• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 춘계학술대회 논문집 유기절연재료 전자세라믹 방전플라즈마 연구회
• /
• pp.127-130
• /
• 2001

The $BaTiO_3+xNb_2O_5$(x=6, 8, 10wt%) ceramics were prepared by conventional mixed oxide method. The structural properties of the $BaTiO_3+Nb_2O_5$ ceramics with the sintering temperature and addition of $Nb_2O_5$ were investigated by XRD and SEM. Increasing the sintering temperature, the $2{\theta}$ value of BT(110) peak was shifted to the lower degree and intensity of the $Ba_6Ti_2Nb_8O_{30}$ (133) peak was increased. Increasing the addition of $Nb_2O_5$, the intensity of $BaTiNb_4O_{13}$ (201) peak was decreased and $Ba_6Ti_2Nb_8O_{30}$ (133) peak was increased. The grain size of the $BaTiO_3+Nb_2O_5$ ceramics sintered at $1500^{\circ}C$ were almost uniform.

• 한국세라믹학회지
• /
• 제35권8호
• /
• pp.864-870
• /
• 1998

The effect of {{{{ {{Nb }_{2 }O }_{5 } }} and CoO addition on the temperature dependence of the {{{{ {BaTiO }_{3 } }}-based ceramic capa-citor has been studied. X7R with moderate temperature dependence has been developed by means of pre-cisely controlled {{{{ {{Nb }_{2 }O }_{5 } }}/CoO ratio. Dielectric constant(K) and dissipation factor(DF) were 3500 and 1.5% respectively. As the content of {{{{ {{Nb }_{2 }O }_{5 } }} was increased the curie temperature(Tc) was shifted to lower tem-perature and the dielectric constant at Tc was decreased. The proper addition of CoO with {{{{ {{Nb }_{2 }O }_{5 } }} improved the temperature dependence of dielectric properties of the {{{{ {BaTiO }_{3 } }}-based ceramic capacitor.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2005년도 춘계학술대회 논문집
• /
• pp.333-336
• /
• 2005

The reduction behavior of $Nb_2O_5$ in aluminum containing self-reducing briquettes(SRNB) was investigated. The time required for slag/metal equilibrium was estimated as about 20 minutes from the addition of SRNB on to the surface of molten steel. The maximum yield of Nb was expected with the slag composition of $60\%CaO-40\%Al_2O_3$. When $CaCO_3$ was used as a flux, the oxidation loss of Al by $CO_2$ should be compensated, and the chemical equivalent ratio of Al to $Nb_2O_5$ of about 1.43 was required to maximize the yield of Nb.

• 한국결정학회지
• /
• 제17권1호
• /
• pp.24-32
• /
• 2006

[ $Zn_3Nb_2O_8$ ]세라믹스에 액상소결제인 $V_2O_5$를 첨가하여 소결하여 고주파 대역에서의 유전특성의 변화를 조사하였다. $1100^{\circ}C$에서 2시간 하소한 결과 $Zn_3Nb_2O_8$를 합성할 수 있었고, $V_2O_5$를 첨가하여 소결한 $Zn_3Nb_2O_8$에서 $V_2O_5$의 mole%증가와 소결온도의 증가에 따라 상대밀도 95%의 소결특성을 확인 하였다. 유전율 특성은 $V_2O_5$ mole ratio가 $2{\sim}4%$의 시편에서 모두 ${\varepsilon}_r\;21$ 이상으로 증가됨을 확인하였고, 품질계수는 $900^{\circ}C$에서 소결한 $V_2O_5$ 2 mole% 시편에서 $Q{\times}f=40,000$을 나타내었다. 온도계수는 $900^{\circ}C$ 소결하고 $V_2O_5$ 1 mole% 첨가한 경우 0에 제일 가까운 $T_{cf}=-54ppm/^{\circ}C$를 나타내었고, 다른 보건에서는 $T_{cf}=-60{\sim}-80ppm/^{\circ}C$의 값을 나타내었다.

