• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.791-797
• /
• 2002

This paper introduces the partial melting process for solder application and characterization of its feasibility using Sn-Ag, and Sn-Cu solder alloys. ill order to show that the liquid phase in the semi-liquid state maintains the similar wettability as single-phase liquid, the wetting balance tests are conducted with varying temperatures and compositions. Also, as a new soldering technology, the microstructural and mechanical test were investigated. The results from this research indicate that the partial melting can yield satisfactory sider joints as long as the liquid phase acquires sufficient chemical activity. At a condition where the partial melting is effective, a direct correlation between the wettability and the surface tension is found to exist.

• Journal of the Microelectronics and Packaging Society
• /
• v.15 no.4
• /
• pp.77-86
• /
• 2008

The reliability of leaded and lead-free solders of BGA type packages on a printed circuit board was investigated by employing the standard drop test and 4-point bending test. Tested solder joints were examined by optical microscopy to identify associated failure mode. Three-dimensional finite element analysis(FEM) with ANSYS Workbench v.11 was carried out to understand the mechanical behavior of solder joints under the influence of bending or drop impact. The results of numerical analysis are in good agreement with those obtained by experiments. Packages in the center of the PCB experienced higher stress than those in the perimeter of the PCB. The solder joints located in the outermost comer of the package suffered from higher stress than those located in center region. In both drop and bending impact tests, the lead-free solder showed better performances than the leaded solders. The numerical analysis results indicated that stress and strain behavior of solder joint were dependent on various effective parameters.

• Journal of the Microelectronics and Packaging Society
• /
• v.14 no.4
• /
• pp.27-36
• /
• 2007

In this study, we investigated the interfacial reactions between various Sn-Ag-Cu(SAC) solder alloys and ENIG(Electroless Ni Immersion Gold) and Cu-OSP(Organic Solderability Preservative) pad finish. In the case of the interfacial reaction between Sb added SAC solder and ENlf thinner P-rich Ni layer was formed at the interface. In the case of the interfacial reaction between Ni added SAC solder and Cu-OSP, the uniform $Cu_6Sn_5$, intermetallic compounds(IMCs) were formed and $Cu_6Sn_5$ grain did not grow after multiple reflows. Thinner $Cu_3Sn$ IMCs were farmed at the interface between $Cu_6Sn_5$ and Cu-OSP after $150^{\circ}C$ thermal aging.

• Journal of Welding and Joining
• /
• v.35 no.3
• /
• pp.7-14
• /
• 2017

The effect of high temperature-moisture on corrosion and mechanical properties for Sn-0.7Cu, Sn-3.0Ag-0.5Cu (SAC305) solders on flexible substrate was studied using Highly Accelerated Temperature/Humidity Stress Test (HAST) followed by three-point bending test. Both Sn-0.7Cu and SAC305 solders produced the internal $SnO_2$ oxides. Corrosion occurred between the solder and water film near flexible circuit board/copper component. For the SAC305 solder with Ag content, furthermore, octahedral corrosion products were formed near Ag3Sn. For the SAC305 and Sn-0.7Cu solders, the amount of internal oxide increased with the HAST time and the amount of internal oxides was mostly constant regardless of Ag content. The size of the internal oxide was larger for the Sn-0.7Cu solder. Despite of different size of the internal oxide, the fracture time during three-point bending test was not significantly changed. It was because the bending crack was always initiated from the three-point corner of the chip. However, the crack propagation depended on the oxides between the flexible circuit board and the Cu chip. The fracture time of the three-point bending test was dependent more on the crack initiation than on the crack propagation.

• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.2
• /
• pp.47-53
• /
• 2000

The fluxless wetting properties of TSM-coated glass substrate were evaluated by the wetting balance method. We could estimate the wettability of the TSM with new parameters obtained from the wetting balance test for one side-coated specimen. It was more effective in wetting to use Cu as a wetting layer and Au as a protection layer than to use Au itself as a wetting layer. The SnSb solder showed better wettability than SnAg, SnBi, and SnIn solders. The contact angle of the one side-coated glass substrate to the Pb-free solders could be calculated from the farce balance equation by measuring the static force and the tilt angle.

• Journal of the Microelectronics and Packaging Society
• /
• v.13 no.1 s.38
• /
• pp.63-72
• /
• 2006

Mobile products, such as cellular phones, PDA and notebook, are subjected to many different mechanical loads, which include bending, twisting, impact shock and vibration. In this study, a cyclic bending test of the BGA package was performed to evaluate the fatigue life. Special bending tester, which was suitable for electronic package, was developed using an electromagnetic actuator. A nonlinear finite element model was used to simulate the mechanical bending deformation of solder joint in BGA packages. The fatigue life of lead-free (95.5Sn4.0Ag0.5Cu) solder joints was compared with that of lead-contained (63Sn37Pb). When the applied load to the specimen is small, the lead-free solder has longer fatigue life than lead-contained solder. The fatigue crack is initialized at the exterior solder joints and is propagated into the inner solder joints.

