• Journal of the Microelectronics and Packaging Society
• /
• v.24 no.3
• /
• pp.57-62
• /
• 2017

In the process for preparing Ag-coated Cu flakes by electroless silver plating using hydroquinone reducing agent, Ag coating qualities were compared by changing various process parameters such as type of pretreatment solution, plating temperature, pH of plating solution, type and injection rate of plating solution, and pulp density. Effective pretreatment solution for removing the oxide layer on a Cu flake was preferentially suggested. The conditions of low plating temperature, pH value of 4.34, slow injection rate of Ag plating solution, elimination of deionized water in the Ag plating solution, and high pulp density significantly suppressed the formation of separated tiny Ag particles, and thus the surface coverage of Ag coating on Cu flakes was enhanced.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.24 no.1
• /
• pp.43-48
• /
• 2015

Silver nanowire (AgNW) is a material that is increasingly being used for transparent electrodes, as a substitute for indium tin oxide (ITO), owing to its flexibility, high transmittance to sheet resistance ratio, and simple production process. This study involves manufacturing large-area organic photovoltaic cells (OPVs) deposited on AgNW electrodes. We compared the efficiency of OPVs with ITO and AgNW electrodes. The results verified that an OPV with an AgNW electrode performed better than that with an ITO electrode. Furthermore, by using the knife coating method, we successfully fabricated large-area OPVs without the loss of efficiency. Use of AgNW instead of ITO demonstrated that an OPV could be produced on various substrates by the solution process method, dropping the productions costs significantly. Additionally, by using the knife coating method, the process time and amount of wasted solution are reduced. This leads to an increase in the efficient fabrication of the OPV.

• Journal of the Semiconductor & Display Technology
• /
• v.19 no.3
• /
• pp.36-42
• /
• 2020

Silver nanowire (AgNW) random-meshes with high transmittance, low sheet resistance, and high oxidation stability and flexibility were fabricated using solution-based processes. The random-mesh structure was obtained by forming bubbles whose sizes and densities were controlled using a corona treatment of polyethylene terephthalate (PET) substrates. To reduce the sheet resistance of the fabricated AgNW electrode, a washing process using ethanol solution was performed. In addition, nickel (Ni) was coated on AgNW to improve resistance to oxidation. The effects of corona treatment and Ni-coating on the transmittance, sheet resistance, oxidation stability, and flexibility of the AgNW electrodes were investigated.

• The Journal of Korean Academy of Prosthodontics
• /
• v.35 no.1
• /
• pp.103-117
• /
• 1997

The purpose of this experiment was to determind whether the gold electrodeposit on Pd-Ag and Ni-Cr alloys influences on the shear bond strength between veneering resin and silicoated metal surface. All the metal specimens were sandblasted with $250{\mu}m$ aluminum oxide and followed by silicoating and resin veneering. According to the metal surfaces to be veneered, experimental groups were divided into five. Group Prec : Gold alloy without gold coating Group Semi : Pd-Ag alloy without gold coating Group Base : Ni-Cr alloy without gold coating Group Semi-G : Pd-Ag alloy with gold coating Group Base-G : Ni-Cr alloy with gold coating All specimens were thermocycled 1,000 times at temperature of $5^{\circ}C$ to $55^{\circ}C$. The effects of gold electrodeposit on the shear bond strength between resin and metal interface were measured and fractured surface of the resin veneered metal was examined under the scaning electron microscope. The following results were obtained 1. The shear bond strength between resin and metal was $64.51{\pm}11.11Kg/cm^2$ in Prec group, $62.77{\pm}11.23Kg/cm^2$ in Base group and $58.97{\pm}9.20Kg/cm^2$ in Semi Group. There was no significant difference among the groups. 2. The bond strength in groups Semi-G and Base-G decreased about 17%, compared to the nongold-electrodeposit groups(Semi, Base). 3. In groups of non electrodeposit(Prec, Semi, Base), fracture occurred at the interface between alloy and resin, while fracture interface was observed between gold coating and resin in group Semi-G, and between metal substrate and gold coating in group Base-G respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.256-259
• /
• 2002

The critical currents of sintered $YBa_{2}Cu_{3}O_{6.5+\delta}$ were measured as the variables with the corrosive time in the humid air. The corrosive process was studied by means of the current changes. Ag coating on the textured YBCO and polytetrafluoroethylene (PTFE) coating on the sintered YBCO were prepared. The critical current densities of different YBCO samples with and without coatings were compared. Both Ag coating and PTFE coating can well protect YBCO from moisture and $CO_{2}$.

