• Korean Journal of Materials Research
• /
• v.15 no.11
• /
• pp.722-729
• /
• 2005

The electrical and dielectric stability of zinc oxide-based varistors were investigated with the cobalt oxide contents in the range of $0.5\~5.0 mo\l%$. As cobalt oxide contents increased, the ceramic density increased in the range of $5.25\~5.55g/cm^3$ and the varistor voltage decreased in the range of $235.3\~86.0V$. The varistor with on addition of cobalt oxide $1.0 mol\%$ exhibited good nonlinearity. in which the nonlinear exponent is 66.6 and the leakage current is $1.2{\mu}A$. Furthermore, the varistors exhibited the highest electrical and dielectric stability, with $\%{\Delta}V_{1mA}=-1.9\%,\;\%{\Delta}{\alpha}=-10.5\%,\;\%{\Delta}I_L=+275.0\%,\;and\;\%{\Delta}tna{\delta}=+55.6\%$, under DC accelerated aging $0.95V_{1mA}/150^{\circ}C/24h$.

• Korean Journal of Materials Research
• /
• v.14 no.10
• /
• pp.713-718
• /
• 2004

To study the dynamic strain aging behavior of Zr-0.4Sn-1.5Nb-0.2Fe sample tube for nuclear fuel cladding in the range of pressurized water reactor (PWR) operation temperature, the tensile tests of the tube specimens, which had been finally heat-treated at $470^{\circ}C\;and\;510^{\circ}C$, had been carried out with the strain rate $1.67{\times}10^{-2}/s\;and\;8.33{\times}10^{-5}/s$ at the various temperatures from room temperature to $500^{\circ}C$. It was observed that the elongation of the specimens got shortened as the temperature increased from $200^{\circ}C\;to\;340^{\circ}C$. The specimens that were finally heat-treated at $470^{\circ}C$ showed a plateau more remarkably on the plot of yield strength-temperature than those heat-treated at $510^{\circ}C$. In the range of $310\sim400^{\circ}C$, the strain rate sensitivity of the specimens finally heat-treated at $510^{\circ}C$ was $30.4\%\sim33.7\%$ lower but the work hardening exponent index of the specimens was a little higher than that without dynamic strain aging effect.

• Journal of Mechanical Science and Technology
• /
• v.16 no.9
• /
• pp.1084-1092
• /
• 2002

The frequency dependency of Rayleigh surface wave is investigated indirectly by measuring the angular dependency of the backward radiation of the incident ultrasonic wave in two kinds of degraded specimens by scuffing or corrosion. Then, the frequency dependency is compared with the residual stress distribution or the corrosion-fatigue characteristics for the scuffed or corroded specimens, respectively. The width of the backward radiation profile increases with the increase of the variation in residual stress distribution for the scuffed specimens. In the corroded specimens, the profile width decreases with the increase of the effective aging layer thickness and is inversely proportional to the exponent, m, in the Paris' law that can predict the crack size increase due to fatigue. The result observed in this study demonstrates high potential of backward radiated ultrasound as a tool for nondestructive evaluation of subsurface gradient of material degradation generated by scuffing or corrosion.

• Atmosphere
• /
• v.17 no.4
• /
• pp.407-420
• /
• 2007

Optical characteristics of aerosols in Seoul are investigated from the measurements of sky radiance by Skyradiometer at Yonsei University from December 2005 to November 2006. Aerosol optical depth (AOD) shows a maximum in June due to weak ventilation and particle growth by aging process and hygroscopic effect. Single scattering albedo (SSA) and Angstrom Exponent (AE) show the lowest value in spring due to the Asian dust. It is clear that coarse mode is dominant in spring and fine mode is dominant in summer from the volume size distribution measured in this study. The explanations on the changes of aerosol loadings are provided through the correlation between AOD and AE, while the pattern of wavelength dependency related to particle size is shown through the correlation between SSA and AE. Backward trajectory analysis by HYSPLIT provides information about origin of aerosol, which allows us to classify the case according to the source region and the path distance. Although the direction of backward trajectory traces back mostly to west, coarse mode particle is dominant in the case of long pathway and fine mode particle is dominant in the case of short pathway. This discrepancy is caused by the regional difference of emitted particles.

