• Journal of the Korea Concrete Institute
• /
• v.17 no.1 s.85
• /
• pp.129-137
• /
• 2005

In Korea, due to the insufficiency of natural aggregates and increasing needs of crushed stones, it is necessary to examine the alkali-silica reaction of the crushed stones. The reaction produces an alkali-silica reaction gel which can imbibe pore solution and swell to generate cracks that are visible In affected concrete. In general, crushed stones are tested by petrograptuc examination, chemical method and mortar-bar method, but the most reliable method Is mortar-bar test. This study tested alkali-silica reactivity of crushed stones of various rock types using ASTM C 227 and C 1260, and compared the results of two test methods. This study also analyzed effects of particle size and grading of reactive aggregate on alkali-silica reaction expansion of mortar-bar. The effectiveness of mineral admixtures to reduce detrimental expansion caused by alkali-silica reaction was investigated through the ASTM C 1260 method. The mineral admixtures used were nv ash, silica fume, metakaolin and ground granulated blast furnace slag. The replacement ratios of 0, 5, 10, 15, 25 and $35\%$ were commonly applied for all the mineral admixtures and the replacement ratios of 45 and $55\%$ were additional applied for the admixtures that could maintain workability. The results indicate that replacement ratios of $25\%$ for ay ash, $10\%$ for silica fume, $25\%$ for metakaolin or $35\%$ for ground granulated blast furnace slag were most effective to reduce alkali-silica reaction expansion under the experimental conditions.

• Computers and Concrete
• /
• v.20 no.6
• /
• pp.705-710
• /
• 2017

The effectiveness of mineral additives in suppressing alkali-silica reactivity has been studied in this work. Experimentation has been performed in accordance with the procedures prescribed in ASTM C 1567. In the scope of the investigation, a quarry aggregate which was reactive according to ASTM C 1260 was tested. In the experimental program, prismatic mortar specimens measuring $25{\times}25{\times}285mm$ were produced. Ten sets of production, three specimens for each set, were made. Length changes were measured at the end of 3, 7, 14 and 28 days and then expansions in percentage have been calculated. Fly ash, silica fume, and metakaolin have been used as cement replacement in different ratios for the testing of the alkali-silicate reactivity of the aggregate. In the mixes performed, the replacement ratios were 20%, 40%, and 60% for the fly ash, and 5%, 10%, and 15% for the silica fume, and 5%, 10%, and 15% for the metakaolin. Mixes without mineral additives were also produced for comparison. The beneficial effect in suppressing alkali-silica reactivity is highly noticeable as the replacement ratios of the mineral additives increase regardless of the type of the mineral additive used. Being more concise, the optimum concentrations of using silica fume and metakaolin in mortar in suppressing ASR is 10%, respectively, while it is 20% for fly ash.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.05a
• /
• pp.49-54
• /
• 2001

Using waste glass in concrete can cause crack and strength loss by the expansion of alkali-silica reaction(ASR). In this study, ASR expansion and properties of strength were analyzed in terms of brown waste glass content, and fibers(steel fiber, polypropylene fiber) and fiber content for reduction ASR expansion due to waste glass. In this accelerated ASTM C 1260 test of waste glass, pessimum content can not be found. Also, when used the fibers with waste g1ass, there is an effect on reduction of expansion and strength loss due to ASR between the alkali in the cement paste and the silica in the waste glass. Specially, adding 1.5 vol.% of steel fiber to 20% of waste glass the expansion ratio was reduced by 40% and flexural strength was developed by up to 110% comparing with only Waste glass ( $80^{\circ}C$ $H_{2}$ O curing).

• Journal of the Korea Concrete Institute
• /
• v.13 no.3
• /
• pp.213-220
• /
• 2001

Incorporation of wastes glass aggregate in mortar may cause crack and this may result in the strength reduction due to alkali-silica reaction(ASR) and expansion. The purposes of this study were to investigate the properties of alkali-silica expansion and strength loss through a series of experiments which had a main experimental variables such as waste glass aggregate contents, glass colors, fiber types, and fiber contents. The steel fibers and polypropylene fibers were used for constraining the ASR expansion and mortar cracking. From the result, green waste glass was more suitable than brown one because of low expansion. And in this accelerated ASTM C 1260 test of waste glass, pessimum content can not be found. Also, when used the fibers with waste glass, there is an effect on reduction of expansion and strength loss due to ASR between the alkali in the cement paste and the silica in the waste glass. Specially, adding 1.5 vol.% of steel fiber to 20% of waste glass, the expansion ratio was reduced by 40% and flexural strength was developed by up to 110% comparing with only waste glass(80$\^{C}$ H$_2$O curing).

