• 대한전자공학회:학술대회논문집
• /
• 대한전자공학회 2001년도 The 6th International Symposium of East Asian Resources Recycling Technology
• /
• pp.478-481
• /
• 2001

The spent petrochemical catalyst used in the manufacturing process of terephthalic-acid contains valuable metals such as cobalt and manganese. To recover these metals, sulfuric acid leaching was performed with hydrogen peroxide as a reducing agent. Low extractions of Mn, Co and Fe were obtained by sulfuric acid leaching without reducing agent. With adding hydrogen peroxide as a reducing agent, the high extraction of these metals could be obtained. Different from general leaching experiment, the extraction rates of metal components were decreased with increasing reaction temperature in this case. Under the optimum condition, the extraction rates of Mn, Co and Fe were 93.0%, 87.0% and 100% respectively.

• 자원리싸이클링
• /
• 제18권5호
• /
• pp.44-51
• /
• 2009

전자스크랩중에 함유된 구리 및 주석을 습식공정으로 회수하기 위하여 기초 연구를 실시하였다. 침출제로 질산을 이용하여 분쇄된 전자스크랩에서 구리, 주석, 납, 철 등의 금속 성분들에 대한 침출율을 조사하고 최적 침출조건을 제시 하였다. 이러한 질산 침출 용액으로부터 TBP를 이용하여 유리질산을 분리 추출하여 재활용하기 위한 기초 연구를 실시하였다. 실험 결과 3.0-4.0 M 질산으로 구리를 효과적으로 침출시킬 수 있었으며, 질산 침출액 중 유리질산을 60% TBP에 의해 95%정도 추출이 가능하였고, 유기상에 추출된 질산의 98%를 증류수에 의해 탈거하여 질산침출액으로 재사용이 가능하였다.

• 자원리싸이클링
• /
• 제11권3호
• /
• pp.10-16
• /
• 2002

폐리튬이온전지로부터 추출한 $LiCoO_2$의 침출에서 황산, 질산과 같은 강산은 Co와 Li을 완전 용해시키므로 Co와 Li을 분리하여 회수하기 위해서는 별도의 공정이 필요하다. 낮은 pH에서 Co oxalate의 용해도가 낮다는 점을 착안한 oxalic acid 침출에서 양극활물질로부터 Co를 선택적으로 회수하는 연구를 수행하였다. 변수실험으로 도출된 최적조건, oxalic acid 3M, 침출온도 $80^{\circ}C$, 초기 광액농도 50g/L.의 조건에서 순수한 $LiCoO_2$를 침출한 결과, Li이 95% 이상 용해되는 반면에 Co는 1% 이하의 침출율을 나타내었다. 같은 침출조건에서 폐리튬이온전지로부터 선별한 양극활물질을 침출한 결과, Co와 Li의 침출율은 각각 0.25%, 99%로 높은 선택성을 보였다. 용액 중에 잔류하는 Li은 $Na_2$$CO_3$혹은 LiOH을 첨가하여 Li 탄산염 흑은 Li 수산화물의 형태로 회수할 수 있다.

• Journal of the Korean Wood Science and Technology
• /
• 제35권5호
• /
• pp.46-57
• /
• 2007

The leachability of boron in zinc borate (ZB)-modified oriented strandboard (OSB) from southern wood species was investigated in this study. The leaching experiments were conducted by exposing edge-sealed OSB samples under running water at $31^{\circ}C$ for 8, 24, 72, and 216 h. The results from leached samples were compared with those from the unleached controls. Boron leaching of the modified OSB occurred upon the initial water exposure, and the leaching rate decreased as the leaching time increased. Initial boric acid equivalent (BAE) level, wood species, and sample thickness swelling significantly influenced the leachability. There was no consistent effect of polyethylene glycol (PEG) on zinc borate leaching. The glue-line washing within OSB due to thickness swelling of the test samples under water and decomposition of the borate to form water-soluble boric acid were thought to be two possible causes for the observed leaching. The relationship between assayed BAE and leaching time followed a decaying exponential function for zinc borate treated OSB. From the boron/zinc ratio after each leaching period, boron element in ZB was more or less leachable. The material constant of the regression models allowed comparing the leachability of the modified OSB for various wood species. An unified leaching method for treated wood composite materials is needed.

• Nuclear Engineering and Technology
• /
• 제32권1호
• /
• pp.10-16
• /
• 2000

Preliminary experiment was peformed to investigate the leaching characteristics of paraffin waste forms that had been recently generated in large quantities at domestic nuclear power plants. At first, waste simulants whose compositions were different in mixing ratio of paraffin to boric acid were prepared. Their compressive strengths were measured and ninety-day leaching test of specimen including cobalt was carried out according to ANSI/ANS-16.1 test procedure. Water immersion test was also conducted keeping pace with leaching test and the weight change and the compressive strength of specimen were observed after ninety days. The compressive strength of waste form exhibited 666 psi (4.53 MPa) in the case where mixing ratio of boric acid to paraffin was 78/22, which was adopted in concentrate waste drying system of domestic nuclear power plants. The leaching test resulted in about 50% of the cumulative fraction leached for boric acid and cobalt, respectively. The specific gravity of waste form was 0.87 ［g/g］whose value was less than that of water because the weight loss of about 39% occurred after the water immersion test of ninety days. It was also observed that the waste form which had undergone ninety-day water immersion test exhibited the compressive strength of 203 psi (1.38 MPa).

