• The Journal of Advanced Prosthodontics
• /
• 제11권4호
• /
• pp.202-208
• /
• 2019

PURPOSE. Fabrication of zirconia restorations with ideal mechanical properties in a short period is a great challenge for clinicians. The purpose of the study was to investigate the effect of heating rate on the mechanical and microstructural properties of monolithic zirconia. MATERIALS AND METHODS. Forty monolithic zirconia specimens were prepared from presintered monolithic zirconia blanks. All specimens were then assigned to 4 groups according to heating rate as Control, Group $15^{\circ}C$, Group $20^{\circ}C$, and Group $40^{\circ}C$. All groups were sintered according to heating rates with the sintering temperature of $1500^{\circ}C$, a holding time of 90 minutes and natural cooling. The phase composition was examined by XRD analysis, three-point bending test was conducted to examine the flexural strength, and Weibull analysis was conducted to determine weibull modulus and characteristic strength. Average grain sizes were determined by SEM analysis. One-way ANOVA test was performed at a significance level of 0.05. RESULTS. Only tetragonal phase characteristic peaks were determined on the surface of analyzed specimens. Differences among the average grain sizes of the groups were not statistically significant. The results of the three-point bending test revealed no significant differences among the flexural strength of the groups (P>.05). Weibull modulus of groups was ranging from 3.50 to 4.74. The highest and the lowest characteristic strength values were obtained in Group $20^{\circ}C$ and Control Group, respectively. CONCLUSION. Heating rate has no significant effect on the flexural strength of monolithic zirconia. Monolithic zirconia restorations can be produced in shorter sintering periods without affecting the flexural strength by modifying the heating rate.

• 한국세라믹학회지
• /
• 제29권7호
• /
• pp.511-516
• /
• 1992

In this study, SiC powder and Si powder were used as the raw materials. Mixture was prepared with addition of Al2O3 and Fe2O3 at 0.1~0.5wt% respectively. After this step, the mixture was pressed and nitrided for 30 hrs at 140$0^{\circ}C$ under NH3-N2 atmosphere. Mechanical properties of sintered specimens were investigated from measurement of porosity, bulk density and three point bending test. nitration reaction extent was observed at the change of mass before and after reaction, and the microstructure and the change of $\alpha$-Si3N4 and $\beta$-Si3N4 were observed by XRD and SEM. In the current work, the results are as follows 1. When Fe2O3 added, the nitridation increased with the content of Fe2O3, and the bending strength was increased from 0.1 wt% to 0.3 wt%, and decreased to 0.5 wt%. 2. When Al2O3 added, the nitridation and the bending strength increased little by little with the content of Al2O3 3. The bending strength of the specimen added with Fe2O3 were higher than that with Al2O3. Because the specimens contained Fe2O3 had much more the whisker type crystal of Si3N4 contributing to strength than contained Al2O3.

• 한국세라믹학회지
• /
• 제35권6호
• /
• pp.551-558
• /
• 1998

Detection of microcrack in {{{{ {Al }_{2 } {O }_{3 } }} ceramics were studided by AE(acoustic emission) technique with 4-point bending test in order to evaluate the fracture process and formation of microcrack. Fully-dense alu-mina ceramics having a different grain size were fabricated by varing the hot-pressing temperature. The grain size of alumina increased with increasing the hot-pressing temperature whereas the bending strength decreasd. The microcracks were observed by SEM and TEM. The generation of AE event increased with increasing the applied load and many AE event was generated at maximum applied load. Alumina with smaller grain size shows the generation of many AE event resulting in an increase of microcrack formation. An intergranular fracture is predominantly observed in fine-grained alumina whereas intragranular fracture occurs predominantly in coarse-grained alumina,. Analysis of micorstructure and AE prove that primary mi-crocracks occur within grain-boundaries of alumina. The larger microcracking were formed by the growth and/or coalesence of primary microcracks. Then the materials become to fracuture by main crack gen-eration at the maximum applied load.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1999년도 학회창립 10주년 기념 1999년도 가을 학술발표회 논문집
• /
• pp.585-588
• /
• 1999

This study is performed to verify the effect of CSA expansive additives for concrete by material properties test and 4 point-bendig test of RC slabs. The result shows that the variations of compress strength, bending strength, and modulus of elasticity of expansive concrete are the same as those of plain concrete. And the crack load of RC slabs with expansive concrete are increased in comparision with that of plain concrete, but the ultimate strength of RC slabs with expansive concrete is decreased.

