• Transactions of the Korean Society of Mechanical Engineers
• /
• v.17 no.6
• /
• pp.1321-1329
• /
• 1993

Long time creep strength and life prediction of 1% Cr-Mo-V and 12% Cr rotor steel were performed by using round-bar type specimens under static load at 500-600.deg. C TTP (time temperature parameter), MCM (minimum commitment method) and ISM (initial strain method newly devised) as life prediction methods were investigated, and the results could be summarized as follows. (1) The minimum parameter of SEE (standard error) by TTP was proved as LMP (larson-miller parameter), and the minimum parameter of RMS (root mean squares), by data less than 10$^{3}$hrs was MHP (manson-haferd parameter). (2) The parameters of the minimum and the maximum strength values predicted in $10^{5}$hrs creep life of 1% Cr-Mo-V steel by TTP were LMP and MSP, respectively. In case of 12% Cr steel above $550^{\circ}C$ OSDP (orr-sherby-dorn parameter) was minimum and MSP (manson-succop parameter) was maximum, but below $550^{\circ}C$, the inverse phenomena was observed. On the other hand the creep strengths before $10^{3}hrs$ life by MCM were similar to those by TTP, but the strengths after $10^{3}hrs$ life were 10-25% lower than those by TTP. (3) Creep strengths by ISM were maximum 5% lower than those by TTP. Because $10^{5}hrs$ strengths were similar to those of the lower band by TTP, the ISM was safer than the TTP.

• Journal of Magnetics
• /
• v.16 no.3
• /
• pp.318-321
• /
• 2011

A new Fe-based amorphous compound powder was prepared from Fe-Si-B amorphous powder by crushing amorphous ribbons as the first magnetic component and Fe-Cr-Mo metallic glassy powder by water atomization as the second magnetic component. Subsequently by adding organic and inorganic binders to the compound powder and cold pressing, the new Fe-based amorphous compound powder cores were fabricated. This new Fe-based amorphous compound powder cores combine the superior DC-Bias properties and the excellent core loss. The core loss of 500 kW/$m^3$ at $B_m$ = 0.1T and f = 100 kHz was obtained When the mass ratio of FeSiB/FeCrMo equals 3:2, and meanwhile the DC-bias properties of the new Fe-based amorphous compound powder cores just decreased by 10% compared with that of the FeSiB powder cores. In addition, with the increasing of the content of the FeCrMo metallic glassy powder, the core loss tends to decrease.

• Journal of Welding and Joining
• /
• v.13 no.1
• /
• pp.89-102
• /
• 1995

The evaluation of reheat cracking susceptibility in CrMoV turbine rotor steel was performed using thermally simulated heat affected zones. The examinations were carried out in terms of microstructural characterization, microhardness measurement and a Charpy type notch opening three point bend test. It was found that reheat cracking susceptibility increased as the peak temperature increased. This effect was due to the combined effects of the carbide dissolution and unrestricted grain growth at 1350.deg. C peak temperature. Reheat cracking susceptibility was estimated based on microhardness measurement and prior austenite grain size. It was established that for this particular material, reheat cracking in coarse grained heat affected zone can be eliminated if the microhardness is below about 360DPH and the grain size is below about 30.mu.m. It is evident that reheat cracking susceptibility can be eliminated or reduced by carefully controlling the welding parameters such that a refined structure is produced in the coarse grained heat affected zone.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.27 no.1
• /
• pp.167-174
• /
• 2003

Fatigue damage of 2.2Ni-1Cr-0.5Mo steel used fir high strength pressure tubes and vessels was evaluated using uniaxial specimens subjected to strain-controlled fatigue loading. Based on the fatigue test results from different strain ratios of -2. -i 0, 0.5, 0.75, the fatigue damage of the steel was represented by using a cyclic strain energy density. Mean stress relaxation depended on the magnitude of the applied strain amplitude. The high pressure vessel steel exhibited the cyclic softening behavior. Total strain energy density consisting of the plastic strain energy density and the elastic tensile strain energy density described fairly well the fatigue life of the steel, taking the mean stress effects into account. Compared to other fatigue damage parameters, fatigue life prediction by the cyclic strain energy density showed a good correlation with the experimental fatigue lift within a factor of 3.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.16 no.8
• /
• pp.1421-1428
• /
• 1992

It has been increasingly recognized that the safety analysis considering fracture mechanics is required of the pressure vessels made of 2 1/4 Cr-1Mo steel for safe operation due to temper-embrittlement during long term service. In this study, the fracture toughnesses of degraded and recovered 2 1/4 Cr-1Mo steels have been studied with J$_{IC}$ test specimens at room temperature and the results will be compared with the data obtained from the Charpy impact test. The fracture toughness data from above experiments will be applied to life prediction based on the surface crack growth for degraded and recovered Cr-Mo pressure vessels.