• Computers and Concrete
• /
• v.13 no.6
• /
• pp.739-748
• /
• 2014

In this article, by using experimental studies and artificial neural network has been tried to investigate the use of nano-silica as concrete admixture to reduce alkali-silica reaction. If there are reactive aggregates and alkali of cement with enough moisture in concrete, a gel will be formed. Then with high reactivity between alkali of cement and existence of silica in aggregates, this gel will expand by absorption of water, and causes expansive pressure and cracks be formed. At the time passes, this gel will reduce both durability and strength of the concrete. By reducing the size of silicate to nano, specific surface area of particles and number of atoms on the surface will be increased, which causes more pozzolanic activity of them. Nano-silica can react with calcium hydroxide ($Ca(OH)_2$) and produces C-S-H gel. In this study, accelerated mortar bar specimens according to ASTM C 1260 and ASTM C 1567, with different mix proportions were prepared using aggregates of Kerman, such as: none admixture and plasticizer, different proportions of nano-silica separately. By opening the moulds after 24 hour and curing in water at $80^{\circ}C$ for 24 hour, then curing in (1N NaOH) at $80^{\circ}C$ for 14 days, length expansion of mortar bars were measured and compared. It was noted that, the lowest length expansion of a specimens shows the best proportion of admixture based on alkali-silica reactivity. Then, prediction of alkali-silica reaction of concrete has been investigated by using artificial neural network. In this study the backpropagation network has been used and compared with different algorithms to train network. Finally, the best amount of nano silica for adding to mix proportion, also the best algorithm and number of neurons in hidden layer of artificial neural network have been offered.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.93-98
• /
• 2001

Using waste glass in concrete can cause crack and strength loss by the expansion of alkali-silica reaction(ASR). In this study, ASR expansion and properties of strength were analyzed in terms of clear waste glass grading, and by-products(fly ash, blast-furnace slag) and by-products content for reduction ASR expansion due to waste glass. In this accelerated ASTM C 1260 test of waste glass, pessimum grading can be found. Also, when the by-products are used with waste glass, there is an effect on reduction of expansion and strength loss due to ASR between the alkali in the cement paste and the silica in the waste glass.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.431-434
• /
• 2005

The effect of ground granulated blast furnace slag to prevent detrimental expansion due to alkali-silica reaction was investigated through the ASTM C 1260 method. This method is one of the most commonly used method because results can be obtained within 16 days. Reactive aggregate used is a metamorphic rock. The replacement ratios of portland cement by ground granulated blast furnace slag were 0, 15, 25, 35 and 55 percent, respectively. The results indicate that 35 percent replacement of portland cement by ground granulated blast furnace slag seems to be effective to reduce alkali-silica reaction expansion under this experimental conditions.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.435-438
• /
• 2005

The effect of content of reactive aggregate on alkali-silica reaction was investigated through the ASTM C 1260 method. The replacement proportions of fine aggregate by reactive aggregate were 25, 50, 75 and $100\%$, respectively. Reactive aggregate and fine aggregate(non-reactive aggregate) used are a metamorphic rock and andesite rock, respectively. The results indicate that the mortar-bar containing $25\%$ replacement of fine aggregate by reactive aggregate shows the lowest expansion but expansion in excess of $0.1\%$ at 16 days, which can distinguished between deleterious and potentially reactive. Although content of reactive aggregate is a small amount, it can cause detrimental expansion due to alkali-silica reaction.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.185-188
• /
• 2004

The effect of fly ash to prevent detrimental expansion due to alkali -silica reaction was investigated through the ASTM C 1260 method that is one of the most commonly used method because results can be obtained within about 16 days. Reactive aggregate used is a netamorphic rock and sedimentary rock. The replacement proportions of portland cement by fly ash were respectively 0, 5, 10, 15, 25 and 35 percent. Expansion of mortar bars due to alkali-silica reaction decreased with the increase of fly ash content. The results show that the expansion due to alkali-silica reaction is dramatically reduced in the presence of high volume fly ash. When the fly ash content examine from all angles (strength and a flow), the replacement proportions of fly ash is about $25\%$ in order to control on expansion.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.11a
• /
• pp.155-156
• /
• 2017

Borosilicate glass was incorporated to improve the neutron shielding capability of concrete. Boron is a typical neutron shielding material, and it is contained in borosilicate glass. However, borosilicate glass causes alkali-silica reaction, which damages the concrete. Therefore, studied to reduce the expansion due to alkali-silica reaction and to improve the neuton shielding capability. The measurement of the expansion due to the alkali-silica reaction was based on ASTM C 1260. Experimental results show that the expansion due to alkali-silica reaction is reduced when borosilicate glass powder incorporated. In addition, the neutron shielding capability was significantly improved when the fine aggregate replaced with borosilicate glass.