• Journal of the Microelectronics and Packaging Society
• /
• v.31 no.2
• /
• pp.1-8
• /
• 2024

Bonding wires are composed of conductive metals of Au, Ag & Cu with excellent electrical conductivities for transmitting power and signals to wafer chips. Wire metals do not provide electrical insulation, adhesion promoter and corrosion passivation. Adhesion between metal wires is extremely weak, which is responsible for wire cut failures during thermal cycling. Organic coating for electrical insulation does not satisfy bondability and manufacturability, and it is complex to apply very thin organic coating on metal wires. Automotive packages require enhanced reliability of packages under harsh conditions. LED and power packages are susceptible to wire cut failures. Contrary to conventional OCB behaviors, forming gas was not required for free air ball formation for both Ag and Pd-coated Cu wires with Al₂O₃ passivation.

• Proceedings of the Optical Society of Korea Conference
• /
• 2001.02a
• /
• pp.262-263
• /
• 2001

저방출 코팅(low-e coating)이란 열 방출에 해당하는 적외선 파장이 가능한 작게 투과하도록 기판 위에 박막을 증착하는 방법이다. 그러므로 유리 기판 위에 저방출 코팅을 하는 것은 냉방시설을 갖춘 건축물 내부에서 에너지 절약과 쾌적한 환경을 구현하거나 자동차 내부의 빠른 온도상승을 저하시키는데 이용될 수 있다. 본 연구에서는 원격 조정 장치의 적외선 파장이 디스플레이의 광원에서 나올 수 있는 동일 파장에 의해 간섭을 받지 않도록 적외선 영역의 투과율은 낮추고 가시광선 영역의 투과율은 높이는 설계를 하고 최적화 하였다. (중략)

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.46 no.4
• /
• pp.28-36
• /
• 2014

We studied the green synthesis and antibacterial activity of paper coated with chitosan-silver (Ag) green nanocomposites for packaging applications. Green synthesis of Ag nanoparticles (AgNPs) was achieved by a chemical reaction involving a mixture of chitosan-silver nitrate ($AgNO_3$) in an autoclave at 15 psi, $121^{\circ}C$, for 30 min. AgNPs and their formation in chitosan was confirmed by UV-Vis spectroscopy, transmission electron microscopy (TEM) and dynamic light scattering (DLS). As-prepared chitosan-AgNPs composite materials were coated on manila paper using Meyer rod. Surface morphology and Ag contents in coating layer were characterized by field emission scanning electron microscopy (FESEM) and energy dispersive spectroscopy (EDS). The mechanical properties such as tensile strength and elongation were significantly affected by coating with chitosan-AgNPs. The antibacterial test of coated paper was performed qualitatively and quantitatively against Escherichia coli (E. coli). It was shown to be effective in suppressing the growth of E. coli with increasing Ag contents on the surface of coated paper and more than 95 R (%) of antimicrobial rate was obtained at chitosan-AgNPs coated papers.

• The Journal of Korean Academy of Prosthodontics
• /
• v.29 no.3
• /
• pp.111-119
• /
• 1991

This study was performed to investigate the effect of gold electrodepositoin on porcelain color of palladium-silver alloy. The specimens were made by firing porcelain on the metal plates cast respectively in Au-Pt alloy, and Pd-Ag alloy. In the case of Pd-Ag alloy specimens, porcelain were fired under three different conditions of the metal plate: 1) without gold coating, 2) firing opaque beforehand on one side, gold coating on the other side, 3) gold coating on both sides of the metal plate. Color change was measured with fiber-optic colorimeter(Model TC-6FX, Tokyo Denshoku Co., Japan). The obtained results were as follows: 1. In the group of firing opaque beforehand on one side and gold coating on the other side, there was no significant differences in their color in comparison to the color of the control group of the Au-Pt alloys. 2. In the group of gold coating on both sides on metal plate, there were no significant differences except their value to the group of firing poaque beforehand on one side and gold coating on the other side.

• The Journal of Engineering Research
• /
• v.3 no.1
• /
• pp.181-187
• /
• 1998

Hydroxyapatite was used as implant materials, because it has a good biocompatibility and is similar to human bone. However it is not expected to have a high strength as implant materials because of a low fracture strength after sintering of HAp. Alumina ($\alpha$-alumina) shows a stable chemical properties and high strength in physiological environments. Thus it was tried to use a HAp coatings on Alumina substrate as implant materials. In this study, HAp was coated on Alumina substrate by lon Beam Assisted Deposition(IBAD). Then Ag was impregnated on HAp coating layer, which showed antimicrobial effects. To carry out the ion exchange of $Ag^+$ with $Ca^{2+}$ in HAp on the surface, HAp coated alumina substrate was immersed in 20ppm, 100ppm $AgNO_3$ solution at room temperature for 48 hours. Antimicrobial test was studied by using bacteria, which normally caused periprosthetic infections. The follwing bacteria was used in antimicrobial test. Escherichia coli, Pseudomonas aeruginosa (gram negative) and staphylococcus epidermidis (gram positive). Ag impregnated HAp shows very good antimicrobial effects against these bacteria. The surface structure of sample, which was treated in $AgNO_3$ solution was studied by SEM, XRD. Ag release curve was studied in Simulated Body Fluid (SBF) solution.