• Korean Journal of Materials Research
• /
• v.7 no.2
• /
• pp.140-144
• /
• 1997

The effects of the particle size of precursor powder on the microstructure and Jc of Ag-sheathed Ri-2223 tapes were investigated. The calcined powder with overall composition of $Bi_{1-89}Pb_{0-41}Sr_{2-01}Ca_{2-23}Cu_{3-03}O_{y}$ was milled for various times using planetary ball mill. The transport property of the tapes were found to depend strongly on the particle size of the precursor powder Enhanced reactivity of the milled powder facilitated the formation of 2223 phase and resulted in an increase of Jc. Excessive milling, however, led to the amorphisation of the powder and degraded the electrical property of the tapes.

• Progress in Superconductivity
• /
• v.5 no.2
• /
• pp.124-127
• /
• 2004

Many of research efforts have been focused on the improvement of critical current density (Jc) of silver-sheathed Bi-2223 tapes far practical applications. In this study, the transformation of Bi-2212 phase was investigated, which was transformed to orthorhombic from tetragonal through pre-annealing during powder packing and drawing process. The relationship between hardness of Bi-2212 orthorhombic phase and workability of Bi-2223/Ag tape was investigated. Bi-2223 superconducting wires with 55 filaments were fabricated by stacking and drawing process with different heat-treatment histories. Before rolling process, round wires were pre-annealing at 76$0^{\circ}C$ and in a low oxygen partial pressure. We confirmed that pre-annealing step was to transform to Bi-2212 orthorhombic structure from Bi-2212 tetragonal structure and to reduce the formation of second phases. However the breakages were created at Ag-alloy clad during rolling for pre-annealed Bi-22231Ag tapes. Several pre-annealing scenarios were introduced to reduce the breakages during rolling process. Microstructure and critical current density of pre-annealed Bi-2223 superconducting tapes were investigated. We could achieve proper pre-annealing conditions for Ag-alloy clad Bi-2223 superconducting tapes.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.48 no.1
• /
• pp.29-33
• /
• 1999

Superconducting tape is being developed for electrical equipment such as superconducting transformers and generators etc. AC loss reduction is primary concerned in the development of such high-efficiency equipment. AC losses in Bi-2223 silver-sheathed tapes, both single and multi-filamentary, were investigated by means of AC magnetization techniques when longitudinal fields are applied. The experiment resultswere compared with the hysteresis loss equation based on Bean model and the eddy current loss equation. The AC loss of the mono-filamentary tape was dominated by the hysteresis. On the contrary, the AC loss of the multi-filamentary tape was substantially dominated by the eddy current loss in the silver matrix.

• KIEE International Transactions on Electrophysics and Applications
• /
• v.5C no.5
• /
• pp.204-210
• /
• 2005

Alternating current (AC) losses of two Bi-2223 ([Bi, Pb]: Sr: Ca: Cu: O = 2:2:2:3) tapes [(Tape I, un-twist-pitch) and the other with a twist-pitch of 10 mm (Tape II)] were measured and compared. These samples, produced by the powder-in-(Ag) tube (PIT) method, are multi-filamentary. Also, it's produced by non-twist and different twist pitch (8, 10, 13, 30, 50 and 70 mm). The critical current measurement was carried out under the environment in liquid Nitrogen and in zero-field by 4-probe method. Susceptibility measurements were conducted while cooling in a magnetic field. Flux loss measurements were conducted as a function of ramping rate, frequency and field direction. The AC flux loss increases as the twist-pitch of the tapes decreased, in agreement with the Norris Equation. Neutron-diffraction measurements have been carried out investigate the crystal structure, magnetic structures, and magnetic phase transitions in Bi-2223([Bi, Pb]:Sr:Ca:Cu:O)

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.04a
• /
• pp.17-20
• /
• 2002

The effects of relatively low lead content (0.2~0.3) on the 2223 phase formation and transport property of Bi-2223/Ag tapes have been investigated. The results show that lead contents have great impact on the phase assemblage of precursors, subsequently, on the phase formation and transport property of silver sheathed BSCCO-2223 tapes. Powders containing Pb=0.25 and Pb=0.3 resulted in the nearly identical $J_c$ values in fully processed tapes, but leaded to significant difference on the phase formation process. For the case of Pb=0.2, both low conversion fraction of 2212 to 2223 and low $J_c$ value were obtained in final reacted tape, which was probably due to lack of enough liquid phase to facilitate the phase transformation.

