• Journal of Welding and Joining
• /
• v.16 no.2
• /
• pp.57-63
• /
• 1998

This study deals with the friction weldability of machine structural carbon steel (SM45C) to Al-Mg-Si aluminium alloy (A6063). The bonding strength of friction welded joints, from all mechanical test, exceeded that of A6063 base metal, under the condition of friction time 1.5 sec, upset pressure 80MPa. The friction welded joints under these conditions exhibited tensile strength of 262MPa, bending angle of 90$^{\circ}$ without crack at weld interface and shear strength of 113MPa. Consequently, the friction weldability of SM4C to A6063 was very excellent, and that was possible without special preparation of weld surfaces.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1041-1042
• /
• 2006

High heat-resistant Al-Fe-V-Si and Al-Fe-V-Si-X rapidly solidified powder metallurgy (RS P/M) alloys have been developed under well-controlled high purity argon gas atmosphere. The $Al_{90.49}Fe_{6.45}V_{0.68}Si_{2.38}$ (at. %) RS P/M alloy exhibited high elevated-temperature strength exceeding 300 MPa and good ductility with elongation of 6 % at 573 K. Reduction of $H_2O$ partical pressure in P/M processing atmosphere led to improvement in mechanical properties of the powder-consolidated alloys under elevated-temperature service conditions. Ti addition to the Al-Fe-V-Si conduced to enhancement of the strength at room temperature. The tensile yeild strength and ultimate strenght were 545 MPa and 722 MPa, respectively.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.5
• /
• pp.134-140
• /
• 2017

In this study, the flexural behavior of high strength concrete members with different curing condition of 90 MPa of compressive strength was investigated. Experimental parameters included normal and low temperature curing conditions, tensile steel amount and concrete compressive strength. 8 beam members were fabricated and flexural tests were carried out. Crack spacing, load-deflection relation, load-strain relation and ductility index were determined. Experimental results show that as the amount of rebar increases, the number of cracks increases and the crack spacing decreases. The higher the concrete strength, the smaller the number of cracks, but the effect is significantly smaller than the amount of rebar. As a result of comparison with the proposed average crack spacing in the design criteria, the experimental results are slightly larger than the results of the proposed formula, but the proposed formula does not reflect the concrete strength and curing conditions. The ductility index of normal temperature cured members was 3.36~6.74 and the ductility index of low temperature cured members was 1.51~2.82. The behavior of low temperature cured members was found to be lower than that of normal temperature cured members. As a result of comparing the ductility index with the existing studies similar to the experimental members, the ductility index of the high strength concrete member was larger than the ductility index of the ordinary strength concrete of the previous study. Further research is needed to understand more specific results.

• Korean Journal of Weed Science
• /
• v.30 no.1
• /
• pp.25-33
• /
• 2010

Several experiments were conducted in growth chambers and a greenhouse to determine the influence of various environmental factors on seed germination and seedling emergence of Indian jointvetch. Fully matured seeds of Indian jointvetch germinated only 42%. The germination percent increased as the storage temperature increased with time. More than 90% seeds germinated when the seeds were kept at $40^{\circ}C$ for seven months, but germination was 58.9 and 55.1% when kept at 25 and $4^{\circ}C$, respectively. Non-dormant seeds of Indian jointvetch germinated 91.1 and 92.4% at 30 and $30/25^{\circ}C$, respectively. Germination percent increased with increasing both prethermal temperature and time. The prethermal temperature of $90^{\circ}C$ for 40 minutes was the best for maximum germination (94.5%). Germination and growth of Indian jointvetch tended to decrease slightly until -0.3 MPa osmotic potential (water stress induction) and then declined drastically and the seeds did not germinate at below -0.5 MPa osmotic potential. Indian jointvetch seems to grow well in moist and flooding conditions since emergence and growth of seedling increased with increasing soil moisture content and the water level.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.31 no.4
• /
• pp.182-189
• /
• 2021

Porous ceramics were manufactured using the foaming method for the development of inorganic insulating materials. Silica fume and SiO₂ were used as main raw materials, and bentonite was used as a rapid setting agent for uniform structure formation of porous ceramics. The porous ceramics were sintered at 1200℃, and porosity, density, compressive strength, microstructure and thermal conductivity were analyzed. As the content of silica fume to SiO₂ of the porous ceramics increased 70 to 90 %, the specific gravity increased from 0.63 to 0.69, and the compressive strength increased from 9.41 Mpa to 12.86 Mpa. But, the porosity showed a tendency to decrease from 72.07 % to 70.82 %, contrary to the specific gravity. As a result of measuring the thermal conductivity, the porous ceramic with a silica fume content of 70 % showed a thermal conductivity of 0.75 to 0.72 W/m·K at 25 to 800℃, respectively, and, another that a silica fume content of 90 % showed a 0.66~0.86 W/m·K. So the lower the silica f ume content, the lower the thermal conductivity, which was conf irmed to be consistent with porosity result. As a result of microstructure analysis using SEM (Scanning Electron Microscope), pores in the range of tens to hundreds ㎛ were observed inside and outside the porous ceramic, and it was confirmed that the pore distribution was relatively uniform.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.04a
• /
• pp.77-78
• /
• 2006

