• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.7
• /
• pp.717-722
• /
• 2011

The purpose of this study is to predict the residual stress in Al6061 during T6 heat treatment. In this study, the variable residual stress in case of the solid solution($530^{\circ}C$, 2h) and artificial ageing($175^{\circ}C$, 9h) of Al6061 subjected to T6 heat treatment is determined at different ageing times. A heat treatment experiment is conducted to determine the heat transfer coefficient, on the basis of which the residual stress during the T6 heat treatment is predicted. In order to take into account the relaxation of residual stress during artificial ageing, a Zener-Wert-Avrami function is used and elasto-plastic nonlinear analysis is conducted through FE-simulation. Further, the residual stress is measured by using the X-ray diffraction(XRD) method, and the result is compared with the result from the FE-simulation. It is found that the residual stress predicted form the FE-simulation is in good agreement with the residual stress measured by using the XRD method.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.23 no.4
• /
• pp.345-349
• /
• 2014

In this study, an age-hardened 6061-T6 alloy sheet was used, which is commonly utilized for auto parts. The junction strength characteristics in relation to the stirring speed and welding speed were studied in accordance with the friction stir welding rotation of the tool pin. Micro hardness measurements of A type and B type pins, for a welding speed of 400 mm/min and a tool rotational speed 3000 rpm, were obtained as Hv104 and Hv111, respectively. For a welding speed of 200 mm/min and a tool rotational speed of 2000 rpm, we obtained Hv48 and Hv50 for A and B type pins, respectively. Microstructure observation showed that the stirring portion was fine and uniform, which occurred because of its plastic deformation. In the thermomechanically affected zone, partial recrystallization was present because of the plastic deformation. The crystal grains in the heat affected zone were coarsened due to the heat generated by friction stir welding.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2010.05a
• /
• pp.907-908
• /
• 2010

• Journal of Welding and Joining
• /
• v.30 no.5
• /
• pp.22-26
• /
• 2012

Butt-joints of A6061-T6 and AZ31 plates were successfully manufactured by using a friction stir welding method. Off-set free joints and off-set joints were fabricated to investigate the effect of the tool plunge position on the mechanical properties of the joints. Hardness test, tensile test and charpy impact test was performed to evaluate the mechanical properties of the joints. Off-set condition resulted in increase of mechanical properties of the joints. The variation of the hardness distribution in the SZ was also stabilized in the off-set condition. Tensile strength of the off-set joint was about 85% against to that of the AZ31 base metal. Impact absorption energy by Charpy-Impact-Test of the off-set joint also increased by almost 2 times against to that of the AZ31 base metal.

• Korean Journal of Materials Research
• /
• v.13 no.6
• /
• pp.374-380
• /
• 2003

The effect of forging parameters, including different forging stock, strain rate and strain, on the mechanical properties of hot-forged Al 6061-T6 was investigated. The forging was conducted using either hydraulic press, crank press or hammer press, respectively, at a forging temperature of $400^{\circ}C$. When using an extruded bar as a forging stock, the tensile strength was lower for the specimens prepared by hammer forging than those by crank press forging. It was found that the coarsening of recrystallized grain was responsible for the decrease in tensile strength with hammer forging. Systematic studies on the effects of strain and strain rate on the tensile properties of hot-forged Al 6061-T6 products using extruded bar as a forging stock further suggested that the coarsening of recrystallized grains and$ Mg_2$Si precipitates complexed the observed trends in the tensile behavior. In case of hot forging with continuous cast bar as a forging stock, on the other hand, the mechanical properties of the specimen were largely improved with hammer press compared to those with crank press, which appeared to be due to the homogenization of microstructure.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.15 no.1
• /
• pp.63-69
• /
• 2006

