• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.303.2-303.2
• /
• 2014

The oxides of group IV transition metals such as titanium, zirconium, hafnium have many important current and future application, including protective coatings, sensors and dielectric layers in thin film electroluminescent (TFEL) devices. Recently, group IV transition metal oxide films have been intensively investigated as replacements for SiO2. Due to high permittivities (k~14-25) compared with SiO2 (k~3.9), large band-gaps, large band offsets and high thermodynamic stability on silicon. Herein, we report the synthesis of new group IV transition metal complexes as useful precursors to deposit their oxide thin films using chemical vapor deposition technique. The complexes were characterized by FT-IR, 1H NMR, 13C NMR and thermogravimetric analysis (TGA). Newly synthesised compounds show high volatility and thermal stability, so we are trying to deposit metal oxide thin films using the complexes by Atomic Layer Deposition (ALD).

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.114-114
• /
• 2012

Metal-oxide-semiconductor field-effect transistors (MOSFETs)의 critical dimension (CD)가 sub 45 nm로 줄어듬에 따라 기존에 gate dielectric으로 사용하고 있는 SiO2에서 발생되는 high gate leakage current 때문에 새로운 high dielectric constant (k) 물질들이 연구되기 시작하였다. 여러 가지 high-k 물질 중에서, aluminum-oxide (Al2O3)는 높은 dielectric constant (~10)와 전자 터널링 barrier height (~2eV) 등을 가지기 때문에 많은 연구가 되고 있다. 그러나 Al2O3를 anisotropic한 patterning을 하기 위해 주로 사용되고 있는 halogen-based 플라즈마 식각 과정에서 나타나는 Al2O3와 하부 layer간의 낮은 식각 selectivity 뿐만 아니라 표면에 발생되는 defect, stoichiometry modification, roughness 변화 등의 많은 문제점들로 인하여 device performance가 감소하기 때문에 이를 해결하기 위한 많은 연구들이 진행중이다. 따라서 본 연구에서는 실리콘 기판위의 atomic layer deposition (ALD)로 증착된 Al2O3를 BCl3/Ar 중성빔을 이용하여 원자층 식각한 후 식각 특성을 분석해 보았다. Al2O3 표면을 BCl3로 absorption시킨 후 Ar 중성빔으로 desorption 시키는 과정에서 volatile한 aluminum-chlorides와 boron oxychloride가 형성되어 layer by layer로 제거됨을 관찰 할 수 있었다.

• Korean Journal of Materials Research
• /
• v.25 no.8
• /
• pp.391-397
• /
• 2015

NiO catalysts/$Al_2O_3$/FeCrAl alloy foam for hydrogen production was prepared using atomic layer deposition (ALD) and subsequent dip-coating methods. FeCrAl alloy foam and $Al_2O_3$ inter-layer were used as catalyst supports. To improve the dispersion and stability of NiO catalysts, an $Al_2O_3$ inter-layer was introduced and their thickness was systematically controlled to 0, 20, 50 and 80 nm using an ALD technique. The structural, chemical bonding and morphological properties (including dispersion) of the NiO catalysts/$Al_2O_3$/FeCrAl alloy foam were characterized by X-ray diffraction, X-ray photoelectron spectroscopy, field-emission scanning electron microscopy and scanning electron microscopy-energy dispersive spectroscopy. In particular, to evaluate the stability of the NiO catalysts grown on $Al_2O_3$/FeCrAl alloy foam, chronoamperometry tests were performed and then the ingredient amounts of electrolytes were analyzed via inductively coupled plasma spectrometer. We found that the introduction of $Al_2O_3$ inter-layer improved the dispersion and stability of the NiO catalysts on the supports. Thus, when an $Al_2O_3$ inter-layer with a 80 nm thickness was grown between the FeCrAl alloy foam and the NiO catalysts, it indicated improved dispersion and stability of the NiO catalysts compared to the other samples. The performance improvement can be explained by optimum thickness of $Al_2O_3$ inter-layer resulting from the role of a passivation layer.

