• Journal of Ocean Engineering and Technology
• /
• v.10 no.4
• /
• pp.38-50
• /
• 1996

Recently carbon fiber reinforced plastic (CFRP) has been used structural materials in corrosive environment such as for water, chemical tank and pipes. However, mechanical properties of such materials may be change when CFRP and exposed to corrosive environment for long periods of time. The degradation behavior of carbon fiber/epoxy resin composite material in distilled water is investigated using acoustic emission (AE) technique, Fracture toughness tests are performed on the compact tension specimens that are pilled by two types of $[O_2/9O_2]_{3s}$ and $[O/9O]_6s$. During the testes, AE test was carried out to monitor the damage of CFRP by moisture absorption. The data was treated by 2-parameter Weibull distribution and the fracture surface was observed by scanning electron microscope.

• Journal of Welding and Joining
• /
• v.12 no.3
• /
• pp.109-117
• /
• 1994

Spot welding has wide used with a high work efficiency in the automotive and aerospace industries. Up to the present, the technique mainly used to test spot welds on production lines has been entirely depended upon destructive chisel or peel testing. Therefore, it's being very important assignment to secure the NDE technique which can be evaluate spot weld quality with more efficiency and high reliability. This paper discusses the feasibility of UNDE techniques to evaluate spot weld quality. For the sake of the approach to the quantitative measurement of nugget diameter and the discrimination of a the corona bond from nugget, ultrasonic c-scan image and distribution of reflective echo amplitude was measured by immersion method with the mechanical and the electronic scanning of point-focussed ultrasonic beam(25 MHz). As the results of this study, corona bond which is the most dangerous types of interface defects can be successfully detected, as well as expulsion and voids. Ultrasonic testing results were confirmed and compared by optical microscope and SAM(Scanning Acoustic Microscope) observation of the spot-weld cross section. The results show that the nugget diameter can be successfully measured with the accuracy of 0.8 mm.

• Smart Structures and Systems
• /
• v.19 no.2
• /
• pp.127-136
• /
• 2017

Fiber reinforced polymer (FRP) has received widespread attention in the field of civil engineering because of its superior durability and corrosion resistance. This article presents the damage mechanisms of a novelty composite called carbon nanofiber modified flax fiber polymer (CNF-modified FFRP). The ability of acoustic emission (AE) to detect damage evolution for different configurations of specimens under uniaxial tension was examined, and some useful AE characteristic parameters were obtained. Test results shows that the mechanical properties of modified composites are associated with the CNF content and the evenness of CNF dispersed in the epoxy matrix. Various damage mechanisms was established by means of scanning electron microscope images. The fuzzy c-means clustering were proposed to classify AE events into groups representing different generation mechanisms. The classifiers are constructed using the traditional AE features -- six parameters from each burst. Amplitude and peak-frequency were selected as the best cluster-definition features from these AE parameters. After comprehensive comparison, a correlation between these AE events classes and the damage mechanisms observed was proposed.

• Magazine of the Korea Concrete Institute
• /
• v.10 no.6
• /
• pp.203-211
• /
• 1998

It is well recognized recently that acoustic emission, which is an elastic wave generated from rapid release of elastic energy in steressed solids, is very useful tool for on-line monitoring of microscopic behavior of deformation of material. In this study, three point bend test was performed to evaluate the microscopic damage progress during the loading and failure mechanism of mortar beam by monitoring the characteristic of AE signal. The relationship between AE characteristic and microscopic failure mechanism is discussed. In addition 2 dimensional AE source location based on triangular method was also done to monitor the intiation and propagation of micro crack around notch tip of mortar beam. It was shown that AE source location was very effective to predict the growth behavior of micro crack in mortar beam specimen.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2005.11a
• /
• pp.157-160
• /
• 2005

The surface energies and acid-base interaction between the untreated and treated Jute or Hemp fibers and different matrix compositions of polypropylene-maleic anhydride polypropylene copolymers (PP-MAPP) were investigated using dynamic contact angle measurement. The contribution of the acid-base property into the interfacial adhesion of the natural fibers/matrix systems were characterized by calculating the work adhesion coming from the acid-base interaction. On the other hand, microfailure mechanism of both single Jute and Hemp fiber bundles were investigated using the combination of single fiber tensile test and acoustic emission. Distinctly different micro failure modes of the different natural fiber/polypropylene systems wet ε observed using optical microscope and determined indirectly by AE and their FFT analysis.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 1999.11a
• /
• pp.28-31
• /
• 1999

