• Journal of Korean Society of Environmental Engineers
• /
• v.39 no.3
• /
• pp.112-117
• /
• 2017

Ion exchange fiber, PADD was synthesized by the reaction between PAN based acrylic fiber and DETA with $AlCl_3{\cdot}6H_2O$, and was analyzed by FT-IR and SEM to investigate its characteristics. The experimental results of Cr(VI) removal by PADD were better fitted with Langmuir adsorption isotherm, and the maximum uptake value ($Q_{max}$) was calculated to be 6.93 mmol/g. The kinetic data can be well described by Lagergen pseudo-second order rate model. The Cr(VI) adsorption capacity of PADD was 4.11 mmol/g at pH 2, which shows the effect of pH changes on the removal of Cr(VI). The adsorption selectivity of Cr(VI) was higher than phosphate and As(V). Total ion exchange capacity of PADD was 4.70 mmol/g, which was measured by acid-base back titration.

• Journal of Technologic Dentistry
• /
• v.35 no.2
• /
• pp.97-103
• /
• 2013

Purpose: The purpose of this study was to investigate the effect of addition of fiber glass on the physical properties of silanized fiber mesh and non silanized mesh of denture base resins. Methods: The denture base resins were used in this study heat curing acrylic resins(Vertex Rs, Lucitone 199, $20{\times}80mm$) and fiber glass(SES, Green B&D co., Ltd, $20{\times}80mm$) were used as reinforcement. The specimens were stored in distilled water at $37{\pm}2^{\circ}C$ for 72 hours before test. Bending strength and tensile strength were measured by an universal testing machine(Instron 4301, Instron Corp.). Penetration distribution on fiber was observed by scanning electron microscopy(JSM 840A, Jeol Ltd). Results: The bending strength and modulus were increased by 30% after adding fiber glass on denture base resins. Tensile strength showed significant increasing by adding fiber glass on denture base resins. Conclusion: In this study, Addition of silanized fiber in denture base resins were improved physical properties. we confirmed the fiber glass possibility of the replacement about conventional materials.

• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.2
• /
• pp.232-242
• /
• 2003

Statement of problem : Fiber-reinforced posts have lower modulus of elasticity than titanium post or cast post-core. With this similar elasticity to that of dentin, fiber-reinforced posts have been known to have a tendency to reduce the risk of root fracture. However, there were few studies on the teeth restored with fiber-reinforced posts under the condition of reduced periodontal support. Purpose : The purpose of this study was to evaluate the fracture strength and failure mode of endodontically treated teeth restored with fiber-reinforced posts and titanium posts under the condition of reduced periodontal support. Material and method : Extracted human maxillary incisor roots were divided into 3 groups (group 1 carbon fiber post, group 2 : glass fiber post, and group 3 : titanium alloy post). After coronectomy and endodontic treatment, teeth were restored with each post systems and resin core according to the manufacturer's recommendation. Then, teeth with simulated periodontal ligament were embedded in the acrylic resin blocks at the level of 4 mm below the cemento-enamel junction. Each specimen was exposed to $10^5$ load cycles with average 30 N force in $36.5^{\circ}C$ water using a computer-controlled chewing simulator. Loads were applied at $45^{\circ}$ angle to the long axis of the teeth. After cyclic loading, teeth were subjected a compressive load until failure at a crosshead speed of 0.5 mm/min. Fracture strength (N) and failure mode were examined. The fracture strength was analyzed with one-way ANOVA and the Scheffe adjustment at the 95% significance level. Results and conclusion : The results were as follows. 1. There was no statistically significant difference in the mean fracture strength among the groups (P<.05). 2. Carbon fiber post and glass fiber post group showed less root fracture tendency than control group. 3. All specimens with root fractures showed fracture lines above the level of acrylic resin block, except for only one specimen in group 3.

• Polymer(Korea)
• /
• v.31 no.6
• /
• pp.512-517
• /
• 2007

The grafting of styrene, glycidylmethacrylate (GMA) or acrylic acid (AAc) onto kapok fiber were performed by $Co_{60}\;{\gamma}-ray$ radiation-induced graft copolymerization. Degree of grafting (DG) of copolymers were increased with increasing monomer concentration and radiation dose. In addition to we confirmed the introduced functional group and measured ion exchange capacity. Morphology of the ion exchange fibers and their structures were analyzed by SEM and FT-IR.

• The Research Journal of the Costume Culture
• /
• v.7 no.5
• /
• pp.165-176
• /
• 1999

The purpose of this study was to evaluate the effect of various knitted fabrics of sports socks on their properties of hygiene and stability. Seventeen men\`s sports socks to represent five groups with different fiber content, knit structure, yarn fineness, and finishing were used. Properties of hygiene and stability of socks were determined. The results were as follows ; 1. Evaluation of Water, vapor and heat transport properties in socks with varing fiber content showed that cotton 100% socks had the highest drop absorbency, wickability, water absorbency and water retention. Polypropylene 100% socks had an excellent wickability and moisture permeability. Acrylic blend socks had the highest thermal resistance. 2. The greatest knit stretch and knit growth of socks having lower power were found to be with cotton 100% socks had the lowest stretch. Acrylic blend socks had a excellent stretch but low fabric growth, which could give a good fir sensation during wear. 3. The commerical antimicrobial finished socks showed excellent durability after repeated cycles of laundering. 4. Length and width shrinkages were found in all laundered samples during initial cycles due to rearrangement by mechanical relaxation. Shrinkages showed no further changes and reached equilibriums after 5 cycles. Cotton 100% or cotton blend socks showed lower dimensional stability than other socks during fabric care.

