• Journal of the Microelectronics and Packaging Society
• /
• v.15 no.4
• /
• pp.87-92
• /
• 2008

The interface microstructure of Sn-3.5Ag/Cu joint was modified by electroplating varying amount of Zn on Cu UBM. As the amount of Zn dissolved in Sn-3.5Ag solder increased with the electroplating Zn thickness, Cu-Sn IMCs such as $Cu_6Sn_5$ and $Cu_3Sn$ were replaced by Zn-containing IMCs such as $Cu_5Zn_8$ and $Ag_5Zn_8$, which increased the drop reliability of solder joints significantly. When the amount of Zn dissolved in solder was about 3.8wt%, drop resistance was best due to the effective suppression of Cu-Sn IMC and voids at the interface.

• Korean Journal of Materials Research
• /
• v.9 no.7
• /
• pp.747-752
• /
• 1999

The interfacial reaction and joint properties of Sn-3.5Ag/Cu and Sn-3.5Ag-1Zn/Cu joint were studied. Modified double lap shear solder joints of Sn-3.5Ag and Sn-3.5Ag- lZn solder were aged for 60days at $100^{\circ}C$ and $150^{\circ}C$ and then loaded to failure in shear. The Sn-3.5Ag/Cu had a fast growth rate of the reaction layer in comparison with the Sn-3.5Ag-lZn at the aging temperature of $150^{\circ}C$ Through the SEM/EDS analysis of solder joint, it was proved that intermatallic layer was $Cu_{6}Sn_5$ phase and aged specimens showed that intermatallic layer grew in proportion to $t_{1/2}$, and the precipitate of $Ag_3Sn$ occur to both inner layer and interface of layer and solder. In case of Zn-containing composite solder, $Cu_{6}Sn_{5}$ phase formed at the side of substrate and $Cu_{5}Zn_{8}$ phase formed at the other side in double layer. The shear strength of the Sn-3.5Ag/Cu joint improved by addition of IZn. The strength of the joint increases with strain rate and decreases with aging temperature

• Journal of Korea Foundry Society
• /
• v.28 no.4
• /
• pp.184-189
• /
• 2008

Ag-Cd alloy has been widely used as an electrical contact material, since Ag-Cd alloy has a good wear resistance and stable contact resistance. But nowadays Ag-Cd alloy is not considered as electrical contact material any more due to detrimental effect on environments. Currently, active researches are being performed on ($Ag-SnO_2$ and $Ag-SnO_{2}-In_{2}O_{3}$) as an alternative solution which can fix the remaining environmental problems. However, $In_{2}O_{3}$ is relatively expensive and Ag-Sn alloy has low wear resistance. Our recent research results show that Ag-X%Zn-Y%Sn has similar physical and chemical properties. In the present study, so we tried to change and to optimize the Zn oxide content to over 6 wt% and Sn oxide content with 0.5, 1.0, 1.5 wt%. Results obtained from the experiments on the Ag-X%ZnO-Y%$SnO_2$ are discussed.

• Journal of Korea Foundry Society
• /
• v.22 no.2
• /
• pp.89-96
• /
• 2002

This study examined the effects of adding Zn to Sn-3.5Ag solder on the microstructure changes and behavior of interface reaction of the solder joint with Cu substrate. The solder/Cu joints were examined with microscope to observe the characteristics of microstructure changes and interfacial reaction layer with aging treatment for up to 120 days at $150^{\circ}C$. Results of the microstructure changes showed that the microstructures were coarsened with aging treatment, while adding 1%Zn suppresses coarsening microstructures. The Sn-3.5Ag/Cu had a fast growth rate of the reaction layer in comparison with the Sn-3.5Ag-1Zn at the aging temperature of $150^{\circ}C$. Through the SEM/EDS analysis of solder joint, it was proved that intermetallic layer was $Cu_6Sn_5$ phase and aged specimens showed that intermetallic layer grew in proportion to $t^{1/2}$, and the precipitate of $Ag_3Sn$ occur to both inner layer and interface of layer and solder. In case of Zn-containing composite solder, $Cu_6Sn_5$ phase formed at the side of substrate and Cu-Zn-Sn phase formed at the other side in double layer. It seems that Cu-Zn-Sn phase formed at solder side did a roll of banrier to suppress the growth of the $Cu_6Sn_5$ layer during the aging treatment.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.481-486
• /
• 2002

We have investigated the effects of plating materials for Cu lead (Sn-lOPb, AwPdJNi, Sn-3.5Ag, Sn-3Bi and Sn-0.7Cu) on properties of QFP joints using a Sn-8Zn-3Bi solder. The results were compared with the joints using Sn-3. 5Ag-0. 7Cu and Sn-37Pb solders. As a result, the joints with the Sn-3.5Ag, Sn-3Bi and Sn-0.7Cu plated Cu lead had the reliability comparable to those of the Sn-3.5Ag-0.7Cu and Sn-37Pb soldered joints with respect to the joint strength after the high temperature holding tests at 348K to 423k. In particular, the joint with the Sn-3.5Ag plated Cu lead had the best reliability. This is caused by the low growth rate of a Cu-Sn interfacial reaction layer that degrades the joint strength of the soldered joints. Consequently, the Sn-3.5Ag plating was found to be most feasible plating for the Sn-8Zn-3Bi soldered joint.

• Korean Journal of Metals and Materials
• /
• v.46 no.7
• /
• pp.443-448
• /
• 2008

Contact materials are used in many electrical devices. Ag-Cd alloy has been widely used in electrical part, because Ag-Cd alloy has a good wear resistance and stable contact resistance. But nowadays Ag-Cd alloy isn't being used because of environmental challenges. Currently new research is being done on ($Ag-SnO_2$ and $Ag-SnO_2-In_2O_3$) as an alternative solution to fix any remainly environmental challenges. However $In_2O_3$ is more expensive and Ag-Sn alloy has low wear resistance. According to our research data Zn has a similar physical and chemical property. In this work, so we changed and optimized the Zn oxide to over 4 and added Sn oxide ratio 0.5, 1.0, 1.5wt%. Conclusions from the data recorded from the experiment of $Ag-ZnO-SnO_2$ are as follows.

