• Journal of the Korean Society for Heat Treatment
• /
• v.4 no.1
• /
• pp.30-36
• /
• 1991

Effects of aging treatment on the mechanical properties of a 18 Ni maraging steel were investigated by considering the reverted austenite. Specimens were heat treated by austenitizing at $840^{\circ}C$ for 1 hr and then aged for various times at $480^{\circ}C$ and $520^{\circ}C$. The main results obtained are as follows : 1) The amounts of reverted austenite are increased up to about 4% at $480^{\circ}C$ and about 22% at $520^{\circ}C$ with 1 to 48 hrs aging time. 2) Decreasing tendencies of impact energy and fracture toughness with increasing aging time are diminished after aging for 2 hrs at two aging temperatures of $480^{\circ}C$ and $520^{\circ}C$. 3) Peak hardness and yield strength are obtained after aging for 4 hrs at $480^{\circ}C$ and 2 hrs at $520^{\circ}C$ respectively. From the above results, it was concluded that the optimum aging condition with which showed good strength and toughness combination are given to be $480^{\circ}C$ for 4 hrs and $520^{\circ}C$ for 2 hrs.

• Korean Journal of Metals and Materials
• /
• v.48 no.1
• /
• pp.19-27
• /
• 2010

This paper investigates the influence of aging time on creep properties via a small punch creep test and evaluates the microstructural change of P122 steel at $600^{\circ}C$. The area fraction of precipitates was quantitatively analyzed to identify the relationship between the creep rupture life and precipitates was coarsening behavior of precipitates along the grain boundaries was also investigated for various aging times. It is found that this coarsening behavior led to a loss of solution hardening and rewulte in a hardness drop and a reduction of creep life.

• Journal of Dental Anesthesia and Pain Medicine
• /
• v.20 no.4
• /
• pp.241-250
• /
• 2020

Background: Placement of full-coverage restorations such as stainless steel crowns (SSCs) for pulpectomy treated primary molars is essential for successful outcomes. The tooth preparation process for SSCs can cause discomfort to gingival tissues since the crown should be seated 1 mm subgingivally. The purpose of this prospective trial was to compare the effectiveness of subgingival and transmucosal application of topical anesthetics on dental pain during SSC tooth preparation among 6- to 8-year-old children. Methods: A consecutive sample of 27 children, aged 6-8 years, who required an SSC after pulp therapy in primary molars were randomly divided into three groups. Group A received infiltration anesthesia before tooth preparation for SSC placement, whereas in Group B and C, only topical anesthesia was applied subgingivally and transmucosally. Wong-Bakers Faces pain rating scale (WBFPS) scores were recorded after tooth preparation. Faces, Legs, Activity, Cry and Consolability (FLACC) scores were evaluated by two blinded and calibrated investigators through video recordings of the patient during tooth preparation. Data were tabulated, and inter-group comparisons were performed using the Kruskal-Wallis and analysis of variance tests. Results: Out of the 27 participants, 48% were boys and 52% were girls, with an overall mean age of 6.83 years. Group A showed the least pain scores according to both the scales, followed by Group B and Group C. The pain intensity was statistically significant on both the pain scales with P = 0.003 for FLACC and P < 0.001 for WBFPS. Conclusion: Subgingival application of topical anesthesia reduced pain to a certain extent but not as effectively as infiltration anesthesia during SSC tooth preparation in primary molars. Transmucosal application of topical anesthesia did not reduce discomfort when compared to the other two interventions.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.23 no.11 s.170
• /
• pp.2014-2021
• /
• 1999

The present investigation is concerned with the degradation characteristics of cast stainless steel(CF8M), exposed to the $\sigma$-phase degradation at $700^{\circ}C$. In the present paper, the degradation of CF8 M at $700^{\circ}C$ is evaluated by a non-destructive test, DL-EPR(double loop electrochemical potentiokinetic reactivation). The surface of specimens is observed by using scanning electron microscopy after DL-EPR test. Also. chromium contents of matrix, grain boundary and ferrite phase are analyzed by electron probe X-ray micro analyzer. Through the experiments, the following results are obtained 1) The degree of sensitization(DOS) of CF8M aged up to 15hr at $700^{\circ}C$ is increased with acing time while that is decreased with aging time from 15hr to 150hr. 2) The impact energy decreases with increase of $\sigma$-phase while DOS increases with $\sigma$-phase until aging time reaches to 15hr. After the aging time. 15hr, the $\sigma$-phase and the rate of impact energy with respect to aging time decreases. Therefore the degradation behavior of the CF8M can be evaluated by comparing SEM micrographs and the value of DOS.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.33 no.2
• /
• pp.181-186
• /
• 2013

We present nondestructive characterization for remanent life of advanced ferritic steels, next-gen energy facility materials by reversible permeability. The reversible permeability is based on the theory that the value of reversible permeability is the same differential of the hysteresis loop. The measurement principle is based on the foundation of harmonics voltage induced in a sensing coil using a lock-in amplifier tuned to the frequency of the exciting one. The peak interval of reversible permeability(PIRP), Vickers hardness, and tensile strength(TS) of the aged samples decreased with aging time. We could estimate the remanent life of advanced ferritic steel by using the relationship between the peak interval of reversible permeability and Larson-Miller parameter(LMP), non-destructively.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.20 no.5
• /
• pp.445-450
• /
• 2000

The integrity of the turbine rotors can be assessed by measuring reversible permeability and Vickers hardness of the aged rotors at service temperature. The measurement system of reversible permeability, which measured by applied alternating perturbing magnetic field, was constructed in order to evaluate material degradation, nondestructively. The test specimen was 1Cr-1Mo-0.25V steel used widely for turbine rotor material, and the specimens were prepared by the isothermal heat treatment at $630\;^{\circ}C$. The reversible permeability of the test materials were measured at room temperature. The peak interval of reversible permeability and Vickers hardness decreased with the increase of degradation. The degradation of test material may be determined nondestructively by the lineality of Vickers hardness and the peak interval of reversible permeability.

