The application field of porous mold is more and more expended. A mixture of alumina and cast iron is used for making porous mold using slip and vacuum casting method in this study. Slip casting is a process that slurry is poured into silicon rubber mold, dried in vacuum oven, debinded and sintered in furnace, In this procedure, slurry is composed of powder, binder, dispersion agent, and water. Vacuum casting is a technique for removing air bubbles existed in the slurry under vacuum condition. Since ceramics has a tendency of over-shrinkage after sintering, cast iron is used to compensate dimensional change. The results shows that sintering temperature has a great effect on characteristics of alumina-cast iron composite sintered parts. Finally ceramic-metal composite sintered mold can be used for aluminum alloy casting of shoe mold using this process.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1099-1100
• /
• 2006

The mechanical properties of ceramics materials can be tailored by designing their microstructures. We have reported that development of texture can be controlled by slip casting in a strong magnetic field followed by heating even for diamagnetic ceramics such as alumina. A strong magnetic field of 12T was applied to the suspension indcuding alumina powder to rotate each particle during slip casting. The sintering was conducted at the desired temperature in air without a magnetic field. C-axis of alumina was parallel to the magnetic field. Bending strength of textured alumina depended on the direction of oriented microstructure.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2004.10a
• /
• pp.234-237
• /
• 2004

As an automotive industry's demand for lighter materials gets bigger and bigger, a lot of new strength Al alloys have been developed recently. In the present study, Al 6xxx series alloys were designed to get the strength level of 350MPa with the elongation of $12\%$. For that purpose, three alloy systems were selected based on the thermodynamics calculation. The effect of both $Mg_{2}Si$ precipitate and excess Si amount on the newly designed alloys was investigated. Also, heat treatment procedure was studied to optimize the mechanical properties.