• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1995년도 봄 학술발표회 논문집
• /
• pp.331-338
• /
• 1995

Results of an experimental of the shear and flexures strength of doubly reinforced concrete beams were summarized. A total of 24 beams was tested; 4 without web reinforcement and 20 with web reinforcement in the form of vertical stirrups. Main variables were compressive strength of concrete which was 26.88MPa and 63.4MPa, spacing of stirrups which was no-stirrups, 200, 150, 120, 100 and 90mm. Tests results were compared with stength predicted using the equations of ACI 318-89. The shear reinforcement ratio of the beams, which failed simultaneously under both flexures and shear, were 0.66pvmax for low strength concrete beams and 0.56pvmax for high strength concrete beams, respectively. Thus, ACI equations for shear reinforcement were very conservative.

• International Journal of Concrete Structures and Materials
• /
• 제7권3호
• /
• pp.215-223
• /
• 2013

This study presents the effect of incorporating metakaolin (MK) on the mechanical and durability properties of high strength concrete for a constant water/binder ratio of 0.3.MK mixtures with cement replacement of 5, 10 and 15 % were designed for target strength and slump of 90 MPa and $100{\pm}25mm$. From the results, it was observed that 10 % replacement level was the optimum level in terms of compressive strength. Beyond 10 %replacement levels, the strength was decreased but remained higher than the control mixture. Compressive strength of 106 MPa was achieved at 10 % replacement. Splitting tensile strength and elastic modulus values have also followed the same trend. In durability tests MK concretes have exhibited high resistance compared to control and the resistance increases as the MK percentage increases. This investigation has shown that the local MK has the potential to produce high strength and high performance concretes.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 춘계학술강연 및 발표대회강연 및 발표논문 초록집
• /
• pp.69-70
• /
• 2006

고주파 유도가열 연소합성법에 의해 2분 이내의 짧은 시간에 단일 공정으로 ZrC와 3Si의 혼합 분말로부터 $ZrSi_2-SiC$ 복합재료의 합성과 치밀화가 동시에 이루어졌다. 60MPa의 압력과 90%의 고주파 출력을 가하여 제조된 복합재료의 상대밀도는 약 97%였으며, $ZrSi_2$ 상과 SiC의 평균 결정립 크기는 약154nm와 78nm이었다. 비커스 경도계를 이용하여 측정된 $ZrSi_2-SiC$ 복합 재료의 경도와 파괴인성 값은 각각 $1180kg/mm^2$과 $2.5MPa{\cdot}m^{1/2}$ 이었다.

• International Journal of Precision Engineering and Manufacturing
• /
• 제3권3호
• /
• pp.69-75
• /
• 2002

Measuring dynamic fracture toughness of brittle and small ceramic specimen is very difficult in a SHPB (Split Hopkinson Pressure Bar). As a countermeasure to this difficulty, a dynamic fracture toughness measuring method by the Chevron-notch ceramic specimen was proposed. Tested chevron specimens were of Chevron notch angles of 90$^{\circ}$, 100$^{\circ}$ and 110$^{\circ}$. Through finite element analysis, shape parameters of the Chevron-notch specimens according to notch angles were calculated. And the static fracture tough1ess of the Chevron-notch alumina specimen was measured as 3.8MPa√m similar to that of CT specimen with a precrack. Dynamic fracture toughness was 4.5MPa√m slightly higher than the static one. It was shown in this study that the proposed Chevron-notch specimens are valid to measure dynamic fracture toughness of extremely brittle materials such as ceramic.

