• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.480-483
• /
• 2001

Epitaxial rutile-TiO$_2$ and anatase-TiO$_2$ films were grown at 80$0^{\circ}C$ on $Al_2$O$_3$ (1102) and LaAlO$_3$ (001), respectively, using pulsed laser deposition. The formation of different phases on different substrates could be qualitatively explained by the atomic arrangements at the interfaces. We also successfully deposited epitaxial rutile-TiO$_2$ and anatase-TiO$_2$ films on conductive RuO$_2$ and La$_{0.5}$Sr$_{0.5}$CoO$_3$ electrodes, respectively Using a Kelvin probe, we measured the photovoltaic properties of these multilayer structures. A rutile-TiO$_2$ film grown on RuO$_2$ showed a very broad peak in the visible light region. An epitaxial anatase-TiO$_2$ film grown on La$_{0.5}$Sr$_{0.5}$CoO$_3$ showed a strong peak with a threshold energy of 3.05 eV 3.05 eV

• Journal of the Korean Ceramic Society
• /
• v.39 no.5
• /
• pp.438-445
• /
• 2002

In this study, the glass frit of $PbO-TiO-2-SiO_2-BaO-ZnO-Al_2O-3-CaO-B_2O_3-Bi_2O_3-MgO$ system was manufactured. The glass was melted at $1,400{\circ}C$, quenched and attrition-milled. The glass frit powder was pressed and fired for 2h at the range of $750~1,000{\circ}C$. The crystallization of glass frit began at about $750{\circ}$ and at low temperature, the main crystal phases were hexagonal celsian($BaAl_2Si_2O_8$) and alumina. As the firing temperature increased, the crystal phases of monoclinic celsian, zinc aluminate, zinc silicate, calcium titanium silicate and titania appeared. And the increase of firing temperature led to transformation of hexagonal celsian to monoclinic. The only glass frit containing 15wt% PbO had the crystal phase of solid solution of $PbTiO_3-CaTiO_3$. At the frequency of 1 MHz, the dielectric constant of glass frit crystallized was in the range of 11~16 and the dielectric loss less than 0.020. But the glass frit containing 15wt% PbO had the dielectric constant of 17~26 and loss of 0.010~0.015 because of crystal phase of solid solution of $PbTiO_3-CaTiO_3$.

• Journal of the Mineralogical Society of Korea
• /
• v.2 no.1
• /
• pp.8-10
• /
• 1989

Sphene from the McDonald pegmatite near Bancroft, Ontario, Canada was analyzed using EPMA. It contains 4.3 to 6.3 weight percent of Nb2O5 with an average formula Ca1.02(Ti0.62Al0.22Nb0.07Fe0.06Ta0.01)Si0.99(O4.85F0.16). Three types of subtitutions are possible; 1)2Ti4+=(Nb, Ta)5+ + (Al, Fe3+), 2) Ti + O = (Al, Fe3+) + (F, OH), and 3) 2Ti + O = Fe2+ + (Nb, Ta)5+ + (F, OH). T재 different schemes of substitutions for balancing the analysis are considered when the iron is either all ferric or all ferrous. Assuming stoichiometry fo Ca and Si, a general formula derived from the two different schemes is Ca(Ti0.64Al0.22Fe3+0.06-X {{{{Fe_{x}^{2+} }} Nb0.01)Sio4.80-XF0.16(OH)0.04+x.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.57 no.5
• /
• pp.808-815
• /
• 2008

The composites were fabricated 61[vol.%] ${\beta}$-SiC and 39[vol.%] $TiB_2$ powders with the liquid forming additives of 8, 12, 16[wt%] $Al_2O_3+Y_2O_3$ as a sintering aid by pressureless annealing at 1650[$^{\circ}C$] for 4 hours. The present study investigated the influence of the content of $Al_2O_3+Y_2O_3$ sintering additives on the microstructure, mechanical and electrical properties of the pressureless annealed SiC-$TiB_2$ electroconductive ceramic composites. Reactions between SiC and transition metal $TiB_2$ were not observed in the microstructure and the phase analysis of the pressureless annealed SiC-$TiB_2$ electroconductive ceramic composites. Phase analysis of SiC-$TiB_2$ composites by XRD revealed mostly of ${\alpha}$-SiC(6H), ${\beta}$-SiC(3C), $TiB_2$, and In Situ YAG($Al_2Y_3O_{12}$). The relative density of SiC-$TiB_2$ composites was lowered due to gaseous products of the result of reaction between SiC and $Al_2O_3+Y_2O_3$. There is another reason which pressureless annealed temperature 1650[$^{\circ}C$] is lower $300{\sim}450[^{\circ}C]$ than applied pressure sintering temperature $1950{\sim}2100[^{\circ}C]$. The relative density, the flexural strength, the Young's modulus and the Vicker's hardness showed the highest value of 82.29[%], 189.5[Mpa], 54.60[Gpa] and 2.84[Gpa] for SiC-$TiB_2$ composites added with 16[wt%] $Al_2O_3+Y_2O_3$ additives at room temperature. Abnormal grain growth takes place during phase transformation from ${\beta}$-SiC into ${\alpha}$-SiC was correlated with In Situ YAG phase by reaction between $Al_2O_3$ and $Y_2O_3$ additive during sintering. The electrical resistivity showed the lowest value of 0.0117[${\Omega}{\cdot}cm$] for 16[wt%] $Al_2O_3+Y_2O_3$ additives at 25[$^{\circ}C$]. The electrical resistivity was all negative temperature coefficient resistance (NTCR) in the temperature ranges from $25^{\circ}C$ to 700[$^{\circ}C$]. The resistance temperature coefficient of composite showed the lowest value of $-2.3{\times}10^{-3}[^{\circ}C]^{-1}$ for 16[wt%] additives in the temperature ranges from 25[$^{\circ}C$] to 100[$^{\circ}C$].