• Clean Technology
• /
• v.11 no.3
• /
• pp.153-164
• /
• 2005

This study found a reliable evaluation for four kinds of pb-Free plating solutions and it's layers, through pure Sn, SnAg, SnBi and SnCu. These four kind of solutions are widely used to pb-Free plating. Hull-cell, Harring-blum, coverage, throwing power, current efficiency, stability, life-time, composition, hardness, roughness, abrasion, scratch, solderability, corrosion, contact angle, morphology, SIR(Surface insulation resistance) and Whisker test were experimented. Also, Using ICP, XRF, FE-SEM, EDS, temperature/humidity chamber, solderability tester, hardness tester, roughness tester, abrasion tester, salt spray tester, contact angle tester, SIR tester, and microscope. In this paper could be shown the systematic and various analysis for reliability about four kinds of pb-Free plating solutions, processes and it's deposit surface.

• Tribology and Lubricants
• /
• v.24 no.1
• /
• pp.27-33
• /
• 2008

A micro-impression creep machine was designed and developed, adopting a small punch in diameter of 150 um, displacement gage with an accuracy of sub-${\mu}m$ scale, and load-cell with an accuracy of mN scale in order to investigate creep behavior of small solder ball in diameter of less than 1 mm. Creep behavior of lead-free solder ball(Sn-3.0Ag-0.5Cu) in diameter of $760\;{\mu}m$ was investigated in the stress range of $8{\sim}60\;MPa$ and at $303\;K{\sim}393\;K$. The applied load became decreased slightly and continuously in the creep rate of $10^{-4}/s$ range during the current experiments. Also, the machine frame was so sensitive to the environmental temperature that nm scaled displacement recording was unstable according to the change in environmental temperature.

• Journal of the Microelectronics and Packaging Society
• /
• v.17 no.3
• /
• pp.33-41
• /
• 2010

Crack propagation mechanisms of Sn-3.0Ag-0.5Cu solder were studied in strain controlled push-pull creepfatigue conditions using the fast-fast (pp) and the slow-fast (cp) strain waveforms at 313 K. Transgranular cracking was found in the pp strain waveform which led to the cycle-dominant crack propagation and intergranular cracking in the cp strain waveform that led to the time-dominant crack propagation. The time-dominant crack propagation rate was faster than the cycle-dominant crack propagation rate when compared with J-integral range which resulted from the creep damage at the crack tip in the cp strain waveform. Clear recrystallization around the crack was found in the pp and the cp strain waveforms, but the recrystallized grain size in the cp strain waveform was smaller than that in the pp strain waveform. The cycle-dominant crack propagated in the normal direction to the specimen axis macroscopically, but the time-dominant crack propagated in the shear direction which was discussed in relation with shear micro cracks formed at the crack tip.

• Journal of the Microelectronics and Packaging Society
• /
• v.10 no.3
• /
• pp.19-27
• /
• 2003

Surface finishes of PCB laminates are important in the solder joint reliability of flip chip package because the types and thicknesses of intermetallic compound(IMC), and compositions and hardness of solders are affected by them. In this study, effects of surface finishes of PCB on the low cycle fatigue resistance of Sn-based lead-free solders; Sn-3.5Ag, Sn-3.5Ag-XCu(X=0.75, 1.5), Sn-3.5Ag-XBi(X=2.5, 7.5) and Sn-0.7Cu were investigated for the Cu and Au/Ni surface finish treatments. Displacement controlled room temperature lap shear fatigue tests showed that fatigue resistance of Sn-3.5Ag-XCu(X=0.75, 1.5), Sn-3.5Ag and Sn-0.7Cu alloys were more or less the same each other but much better than that of Bi containing alloys regardless of the surface finish layer used. In general, solder joints on the Au/Ni finish showed better fatigue resistance than those on the Cu finish. Cross-sectional fractography revealed microcracks nucleation inside of the interfacial IMC near the solder mask edge, more frequently on the Cu than the Au/Ni surface finish. Macro cracks followed the solder/IMC interface in the Bi containing alloys, while they propagated in the solder matrix in other alloys. It was ascribed to the Bi segregation at the solder/IMC interface and the solid solution hardening effect of Bi in the $\beta-Sn$ matrix.