• Journal of the Korean Ceramic Society
• /
• v.40 no.11
• /
• pp.1067-1072
• /
• 2003

The electrical stability of the varistor ceramics composed of Zn-Pr-Co-Cr-Dy oxides-based varistors was investigated at 0.0∼2.0 mol% Dy$_2$O$_3$ content under DC accelerated aging stress. The ceramic density was increased up to 0.5 mol% Dy$_2$O$_3$ whereas further addition of Dy$_2$O$_3$ decreased sintered ceramic density. The density sailently affected the stability due to the variation of conduction path. The nonlinearity of varistor ceramics was greatly improved above 45 in the nonlinear exponent and below nearly 1.0 ${\mu}$A by incorporating Dy$_2$O$_3$. Under 0.95 V$\_$1mA/150$^{\circ}C$/24 h stress state, the varistor ceramics doped with 0.5 mol% Dy$_2$O$_3$ exhibited the highest electrical stability, in which the variation rates of varistor voltage, nonlinear exponent, and leakage current were -0.9%, -14.4%, and +483.3%, respectively. The variation rates of relative permittivity and dissipation factor were +7.1% and +315.4%, respectively. The varistors with further addition of Dy$_2$O$_3$ exhibited very unstable state resulting in the thermal runaway due to low density.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.1
• /
• pp.50-56
• /
• 2005

The electrical properties, clamping voltage characteristics, and stability of dysprosia-doped ZnO-P $r_{6}$ $O_{11}$-based varistors were investigated with different dysprosia contents from 0 to 2.0 mol%. The incorporation of dysprosia in varistor ceramics greatly increased the varistor voltage from 50 to 481.0 V/mm. It was found that the dysprosia is good additive improving a nonlinearity, in which the nonlinear exponent is above or near 50, and the leakage current is below 1.0 $\mu$A. The dysprosia-doped varistors exhibited superior clamping voltage characetristics, in which clamping voltage ratio is above or neat 2 at surge current of 50 A. The 0.5 mol% dysprosia-doped varistors only exhibited high stability, with the rate of varistor voltage of -0.9%, under DC acceleraetd aging stress, 0.95 $V_{lmA}$/15$0^{\circ}C$/24 h.h.h.h.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.20 no.5
• /
• pp.397-401
• /
• 2000

The corrosion-fatigue characteristics of the 12Cr steel, which is widely used in fossil power plants as a turbine blade material, are evaluated nondestructively by use of the Rayleigh surface wave. In this study, the frequency dependency of the Rayleigh surface wave is investigated indirectly by measuring the angular dependency of the backward radiation of the incident ultrasonic wave in the aged specimens, and then compared to the corrosion-fatigue characteristics. The width of the backward radiation profile decreases as the increase of the aging temperature, which seems to result from the increase of the effective degrading layer thickness. This parameter also shows an inversely proportionality to the exponent, m, in the Paris law which predicts the crack size increasement due to fatigue. The result observed in this study demonstrates high potential of the backward radiated ultrasound as a tool for the nondestructive evaluation of the corrosion-fatigue characteristics of the aged materials.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.3
• /
• pp.136-142
• /
• 2019

Nuclear power plant concrete structures are in contact with the coast, and durability due to chloride attack is very important because it is used as cooling water by taking seawater. For this purpose, a 3-year long-term saltwater immersion test was carried out to evaluate chloride ion diffusion coefficient and age apponent (m) The m values of the foundation with 4,000 class was 0.35 ~ 0.39, similar to KCI or ACI suggested values. essential service water constructions and tunnels of 5,000 class were 0.44 ~ 0.53 and 6,000 class, and 0.62 of reactor containment buildings were similar to the proposed values of FIB. As a result of the prediction of the service life with the measured age coefficient, all the safety related concrete structures of the nuclear power plants satisfied the service life of more than 60 years.