• 한국전기전자재료학회논문지
• /
• 제17권3호
• /
• pp.289-293
• /
• 2004

PNW-PMN-PZT ceramics were fabricated with the variations of Nb$_2$O$_{5}$ addition and their microstructural and piezoelectric characteristics were investigated. When the amount of Nb$_2$O$_{5}$ increased, grain size decreased gradually. At 0.3wt％ Nb$_2$O$_{5}$ which is the same weight percent with Fe$_2$O$_3$, maximum tetragonality(c/a) and density were shown due to the complexed doping effects. Also, this composition that showed Qm of 2,041, kp of 0.55, grain size of 2.5${\mu}{\textrm}{m}$ and $\varepsilon$r of 1704 were proper for high power application. Using this composition, Rosen-type piezoelectric transformer was fabricated as the size of 1 ${\times}$ 16 ${\times}$ 5㎣ and its electrical characteristics were investigated with the variations of load resistance and driving frequency. At the resistance of 200㏀, maximum step-up ratio of 13.68 was shown. After driving PDA CCFL for 25 min using the inverter circuit, at driving frequency of 214.4KHz, input voltage of 31.78 V and input current of 21.1mA were measured at the input part of piezoelectric transformer. And then, output voltage of 293.2 V and output current of 2.2mA were shown at the output part of piezoelectric transformer. At the same time, efficiency of 96.2％ and temperature rise of 3.5$^{\circ}C$ were appeared at the piezoelectric transformer.ormer.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.2
• /
• pp.632-635
• /
• 2003

[ $(Ba,Sr,Ca)TiO_3$ ] powders, prepared by the sol-gel method, were mixed with organic vehicle and the BSCT thick films were fabricated by the screen printing techniques on alumina substrates. The dielectric properties were investigated for various composition ratio and $Nb_2O_5$ doping contents. All the BSCT thick films, sintered at $1420^{\circ}C$, showed the typical XRD patterns of a perovskite polycrystalline structure. The Curie temperature and the relative dielectric constant decreased with increasing Ca content and $Nb_2O_5$ doping amount. The relative dielectric constant, dielectric loss and tunability of the BSCT(50/40/10) thick films doped with 1.0wt% $Nb_2O_5$ were 1410, 0.65% and 17.29% respectively.

• 한국재료학회지
• /
• 제29권5호
• /
• pp.328-335
• /
• 2019

Nb-doped $TiO_2$(NTO) coated NiCrAl alloy foam for hydrogen production is prepared using ultrasonic spray pyrolysis deposition(USPD) method. To optimize the size and distribution of NTO particles based on good physical and chemical stability, we synthesize particles by adjusting the weight ratio of the Nb precursor solution(5 wt%, 10 wt% and 15 wt%). The morphological, chemical bonding, and structural properties of the NTO coated NiCrAl alloy foam are investigated by X-ray diffraction(XRD), X-ray photo-electron spectroscopy(XPS), and Field-Emission Scanning Electron Microscopy(FESEM). As a result, the samples of controlled Nb weight ratio exhibit a common diffraction pattern at ${\sim}25.3^{\circ}$, corresponding to the(101) plane, and have chemical bonding(O-Nb=O) at 534 eV. The NTO particles with the optimum weight ratio of N (10 wt%) show a uniform distribution with a size of ~18.2-21.0 nm. In addition, they exhibit the highest corrosion resistance even in the electrochemical stability estimation. As a result, the introduction of NTO coated NiCrAl alloy foam by USPD improves the chemical stability of the NiCrAl alloy foam by protecting the direct electrochemical reaction between the foam and the electrolyte. Thus, the optimized NTO coating can be proposed for excellent protection of NiCrAl alloy foam for hydrocarbon-based steam methane reforming(SMR).

