• Fire Science and Engineering
• /
• v.22 no.2
• /
• pp.44-48
• /
• 2008

In this paper, we measured a contact angle, surface resistivity and XPS to study the thermal aging characteristics of the epoxy resin for cast resin transformer. As a result of this experiment, we found that the contact angle increases up to $200^{\circ}C$ as it causes a re-crosslinking on the surface, but starts decreasing at $250^{\circ}C$ as it causes heat condensation. As a result of examining the oxygen/carbon peaks through the XPS analysis, we obtained a higher oxygen peak vs. carbon in the first untreated sample, but it showed the opposite trend after heat treatment. That rise in the carbon peak continued up to $200^{\circ}C$, but decreased again at the temperatures above. That's because it kept forming a stable surface structure up to $200^{\circ}C$ but its carbon combination got destroyed due to a rapid oxidization at $250^{\circ}C$. And a conduction path was formed easily with the hydrophile property caused by rapid surface activation.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.3
• /
• pp.280-286
• /
• 2006

As a way to expand electric capacity in conductor with electric power demand, STACIR/AW (Super Thermal-resistant Aluminum-alloy Conductors Aluminum-clad Invar-Reinforced) conductor which has high electric current and heat resistance characteristics have been developed. STACIR/AW power line is mechanical composite wire composed of steel cores for dip control and aluminum conductors for sending electric current. Recently, to ensure stable operation and prediction of wire life span of STACIR/AW conductor, a heat property of STACIR/AW conductor have been investigated. In the present work, a change of essential property with long term-heat exposure of STACIR/AW conductor and its structure material, INVAR wire and Al conductor, have been investigated. INVAR/AW is approximately $3.2\;{\mu}m/m^{\circ}C$. thermal expansion coefficient of INVAR/AW wire increases with time of heat exposure. the thermal expansion coefficient of INVAR/AW is markedly influenced by heat and mechanical treatment. creep rate(0.242) of STACIR/AW $410\;mm^2$ conductor at room temperature is much higher than that(0.022) at $210\;^{\circ}C$ STACIR/AW $410\;mm^2$ conductor has minimum creep rate at operating temperature. To lower creep rate with increase temperature is more unique characteristics in STACIR/AW. It is expected that STACIR/AW turned its tension to INVAR/AW at the transition temperature. at room temperature, the tension apportionment of INVAR/AW in STACIR/AW is about $50\;\%$. but whole tension of STACIR/AW is placed on the INVAR/AW alone of core metal above transition temperature.

• Journal of Physiology & Pathology in Korean Medicine
• /
• v.17 no.3
• /
• pp.791-797
• /
• 2003

This study investigated the effect of Yanggyuksanhwa-tang on cerebral ischemia of the rats. Considering age-related impact on cerebral ischemia, aged rats (18 months old) were used for this study. Ischemic damage was induced by the transient occlusion of bilateral common carotid arteries (BCAO) under the hypotension. Yanggyuksanhwa-tang was administered twice orally. Then changes of pyramidal neurons and heat shock protein 72 (HSP72) expressions in ischemic damaged hippocampus were of observed. The BCAO in aged rats led significant decrease of pyramidal neurons in CA1 hippocampus. While the treatment of Yanggyuksanhwa-tang significantly attenuated the reduction of pyramidal neurons in CA1 hippocampus following BCAO ischemia. The BCAO in aged rats led significant increase of HSP72 expression in CA1 and mild in CA3 hippocampus. While the treatment of Yanggyuksanhwa-tang significantly attenuated the increase of HSP72 expression in CA1 hippocampus following BCAO ischemia. The extent of HSP72 expression in CA2 and DG of hippocampus was not different between the sham operated group, the BCAO ischemia control group, and the group of Yanggyuksanhwa-tang administration after BCAO ischemia. The treatment of Yanggyuksanhwa-tang significantly attenuated the increase of normalized optical density depending on HSP72 expression in CA1 hippocampus following BCAO ischemia.

• Journal of the Korean Applied Science and Technology
• /
• v.22 no.4
• /
• pp.306-314
• /
• 2005

In this study, spherical $pre-BaTiO_3$ particles are prepared by gelation and aging process in autoclave without catalysts. The (Ba-Ti) gel used as a starting material was prepared by aging mixtures of titanyl acylate with barium acetate aqueous solution([glacial acetic acid (AcOH)]/[titanium isopropoxide (TIP)] 4, [barium acetate]/[TIP] 1) at $45^{\circ}C$ for 48hrs. XRD and SEM results for the (Ba-Ti) gel sample at aging process showed that the gel was formed via aggregation of the fine particles. It seems to be the primary particles of bulk (Ba-Ti) gel amorphous, but the spatial arrangement of barium and titanium in the (Ba-Ti) gel is similar to that in crystalline $BaTiO_3$ particles. From XRD and FT-IR. spectroscopy analysis it was found that the crystal structure of the prepared particles continuously transformed from amorphous to tetragonal as the calcination temperature increased, and crystallized spherical cubic and tetragonal $BaTiO_3$ powder obtained at the very low calcination temperature between $500^{\circ}C$ and $900^{\circ}C$ after 1hrs of heat treatment respectively. According to BET analysis result, final particle have pore structure of ink bottle shape which is produced by aggregation of fine spherical particles with surface area of $280m^2/g$ and average pore size of 130nm.

