• Nuclear Engineering and Technology
• /
• v.52 no.3
• /
• pp.589-596
• /
• 2020

Many components in the assembly section of Sodium-cooled Fast Reactor are made of good corrosionresistant 316 LN Stainless Steel material. To avoid self-welding of the components with the coolant sodium at elevated temperature, hardfacing is inevitable. Ni-based colmonoy-5 is used for hardfacing due to its lower dose rate by Plasma Transferred Arc process due to its low dilution. Since Ni-Cr-B-Si alloy becomes very fluidic while depositing, the major height of the weld overlay rests inside the groove. Hardfacing is also done over the plain surface where grooving is not possible. Therefore, grooved and ungrooved hardfaced specimens were prepared at different travel speeds. Fe content at every 100 ㎛ of the weld overlay was studied by Energy Dispersive Spectroscopy and also the micro hardness was determined at those locations. A correlation between iron dilution from the base metal and the micro hardness was established. Therefore, if the Fe content of the weld overlay is known, the hardness at that location can be obtained using the correlation and vice-versa. A new correlation between micro hardness and dilution coefficient is obtained at different locations. A comparative study between those specimens is carried out to recommend the optimum travel speed for lower dilution.

• Journal of Advanced Marine Engineering and Technology
• /
• v.28 no.8
• /
• pp.1270-1278
• /
• 2004

This paper describes the effectiveness of laser pulse shaping in eliminating weld defects such as porosity, cracks and undercuts in pulsed Nd:YAG laser welding. A large porosity was formed in a keyhole mode of deeply penetrated weld metal of any stainless steel. Solidification cracks were present in STS 310S with above 0.017%P and undercuts were formed in STS 303 with about 0.3%S. The conditions for the formation of porosity were determined in further detail in STS 316. With the objectives of obtaining a fundamental knowledge of formation and prevention of weld defects, the fusion and solidification behavior of a molten puddle was observed during laser spot welding of STS 310S through a high speed video photographing technique. It was deduced that cellular dendrite tips grew rapidly from the bottom to the surface, and consequently residual liquid remained at the grain boundaries in wide regions and enhanced the solidification cracking susceptibility. Several laser pulse shapes were investigated and optimum pulse shapes were proposed for the reduction and prevention of porosity and solidification cracking.

• Korean Journal of Metals and Materials
• /
• v.50 no.8
• /
• pp.583-589
• /
• 2012

This work is concerned with a statistical approach to the life prediction on irradiation-assisted stress corrosion cracking (IASCC) of stainless steel (SS) for core internals of a pressurized water reactor (PWR). The previous results of the time-to-failure of IASCC measured on neutron-irradiated stainless steel components were statistically analyzed in terms of stress and irradiation. The accelerating life testing model of IASCC of cold worked Type 316 SS was established based on an inverse power model with two stress-variables, the applied stress and irradiation dose. Considering the variation of the yield strength and applied stress with the irradiation dose in the model, the remaining life of the baffle former bolt was statistically predicted during operation under complex environments of stress and irradiation.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.22 no.3
• /
• pp.325-338
• /
• 2024

Interim dry cask storage systems comprising AISI 304 or 316 stainless steel canisters have become critical for the storage of spent nuclear fuel from light water reactors in the Republic of Korea. However, the combination of microstructural sensitization, residual tensile stress, and corrosive environments can induce chloride-induced stress corrosion cracking (CISCC) for stainless steel canisters. Suppressing one or more of these three variables can effectively mitigate CISCC initiation or propagation. Surface-modification technologies, such as surface peening and burnishing, focus on relieving residual tensile stress by introducing compressive stress to near-surface regions of materials. Overlay coating methods such as cold spray can serve as a barrier between the environment and the canister, while also inducing compressive stress similar to surface peening. This approach can both mitigate CISCC initiation and facilitate CISCC repair. Surface-painting methods can also be used to isolate materials from external corrosive environments. However, environmental variables, such as relative humidity, composition of surface deposits, and pH can affect the CISCC behavior. Therefore, in addition to research on surface modification and coating technologies, site-specific environmental investigations of various nuclear power plants are required.

