• 한국자동차공학회논문집
• /
• 제13권6호
• /
• pp.56-62
• /
• 2005

The fatigue analysis and lifetime evaluation are very important in design procedure to assure the safety and reliability of the rubber components. Fatigue lifetime prediction methodology of the rubber component was proposed by incorporating the finite element analysis and fatigue damage parameter from fatigue test. Finite element analysis of 3D dumbbell specimen and rubber component were performed based on a hyper-elastic material model determined from material test. The Green-Lagrange strain at the critical location determined from the FEM was used for evaluating the fatigue damaged parameter of the natural rubber. Fatigue life of the rubber component are predicted by using the fatigue damage parameter at the critical location. Predicted fatigue lifes of the rubber component agreed fairly well the experimental fatigue lives.

• 대한치과보철학회지
• /
• 제52권2호
• /
• pp.67-73
• /
• 2014

연구 목적: 본 연구의 목적은 주조, 3-D printing laser sintered 및CAD/CAM technology를 이용한 milling 방법으로 제작된 치과용 코발트-크롬 합금의 기계적 물성을 비교하고 파절 단면의 미세 구조를 살펴보는 데 있다. 이를 통해 새롭게 소개된 제작 기법 - 3D-printing laser sintered - 이 치과용 합금 제작으로 적합한 지 알아보고자 한다. 연구 재료 및 방법: 36개의 flat disc 모양의 시편을 제작하여 제작 방법에 따라 세 집단으로 나누었다; 주조 방식으로 제작한 12개, laser sintering 방법으로 12개, CAD/CAM milling 방법으로 12개의 시편을 제작하여 표면 경도 시험을 시행하였다. 또한 각 집단 별로 12개의 dumbbell 모양의 시편을 제작하여 인장 강도 시험을 시행하였다. 통계량이 비모 수적 통계 분포를 보였으므로 Kruskal-Wallis 검정을 이용하여 각 실험군의 인장 강도 시험 결과를 비교했으며, 통계적 유의 수준은P=.05로 설정하여 Mann-Whitney 및 Bonferroni 사후 검정을 시행하였다. 전자 주사 현미경을 사용하여 파절 단면의 미세 구조를 관찰하였다. 결과: Vickers hardness test에서 세 집단간에 모두 유의한 차이가 있었고, 주조 방식으로 제작된 실험군에서 가장 큰 표면 경도(455.88 Hv)가, CAD/CAM milling으로 제작된 실험군에서 가장 낮은 표면 경도(243.40 Hv)를 나타냈다. 최대 인장 강도, 0.2% 항복강도, elongation 및 elastic modulus에서 세 집단간에 모두 유의한 차이가 나타났으며, CAD/CAM milling으로 제작한 실험군에서 가장 높은 최대 인장 강도(1442.94 MPa)가, laser sintered 실험군에서 가장 큰 0.2% 항복 강도(1136.15 MPa)가 나타났다. 파절 단면의 전자 주사 현미경 관찰 결과, 주조 시편에서는 독특한 성긴 모양과 전형적인 주조 다공성 구조가 관찰되었고, laser sintered 시편에서는 편평한 면을 동반한 거친 결정 구조가, 그리고 milled 시편에서는 균일하고 규칙적인 치밀 미세 구조가 나타났다. 결론: 서로 다른 제작 방법은 코발트-크롬 합금의 물리적 성질과 파절 단면의 미세 구조에 영향을 미쳤다. 주조 방식으로 제작된 시편에서 가장 큰 표면 경도가, milling으로 제작된 시편에서 가장 큰 인장 강도를 나타냈으며, 본 연구의 모든 실험군에서 치과용 합금의 ISO 기준에 부합하는 물성을 보였다.

• Elastomers and Composites
• /
• 제55권2호
• /
• pp.81-87
• /
• 2020

Service life prediction and evaluation of rubber components is the foundational technology necessary for securing the safety and reliability of the product and to ensure an optimum design. Even though the domestic industry has recognized the importance thereof, technology for a systematic design and analysis of the same has not yet been established. In order to develop this technology, identifying the fatigue damage parameters that affect service life is imperative. Most anti-vibration rubber components had been damaged by repeated load and aging. Hence, the evaluation of the fatigue characteristics is indispensable. Therefore, in this paper, we propose a method that can predict the service life of rubber components relatively accurately in a short period of time. This method works even in the initial designing stage. We followed the service life prediction procedure of the proposed rubber components. The weak part of the rubber and the maximum strain were analyzed using finite element analysis of the rubber bushing for the tracked vehicles. In order to predict the service life of the rubber components that were in storage for a certain period of time, the fatigue test was performed on the three-dimensional dumbbell specimen, based on the results obtained by the rubber material acceleration test. The service life formula of the rubber bushing for tracked vehicles was derived using both finite element analysis and the fatigue test. The service life of the rubber bushing for tracked vehicles was estimated to be about 1.7 million cycles at room temperature (initial stage) and about 400,000 cycles when kept in storage for 3 years. Through this paper, the service life for various rubber parts is expected be predicted and evaluated. This will contribute to improving the durability and reliability of rubber components.

• Elastomers and Composites
• /
• 제42권4호
• /
• pp.209-216
• /
• 2007

가변진폭 하중에서 고무부품의 피로수명 예측방법에 대하여 연구하였다. 서로 다른 변위에서 변위제어 피로시험을 수행하였으며 피로손상변수로 최대 Green-Lagrange 변형률을 선정하였다. Green-Lagrange 변형률에 의한 고무의 피로수명 곡선은 3차원 덤벨시편의 비선형 유한요소법을 이용하여 결정하였다. 피로수명 예측을 위하여 가변진폭 하중이력으로 SAE의 하중이력을 이용하였다. 레이스트랙법과 단순화된 레인플로집계법을 이용하여 하중이력신호를 축약하였다. 누적손상피로를 계산하는 방법으로 수정Miner 법칙을 이용하였으며, 최종적으로 하중이력신호에서 최대 진폭의 30% 이하를 노이즈로 간주하여 예측하였을 경우의 피로수명은 실제 가변진폭 하중 하에서의 피로시험결과와 비교적 잘 일치하였다.