• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.05c
• /
• pp.127-130
• /
• 2001

The $BaTiO_3+xNb_2O_5$(x=6, 8, 10wt%) ceramics were prepared by conventional mixed oxide method. The structural properties of the $BaTiO_3+Nb_2O_5$ ceramics with the sintering temperature and addition of $Nb_2O_5$ were investigated by XRD and SEM. Increasing the sintering temperature, the $2{\theta}$ value of BT(110) peak was shifted to the lower degree and intensity of the $Ba_6Ti_2Nb_8O_{30}$ (133) peak was increased. Increasing the addition of $Nb_2O_5$, the intensity of $BaTiNb_4O_{13}$ (201) peak was decreased and $Ba_6Ti_2Nb_8O_{30}$ (133) peak was increased. The grain size of the $BaTiO_3+Nb_2O_5$ ceramics sintered at $1500^{\circ}C$ were almost uniform.

• Journal of the Korean Ceramic Society
• /
• v.35 no.8
• /
• pp.864-870
• /
• 1998

The effect of {{{{ {{Nb }_{2 }O }_{5 } }} and CoO addition on the temperature dependence of the {{{{ {BaTiO }_{3 } }}-based ceramic capa-citor has been studied. X7R with moderate temperature dependence has been developed by means of pre-cisely controlled {{{{ {{Nb }_{2 }O }_{5 } }}/CoO ratio. Dielectric constant(K) and dissipation factor(DF) were 3500 and 1.5% respectively. As the content of {{{{ {{Nb }_{2 }O }_{5 } }} was increased the curie temperature(Tc) was shifted to lower tem-perature and the dielectric constant at Tc was decreased. The proper addition of CoO with {{{{ {{Nb }_{2 }O }_{5 } }} improved the temperature dependence of dielectric properties of the {{{{ {BaTiO }_{3 } }}-based ceramic capacitor.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.05a
• /
• pp.333-336
• /
• 2005

The reduction behavior of $Nb_2O_5$ in aluminum containing self-reducing briquettes(SRNB) was investigated. The time required for slag/metal equilibrium was estimated as about 20 minutes from the addition of SRNB on to the surface of molten steel. The maximum yield of Nb was expected with the slag composition of $60\%CaO-40\%Al_2O_3$. When $CaCO_3$ was used as a flux, the oxidation loss of Al by $CO_2$ should be compensated, and the chemical equivalent ratio of Al to $Nb_2O_5$ of about 1.43 was required to maximize the yield of Nb.

• Korean Journal of Crystallography
• /
• v.17 no.1
• /
• pp.24-32
• /
• 2006

The microwave dielectric properties of $Zn_3Nb_2O_8\;with\;V_2O_5$ addition were investigated. The addition of $V_2O_5$ enhanced the sinterability of $Zn_3Nb_2O_8$, which resulted in high density of $Zn_3Nb_2O_8$ ceramic greater than 95% of the theoretical value when sintered at $900^{\circ}C$ for 4 hours. X-ray diffraction analysis of sintered $Zn_3Nb_2O_8$ ceramic showed no second phase with $V_2O_5$ addition. Dielectric permittivity(${\varepsilon}_r$) and quality factor($Q{\times}f$) varied with both density at different sintering temperature and $V_2O_5$ addition. Dielectric permittivity, quality factor and temperature coefficient($T_{cf}$) of the two mole of $V_2O_5\;added\;Zn_3Nb_2O_8$ that was sintered at $900^{\circ}C$ were 21.4, 40,000, $-54ppm/^{\circ}C$, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.3
• /
• pp.289-293
• /
• 2004

PNW-PMN-PZT ceramics were fabricated with the variations of Nb$_2$O$_{5}$ addition and their microstructural and piezoelectric characteristics were investigated. When the amount of Nb$_2$O$_{5}$ increased, grain size decreased gradually. At 0.3wt％ Nb$_2$O$_{5}$ which is the same weight percent with Fe$_2$O$_3$, maximum tetragonality(c/a) and density were shown due to the complexed doping effects. Also, this composition that showed Qm of 2,041, kp of 0.55, grain size of 2.5${\mu}{\textrm}{m}$ and $\varepsilon$r of 1704 were proper for high power application. Using this composition, Rosen-type piezoelectric transformer was fabricated as the size of 1 ${\times}$ 16 ${\times}$ 5㎣ and its electrical characteristics were investigated with the variations of load resistance and driving frequency. At the resistance of 200㏀, maximum step-up ratio of 13.68 was shown. After driving PDA CCFL for 25 min using the inverter circuit, at driving frequency of 214.4KHz, input voltage of 31.78 V and input current of 21.1mA were measured at the input part of piezoelectric transformer. And then, output voltage of 293.2 V and output current of 2.2mA were shown at the output part of piezoelectric transformer. At the same time, efficiency of 96.2％ and temperature rise of 3.5$^{\circ}C$ were appeared at the piezoelectric transformer.ormer.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.632-635
• /
• 2003

[ $(Ba,Sr,Ca)TiO_3$ ] powders, prepared by the sol-gel method, were mixed with organic vehicle and the BSCT thick films were fabricated by the screen printing techniques on alumina substrates. The dielectric properties were investigated for various composition ratio and $Nb_2O_5$ doping contents. All the BSCT thick films, sintered at $1420^{\circ}C$, showed the typical XRD patterns of a perovskite polycrystalline structure. The Curie temperature and the relative dielectric constant decreased with increasing Ca content and $Nb_2O_5$ doping amount. The relative dielectric constant, dielectric loss and tunability of the BSCT(50/40/10) thick films doped with 1.0wt% $Nb_2O_5$ were 1410, 0.65% and 17.29% respectively.