This study deals with the friction welding of A2024- T6 to A6061- T6; The friction time was variable conditions under the conditions of spindle revolution of 2000rpm, friction pressure of 50MPa, upset pressure of 100MPa, and upset time of 5.0seconds. Under these conditions, the microstructure of weld interface, tensile fracture surface and mechanical tests were studied, of friction weld, and so the results were as follows. 1. When the friction time was 1.5seconds under the conditions, the maximum tensile strength of the friction weld happened to be 292MPa, which is $94.2\%$ of the base material's tensile strength(310MPa). At the same condition, the maximum shear strength was 2l2MPa, which is equivalent to $103\%$ of the base material's shear strength (205MPa). 2. At the same condition, the maximum vickers hardness was Hv 146 at A2024- T6 nearby weld interface, which is higher Hv3 than condition of the friction time 0.5seconds, and the maximum vickers hardness was Hvl20 from weld interface of A6061-T6, which is higher Hv28 then base material's. 3. The results of microstructure analysis show that the structures of two base materials have fractionized and rearranged along a column due to heating and axial force during friction, which has affected in raising hardness and tensile strength.

• Korean Journal of Materials Research
• /
• v.13 no.1
• /
• pp.64-68
• /
• 2003

The 1.6 vol% and 2.5 vol% TiNi/6061Al composites were fabricated by permanent mold casting for investigating the effect of heat treatment on tensile strength for composites. The tensile strength without T6 treatment at 293 K was increased with increasing the volume fraction of TiNi fiber and at 363 K the higher the pre-strain, the higher the tensile strength. The tensile strength of the composite with $T_{6}$ treatment at 293 K was found to increase with increasing both the amount of pre-strain and the volume fraction of TiNi fiber and was higher than that without $T_{6}$ treatment. It should be noted that the tensile strength 2.5vol%TiNi/6061Al composites rolled at a 38% reduction ratio was the maximum value of 298 MPa. The tensile strength of composites decreased with increasing the reduction ratio over 38% because of the rupture of TiNi fiber.

• International Journal of Precision Engineering and Manufacturing
• /
• v.1 no.2
• /
• pp.55-60
• /
• 2000

A comparison of Riveted and bonded repairs, bearing and net tension failures, and Al 6061-T6 plates is presented. The results are then compared with previous papers about bonded repairs on different patch materials and shapes. Aluminum alloys, including Al 6061-T6, have a face-centered-cubic crystal structure. Under normal circumstances, these types of crystal structures do not exhibit cleavage fractures even at very low temperatures. In aluminum-base structures, the cracked plate structures are frequently repaired using mechanical fasteners-either rivets of bolts- even though patch-bonding techniques are applied to repair and reinforce the structure. Static test results indicate that the riveted repairs are affected by the position of the rivers. When using the same size of patch, the bonded repair technique is stronger; the rate of elongation is also increased. Form FEM analysis, it is revealed the origin of patch debonding in patch-bonded structures is the edge of the patch along to the tensile strength.

• Corrosion Science and Technology
• /
• v.19 no.6
• /
• pp.318-325
• /
• 2020

Generally, Al alloys of 5000 and 6000 series show excellent weldability, workability, and specific strength, and are widely used in ship building. A combined experiment via cavitation erosion and corrosion damage involving 6061-T6 Al alloy was performed using potentiodynamic polarization under cavitation erosion (hybrid experiments) with amplitude (cavitation strength). The corrosion current density was approximately 52-fold higher at 30 μm than under static conditions, suggesting that the amplitude greatly affected the damage. The degree of damage increased with increasing cavitation amplitude. After the hybrid experiment, the corrosion rate was compared according to the weight loss and damage depth, and the relationship between the two values was expressed as alpha value. The alpha (α) values at amplitudes of 5 μm, 10 μm and 30 μm were 5.11, 12.81 and 8.74, respectively, suggesting that the α value at 10 μm was greater than at 5 μm, and indicating local corrosion damage. However, the α value at 30 μm was smaller than that of 10 μm, which is attributed to higher damage via uniform corrosion than damage induced by local corrosion.

• Transactions of Materials Processing
• /
• v.16 no.6
• /
• pp.443-446
• /
• 2007

The semi-solid process has been developed near net-shape components for kinds of methods. Thixo-forming with reheating prepared billet and rheo-forming with cooled melt until semi-solid state. Material is applied electromagnetic stirring system to slurry with aluminum 6061 alloy. An experiment has variation factors which are pressure, solid-fraction, stirring current and stirring time. The mechanical properties are compared to forge sample with to apply heat treatment T6. This study is researched function a virtual pressure and fine shape zone. Optimum pressure is found to prevent defect of porosity.