• Journal of the Korean Ceramic Society
• /
• v.29 no.8
• /
• pp.667-673
• /
• 1992

The alumina-zirconia composite powders of core particle ZrO2 coated with Al2O3 were prepared by the hydrolysis-deposition of the mixed aluminum salt solution of Al2(SO4)3-Al(NO3)3-Urea. The effects of hydrolysis reaction and coating parameters on characteristics of coated powders and composites were also investigated. The degree of coating could be estimated from the ratio of tetra-/mono-ZrO2 present at the room temperature after heat-treating coated powders at 120$0^{\circ}C$ and the result of TEM observations. When the content of ZrO2 in the dispersed coating system, the coating time, and the volume ratio of water/solution were 50 mg/g, 180 min, and 5, respectively the coating efficiency was maximum (the ratio of tetra-/mono-ZrO2 was 87/13). The relative densities of coated Al2O3-ZrO2 composites sintered at 1$650^{\circ}C$ for 4 hrs were about 91~98% and the maximum ratio of tetra-/mono-ZrO2 in Al2O3-20wt% ZrO2 composites was 62/38.

• Journal of the Korean Ceramic Society
• /
• v.30 no.10
• /
• pp.811-818
• /
• 1993

Al2O3/ZrO2-Spinel composites were prepared by infiltrating magnesium sulfate solution into the porous preform made from Al2O3-20wt% ZrO2 composite powders derived through an emulsion route. The microstructure and composition of the modified composites could be controlled by manipulating the presingtering temperature of the preform, infiltration time, and so on. It was found that spinel phases were concentrated near the surface than in the interior of the Al2O3/ZrO2-Spinel composites infiltrated for 6hrs, while spinel phases were uniformly distributed in the comosites infiltrated for 2 days. The relative density and fracture toughness of the composite infiltrated for 6 hrs were 98.6% and 7.2MN/m3/2, respectively.

• Journal of the Korean Ceramic Society
• /
• v.23 no.3
• /
• pp.44-52
• /
• 1986

$Al_2O_3-ZrO_2$ ceramics was obtained by the co-precipitation method using $Al_2(SO_4)_2$.$18H_2O$ and $ZrOCl_2$.$8H_2O$ as starting materials $MgCl_2$.$6H_2O$ as a sintering aid and NH4OH as a hydrolyzing agent. The coprecipitate from the above raw materials was calcined at 125$0^{\circ}C$ for 1h and again sintered at 1$650^{\circ}C$ for 2h before measurements of strength hardness and fracture toughness. MgO addition was found to increase mechanical properties of the $Al_2O_3-ZrO_2$ system. The strength and frac-ture toughness of $Al_2O_3-ZrO_2$ ceramics were considered to be increased by stress-induced phase tranforma-tion of $ZrO_2$.

• Journal of the Korean Ceramic Society
• /
• v.28 no.1
• /
• pp.53-59
• /
• 1991

The reaction product between Si3N4 and ZrO2 has been studied by heat treatment of Si3N4-Zr(Y)O2 composite in high vacuum(<10-5 torr) and in air at $700^{\circ}C$. ZrN was formed after heat treatment in vacuum and easily oxidized after heat treatment in air. The amount of ZrN is related to the Y2O3 content dissolved in ZrO2. After the heat treatment in air the toughness increased and the spalling due to the oxidation of ZrN in specimen surface was observed. As a result, it is suggested that the formation of ZrN phase in Si3N4-ZrO2 composite enhance the toughness of the composite in an oxidation conditon.

• Journal of the Korean Ceramic Society
• /
• v.44 no.1 s.296
• /
• pp.58-64
• /
• 2007

In this study, we investigated $Li_2ZrO_3$ membrane as a candidate material for high-temperature $CO_2$ separation and evaluated mechanical property. $Li_2ZrO_3$ powder was synthesized by solid state reaction of $Li_2CO_3\;and\;ZrO_2$. Then we fabricated $Li_2ZrO_3$ tape using tape casting method. Dense $Li_2ZrO_3$ membrane prepared by sintering at $1600^{\circ}C$ for 2 h after pressing $Li_2ZrO_3$ tape using lamination machine. Mechanical properties before and after $CO_2$ absorption of fabricated $Li_2ZrO_3$ membrane such as Hertzian indentation, Victors hardness and 3-point bending testing were evaluated.

• Korean Journal of Materials Research
• /
• v.13 no.9
• /
• pp.572-580
• /
• 2003

Synthesizing behavior and microstructural evolution of $CaZrO_3$and $m-ZrO_2$in a thermal reaction process of $ZrSiO_4$-$xCaCO_3$mixtures, where x is 7 and 19, were investigated to determine the addition amount of CaO in CaO:$ZrO_2$:$SiO_2$ternary composition. CaZrO$_3$-Ca$_2$SiO$_4$precursor prepared by the mixture of $ZrSiO_4$and CaCO$_3$in aqueous suspending media was controlled to the acidic (pH=4.0) condition with HCI solution to enhance the thermal reaction. The addition amount of dispersant into the $ZrSiO_4$-$xCaCO_3$slip increased with increasing mole ratio of $CaCO_3$, which was associated with the viscosity of slip. Decarbonation reaction was activated with an increase of the addition amount of $CaCO_3$, showing different final temperatures in $ZrSiO_4$-$7CaCO_3$and $ZrSiO_4$-$19CaCO_3$mixtures as about 980 and 116$0^{\circ}C$, respectively, for finishing decarbonation reaction. The grain morphology was changed to spherical shape for all samples with an increase of sintering temperature. The grain size and phase composition of the synthesized composites depended on the mixture ratio of Zrsi04 and CacO3 powders, indicating that the main crystals were m-ZrO2 ($\leq$3 $\mu\textrm{m}$) and $CaZrO_3$ ($\leq$ 7 $\mu\textrm{m}$) in $ZrSiO_4$$>-7CaCO_3$and $ZrSiO_4$-$19CaCO_3$mixtures, respectively.