• Current Photovoltaic Research
• /
• v.5 no.2
• /
• pp.63-67
• /
• 2017

Aluminum oxide ($Al_2O_3$) film deposited by atomic layer deposition (ALD) is known to supply excellent surface passivation properties on crystalline Si surface. The quality of passivation layer is important for high-efficiency silicon solar cell. double-layer structures have many advantages over single-layer materials. $Al_2O_3/SiN_X$ passivation stacks have been widely adopted for high- efficiency silicon solar cells. The first layer, $Al_2O_3$, passivates the surface, while $SiN_X$ acts as a hydrogen source that saturates silicon dangling bonds during annealing treatment. We explored the properties on passivation film of $Al_2O_3/SiN_X$ stack layer with changing the conditions. For the post annealing temperature, it was found that $500^{\circ}C$ is the most suitable temperature to improvement surface passivation.

• Korean Journal of Materials Research
• /
• v.15 no.4
• /
• pp.275-280
• /
• 2005

The growth of hafnium oxide thin films by atomic layer deposition was investigated in the temperature range of $175-350^{\circ}C$ using $Hf[N(CH_3)_2]_4\;and\;O_2$ as precursors. A self-limiting growth of $0.6\AA/cycle$ was achieved at the substrate temperature of $240-280^{\circ}C$. The films were amorphous and very smooth (0.76-0.80 nm) as examined by X-ray diffractometer and atomic force microscopy, respectively. X-ray photoelectron spectroscopy analysis showed that the films grown at $300^{\circ}C$ was almost stoichiometric. Electrical measurements performed on $MoW/HfO_2$(20 nm)/Si MOS structures exhibited high dielectric constant$(\~17)$ and a remarkably low leakage current density of at an applied field of $1.5-6.2\times10^{-7}A/cm^2$ MV/cm, probably due to the stoichiometry of the films.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.47-50
• /
• 2002

ZnO nanowires were coated conformally with aluminum oxide ($Al_{2}O_{3}$) material by atomic layer deposition (ALD). The ZnO nanowires were first synthesized on a Si (100) substrate at $1380^{\circ}C$ from ball-milled ZnO powders by a thermal evaporation procedure with an argon carrier gas without any catalysts; the length and diameter of these ZnO nanowires are $20\sim30{\mu}m$ and $50{\sim}200$ nm, respectively. $Al_{2}O_{3}$ films were then deposited on these ZnO nanowires by ALD at a substrate temperature of $300^{\circ}C$ using trimethylaluminum (TMA) and distilled water ($H_{2}O$). Transmission electron microscopy (TEM) images of the deposited ZnO nanowires revealed that 40nm-thick $Al_{2}O_{3}$ cylindrical shells surround the ZnO nanowires.

• Proceedings of the KIEE Conference
• /
• 2002.11a
• /
• pp.79-81
• /
• 2002

ZnO 나노와이어는 ZnO 파우더를 볼밀 처리하여 열증착 방법으로 $1380^{\circ}C$에서 촉매없이 Si 기판위에서 합성되었다. 합성된 ZnO 나노와이어의 길이와 직경은 $20{\sim}30{\mu}m$와 $50{\sim}200$ nm 였다. ZnO 나노와이어 표면을 atomic layer deposition(ALD) 방법으로 $Al_2O_3$ 박막을 얇게 코팅하였다. 성장온도는 $300^{\circ}C$였고, 사용한 전구체는 Trimethlaluminum(TMA)와 distilled water($H_2O$) 이다. Transmission electron microscopy(TEM) 으로 측정한 $Al_2O_3$ 박막의 두께는 40 nm 로서 매우 균일하게 ZnO 나노와이어에 증착되었음을 알 수 있었다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.211-212
• /
• 2010