• Progress in Superconductivity
• /
• v.4 no.2
• /
• pp.180-183
• /
• 2003

We evaluated the effect of alloying-element additions to Ag sheath on thermal conductivity of Bi-2223 superconductor tapes. In order to evaluate the effect of sheath alloys and their configuration on the properties of tape, various combinations of Ag and Ag alloys were selected as inner and outer sheath. Thermal conductivity of the tapes was measured by using thermal integral method at 10∼120 K. It is observed that the presence of alloying-elements such as Mg, Sb, and Au in Ag sheath results in decreased thermal conductivity at low temperature. Specifically, the thermal conductivity of AgMg, AgSb, and AgAu at 40 K were 411.4, 142.3, and 109.7 W/(m·K), respectively, which is about 2∼9 times lower than that of Ag (1004.6 W/(m·K)). In addition, the thermal conductivity of alloy-sheathed tape was significantly dependent on their values of constituent sheath materials.

• Journal of the Korean Ceramic Society
• /
• v.39 no.10
• /
• pp.1001-1006
• /
• 2002

Bond strength of $SrZrO_3$ resistive oxide barrier on Ag sheathed Bi(2223) tapes prepared by the sol-gel and dip-coating method was evaluated with an aid of Taguchi method and $L_18(2^1{\times}3^7)$ orthogonal arrays to determine the optimal process combination of levels of factors that best satisfy the bigger is better quality characteristic. The observed optimal condition is as follows: Sr/Zr mol ratio(0.3/0.7), amount of organic vehicle(5 wt%), drying temperature and time(160${\circ}C$, 10 min), heat treatment temperature and time(500${\circ}C$, 20 min), respectively. ANOVA analysis suggested that the influence of the factors within ${\alpha}$=0.1 was significant with a 90% confidence level.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.04a
• /
• pp.59-63
• /
• 2002

The purpose of this paper is to investigate the crystal texture of the 2223 phase and its relationship with PIT processing parameter. Ag-sheathed Bi-2223 multi-filament tapes were prepared by changing rolling reduction ratio. We analysed the degree of texture for 2223 phase after heat-treatment. According to X-ray pole-figure, the texture of the filaments located near surface and center were not so different each other for all rolling conditions. we found a little higher degree of texture for 60% rolling reduction. But its difference is not so high compared with those tapes with a lower rolling reduction ratio. Reaction induced texturing seemed to contribute with a large portion under present condition.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2003.10a
• /
• pp.131-133
• /
• 2003

The effect of axial strain and thermal cycling on the critical current is investigated for the Bi-2223/Ag PIT tapes. The axial strain was applied to the tapes by the U-shape sample holder. Two kinds of Bi-2223/Ag tapes with different Ag sheath are used to know the effect of sheath alloying for the tensile strain. The influence of thermal cycling between room temperature and 77 K on critical current are examined. Critical current is drastically decreased for Ag/alloy and Ag/alloy/alloy sheathed tapes at tensile strain above 0.22％ and 0.3％, respectively.

• KIEE International Transactions on Electrophysics and Applications
• /
• v.3C no.6
• /
• pp.211-215
• /
• 2003

Alternating current (AC) losses of two Bi-2223 ([Bi, Pb] : Sr : Ca : Cu :O = 2:2:2:3) tapes [one untwisted (Tape I, twist-pitch of $\infty$ mm) and the other with a twist-pitch of 8mm (Tape II) ] were measured and compared. These samples, produced by the powder-in-tube (PIT) method, are multi-filamentary and have a Ag/Au and Ag matrix, respectively. Susceptibility measurements were conducted while cooling in a magnetic field. Flux loss measurements were conducted as a function of ramping rate, frequency and field direction. The AC flux loss increases as the twist-pitch of the tapes decreased, in agreement with the Norris Equation.