• Journal of the Korean Ceramic Society
• /
• v.25 no.4
• /
• pp.364-372
• /
• 1988

The mechanical properties and microstructure of ceramics of the system Al2O3-ZrO2-Y2O3 sintered at 1$650^{\circ}C$ for 2h after powder preparation by the precipitation method from Al2(SO4)3.18H2O, ZrOCl2.8H2O and YCl3.6H2O were investigated. The Al2O3-ZrO2-Y2O3 ceramics sintered at 1$650^{\circ}C$ for 2h after mixing alpha-Al2O3 and ZrO2-Y2O3 powders, both were separately precipitated and calcined, were found to have the relative density higher than 97.5% so that the strengthening and toughening mechanisms could be explained mainly as the stress-induced phase transformation. On the other hand, the sintered bodies prepared by co-precipitating the three starting materials were measured to have the relative density lower than 85% so that the degradation of strength were observed above 15 vol% ZrO2 contents due to the high porosity by which the effect of stress-induced phase transformation was assumed to be depressed.

• Applied Chemistry for Engineering
• /
• v.7 no.5
• /
• pp.1006-1014
• /
• 1996

A series of catalysts, $NiO-ZrO_2/WO_3$, for ethylene dimerization were prepared by coprecipitation from a solution of nickel chloride - zirconium oxychloride mixture followed by dry impregnation with an aqueous solution of ammonium metatungstate and calcination in air. On the basis of the results obtained from x-ray diffraction and DSC, the addition of NiO and $WO_3$ to $ZrO_2$ shifted the transition of $ZrO_2$ from amorphous to a tetragonal phase toward higher temperatures due to the interaction between NiO(or $WO_3$) and $ZrO_2$. $NiO-ZrO_2$ without $WO_3$ was inactive for the ethylene dimerization, but $NiO-ZrO_2/WO_3$ was found to be very active even at room temperature. The high catalytic activity of $NiO-ZrO_2/WO_3$ was closely correlated with the increase of acid strength by the inductive effect of $WO_3$.

• Journal of the Korean Ceramic Society
• /
• v.21 no.2
• /
• pp.149-155
• /
• 1984

The effect of $ZrO_2$ dispersed phase on the mechanical properties in $Al_2O_3$-$ZrO_2$system has been studied. There are both metastable tetragonal phase and stable monoclinic phase of $ZrO_2$particles diespersed in Al2O3 matrix at room temperature. Metastable tetragonal $ZrO_2$ changes to the stable monoclinic structure within the stress field of the crack. And microcracks are formed by the expansion of $ZrO_2$during the tetragonal-monoclinic transformation on cooling. Therefore stress-induced phase transformation and inclusion-induced microcracking contribute to the mec-hanical properties of $Al_2O_3$-$ZrO_2$system. Sintered composites containing 10m/o $ZrO_2$ yield KiC values of 6.5MN/$m^{3/2}$ much greater than that of pure $Al_2O_3$ This increase results from microcrack extension and stress-induced phase transformation absor-bing energy by crack propagation. Flexural strength of composites is decreased considerably in comparison with pure $Al_2O_3$ This decrease results from microcrack as a crack former and higher porosity than pure $Al_2O_3$.

• Korean Journal of Materials Research
• /
• v.9 no.1
• /
• pp.73-80
• /
• 1999

The effect of alloy compositions of the bond coating on the plasma sprayed-thermal barrier coatings was investigated. The performance of the coating composed of Rene80/NiCrAl/ZrO$_2$-CeO$_2$-Y$_2$O$_3$ and Rene80/CoNiCrAlY/ZrO$_2$-CeO$_2$-Y$_2$O$_3$was evaluated by isothermal and thermal cyclic test in an ambient atmosphere at 115$0^{\circ}C$. The failure of Rene80/NiCrAl/ZrO$_2$-CeO$_2$-Y$_2$O$_3$ coatings was occurred at the bond coating/ceramic coating interface while Rene80/CoNiCrAlY/ZrO$_2$-CeO$_2$-Y$_2$O$_3$ coating was failed at the substrate/bond coating interface after thermal cyclic test. The lifetime of Rene80/NiCrAl/ZrO$_2$-CeO$_2$-Y$_2$O$_3$coatings was longer than Rene80/CoNiCrAlY/ZrO$_2$-CeO$_2$-Y$_2$O$_3$coating. The oxidation rate of the NiCrAl bond coating examined by TGA was lower than CoNiCrAlY bond coatings. In summary, these results suggest that Rene80/CoNiCrAlY/ZrO$_2$-CeO$_2$-Y$_2$O$_3$system as thermal barrier coating be not suitable considering the durability of the coating layer for high temperature oxidation and thermal stress.