• 한국전기전자재료학회논문지
• /
• 제24권7호
• /
• pp.559-562
• /
• 2011

In this study, the effect of $Nb_2O_5$ and sintering time on the positive temperature of coefficient of resistivity (PTCR) behavior of lead free $Ba_{0.99}(Bi_{0.5}Na_{0.5})_{0.01}TiO_3$ (BBNT) ceramics were investigated in order to fabricate a PTC thermistor with high $T_c$ temperature more than $140^{\circ}C$. In particular, BBNT ceramic doped with 0.1mol% $Nb_2O_5$ and sintered at $1350^{\circ}C$ for 4 h has significantly increased Curie temperature ($T_c$) of about $200^{\circ}C$, showed good PTCR behavior of room-temperature resistivity ($\rho_{rt}$) of $40{\Omega}{\cdot}cm$, a high $\rho_{max}/\rho_{min}$ ratio of $43.78{\times}10^3$ and a large resistivity temperature factor (${\alpha}$) of 16.1%/$^{\circ}C$. With increasing addition of $Nb_2O_5$ content, the $\rho_{rt}$ decreased to a minimum value of $40\;{\Omega}cm$ at 0.1mol% $Nb_2O_5$ and the $\rho_{rt}$ increased for x value over 0.1 mol%.

• 한국재료학회지
• /
• 제18권9호
• /
• pp.475-481
• /
• 2008

Positive temperature coefficient of resistivity (PTCR) characteristics of (1-x)$BaTiO_3-x(Bi_{0.5}K_{0.5})TiO_3$ ceramics doped with $Nb_2O_5$ were investigated in order to develop the Pb-free PTC thermistor available at high temperatures of > $120^{\circ}C$. The PTCR characteristics appearing in the ($B_{i0.5}K_{i0.5})TiO_3$ (< 5 mol%) incorporated $BaTiO_3$ ceramics, which might be mainly due to $Bi^{+3}$ ions substituting for $Ba^{+2}$ sites. The 0.99$BaTiO_3-0.01(Bi_{0.5}K_{0.5})TiO_3$ ceramics showed good PTCR characteristics of a low resistivity at room temperature (${\rho}_r$) of $31{\Omega}{\cdot}cm$ a high ${\rho}_{max}/{\rho}_{min}$ ratio of $5.38{\times}10^3$, and a high resistivity temperature factor (${\alpha}$) of $17.8%/^{\circ}C$. The addition of $Nb_2O_5$ to 0.99$BaTiO_3-0.01(Bi_{0.5}K_{0.5})TiO_3$ ceramics further improved the PTCR characteristics. Especially, 0.025 mol% $Nb_2O_5$ doped 0.99$BaTiO_3-0.01(Bi_{0.5}K_{0.5})TiO_3$ ceramics exhibited a significantly increased ${\rho}_{max}/{\rho}_{min}$ ratio of $8.7{\times}10^3$ and a high ${\alpha}$ of $18.6%/^{\circ}C$, along with a high $T_c$ of $148^{\circ}C$ despite a slightly increased ${\rho}_r$ of $31{\Omega}{\cdot}cm$.

• 한국결정성장학회지
• /
• 제7권2호
• /
• pp.253-258
• /
• 1997

반도체화 첨가제인 $Y_2O_3$와 $Nb_2O_5$ 첨가랑 변화에 따른 PTCR $BaTiO_3$ 세라믹스의 결정구조 해석과 상전이 특성을 연구하기 위하여 ($Ba_{0.85}Ca_{0.15})TiO_3$ ＋ X m/o $Nb_2O_5$(Y m/o $Y_2O_3$) ＋ 0.08 w/o $Mn(NO_3)_2$ㆍ$6H_2O$ ＋ 0.25 w/o $SiO_2$ 계에서 X는 0.1 ~ 0.4로 Y는 0.2 ~ 0.4로 각각 변화시켜 실험을 수행하였다. $Nb_2O_5$의 첨가시 B-site 치환에 따라서 격자상수가 선형적으로 변화하다가 0.3 mol% 이상 치환할 경우 c 축의 격자상수가 급격히 감소함을 알 수 있었다. 이는 octahedron distortion둥의 원인으로 판단되며, 이러한 격자상수 변화는 상전이 온도 결과와도 잘 일치함을 확인할 수 있었다. 또한 $Y_2O_3$ 첨가의 경우 0.3 mol%가지는 A, B-site를 각각 치환하며 그 이상부터는 A-site 이온을 주로 치환하는 것을 격자상수 변화와 상전이 온도결과를 통해 알 수 있었으며, Rietveld 해석결과 $Y^{3+}$가 A-site 치환시 $Ba^{2＋}$와 $Ca^{2＋}$를 같은 비율로 치환한다는 것을 알 수 있었다.