• Corrosion Science and Technology
• /
• v.16 no.6
• /
• pp.305-316
• /
• 2017

Austenitic stainless steels have been widely used for various systems of nuclear power plants. Among these stainless steels, small pipes with diameter less than 14 inch have been produced in the form of seamless pipe. Annealing and cooling process during the manufacturing process can affect corrosion properties of seamless stainless steels. Therefore, 12 inch-diameter of as-received 304L stainless steel pipe was annealed and aged in this study. Intergranular corrosion resistance was evaluated by ASTM A262 Practice A, C, and E methods. The degree of sensitization was determined using a DL-EPR test. U-bend method in an autoclave was used to evaluate the SCC resistance in 0.01 M $Na_2S_4O_6$ or 40% NaOH solution at $340^{\circ}C$. As-received specimen showed relatively high degree of sensitization and intergranular corrosion rate. Carbon segregation was also observed near grain boundaries. Annealing treatment could give the dissolution of segregated carbon into the matrix. Aging treatment could induce segregation of carbon and finally form carbides. Microstructural analysis confirmed that high intergranular corrosion rate of the as-received seamless pipe was due to micro-galvanic corrosion between carbon segregation and grains.

• Nuclear Engineering and Technology
• /
• v.53 no.9
• /
• pp.2982-2989
• /
• 2021

One of the consequences of the 475 ℃ embrittlement of duplex stainless steels is the reduction of the resistance to localized corrosion. Therefore, the detection of this type of embrittlement before the material exhibits significant loss in toughness, and corrosion resistance is important to ensure the structural integrity of critical components under corrosion threats. In this research, conductivity measurements are performed using the alternating current potential drop (ACPD) technique with using a portable four-point probe as a nondestructive evaluation (NDE) method for detecting the embrittlement in a 2507 (UNS S32750) super duplex stainless steel (SDSS) aged at 475 ℃ from as-received condition to 300 h. The electric conductivity results were compared against two electrochemical tests namely double loop electrochemical potentiokinetic reactivation (DL-EPR) and critical pitting temperature (CPT). Mechanical tests and the microstructure characterized using scanning electron microscopy (SEM) imaging are conducted to track the progress of embrittlement. It is shown that the electric conductivity correlates with the changes in impact energy, microhardness, and CPT corrosion tests result demonstrating the feasibility of the four-point probe as a possible field-deployable method for evaluating the 475 ℃ embrittlement of 2507 SDSS.

• Korean Journal of Metals and Materials
• /
• v.49 no.2
• /
• pp.93-103
• /
• 2011

Precipitation behavior of high-nitrogen duplex Fe-24Cr-7Mn-4Ni-4Mo-0.43N stainless steel aged at $850^{\circ}C$ was investigated using scanning transmission electron microscopy. Based on the analyses of selected area diffraction patterns, four kinds of precipitates (intermetallic sigma (${\sigma}$) and chi (${\chi}$), $Cr_2N$ and secondary austenite) were identified. At the ferrite/austenite phase boundary, the ${\sigma}$ phase and secondary austenite were formed via ${\alpha}{\rightarrow}{\gamma}+{\sigma}$ eutectoid reaction. The precipitation of $Cr_2N$ occurred at the austenite grain boundary as well as the interior of the ferrite. The intermetallic ${\chi}$ phase also formed within the ferrite and showed a cube-cube orientation relationship with the ferrite. Further aging produced a lamellar structure composed of $Cr_2N$ and austenite along the ferrite/austenite boundary and enhanced the precipitation of the ${\chi}$ phase. The crystallographic features of the precipitates were also examined in terms of the orientation relationship with the austenite or ferrite matrix.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.4
• /
• pp.50-58
• /
• 2014

Due to the cost burden of new construction, the necessity of repair and retrofitting of aged structures is sharply increasing as the domain of repair and retrofitting construction is expanding. Because of the necessity, new technologies for repair and retrofitting are continuously studied in Korea and foreign countries. Steel adhesive method, fiber reinforced plastic (FRP) surface adhesive method, and external prestressing method are used to perform the repair and retrofitting works in Korea. In order to consider a repair method using steel mesh reinforced cement mortar (SMCM), 3-point flexural member test was conducted considering repair area and layer number of SMCM. Five types of specimens including ordinary reinforced concrete (RC) specimen with dimensions of $1400{\times}500{\times}200$ (mm) were cast for testing the deflection measurement, a LVDT was installed at the top center of the specimens. Also, a steel strain gauge and a concrete strain gauge were placed at the center of the specimens. A steel strain gauge was also installed on the shear reinforcement. The 3 point flexural member test results showed that the maximum load of SMCM reinforced specimen was higher than that of basic RC specimen in all of the load-displacement curves. Also, the results showed that, when the whole lower part of the basic RC specimen was reinforced, the maximum load and strain were 1.18 and 1.37 times higher than that of the basic RC specimen, respectively. Each specimen showed a slightly different failure behavior where the difference of the results was caused by the difference in the adhesive level between SMCM and RC. Particularly, in SM-B1 specimen, SMCM spalled off during the experiment. This failure behavior showed that the adhesive performance for RC must be improved in order to utilize SMCM as repair and retrofitting material.