• The Korean Journal of Ceramics
• /
• 제2권4호
• /
• pp.212-215
• /
• 1996

This paper focuses the strength and wear resistance of CVD diamond films. The strength of free-standing CVD diamond films synthesized by microwave plasm CVD, DC plasma CVD, RF plasma CVD and arc discharge plasma jet CVD has been measured by three-point bending test. The wear resistance of CVD diamod films has been evaluated by the pin-on-disk type testing. diamond films coated on the base of sintered tungsten carbide pin by hot filament CVD have been rubbed with a sintered diamond disk in muddy water. Volume removed wear of CVD diamond has been compared with stellite, WC alloy and bearing steel.

• 한국세라믹학회지
• /
• 제26권6호
• /
• pp.789-794
• /
• 1989

The high-temperature strength of Ce-TZP was measured at 200, 650 and 100$0^{\circ}C$ by 4-point bending test. And its fracture behavior was observed by SEM. Below $650^{\circ}C$ of the temperature, where monoclinic fraction was almost zero, the decreasing rate of bending strength was relatively slow, but above this temperature, high temperature strength was largely decreased as a result of the decrease of stress-induced transformation of zirconia. The observation of fracture surface bended at 100$0^{\circ}C$ indicated that the fracture mode changed from intergranular-into transgranular-form with regardless of ceria contents.

• 산업기술연구
• /
• 제20권A호
• /
• pp.169-178
• /
• 2000

The 4-point bending tests have been performed In order to estimate the effect of TIG-dressing on fatigue strength and fatigue characteristics quantitatively for non load-carrying fillet welded joints subjected to pure bending. As a result of fatigue tests, fatigue strengths of as-welded specimens have satisfied the grade of fatigue strength prescribed in specifications of korea, AASHTO and JSSC. Fatigue strength at 2 million cycles of TIG-dressing specimens have increased compared with as-welded specimens. As the result of beachmark tests, fatigue cracks occurred at several points, where the radius of curvature and flank angle in the weld bead toes were low, and grew as semi-elliptical cracks, then approached to fracture. As a result of finite element analysis, stress concentration factor in weld bead toes has closely related to the flank angle and radius of curvature, and between these, the radius of curvature has more largely affected in stress concentration factor than flank angle. As a result of fracture mechanics approaches, the crack correction factor of test specimens has largely affected on stress gradient correction factor in case a/t is below 0.4. From the relations between stress intensity factor range estimated from FEM analysis and fatigue crack growth rate, fatigue life has been correctly calculated.

• 한국세라믹학회지
• /
• 제36권9호
• /
• pp.997-1005
• /
• 1999

• Advances in nano research
• /
• 제15권4호
• /
• pp.305-313
• /
• 2023

This study is aimed to investigate the electrically conductive properties of epoxy nanocomposites exposed to an acidic environment under various mechanical loads. For simultaneous assessment of the acidic environment and mechanical load on the electrical conductivity of the samples, the samples with and without carbon nanotubes were exposed to the acidic environment under three different loading conditions for 20 days. Then, the aged samples' strength and flexural stiffness degradation under crude oil and bending stress were measured using a three-point flexural test. The aged samples in the acidic environment and under 80 percent of their intact ultimate strength revealed a 9% and 26% reduction of their electrical conductivity for samples with and without CNTs, respectively. The presence of nanoparticles declined flexural stiffness by about 16.39%. Scanning electron microscopy (SEM) images of the specimen were used to evaluate the dispersion quality of CNTs. The results of this study can be exploited in constructing conductive composite electrodes to be used in petroleum environments such as crude oil electrostatic tanks.

• Advances in nano research
• /
• 제15권4호
• /
• pp.285-294
• /
• 2023

This study is aimed to investigate the electrically conductive properties of epoxy nanocomposites exposed to an acidic environment under various mechanical loads. For simultaneous assessment of the acidic environment and mechanical load on the electrical conductivity of the samples, the samples with and without carbon nanotubes were exposed to the acidic environment under three different loading conditions for 20 days. Then, the aged samples' strength and flexural stiffness degradation under crude oil and bending stress were measured using a three-point flexural test. The aged samples in the acidic environment and under 80 percent of their intact ultimate strength revealed a 9% and 26% reduction of their electrical conductivity for samples with and without CNTs, respectively. The presence of nanoparticles declined flexural stiffness by about 16.39%. Scanning electron microscopy (SEM) images of the specimen were used to evaluate the dispersion quality of CNTs. The results of this study can be exploited in constructing conductive composite electrodes to be used in petroleum environments such as crude oil electrostatic tanks.