• Journal of the Korean Ceramic Society
• /
• v.38 no.3
• /
• pp.287-292
• /
• 2001

본 실험은 목적은 CRT(Cathode Ray Tube)용 청색 형광체인 ZnS:Ag 분말 표면에 액상법으로 SnO$_2$를 균일하게 코팅하는 공정조건을 연구하는 것이다. 용매로서 물을 사용하고, Sn의 공급물질로서 SnCl$_4$.4$H_2O$, 침전 촉매로서 CO(NH$_2$)$_2$를 각각 사용하여, 균일 침전 방법으로 ZnS:Ag 분말표면에 SnO$_2$를 코팅할 수 있었다. 초기에 첨가되는 SnCl$_4$.4$H_2O$의 량이 Sn/Zn의 몰비기준으로 0.017인 경우에 ZnS:Ag 분말표면에 Sn(OH)$_4$가 균일하게 코팅되지만, 그 이상 첨가되면 과량의 Sn(OH)$_4$가 입자들 사이에 응집되었다. 코팅된 Sn(OH)$_4$는 비정질 구조로 규명되었으며, 이를 SnO$_2$결정상으로 전이시키기 위하여 300~$700^{\circ}C$ 범위 내에서 열처리를 행하였다. 비정질 Sn(OH)$_4$는 20$0^{\circ}C$이하에서 탈수되었고 45$0^{\circ}C$부터 SnO$_2$로 결정화되기 시작하였다. 순수한 ZnS의 경우, 50$0^{\circ}C$이하에서는 상변화가 없으나, $600^{\circ}C$에서 일부 산화되었으며 $700^{\circ}C$에서는 완전히 ZnO로 산화되므로, ZnS의 산화방지 및 SnO$_2$의 결정화를 동시에 만족하는 최고 열처리온도는 50$0^{\circ}C$로 규명되었다. 그러나 ZnS에 SnO$_2$가 코팅된 시편의 경우에는 $600^{\circ}C$가 되어도 ZnS 상이 거의 산화되지 않았고, $700^{\circ}C$에서도 ZnS와 ZnO 상이 공존한 것으로 보아 SnO$_2$코팅이 ZnS의 산화를 억제하는 것으로 나타났다.

• Journal of Korea Foundry Society
• /
• v.18 no.6
• /
• pp.570-577
• /
• 1998

An investigation has been conducted to describe solidification characteristics in Sn-Zn binary system and Sn-Zn-Ag ternary system added by Ag produced by the continuous casting process using heated mold as a basic study for developing Pb-free solder materials. To obtain the continuous casting rods with mirror surface and near net shape at higher casting speed, water flow rates must be increased and mold temperature must be lowered. However, surface tearing in the casting rods occured at lower continuous casting speed while break out occured at higher continuous casting speed even if optimum conditions such as water flow rate and heated mold temperature are determined. Primary ${\alpha}Sn$ and eutectic structure in unidirectioally solidified Sn-Zn alloys were finer with increased casting speed. But, directionality may not be expected for primary Zn in hypereutectic Sn-Zn alloy. It was found that the addition of $0.2{\sim}0.8%$ Ag promoted the growth of primary ${\alpha}Sn$ dendrites. The changes of tensile strength and elongation in Sn-Zn binary alloys were not observed while the increase of tensile strength and the decrease of elongation in Sn-Zn-Ag ternary alloys were observed with increased casting speed.

• Journal of the Microelectronics and Packaging Society
• /
• v.12 no.1 s.34
• /
• pp.35-40
• /
• 2005

The oxidation of pure Sn and Sn-0.7Cu, Sn-3.5Ag, Sn-lZn, and Sn-9Zn alloys at $150^{\circ}C$ was investigated. Both the chemical nature and the amount of oxides were characterized using electrochemical reduction analysis by measuring the electrolytic reduction potential and total transferred electrical charges. X-ray photoelectron spectroscopy (XPS) was also conducted to support the results of reduction analysis. The effect of Cu, Ag and Zn addition on surface oxidation of Sn alloys is reported. For Sn, Sn-0.7Cu and Sn-3.5Ag, SnO grew first and then the mixture of SnO and $SnO_2$ was found. $SnO_2$ grew predominantly for a long-time aging. For Zn containing Sn alloys, both ZnO and $SnO_2$ were formed. Zn promotes the formation of $SnO_2$. Sn oxide growth rate of Pb-free solder alloys was also discussed in terms of alloying elements.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.10a
• /
• pp.313-316
• /
• 2008

This work sought to examine the suitability of twin roll strip casting for Ag-27%Cu-25%Zn-3%Sn brazing alloy (BAg-7A) and to investigate the mechanical properties and microstructure of the strip. The effect of aging heat treatment on the properties was also studied,. This new manufacturing process has applications in the production of the brazing alloy. XRD and microstructural analysis of the Ag-27%Cu-25%Zn-3%Sn strip represented eutectic microstructure of a Cu-rich phase and a Ag-rich matrix regardless of heat treatment. The results of mechanical tests showed tensile strength of 470MPa, a significant enhancement, and an 18% elongation of the twin roll casted strip, due mainly to the solid solution strengthening of Zn atoms (${\sim}20%$) in the Cu-rich phases. Tensile results showed gradually decreasing strengths and increasing elongation with aging heat treatment. Microstructural evolution and fractography were also investigated and related to the mechanical properties.