• 자원리싸이클링
• /
• 제19권5호
• /
• pp.25-30
• /
• 2010

CMSX-4 초내열합금의 순환활용을 위한 습식제련기술 개발의 일환으로 영신에서의 니켈, 코벨트, 크롬, 알루미늄 등 주요 구성 금속성분들의 침출 특성을 조사하였다. 염산농도에 따른 합금시료 내 주요 금속성분들의 침출율은 염산농도가 높아짐에 따라 증가하였으나, 3 M 이상에서는 둔화되었다 염산농도 4 M, 고액비 10 g/L, 침출시간 60 분 조건에서 침출온도가 높아짐에 따라 침출율은 급격히 증가하였으며, $90^{\circ}C$에서 니켈 93.2%, 알루미늄 89.9%, 코발트 80.4%, 크롬 79.1%의 침출율을 나타내었다. 한편 침출 초기에는 니켈과 알루미늄의 침출속도가 빠르고 60 분 이후 급격히 둔화되는 형태를 보인 반면 코발트와 크롬은 침출이 느리고 60 분 이후의 감소율만 상대적으로 적었다. 120 분 경과 시 주요 금속원소들의 침출율은 모두 99% 수준에 도달하였다. 고액비가 높아지면 침출율은 서서히 감소하였으며, 니켈과 알루미늄이 코발트와 크롬에 비하여 침출율 감소가 적었다. 염산농도 4 M, 침출온도 $90^{\circ}C$, 침출시간 120 분의 조건에서 고액비 125 g/L 이하의 조건이 주요 금속 성분의 침출에 효과적임을 확인하였으며, 이는 CMSX-4 합금의 금속학적 조직구조와 관련이 있는 것으로 생각된다.

• 대한화학회지
• /
• 제11권1호
• /
• pp.28-32
• /
• 1967

The direct acid leaching of domestic Marmatite concentrate at elevated temperatures and pressures was investigated. Almost 100 percent of zinc was extracted from the concentrate liberating free sulfur in 4 hours at $100^{\circ}C$ when the oxygen partial pressure was 5 atm. in sulfuric acid solution. By applying the Arrhenius equation to leach reaction in the range of $60^{circ}$ to $100^{\circ}C$ at the same oxygen partial pressure, 15.7 kcal per mole of activation energy was calculated. At the initial stage of leaching, the rate of reaction increased linearly by increasing temperature and pressure. The concentration of sulfuric acid gave minor effect to leaching velocity in the range of 5 to 20 percent. The particle size should be under 270 mesh for 100 percent extraction of zinc.

• 자원리싸이클링
• /
• 제20권6호
• /
• pp.63-70
• /
• 2011

코발트 정광으로부터 코발트와 구리의 회수를 위한 환경친화적인 침출공정 개발의 일환으로 유기산을 침출제로 사용하여 각 금속의 침출 거동에 대하여 기초 연구를 실시하였다. 주요 실험 변수로는 유기산 종류 및 농도, 반응 시간 및 온도 그리고 고액농도비 등 코발트와 구리의 침출에 영향을 미칠 수 있는 인자들에 대하여 고찰하여 최적 조건을 얻고자 하였다. 실험 결과 유기산중 구연산이 코발트 및 구리의 침출에 효과적이었다. 한편, 구연산을 이용한 침출실험 결과 구연산의 농도가 2.0M에서 코발트 99 %, 구리 95%, 니켈 70%의 높은 침출율을 나타내었다. 또한, 과산화수소는 약 3 vol. % 정도 첨가하는 것이 적당하였고, 최적 반응온도는 $70^{\circ}C$이었다.

• 자원리싸이클링
• /
• 제24권6호
• /
• pp.24-30
• /
• 2015

본 연구에서는 페로망간 제조공정에서 발생한 집진분의 황산침출에 대하여 조사하였다. 황산의 농도, 반응온도, 교반속도, 입자크기 및 고-액비가 집진분 중의 Mn과 Fe의 침출에 미치는 영향에 대하여 검토하였다. Mn과 Fe의 침출속도는 황산의 농도가 높고 반응온도가 높을수록 높아졌다. 실험결과를 입자수축모델을 이용하여 검토한 결과 침출반응은 입자표면에서의 화학반응에 의해서 율속되는 것으로 생각된다. Mn과 Fe 침출반응의 활성화에너지는 각각 79.55 kJ/mol과 77.48 kJ/mol로 계산되었다.

• 자원환경지질
• /
• 제52권6호
• /
• pp.595-604
• /
• 2019

본 연구 목적은 비-가시성 금 정광을 마이크로웨이브-질산용출 시키고, 여과지를 이용하여 금을 단순하게 얻고자 하였다. 본 실험에서 사용된 시료의 경우 질산농도별로 마이크로웨이브-질산용출실험을 수행한 결과 Fe, Te, Ag 등은 완전용출(100%) 되었지만, Au는 용해되지 않았다. 용출용액을 3장의 여과지로 여과하여 SEM/EDS 분석한 결과 첫 번째, 두 번째 및 세 번째 여과지의 표면 및 단면 모두에서 Au가 검출되었다. 고체-잔류물이 포함된 여과지 3장을 모두 납-시금법에 사용한 결과 질산농도 모두에서 금 입자들이 회수되었다. 최대 금 입자(452.50g/t)가 얻어진 용출조건은 질산농도 6M에서 그리고 마이크로웨이브 조사시간 12분에서였다.