• Journal of the Korean institute of surface engineering
• /
• v.51 no.3
• /
• pp.149-156
• /
• 2018

The corrosion and strength degradation characteristics of 1.25Cr-0.5Mo steels were studied under $650^{\circ}C$ in $76%N_2+6%O_2+16%CO_2+2%SO_2$ gas condition up to 500 hrs. Corroded specimens were characterized by weight gain, scanning electron microscope(SEM), energy dispersive X-ray spectroscopy(EDS), and X-ray diffraction(XRD). The tensile test was conducted to evaluate the mechanical strength and fracture mode with corrosion at high temperature. As the results of the experiments, thick Fe-rich oxide layers over $200{\mu}m$ were formed on the surface within 500 hrs. The thick oxide layers are formed with reduction of the cross-sectional area of the specimens. Thus, the strength tended to decrease with reduction of the cross-sectional area.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.10 no.3
• /
• pp.61-67
• /
• 2001

The remaining life estimation for the aged component is very important because mechanical properties of the compo-nents are degraded with time of service exposure in high temperature etc. The destructive method is widely used for the estimation of material degradation, but it has a difficulty in preparing specimens from in-service industrial facilities. In order to evaluate the feasibility of ultrasonic evaluation method for properties of high temperature materials, 2.25Cr-1Mo steel specimens which were prepared by the isothermal aging heat treatment at 63$0^{\circ}C$ were evaluated by ultra-sonic measurements investigating the change of velocities and attenuation coefficient. In this results, attenuation coefficient was found to be sensitive to material degradation mainly attributed to the change of grain size and the precipitation of impurities in grain boundaries, but velocity was not for all specimens.

• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.176-176
• /
• 2000

Recently developed Austenite stainless steel,309L was to overlay on 3Cr-1Mo-V-Ti-B steels, using Electroslag welding process, which wide electrodes were adopted. Transition region in welding interlayer relating to disbonding crack was investigated. Also. the effect of welding condition on the width of transition region and coarsening grains of the austenite were studied.1) With increasing welding speed the width of martensite at transient region was increased, but the amount of delta ferrite in weld metal was reduced, being fine grained.2) The form of martensite at the transition region was occured by reversible transition region, leading to increasing Ms point.3) With increasing welding speed, the grain of austenite formed at the welding interface was finer. With increasing welding current under the same welding speed, the grain size of the austenite was finer. At high current, original grain size of the austenite is coarse, but the austenite has fine grains because the austenite was transformed to martensite during cooling.4) In the case of high welding speed, the width of martensite at the welding interface was increased, but the grain size of austenite at the welding interface was finer. This indicates that the inhibition of disbonding crack may be achieved through dispersening fine carbides in the grain boudary.(Received August 3, 1999)

• Corrosion Science and Technology
• /
• v.2 no.1
• /
• pp.18-25
• /
• 2003

Effects of the precipitation of $\sigma$ phase on the metastable pitting as a precursor of stable pitting corrosion and also on the progress of stale pitting of the 25Cr-7Ni-3Mo-0.25N duplex stainless steel were investigated in chloride solution. Electrochemical potential and current noises of the alloy were measured in 10 % ferric chloride solution ($FeCl_3$) with zero resistance ammeter (ZRA), and then analyzed by power spectral density (PSD) and by corrosion admittance ($A_c$) spectrum. With aging at $850^{\circ}C$, the passive film of the alloy was found to get significantly unstable as represented by power spectral density (PSD) and a transition from metastable pitting state to stable one was observed. In the corrosion admittance spectrum, the number of negative $A_c$ corresponding to the state of localized corrosion increased with aging, suggesting that the precipitation of $\sigma$ phase considerably degraded the passive film by depleting Cr and Mo around it at $\alpha/\sigma$ or $\gamma/\sigma$ phase boundaries, thereby leading to the initiation of the pitting corrosion. However, the Cr and Mo at $\alpha/\sigma$ or $\gamma/\sigma$ phase boundaries which were once depleted due to the precipitation of the $\sigma$ phase were partly replenished by the diffusion of Cr and Mo from the surrounding matrix with aging time longer. The initiation of pitting seems to be associated with the precipitation density of the $\sigma$ phase with an effective size needed to induce the sufficient depletion of Cr and Mo around it.

• Journal of Welding and Joining
• /
• v.14 no.3
• /
• pp.75-85
• /
• 1996

In this paper the influence of postweld heat treatment on mechanical properties of SMAW and FCAW stainless steel weldments was examined and the obtained results are as follows ; (1) The amount of $\delta$-ferrite formed by SMAW and FCAW process decreased with increasing holding temperature and time in post weld heat treatment(PWHT), and it was found that the reduced ferrite was transformed into sigma phase after $800^{circ}C{\times}50hr$ PWHT. This sigma phase, even though it was very small, resulted in brittleness of dissimilar weldment between carbon steel and stainless steel in bending test, however in similar weldment between stainless steel and stainless steel was not occured. (2) The chemical composition of sigma phase was measured to 28-30%Cr, 7-9%Mo, 4-6Ni in 316L weldment, and also 35-37%Cr, 0.9-1.0Mo, 6-8%Ni in 309L weldment by EDS analysis.