급속소결방법인 고주파유도가열 소결법과 펄스전류활성 소결법을 이용하여 습식 볼밀링으로 혼합한 WC-8wt.%Ni분말에 60MPa의 압력과 고주파유도가열장치의 경우 전체 용량 (15kw)의 90%에 해당하는 고주파출력을, 펄스전류활성 소결장치의 경우 2800A의 펄스전류를 가하여 치밀한 소결체를 2분이내의 짧은 시간에 제조하였다. WC 초기입자크기가 증가함에 따라 제조된 소결체의 입자크기와 평균자유행로는 증가하였다. 또한 WC 결정립 크기가 증가함에 따라 경도는 증가하였으며, 파괴인성은 감소함을 알 수 있었다. $0.5{\mu}m$의 분말을 60MPa의 압력하에서 고주파유도가열 소결법에 의해 얻어진 소결체의 파괴인성과 경도는 각각 $1813kg/mm^2$과 $8.9MPa{\cdot}m^{1/2}$ 이었고, 펄스전류활성 소결법에 의해 제조된 소결체의 경도와 파괴인성은 각각 $1839kg/mm^2$과 $8.5MPa{\cdot}m^{1/2}$ 이었다.

• Journal of the Korean Society for Heat Treatment
• /
• v.21 no.3
• /
• pp.131-136
• /
• 2008

The fatigue characteristics of the carbon fiber reinforced carbon composites (CFRC) material are necessary for the advanced industries requiring the thermal resistance. The research and development of CFRC have been in progress in the field of aerospace and defense industry. In this paper, we investigated the fatigue characteristics of CFRC by using an aircraft brake disk system. As the results of a series of tensile tests, the tensile strengths of CFRC were appeared 102.8 MPa ($0^{\circ}$), 98.6 MPa ($60^{\circ}$), and 95.5 MPa ($90^{\circ}$), respectively. It was showed that CFRC had better tensile property than the usual composite materials. As the results of fatigue tests, the fatigue limit was ~ 77 MPa, which is under the 75% of the maximum tensile load. CFRC is recommended as a strong potential composite materials because the carbon fibers are closely packed and strongly bonded between the carbon fibers.

• Proceedings of the KSME Conference
• /
• 2000.04a
• /
• pp.25-30
• /
• 2000

Residual stresses induced in U-bending and tube-to-tubesheet joining processes of PWR's steam generator row-1 tube were measured by X-ray method and Hole-Drilling Method(HDM). The stresses resulting from the Internal pressure and the temperature gradient in the steam generator were also estimated theoretically. In U-bent lesions, the residual stresses at extrados were induced with compressive stress(-), and its maximum value reached -319 MPa in axial direction at ${\psi}=0^{\circ}$ in position. Maximum tensile residual stress of 170MPa was found to be at the flank side at Position of${\psi}=90^{\circ}$, i.e., at apex region. In tube-to-tubesheet fouling methods, the residual stresses induced by the explosive joint method were found to be lower than that by the mechanical roll method. The gradient of residual stress along the expanded tube was highest at the. transition region, and the residual stress in circumferential direction was found to be higher than the residual stress in axial direction. Hoop stress due to an internal pressure between primary and secondary side was analyzed to be 76 MPa and thermal stress was 45 MPa.

• Journal of the Korean Ceramic Society
• /
• v.32 no.9
• /
• pp.989-994
• /
• 1995

Rigid porous carbon fiber composites with the uniform pore size distribution were prepared by vacuum forming from water slurries containing carbonized PAN fibers, a phenolic resin and ceramic binders. The composites were designed to use for highly efficient carbon fiber filters for particulate filtration and gas adsorption. As the as-received carbon fibers of 1mm in length were milled to an approximate average length of 300${\mu}{\textrm}{m}$, modulus of rupture (MOR) of the composite filter was increased from 1MPa to the value larger than 5 MPa. Modulus of rupture (MOR) for the composite filter fabricated using the milled carbon fiber was increased from 5 MPa to 10 MPa as the carbonization temperature of the PAN fiber was raised from 90$0^{\circ}C$ to 140$0^{\circ}C$. The air permeability and an average pore size of the composite filter were increased from 40 to 270cc/min.$\textrm{cm}^2$ and from 35 to 80${\mu}{\textrm}{m}$, respectively, as the apparent porosity increased from 80 to 95%. It was shown that the MOR of the carbon fiber composite filter was dependent primarily on the average length of carbon fiber, carbonization temperature and the type of bonding materials.

• Journal of the Korean Ceramic Society
• /
• v.25 no.6
• /
• pp.704-712
• /
• 1988

In order to investigate the effect of the second phase on Al2O3 matrix, SiC whisker was dispersed in Al2O3 matrix as a second phase over the content range of 5vol% to 20vol%. To this mixture, Y2O3 or TiO2 powder was added as a sintering additive before isostatically pressing and pressureless sintering at 1800-190$0^{\circ}C$ for 90min in N2 atmosphere. With increasing SiC whisker content, relative densities of composites were decreased and the grain growth of Al2O3 was restricted. When Y2O3 was added as a sintering aid the sintering temperature was 180$0^{\circ}C$, the maximum values of flexural strength, hardness and fracture toughness were 537MPa, 12.1GPa, 3.7MPa.m1/2, respectively. However, when the sintering temperature was elevated to 190$0^{\circ}C$, maximum values of flexural strength, hardness and fracture toughness were 453MPa, 17.5GPa, 4.9MPa.m1/2, respectively. Improved mechanical properties are assumed to be attributed to the crack deflection by the second phase SiC whisker and whisker pullout mechanism.