• 한국재료학회지
• /
• 제5권1호
• /
• pp.140-148
• /
• 1995

Transfer matrix를 사용하여 $TiO_{2}$ 및 Ag 단일 박막과 $TiO_{2}/Ag/TiO_{2}$ 다층 박막의 두계에 따른 투과도 특성을 예측하였으며, 이를 실제 스퍼터 증착하여 제조한 박막의 광학 특성과 비교하였다. $TiO_{2}$ 및 Ag 박막에서는 복소굴절률을 사용하므로써 실제 증착박막에서 측정된 특성과 근접한 투과도 곡선의 예측이 가능하였다. $TiO_{2}/Ag/TiO_{2}$ 3층 박막의 광학 특성은 Ag의 $TiO_{2}$층으로의 확산 및 응집에 의해 transfer matrix로 예측한 투과도 특성과 전혀 다른 거동을 나타내었다. 그러나 4nm 및 6nm 두계의 Ti 박막을 확산방지층으로 증착한 Ti$O_{2}$/Ti/Ag/Ti/Ti$O_{2}$ 구조의 5층 박막에서는 transfer matrix를 사용하여 예측한 $TiO_{2}/Ag/TiO_{2}$ 3층 박막의 투과도 곡선과 유사한 광학 특성을 얻을 수 있었다.

• 한국재료학회지
• /
• 제28권11호
• /
• pp.620-626
• /
• 2018

Highly self-cleaning thin films of $TiO_2-SiO_2$ co-doped with Ag and F are prepared by the sol-gel method. The asprepared thin films consist of bottom $SiO_2$ and top $TiO_2$ layers which are modified by doping with F, Ag and F-Ag elements. XRD analysis confirms that the prepared thin film is a crystalline anatase phase. UV-vis spectra show that the light absorption of $Ag-F-TiO_2/SiO_2$ thin films is tuned in the visible region. The self-cleaning properties of the prepared films are evaluated by a water contact angle measurement under UV light irradiation. The photocatalytic performances of the thin films are studied using methylene blue dye under both UV and visible light irradiation. The $Ag-F-TiO_2/SiO_2$ thin films exhibit higher photocatalytic activity under both UV and visible light compared with other samples of pure $TiO_2$, Ag-doped $TiO_2$, and F-doped $TiO_2$ films.

• 한국세라믹학회지
• /
• 제31권12호
• /
• pp.1483-1490
• /
• 1994

YBa2Cu3Ox-Ag(YBCO-Ag) thick films were fabricated on the zirconia substrate by a screen printing method. The starting powder was a mixture of YBCO, prepared by a coprecipitation in oxalic acid, and Ag2O. The influence of heat treatment conditions on properties of thick films was investigated. It was observed that Jc of thick films was directly proportional to the orientation factor of thick films and the optimimum preparation condition was the heat treatment of thick films at 100$0^{\circ}C$ for 3 min in O2. The improvement of Jc by the addition of Ag was considered as a result of the suppression of microcracks in the films.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2009년도 춘계학술발표대회
• /
• pp.36.2-36.2
• /
• 2009

In this work, the high power CW Nd:YAG laser has been used for thermal treatment of inkjet printed Ag films-involving eliminating organic additives (dispersant, binder, and organic solvent) of Ag ink and annealing Ag nanoparticles. By optimizing laser parameters, such as laser power and defocusing value, the laser energy can totally be converted to heat energy, which is used to thermal treatment of inkjet printed Ag films. This results in controlling the microstructures and the resistivity of films. We investigated the thermal diffusion mechanisms during laser annealing and the resulting microstructures. The impact of high power laser annealing on microstructures and electrical characteristic of inkjet printed Ag films is compared to those of the films annealed by a conventional furnace annealing. Focused ion beam (FIB) channeling image shows that the laser annealed Ag films have large columnar grains and dense structure (void free), while furnace annealed films have tiny grains and exhibit void formation. Due to these microstructural characteristics of laser annealed films, it has better electrical property (low resistivity) compared to furnace annealed samples.

• 한국전기전자재료학회논문지
• /
• 제30권11호
• /
• pp.740-744
• /
• 2017

Herein we studied the electrical and optical properties of indium tin oxide ITO/Ag/ITO multilayer thin films for application in transparent conducting electrodes. The ITO and Ag thin films were deposited onto soda lime glass (SLG) using radiofrequency and DC-sputtering methods, respectively. The as-synthesized ITO/Ag/ITO multilayer thin films were analyzed using 4-point probe, UV-Visible spectroscopy, and Hall measurement. We observed a rapid increase in electron concentration with increasing Ag thickness. However, electron mobility decreased with increasing Ag thickness. Finally, ITO/Ag/ITO multilayer thin films showed a characteristic low sheet resistance of $18{\Omega}/sq$ and high optical transmittance value (80%) with variation of Ag thickness (5~10 nm).