• 한국안전학회지
• /
• 제12권4호
• /
• pp.79-85
• /
• 1997

In order to improve the surface characteristics of polymethylmethacrylate(PMMA), oxide thin film coatings were applied using the sol-gel dip-coating technique. The $Si(OC_2H_5)_4$, tetra-ethyl-ortho-silicate(TEOS) was used as a starting material for $SiO_2$ coating. The hardness of the alkoxy-derived oxide-coated PMMA was increased from 190 MPa for non-coated PMMA with increasing film thickness. By optimizing the heating conditions and the hydrolysis conditions, a maximum apparent hardness obtained In the present study was achieved 310 MPa using the withdrawal velocity of 5cm/min and heat treatment at $90^{\circ}C$ for 5 hours, which is about 1.6 times larger than that of uncoated PMMA.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2003년도 international symposium on advanced powder metallurgy
• /
• pp.39-40
• /
• 2003

1) Using a developed high-frequency induction heated sintering method, the rapid densification of WC-Co hard materials was accomplished using ultra fine powders with 260 nm size within 1 minute. 2) The relative density of the composite was 99.5% for the applide pressure of 60MPa and the induced current for 90% output of total capacity. 3) The grain size of WC-Co hard materials is about 260nm and the average thickness of the binder phase determined is about 11nm. The fracture toughness and the hardness of this work 12 $MPa{\cdot}nm^2$, respectively. 4) Using pressureless sintering, we produced dense WC-Co hard materials with a relative density of 97% without applying pressure.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 추계 학술발표회 제16권2호
• /
• pp.715-718
• /
• 2004

The evaluation of durability of resin concrete was examined through various tests, i.e., compressive strength, absorption, abrasion, chemical attack resistance and bond between general and resin concrete. 2 types of concrete were used such as 40 MPa of general concrete and 90 MPa of resin concrete. The characteristics of resin concrete was more improved than that of general concrete, and especially, resin concrete was most effective on compressive strength, the resistance to $H_2SO_4$ solution attack and absorption. However, abrasion. is almost same between general concrete and resin concrete.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 추계 학술발표회 논문집
• /
• pp.673-676
• /
• 2006

Steel FibreReinforced Shotcrete(SFRS) is one of the main tunnel support along with the rock bolt during the excavation and after the completion of the tunnel. In the standard qualification of the SFRS defined by Korea Highway Corporation, 28 day core specimen has to meet the compressive strength of 19.6 MPa and over 90 % fibre contents. Furthermore, for the 28 days brick shaped specimen made by shooting, flexural strength should be over 4.4 MPa and flexural toughness ratio which can be calculated from flexural toughness factor has to meet more than 68% of flexural strength. In shotcrete, accelerating agent is added for the rapid strength development. Silicate and aluminate type agents are known to develop shotcrete strength rapidly, however, has such problem to degrade the middle and long term strength. Hence, using poly carboxylic super plasticizer, it was aimed to enhance the quality of the shotcrete with the lower water-cement ratio and the same level of workability. The present paper shows the part of the field test result and its analysis.

• 한국세라믹학회지
• /
• 제29권2호
• /
• pp.143-151
• /
• 1992

Partially stabilized alpha-sialon composition (X=0.1) powder was hot-pressed at 1800~200$0^{\circ}C$ for 0~90 min with 30 MPa. Sintering behavior, phase changes and mechanical properties for the specimens were studied. As sintering temperature was raised from 1800 to 190$0^{\circ}C$, the relative density tended to increase and reached 99% of theoretical at 190$0^{\circ}C$. However the amount of alpha-sialon decreased because alpha-sialon transformed to beta-Si3N4 and yttrium rich silicate glass. In the case of hot-pressing at 190$0^{\circ}C$ for various times, densification increased with sintering time and full densification above 99% of theoretical was attained by 30 min. The amount of alpha-sialon decreased with sintering time. The maximum strength of 825 MPa was obtained by hot-pressing at 190$0^{\circ}C$ for 60 min.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.360-361
• /
• 2006

Nanostructured aluminum powders were obtained by means of planetary ball milling with methanol as the Process Control Agent (PCA). The behavior, during milling, was considered measuring the microhardness and grain size at different milling times. Bulk near-full density samples were sintered using the Spark Plasma Sintering technology with different schedules: temperature of $500^{\circ}C$ and $550^{\circ}C$, pressure of 30 MPa and 60 MPa and different modes of applying the pressure were changed in order to understand the behavior during sintering. All the samples retained their nanostructure with an increase of the grain size from about 46 up to 70-90 nm.