• Journal of Welding and Joining
• /
• v.22 no.2
• /
• pp.59-68
• /
• 2004

Plasma transferred arc welding (PTAW) has been taken into consideration for repairing Ni-based superalloy components used gas turbine blades. Various cracks has been generally reported to be found in the base metal heat affected zone(HAZ) along grain boundary. Thus, hot cracking susceptibility of Ni-based superalloys was evaluated according to heat treatments. Hot ductility test was conducted on specimens with solution treated at 112$0^{\circ}C$ for 2 hours and aging treated at 845$^{\circ}C$ for 24hours after solution treatment. The results of the hot ductility test appeared that solution treated specimens were the highest ductility recovery rate among three conditions. The loss of ductility at high temperature in Ni-based superalloy was mainly controlled by the degree of pain boundary wetting due to constitutional liquation of MC carbide precipitates. Meanwhile, the highest ductility recovery rate in solution-treated alloys seems to be lack of M23C6, which can be dissolved during heating and then result in the local enrichment of Cr in the vicinity of the grain boundary.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.10 no.5
• /
• pp.625-634
• /
• 1986

The strain distribution on a welded aluminum alloy transition joint produced by a static tensile load has been measured using a moire method combined with photoelastic coating method. The test specimens were made of aluminum alloy 6061-T6 and 2014-T6 butt welded with ER-4043 filler metal, and were post welded heat treated (solid solution heat treatment 502.deg. C 70min.) and precipitated (artificial aging 171.deg. C 600min.) to cause an abrupt change of mechanical properties between the base metals and weld metal. The photoelastic epoxy rubber was cemented on the specimen grating which had been reproduced on the specimen surface by using an electropolishing. The measurements were compared with strains computed by Finite Element Analysis. The following results were abtained. (1) The maximum strain were distributed along the center line in the transverse directiion of the weld metal. (2) The strain gradient along the fusion line increased approaching the V-groove tip and the maximum value was observed at a quarter of width from the V-groove tip. (3) The moire method combined with photoelastic coating was proved very useful for real time strain measurement in the welded aluminum alloy transition joint.

• Journal of the Korean Society of Fashion and Beauty
• /
• v.2 no.1 s.1
• /
• pp.5-13
• /
• 2004

This study was analyzed on relationship of blood vessel pressure massage and skin and management method on blood vessel pressure for skin care with Yin-yang 5 factors theory, Yin-yang 5 factors theory of blood vessel pressure massage with related Korean medicine is essential for descriptions of the physiology of human body and disease. Six elements(wind, heat, fire, dryness, wetness, and cold) and seven emotions(anger, happiness, thought, worry, sadness, surprise, and fear) effected on skin care and the five viscera and the six stomach. Blood vessel pressure massage related with skin consists of the five viscera and the six stomach and is improved blood circulation and is retarded aging of skin by controls of hormone and free nerve system. Blood vessel pressure massage for skin care improved in the intestine system and blood circulation and got healthy. The blood vessel pressure massage treatment of beauty art can aid the function of bio-rhythm of a human body and make our body health by healing the problems of the five viscera organs and the six stomach. It also help circulate of the blood flow and vigor. The study expects the related researches to improve the various treatments through this treatment. The researcher encountered many problems with the lack of concerned materials and former studies but expects this study to be a study to retard aging the skin and prevent the diseases through the study of the blood vessel pressure massage.

• Journal of the Microelectronics and Packaging Society
• /
• v.18 no.2
• /
• pp.49-55
• /
• 2011

The failure of electronic instruments is mostly caused by heat and shock. This shock causes the crack initiation at the solder joint interface of PCB component which is closely related with the formation of intermetallic compound(IMC). The Ag content in Pb-free Sn-xAg-0.5Cu solder alloy used in this study was 1.0, 1.2 and 3.0 wt.%, respectively. After soldering with PCB component, isothermal aging was performed to 1000 hrs. The growth of IMC layer was observed during isothermal aging. The drop impact property of solder joint was evaluated by impact bending test method. The solder joint made with the solder containing lower Ag content showed better impact bending property compared with that with higher Ag content. On the contrary to this result, the solder joint made with solder containing higher Ag content showed better impact bending property after aging. It should be caused by the formation of fine $Ag_3Sn$, which relieved the impact. It showed consequently the different effect of fine $Ag_3Sn$ and coarse $Cu_6Sn_5$ particles formed in the IMC layer on the impact bending property.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2002.05a
• /
• pp.155-158
• /
• 2002

Fabrication process of metal/intermetallic laminated composites by using self-propagating high temperature synthesis(SHS) reactions between Ni and Al elemental metal foils have been investigated. Al foils were sandwiched between Ni foils and heated in a vacuum hot press to the melting point of aluminium. SHS reaction kinetics was thermodynamically analyzed through the final volume fraction of the unreacted Al related with the initial thickness ratio of Ni:Al and diffusion bonding stage before SHS reaction. Thermal aging of laminated composites resulted in the formation of functionally gradient series of intermetallic phases. Microstructure showed that the main phases of intermetallics were NiAl and $Ni_3Al$ having higher strength at room and high temperatures. The volume fractions of intermetallic phases were measured as 82.4, 58.6, 38.4% in 1:1, 2:1, 4:1 initial thickness ratio of Ni:Al.

• Journal of Mechanical Science and Technology
• /
• v.18 no.8
• /
• pp.1368-1374
• /
• 2004

The remaining life estimation for the aged components in power plants as well as chemical plants are very important because mechanical properties of the components are degraded with in-service exposure time in high temperatures. Since it is difficult to take specimens from the operating components to evaluate mechanical properties of components, nondestructive techniques are needed to evaluate the degradation. In this study, test materials with several different degradation levels were prepared by isothermal aging heat treatment at $630^{\circ}C$. The DC potential drop method and destructive methods such as tensile and fracture toughness were used in order to evaluate the degradation of 1Cr-1Mo-0.25V steels. In this result, we can see that tensile strength and fracture toughness can be calculated from resistivity and it is possible to evaluate material degradation using DC potential drop method, non-destructive method.