• Korean Journal of Materials Research
• /
• v.29 no.5
• /
• pp.328-335
• /
• 2019

Nb-doped $TiO_2$(NTO) coated NiCrAl alloy foam for hydrogen production is prepared using ultrasonic spray pyrolysis deposition(USPD) method. To optimize the size and distribution of NTO particles based on good physical and chemical stability, we synthesize particles by adjusting the weight ratio of the Nb precursor solution(5 wt%, 10 wt% and 15 wt%). The morphological, chemical bonding, and structural properties of the NTO coated NiCrAl alloy foam are investigated by X-ray diffraction(XRD), X-ray photo-electron spectroscopy(XPS), and Field-Emission Scanning Electron Microscopy(FESEM). As a result, the samples of controlled Nb weight ratio exhibit a common diffraction pattern at ${\sim}25.3^{\circ}$, corresponding to the(101) plane, and have chemical bonding(O-Nb=O) at 534 eV. The NTO particles with the optimum weight ratio of N (10 wt%) show a uniform distribution with a size of ~18.2-21.0 nm. In addition, they exhibit the highest corrosion resistance even in the electrochemical stability estimation. As a result, the introduction of NTO coated NiCrAl alloy foam by USPD improves the chemical stability of the NiCrAl alloy foam by protecting the direct electrochemical reaction between the foam and the electrolyte. Thus, the optimized NTO coating can be proposed for excellent protection of NiCrAl alloy foam for hydrocarbon-based steam methane reforming(SMR).

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.7
• /
• pp.559-562
• /
• 2011

In this study, the effect of $Nb_2O_5$ and sintering time on the positive temperature of coefficient of resistivity (PTCR) behavior of lead free $Ba_{0.99}(Bi_{0.5}Na_{0.5})_{0.01}TiO_3$ (BBNT) ceramics were investigated in order to fabricate a PTC thermistor with high $T_c$ temperature more than $140^{\circ}C$. In particular, BBNT ceramic doped with 0.1mol% $Nb_2O_5$ and sintered at $1350^{\circ}C$ for 4 h has significantly increased Curie temperature ($T_c$) of about $200^{\circ}C$, showed good PTCR behavior of room-temperature resistivity ($\rho_{rt}$) of $40{\Omega}{\cdot}cm$, a high $\rho_{max}/\rho_{min}$ ratio of $43.78{\times}10^3$ and a large resistivity temperature factor (${\alpha}$) of 16.1%/$^{\circ}C$. With increasing addition of $Nb_2O_5$ content, the $\rho_{rt}$ decreased to a minimum value of $40\;{\Omega}cm$ at 0.1mol% $Nb_2O_5$ and the $\rho_{rt}$ increased for x value over 0.1 mol%.

• Korean Journal of Materials Research
• /
• v.18 no.9
• /
• pp.475-481
• /
• 2008

Positive temperature coefficient of resistivity (PTCR) characteristics of (1-x)$BaTiO_3-x(Bi_{0.5}K_{0.5})TiO_3$ ceramics doped with $Nb_2O_5$ were investigated in order to develop the Pb-free PTC thermistor available at high temperatures of > $120^{\circ}C$. The PTCR characteristics appearing in the ($B_{i0.5}K_{i0.5})TiO_3$ (< 5 mol%) incorporated $BaTiO_3$ ceramics, which might be mainly due to $Bi^{+3}$ ions substituting for $Ba^{+2}$ sites. The 0.99$BaTiO_3-0.01(Bi_{0.5}K_{0.5})TiO_3$ ceramics showed good PTCR characteristics of a low resistivity at room temperature (${\rho}_r$) of $31{\Omega}{\cdot}cm$ a high ${\rho}_{max}/{\rho}_{min}$ ratio of $5.38{\times}10^3$, and a high resistivity temperature factor (${\alpha}$) of $17.8%/^{\circ}C$. The addition of $Nb_2O_5$ to 0.99$BaTiO_3-0.01(Bi_{0.5}K_{0.5})TiO_3$ ceramics further improved the PTCR characteristics. Especially, 0.025 mol% $Nb_2O_5$ doped 0.99$BaTiO_3-0.01(Bi_{0.5}K_{0.5})TiO_3$ ceramics exhibited a significantly increased ${\rho}_{max}/{\rho}_{min}$ ratio of $8.7{\times}10^3$ and a high ${\alpha}$ of $18.6%/^{\circ}C$, along with a high $T_c$ of $148^{\circ}C$ despite a slightly increased ${\rho}_r$ of $31{\Omega}{\cdot}cm$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.2
• /
• pp.253-258
• /
• 1997

The characteristics of crystal structure and phase transition with dopants ($Nb_2O_5$= 0.1~0.4 mol% and $Y_2O_3$ : 0.2~0.4 mol%) on the PTCR $BaTiO_3$ system were investigated. In the case of $Nb_2O_5$ additive, the lattice parameter of PTCR $BaTiO_3$ was changed linearly with the increasement of $Nb_2O_5$ which substituted B-site of BaTiO$_3$ and the lattice parameter of c-axis decreased abruptly at 0.3 mol%. These phenonmena were assumed to originate from the distortion of octahedron and we could confirm that the change of lattice parameter accorded with the characteristics of the phase transition temperature. $Y^{3+}$ ions substituted both of A- and B-site until the 0.3 mol% addition, but $Y^{3+}$ substitution preferred A- to B-site above 0.3 mol%. This was affirmed by the variation ,of lattice parameter and the characteristics of phase transition. It also was found that $Y^{3+}$ions in the A-site substituted both of $Ba^{2＋}$ and $Ca^{2＋}$ ions with equal ratio by Rietveld method.