GaN 기반의 상부발광형 LED는 동작되는 동안 생기는 전기적 단락, 그리고 칩 위의 p-형 전극과 n-형 전극 사이에 생기는 누설전류 및 신뢰성 확보를 위하여 칩 표면에 passivation 층을 형성하게 된다. SiO2, Si3N4와 같은 passivation layers는 일반적으로 PECVD (Plasma Enhanced Chemical Vapor Deposition)공정을 이용한다, 하지만 이는 공정 특성상 plasma로 인한 damage가 유발되기 때문에 표면 누설 전류가 증가 한다. 이로 인해 forward voltage와 reverse leakage current의 특성이 저하된다. 본 실험에서는 원자층 단위의 박막 증착으로 인해 PECVD보다 단차 피복성이 매우 우수한 PEALD(Plasma Enhanced Atomic Layer Deposition)공정을 이용하여 Al2O3 passivation layer를 증착한 후, 표면 누설전류와 빛의 출력 특성에 대해서 조사해 보았다. PSS (patterned sapphire substrate) 위에 성장된 LED 에피구조를 사용하였고, TCP(Trancformer Copled Plasma)장비를 사용하여 에칭 공정을 진행하였다. 이때 투명전극을 증착하기 위해 e-beam evaporator를 사용하여 Ni/Au를 각각 $50\;{\AA}$씩 증착한 후 오믹 특성을 향상시키기 위하여 $500^{\circ}C$에서 열처리를 해주었다. 그리고 Ti/Au($300/4000{\AA}$) 메탈을 사용하여 p-전극과 n-전극을 형성하였다. Passivation을 하지 않은 경우에는 reverse leakage current가 -5V 에서 $-1.9{\times}10-8$ A 로 측정되었고, SiO2와 Si3N4을 passivation으로 이용한 경우에는 각각 $8.7{\times}10-9$과 $-2.2{\times}10-9$로 측정되었다. Fig. 1 에서 보면 알 수 있듯이 5 nm의 Al2O3 film을 passivation layer로 이용할 경우 passivation을 하지 않은 경우를 제외한 다른 passivation 경우보다 reverse leakage current가 약 2 order ($-3.46{\times}10-11$ A) 정도 낮게 측정되었다. 그 이유는 CVD 공정보다 짧은 ALD의 공정시간과 더 낮은 RF Power로 인해 plasma damage를 덜 입게 되어 나타난 것으로 생각된다. Fig. 2 에서는 Al2O3로 passivation을 한 소자의 forward voltage가 SiO2와 Si3N4로 passivation을 한 소자보다 각각 0.07 V와 0.25 V씩 낮아지는 것을 확인할 수 있었다. 또한 Fig. 3 에서는 Al2O3로 passivation을 한 소자의 output power가 SiO2와 Si3N4로 passivation을 한 소자보다 각각 2.7%와 24.6%씩 증가한 것을 볼 수 있다. Output power가 증가된 원인으로는 향상된 forward voltage 및 reverse에서의 leakage 특성과 공기보다 높은 Al2O3의 굴절률이 광출력 효율을 증가시켰기 때문인 것으로 판단된다.

• Journal of the Semiconductor & Display Technology
• /
• v.18 no.1
• /
• pp.32-37
• /
• 2019

Titanium dioxide ($TiO_2$) is a promising dielectric material in the semiconductor industry for its high dielectric constant. However, for utilization on Si substrate, $TiO_2$ film meets with a difficulty due to the large leakage currents caused by its small conduction band energy offset from Si substrate. In this study, we propose an in-situ plasma oxidation process in plasma-enhanced atomic layer deposition (PE-ALD) system to form an oxide barrier layer which can reduce the leakage currents from Si substrate to $TiO_2$ film. $TiO_2$ film depositions were followed by the plasma oxidation process using tetrakis(dimethylamino)titanium (TDMAT) as a Ti precursor. In our result, $SiO_2$ layer was successfully introduced by the plasma oxidation process and was used as a barrier layer between the Si substrate and $TiO_2$ film. Metal-oxide-semiconductor ($TiN/TiO_2/P-type$ Si substrate) capacitor with plasma oxidation barrier layer showed improved C-V and I-V characteristics compared to that without the plasma oxidation barrier layer.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.08a
• /
• pp.130-132
• /
• 2003

ALD(Atomic Layer Deposition) 법으로 박막 알루미나를 형성한 후 웨이퍼 접합과 박막화 공정으로 알루미나를 매몰절연막으로 하는 SOI 구조를 제조하고 그 특성을 조사하였다. 알루미나 박막의 유전 특성과 실리콘과의 계면 특성은 C-V 측정으로, 단면 분석은 SEM(Scanning Electron Microscope) 촬영으로 조사하였다. 알루미나와 실리콘을 접합하기 위하여 1100C에서 열처리를 행한 후 알루미나와 실리콘의 계면 상태 밀도는 $2.5{\times}10^{11}/cm^2-eV$였다. 그리고 SEM의 단연 분석과 AES(Auger Electron Spectroscope)의 깊이 방향 분석을 통해서 매몰 알루미나층의 존재를 확인하였다. 알루미나는 실리콘 산화막보다 높은 열전도성을 가지므로 이를 매몰절연막으로 하여 SOI 구조를 제조하면 기존의 실리콘산화막을 매몰절연막으로 하는 SOI를 기판으로 하여 제조되는 소자보다 selg heating 효과가 감소된 우수한 특성의 소자를 제조할 수 있다.