• Applied Microscopy
• /
• v.47 no.3
• /
• pp.110-120
• /
• 2017

Non-isothermal thermogravimetry (TG) measurements on melt-quenched $Bi_xSe_{100-x}$ specimens (x=0, 2.5, 7.5 at%) were made at a heating rate ${\beta}=10^{\circ}C/min$ in the range $T=35^{\circ}C{\sim}950^{\circ}C$. The as-measured TG curves confirm that $Bi_xSe_{100-x}$ samples were thermally stable with minor loss at $T{\leq}400^{\circ}C$ and mass loss starts to decrease up to $600^{\circ}C$, beyond which trivial mass loss was observed. These TG curves were used to estimate molar (Se/Bi)-ratios of $Bi_xSe_{100-x}$ samples, which were not in accordance with initial composition. Shaping features of conversion curves ${\alpha}(T)-T$ of $Bi_xSe_{100-x}$ samples combined with a reliable flow chart were used to reduce kinetic mechanisms that would have caused their thermal mass loss to few nth-order reaction models of the form $f[{\alpha}(T)]{\propto}[1-{\alpha}(T)]^n$ (n=1/2, 2/3, and 1). The constructed ${\alpha}(T)-T$ and $(d{\alpha}(T)/dT)-T$ curves were analyzed using Coats-Redfern (CR) and Achar-Brindley-Sharp (ABS) kinetic formulas on basis of these model functions, but the linearity of attained plots were good in a limited ${\alpha}(T)-region$. The applicability of CR and ABS methods, with model function of kinetic reaction mechanism R0 (n=0), was notable as they gave best linear fits over much broader ${\alpha}(T)-range$.