• Membrane Journal
• /
• v.24 no.4
• /
• pp.311-316
• /
• 2014

The polyacrylonitrile (PAN) hollow fiber composite membranes were prepared and their pervaporation performance was tested to concentrate the acetic acid aqueous solution. The coating of the composite membranes were confirmed by SEM images and the coating thickness was averagely $3.85{\mu}m$. As the crosslinking agent and the crosslinking temperature increase, the permeability decreases while the separation factor increases. Typically, the permeability $250g/m^2{\cdot}hr$ and the separation factor 13 were obtained for glutaraldehyde 13 wt% as the crosslinking agent and crosslinking temperature $140^{\circ}C$. And for the use of another crosslinking agent, poly (acrylic acid) 9 wt% and crosslinking temperature $140^{\circ}C$, the permeability $330g/m^2{\cdot}hr$ and separation factor 9 were obtained.

• Proceedings of the Korean Fiber Society Conference
• /
• 2003.10a
• /
• pp.88-89
• /
• 2003

A series of novel spinning acrylic polymer containing silk protein were synthesized by copolymerization of acrylonitrile (AN) and silk fibroin peptide (SFP) modified by acryloyl chloride (AC) with vinyl groups. The viscosity values of these copolymers showed that the copolymers have good spinnability, which are synthesized under the condition of putting a micro amount of metal ions into synthesizing solvent. The fiber based on the poly (AN-co-SFP) was prepared and characterized by SEM, FTIR measurement of its shell and core flakes, and moisture absorption. The fiber appeared a smooth surface and could be assumed to have excellent adhesive between SFP and PAN. Furthermore, these fibers showed a shell-core structure and excellent moisture absorption.

• Proceedings of the IEEK Conference
• /
• 2002.07c
• /
• pp.1398-1400
• /
• 2002

A new PLF-BLU (Plastic Light Fiber-Back Light Unit) using side glowing light fiber rods array for the 42" LCD TV display has been evelopedd. The light fibers were 14mm in diameter and 50cm long pure transparent acrylic rods of 1.49 refractive index. Fine seratees were made on the flat side of rod. extremely bright incandscent light from lamp fed into the fiber si scattered at scratches then emerges through the surface of rod. A typical PLF-BLU system consists of 24 PLFs produced side glow of brightness of 4,500cd/㎡ to 6,500cd/㎡. New PLF-BLU is proved to be a BLU of rigid, bright, no heat generation, and low power consumption, hence a prospective BLU system for very and/or ultra large size TVs. A new LED-PLF-BLU system considered to be a revolutionary to break-through of the BLU technologies has also been developed, and is decribed briefly.

• Membrane and Water Treatment
• /
• v.11 no.3
• /
• pp.231-235
• /
• 2020

Industrialization and modern developments have led to an influx of toxic heavy metals into the aquatic environment, and the accumulation of heavy metals has serious adverse effects on humans. Among the various heavy metal treatment methods, adsorption is very useful and frequently used. Plastic materials, such as polypropylene and polyethylene, have been widely used as filter media due to their mechanical and chemical stability. However, the surface of plastic material is inert and therefore the adsorption capability of heavy metals is very limited. In this study, granular media and fiber media composed of polypropylene and polyethylene are used, and the surface modification was conducted in order to increase adsorption capability toward heavy metals. Oxygen plasma generated hydroxyl groups on the surface of the media to activate the surface, and then acrylic acid was synthesized on the surface. The grafted carboxyl group was confirmed by FT-IR and SEM. Heavy metal adsorption capability of pristine and surface modified adsorbents was also evaluated. Overall, heavy metal adsorption capability was increased by surface modification due to electrostatic interaction between the carboxyl groups and heavy metal ions. Fibrous PP/PE showed lower improvement compared to granular PP media because pore blockage occurred by the surface modification step, thereby inhibiting mass transfer.

• Textile Coloration and Finishing
• /
• v.26 no.3
• /
• pp.187-194
• /
• 2014

To improve the deep coloring effect of PET fabrics, the alkali treated and black dyed PET fabrics were treated with 2 kinds of low refractive compounds such as acrylic resin and silicone resin. The color depth effect of treated PET fabrics was evaluated as lightness(L) change by UV-visible spectrophotometer. As the weight loss of PET fiber treated with alkali increased, the color depth of PET fabrics increased. Lightness(L) of PET fabrics treated with deep coloring agent was lower than that of untreated PET fabrics. The optimum concentration of treated PET with deep coloring agent was 4% o.w.s. The deep coloring effect of PET fabrics treated with silicone resin was higher than one treated with acrylic resin. PET fabrics treated with silicone resin only might be more appropriate process than PET fabrics treated with acrylic and silicone resin for giving deep coloring effect for polyester fabrics.