• 한국전기전자재료학회논문지
• /
• 제26권7호
• /
• pp.510-514
• /
• 2013

In order to prevent heat loss that occurs through the glass, low-emissivity (Low-E) coating methods with good insulating properties and high transmittance were used. InGaZnO/Ag/InGaZnO (IGZO/Ag/IGZO) multilayer thin films have been deposited on XG glass substrate by RF magnetron sputtering. Depending on the different thickness of Ag in multilayer films, the structural and optical properties of Low-E multilayer films were analyzed. By XRD analysis results, the multilayer thin films were observed to be amorphous structure regardless of Ag thickness. According to the AFM results, surface morphology of the multilayer films was observed and compared. Using UV-VIS spectroscopy, low emissivity property has been observed clearly with the transmittance of higher than 85% at visible range and lower than 30% at IR range.

• 대한금속재료학회지
• /
• 제46권5호
• /
• pp.283-288
• /
• 2008

We observed the in-situ stress behavior of Cu and Ag thin films during deposition using a thermal evaporation method. Multi-beam curvature measurement system was used to monitor the evolution of in-situ stress in Cu and Ag thin films on 100 Si(100) substrates. The measured curvature was converted to film stress using Stoney formula. To investigate the effects of the deposition rates on the stress evolution in Cu and Ag thin films, Cu and Ag films were deposited at rates ranging from 0.1 to $3.0{\AA}/s$ for Cu and from 0.5 to $4.0{\AA}/s$ for Ag. Both Cu and Ag films showed a unique three stress stages, such as 'initial compressive', 'a tensile maximum' and followed by 'incremental compressive' stress. For both Cu and Ag films, there is no remarkable effect of deposition rate on the thickness and average stress at the tensile maximum. There is, however, a definite decrease in the incremental compressive stress with increasing deposition rate.

• 방사선산업학회지
• /
• 제7권2_3호
• /
• pp.141-147
• /
• 2013

The simple and facile radiation technique of the preparation of antibacterial biodegradable polymer films containing silver nanoparticles (Ag NPs) was described. The biodegradable poly(butylene adipate-co-terephthalate) (PBAT) films containing silver trifluoroacetate (Ag TFA) were prepared by a solvent casting method, and then the films were irradiated by electron beams at the various doses ranging from 20 to 200 kGy to form Ag NPs in the biodegradable polymers. The results of UV-vis and FE-SEM/EDX analyses revealed that the Ag NPs were successfully formed in the PBAT matrix during the electron beam irradiation, and their amounts were dependant on the absorbed dose and Ag TFA concentrations. Furthermore, on the basis of the results of the antibacterial test through disk diffusion and colony counting test, the irradiated PBAT/Ag TFA films exhibited the antibacterial property due to the formation of Ag NPs.

• 한국전기전자재료학회논문지
• /
• 제30권3호
• /
• pp.162-169
• /
• 2017

Indium tin oxide (ITO) thin films show a low sheet resistance and high transmittance in the visible range of the spectrum. Therefore, they play an important role as transparent electrodes for flat panel displays. However, their resistivity is rather high for use as a transparent electrode in large displays. One way to improve electrical and optical properties in large displays is to use ITO/Ag/ITO multilayer films. ITO/Ag/ITO multilayer films have lower sheet resistance than single layer ITO films with the same thickness. Prior to the ITO/Ag/ITO multilayer experiments, optimal condition for thickness change are necessary. Their thicknesses were deposited differently in order to analyze electrical and optical properties. However, when optimal single film characteristics are applied to ITO/Ag/ITO multilayer films, other phenomena appeared. After analyzing the electrical and optical properties by changing ITO and Ag film thickness, ITO/Ag/ITO multilayer films were optimized. By combining ITO film at $586\;{\AA}$ and Ag film at 10 nm, the ITO/Ag/ITO multilayer films showed optimized high optical transmittance of 87.65%, and the low sheet resistance of $5.5{\Omega}/sq$.

• 반도체디스플레이기술학회지
• /
• 제13권2호
• /
• pp.13-16
• /
• 2014

We prepared the ITO/Ag multilayer thin films on soda-lime glass substrate by the Facing Target Sputtering System (FTS) at room temperature. To confirm the effect of Ag layer in ITO/Ag multilayer thin films, we have prepared various range of Ag layer in its thickness and investigated prior to the setting of ITO/Ag multilayer thin films. The thickness of Ag layer was controlled by the sputtering deposition time. Properties of as-prepared samples were investigated by using a four-point probe, UV-Visual spectrometer with a spectral visual range (400 - 800 nm) and X-ray diffractometer (XRD). As a result, the transmittance of as-prepared samples turned out to be very low in the visible range due to light-scattering on the surface of thin film as the thickness of Ag layer got increased. However, reduction of phenomenon of light-reflection in visual range was observed around 20nm of Ag thickness. We prepared the ITO/Ag multilayer thin film with a resistivity of about $8{\times}10^{-5}[{\Omega}-cm]$ and a transmittance of more than 80 % at 550 nm.