• Journal of Environmental Science International
• /
• v.32 no.5
• /
• pp.385-394
• /
• 2023

There is a need for a method that can effectively remove wastewater containing small-sized particles such as TiO₂. In this study, we attempted to remove TiO₂ wastewater using electrocoagulation-electroflotation two-step separation. The TiO₂ wastewater was effectively removed via batch electrocoagulation-electroflotation separation. However, in the batch process, the simultaneous operation of electrocoagulation and electoflotation was challenging due to the high residual turbidity. In the continuous operation, electrocoagulation and electoflotation reactors were kept separate. The turbidity removal in continuous operation was similar to that in the batch process, nevertheless, the residual Al concentration was high, leading to the conclusion that counterterm ensures against residual Al were necessary.

• Korean Journal of Metals and Materials
• /
• v.50 no.4
• /
• pp.310-315
• /
• 2012

Nano-powders of 1.5TiAl and $Al_2O_3$ were synthesized from $1.5TiO_2$ and 3Al powders by high energy ball milling. Nanocrystalline $Al_2O_3$ reinforced composite was consolidated by pulsed current activated sintering within 2 minutes from mechanochemically synthesized powders of $Al_2O_3$ and 1.5TiAl. The relative density of the composite was 99.5%. The average hardness and fracture toughness values obtained were $1250kg/mm^2$ and $10MPa{\cdot}m^{1/2}$, respectively.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.148-149
• /
• 2012

As one of zero-expansion coefficient materials $Al_2TiO_5$ ceramics was prepared and the thermal shock-resistance was investigated by using DV-X analysis. In this report the mechanism of thermal shock-resistance and low mechanical strength.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.163-164
• /
• 2006

A QM-ISP-4 Planetary Mill was employed to activate mechanically the mixtures of anatase and corundum at room temperature for different times. The milled powder mixtures were then sintered at $1300^{\circ}C$ for 1 h. The XRD results showed that the milled powder mixtures were completely transformed into $Al_2TiO_5$ after sintering, except the mixtures milled for 5 and 10 hours. The SEM observations showed the typical morphology of rod-like $Al_2TiO_5$ vary in the range: widths from 0.6 to $1.2\;{\mu}m$, and lengths from 3.0 to $6.0\;{\mu}m$. The rod-like $Al_2TiO_5$ formation was attributed to the positive effects caused by the mechanical activation.

• Applied Chemistry for Engineering
• /
• v.7 no.6
• /
• pp.1192-1203
• /
• 1996

$Al_2O_3-TiO_2$ composite oxide adsorbents which could be applied in high-temperature water were prepared by hydrolysis of aluminum and titanium alkoxide. The prepared adsorbents were calcined at $600{\sim}1400^{\circ}C$ and in order to investigate the various properties - the transition of crystals, thermal properties, and specific surface area, X-ray diffractometry, thermal analysis, FT-IR, SEM and BET method were employed. And the $Co^{2+}$ adsorption characteristics of these adsorbents in high-temperature water were investigated by batch adsorption experiment in a stirred autoclave. Since the adsorption of $Co^{2+}$ on the $Al_2O_3-TiO_2$ adsorbents was irreversible endothermic in the temperature range of $150{\sim}250^{\circ}C$, the standard enthalpy changes of 26, 43, and 80 mol% of $TiO_2$ on $Al_2O_3$ were in the range of $16.5{\sim}26.0kJ{\cdot}mol^{-1}$. The adsorbent of 26 mol% of $TiO_2$ on $Al_2O_3$ which was calcined at $600^{\circ}C$ for 2 hours showed the adsorption amount of $0.1674meq{\cdot}g^{-1}$ in the high temperature water at $250^{\circ}C$.

• Journal of the Korean institute of surface engineering
• /
• v.25 no.5
• /
• pp.253-261
• /
• 1992

Ti-Al intermetallic compounds which can be used in gas turbine at elevated temperature were inves-tigated in order to improve oxidation resistance by the formation of protective oxide scale. Four Ti-Al alloys were prepared by plasma arc melting. As the amount of Al was increased among the alloys, oxida-tion resistance was improved by the formation of relatively purer Al2O3 layer. However, the alloys which have less amount of Al formed a duplex layer of Al2O3 and TiO2. When samples were oxidized in pure oxygen instead of air, oxidation resistance was improved because of formation of the purer Al2O3 layer.