• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.1
• /
• pp.33-38
• /
• 2000

In this study, multilayer piezoelectric actuators were fabricated with 75 layers by a conventional multi-layer capacitor (MLC) techniques, using 70Ag/30Pd paste as an internal electrode which can be sintered at low temperature and have cost down effect in mass productions. The multilayer piezoelectric actua-tors had no defects such as diffusions of internal electrode to ceramic bodies and shortages of internal electrodes. The multilayer piezoelectric actuators did not show the crack in the ceramics parts and the gapping phenomena in the external eletrodes when Ag paste was used as external electrodes. The multilayer piezoelectric actuators showed a maximum displacement of 4${\mu}{\textrm}{m}$ at 100V dc voltage and kept the maximum displacement constant for 300 seconds. The multilayer piezoelectric actuators showed good matching properties between ceramic bodies and AgPd internal electrodes. We confirmed the possibility of large-scaled production of the multilayer piezoelectric actuators with superior electrical properties and cost down effect using 70Ag/30Pd paste as an internal electrodes.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.873-876
• /
• 2000

Characteristics of piezoelectric thick films prepared by screen printing method were investigated. The piezoelectric thick films were printed using Pb(Mg,Nb)O$_3$-Pb(Zr,Ti)O$_3$system. The lower electrodes were coated with various thickness of Ag-Pd by screen printing to investigate the effect as a diffusion barrier and deposited with Pt by sputtering on Ag-Pd. The ceramic paste was prepared by mixing powder and binder with various ratios using three roll miller. The fabricated thick films were burned out at 650$^{\circ}C$ and sintered at 950$^{\circ}C$ in the O$_2$condition for each 20, 60min after printing with 350mesh screen. The thickness of piezoelectric thick film was 15∼20 $\mu\textrm{m}$ and the Ag-Pd electrode acted as a diffusion barrier above 3 $\mu\textrm{m}$ thickness. When the lower electrode Ag-Pd was 6 $\mu\textrm{m}$ and the piezoelectric thick films were sintered by 2nd step (650$^{\circ}C$/20min and 950$^{\circ}C$/1h) using paste mixed Pb(Mg,Nb)O$_3$-Pb(Zr,Ti)O$_3$$.$ MnO$_2$+ Bi$_2$O$_3$. V$_2$O$\_$5/ and binder in the ratio of 70:30, the remnant polarization of thick film was 9.1 ${\mu}$C /cm$^2$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.11
• /
• pp.921-925
• /
• 2000

Characteristics of Pb(Mg, Nb)O$_3$-Pb(Zr, Ti)O$_3$system thick films fabricated by a screen printing method were investigated. The buffer layer were coated with various thickness of Ag-Pd by screen printing to investigate the effect as a diffusion barrier and deposited Pt as a electrode by sputtering on Ag-Pb layer. The printed thick films were burned out at 650$\^{C}$ and sintered at 950$\^{C}$ in O$_2$condition for each 20, 60min after printing with 350mesh screen. The thickness of piezoelectric thick film was 15∼20㎛ and Ag-Pb layer acted as a diffusion barrier above 3㎛ thickness. The PMN-PZT thick films were screen printed on Pt/Ag-Pb(6m) and sintered by 2nd step (650$\^{C}$/20min and 950$\^{C}$/1h) using paste mixed PMN-PZT and binder in the ratio of 70:30, and the remnant polarization of thick film was 9.1$\mu$C/㎠ in this conditions.