZ91HP$ Mg composites are studied on the basis of microstructural analysis using transmission electron microscopy (TEM). The products of interfacial reaction are identified as $Mg_2Si$, MgO and $Mg_{17}Al_{12}$ phases and the crystallized phases are found to be orthorhmbic $Al_6Mn$ and decagonal T phases. It is shown that $Mg_2Si$ and $Mg_{17}Al_{12}$ phases are found at the surface of $SiC_p$ and $Al_6Mn$ is found near interface and crystallized on the matrix. Phase identification is carried out by crystallographic work based on primitive cell volume, zero order Laue zone (ZOLZ) patterns and single convergent beam electron diffraction (CBED) patterns containing higher order Laue zone ring from a nanosized region.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.10a
• /
• pp.209.1-209
• /
• 2003

• Journal of Power System Engineering
• /
• v.9 no.4
• /
• pp.130-136
• /
• 2005

The effects of additional Mg content, the size and volume fraction of reinforcement phase on the mechanical properties of ceramic particle reinforced aluminium matrix composites fabricated by pressureless metal infiltration process were investigated. The hardness of $SiC_p/AC8A$ composites increased gradually with an increase in the additive Mg content, while the bending strength of $SiC_p/AC8A$ composites increased with an increase in additive Mg content up to 5%. However, this decreased when the level of additive Mg content was greater than 5% due to the formation of coarse precipitates by excessive Mg reaction and an increase in the porosity level. The hardness and strength of the composites increased with decreasing the size of SiC particle. It was found that the composites with smaller particles enhanced the interfacial bonding than those with bigger particles from fractography of the composites. The hardness of $Al_2O_{3p}/AC8A$ composites increased gradually with an increase in the volume fraction, however, the bending strength of $Al_2O_{3p}/AC8A$ composites decreased when the volume fraction of alumina particle was greater than 40% owing to the high porosity level.

• Proceedings of the KIEE Conference
• /
• 2002.11a
• /
• pp.106-108
• /
• 2002

The composites were fabricated 61vol.% $\beta-SiC$ and 39vol.% $TiB_2$ powders with the liquid forming additives of l2wt% $Al_2O_3+Y_2O_3$ by pressureless annealing at $1700^{\circ}C,\;1750^{\circ}C,\;1800^{\circ}C$ for 4 hours respectively. The result of Phase analysis of composites by XRD revealed $\alpha-SiC$(6H), $TiB_2$, and YAG($Al_5Y_3O_{12}$) crystal phase. The relative density and the Young's modulus showed the highest value of 92.9701% and 92.884Gpa for composites by pressureless annealing temperature $1700^{\circ}C$ at room temperature.

• Korean Journal of Materials Research
• /
• v.10 no.12
• /
• pp.793-798
• /
• 2000

The age-hardening behavior of unreinforced 6061 Al alloy and SiCp/6061 Al alloy composites reinforced with different size of SiC particle (average diameter ; 0.7$\mu\textrm{m}$ and 7.0$\mu\textrm{m}$) was investigated by hardness measurement, calorimetric technique and transmission electron microscopy. At 17$0^{\circ}C$ isothermal aging treatment, the peak aging time of 0.7$\mu\textrm{m}$SiCp/6061Al alloy composite and 7.0$\mu\textrm{m}$SiCp/6061Al alloy composite is shorter than that of unreinforced 6061Al alloy, and the aging of 7.0$\mu\textrm{m}$SiCp/6061Al alloy composite is accelerated more than that of 0.7$\mu\textrm{m}$SiCp/6061Al alloy composite. This acceleration is due to the increase of dislocation density by the compositeness with SiCp and the SiC particle size. In the peak aged condition, the major strengthening phase of these materials is intermediate $\beta$ phase(Mg$_2$Si), and the activation energy for the formation of $\beta$ phase is considerably decreased by the compositeness with SiCp and the increasing of SiC Particle site.