Carbon fiber/epoxy composites using electrodeposited monomeric and polymeric coupling agents were compared with the dipping and the untreated cases. Treating conditions such as time, concentration and temperature were optimized. Four-fibers embedded micro-composites were prepared for fragmentation test. Interfacial properties of four-fiber composites with different surface treatments were investigated with simultaneous acoustic emission (AE) monitoring. The microfailure mechanisms occurring from fiber break, matrix and interlayer crackings were examined by AE parameters and an optical microscope. It was found that interfacial shear strength (IFSS) of electrodeposited carbon fibers was much higher than the other cases under dry and wet conditions. Well separated and different-shaped AE groups occurs for the untreated and ED treated case, respectively.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.20 no.2
• /
• pp.110-115
• /
• 2000

The electromechanical reciprocity identity is introduced to relate the voltage at the terminals of a transducer to the acoustic wavefields scattered from the specimen. The voltage at the terminals of the transducer is expressed as an integral equation in terms of the displacement and stress of the incident and scattered waves on the closed surface enclosing the scatterer. The equation is used to relate the voltage at the terminals of an acoustic microscope's transducer to the acoustic wavefields at the interface between the specimen and the coupling fluid. The voltage calculated using the integral equation is compared with the experimental result.

• Journal of Welding and Joining
• /
• v.19 no.1
• /
• pp.40-48
• /
• 2001

An ultrasonic test method, as a nondestructive test is applied to ensure the clad interface quality assessment. According to the reference codes and standards, not only korea Industrial Standard(KS) but also American Society for Testing and Materials (ASTM) Standard, ultrasonic examination procedures use the pulse-echo, A-scan, back reflection signal drop method and/or side drilled reference hole used to establish the acceptance criteria of clad material test. But the variety of bonding materials and sizes makes it difficult to produce the reference blocks, or thus the criteria. In order to overcome these practical difficulties, new ultrasonic testing criterion is suggested. In this new method, the theoretical interface reflection signal amplitude level is calculated and suggested as an acceptance criteria with the back reflection signal set to 100% FSH(Full Screen Height) which is based on acoustic impedance mismatch at the clad interface for the explosive clad ultrasonic inspection. Applicability of suggested criterion, for the explosive clad Fe-Naval Brass with different bonding quality is confirmed to the pre-existed KS and ASTM specifications and verified by using SEM (Seanning Electron Microscope) micrograph. The results obtained by the suggested method is more conservative than the results according to the KS B 0234 and ASTM A 578 specifications The suggested method could be applicable to any other combination of explosive clad ultrasonic inspection.

• Tribology and Lubricants
• /
• v.35 no.5
• /
• pp.317-322
• /
• 2019

In spite of progress in tribological research, machine component failure due to friction and wear has been reported frequently. This failure may lead to secondary damage that can cause huge expense for maintenance and repair. To prevent economic loss, it is important to detect and predict the initial failure point. In this sense, various researchers have been tried to develop Condition Monitoring (CM) method using Acoustic Emission (AE) generated while the materials undergo failure. In this study, effect of particles on friction and wear was investigated using the pin-on-plate friction test and AE signal was recorded with a band-width type AE sensor. The experiments were performed in dry and lubricant conditions using steel and glass as specimens. After the experiment, 3D laser microscope image was captured to evaluate the wear behavior quantitatively. The AE signal was analyzed in time-domain and frequency-domain. The amplitude was compared with the frictional results. The results of this study showed that particle generation accelerate wear, generate high magnitude AE signal and change the frequency characteristics of the signal. Also, lubricant condition test results showed low coefficient of friction, low wear rate, and low magnitude of AE signal compared to the dry condition. It is expected that the results of this study will aid in better assessment of wear in CM technology

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.17 no.2
• /
• pp.237-247
• /
• 1993

Carbon fiber reinforced plastics(CFRP) have gained increased application in aerospace structures because of their specific strength and stiffness, but are sensitive to impact-induced damage. An experimental investigation was carried out to evaluate the impact resistance of CFRP according to the ply angle. The specimens of angle ply laminate composites were employed with [0.deg. $_{6}$/ .deg.$_{10}$/0.deg.$_{6}$], in which 6 kinds of ply angle such as .deg.=15.deg., 30.deg., 45.deg., 60.deg., 75.deg. and 90.deg. were selected. The impact tests were conducted using the air gun type impact testing machine by steel balls of diameter of 5 mm and 10 mm, and impact-induced damages were evaluated under same impact speed of V=60m/s. The impact damaged zones were observed through a scanning acoustic microscope (SAM). The obtained results were summarized as follows: (1) Delaminations on the interfacial boundaries showed th directional characteristics to the fiber directions. The delamination area on the impact side (interface A) was considerably smaller compared to that of the opposite side (interface B). (2) Cracks corresponding to other delaminations than those mentioned in SAM photographs were also seen on the impact damaged zone. (3) The delamination patterns were affected by the ply-angle, the dimensions of the specimen, and the boundary conditions. (4) The impact damaged zone showed zone showed the delamination on the interfacial boundaries, transverse shear cracks of the surface layer, and bending cracks of the bottom layer.r.r.r.