• Journal of the Society of Naval Architects of Korea
• /
• v.45 no.5
• /
• pp.530-537
• /
• 2008

Austenitic stainless steels(SUS 304, SUS 316), which are used for safety control valve of LNG carrier, are occasionally exposed in the cryogenic environment. In this regards, it is required to evaluate the mechanical characteristics under the low temperature environment. In this study, a series of uniaxial tensile test was carried out varying temperature for austenitic stainless steel. The phenomena of the strain-induced plasticity have been observed on the all temperature ranges. The critical value for threshold of 2nd hardening due to the phase transformation induced plasticity as well as the increase of hardening have been reported. The summarized experimental results would be used for the validation of numerical techniques applicable for the nonlinear hardening behavior of austenitic stainless steel under the cryogenic temperature environment.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2004.05a
• /
• pp.331-336
• /
• 2004

Dissimilar friction welding were produced using 10mm and 11mm diameter solid bar in Inconel ally(IN X-750) to Stainless steel(STS316L) to investigate their mechanical properties. The main friction welding parameters were selected to endure good quality welds on the basis of visual examination, tensile tests, Virkers hardness surveys of the bond of area and HAZ and macro-structure investigations. The specimens were tested as welded, not heat-treated. The tensile strength of the friction welded steel bars was increased up to $95\%$ of the STS316L base metal under the condition of all heating time. Optimal welding conditions were n=2,000(rpm), $P_1=220(MPa),\;P_2=260(MPa),\;t_1=4(s),\;t_2=4(s)$ when the total upset length is 7(mm).

• Journal of Ocean Engineering and Technology
• /
• v.15 no.2
• /
• pp.88-93
• /
• 2001

In this paper, joints of Cu-1Cr-0.1Zr alloy to STS316L were performed by friction welding method. Particularly, Cu-1Cr-0.1Zr alloy is attractive candidate as nuclear power plant material and exibit the best combination of high strength and good electrical and thermal conductivity of any copper alloy examined. The stainless steel is a structural material while copper alloy acts as a heat sink material for the surface heat flux in the first wall. So, in this paper, not only the development of optimizing of friction welding with more reliability and more applicability but also the development of in-process real-time weld quality (such as strength and toughness) evaluation technique by acoustic emission for friction welding of such nuclear reactor component of Cu-1Cr-0.1Zr alloy to STS316L steel sere performed.

• Journal of Advanced Marine Engineering and Technology
• /
• v.35 no.1
• /
• pp.68-74
• /
• 2011

This papers investigated the mechanical characteristics and the weldability of identical as well as dissimilar welding by GTAW for STS 304 and STS 316L. It is applied to double wall gas pipe of duel fuel engine for LNG carrier. Consequently, the weldability of dissimilar and identical welded zone of STS 304 decreased compared to base metal significantly. The result of microstructure observation for welded zone, a degree of acicular ferrite in welding zone for STS 304 presented more than STS 316L. The hardness of welding zone for STS 304 presented higher value than that for STS 316L by this effect.

• Corrosion Science and Technology
• /
• v.16 no.6
• /
• pp.305-316
• /
• 2017

Austenitic stainless steels have been widely used for various systems of nuclear power plants. Among these stainless steels, small pipes with diameter less than 14 inch have been produced in the form of seamless pipe. Annealing and cooling process during the manufacturing process can affect corrosion properties of seamless stainless steels. Therefore, 12 inch-diameter of as-received 304L stainless steel pipe was annealed and aged in this study. Intergranular corrosion resistance was evaluated by ASTM A262 Practice A, C, and E methods. The degree of sensitization was determined using a DL-EPR test. U-bend method in an autoclave was used to evaluate the SCC resistance in 0.01 M $Na_2S_4O_6$ or 40% NaOH solution at $340^{\circ}C$. As-received specimen showed relatively high degree of sensitization and intergranular corrosion rate. Carbon segregation was also observed near grain boundaries. Annealing treatment could give the dissolution of segregated carbon into the matrix. Aging treatment could induce segregation of carbon and finally form carbides. Microstructural analysis confirmed that high intergranular corrosion rate of the as-received seamless pipe was due to micro-galvanic corrosion between carbon segregation and grains.

• Korean Journal of Metals and Materials
• /
• v.48 no.12
• /
• pp.1090-1096
• /
• 2010

This pitting corrosion study of welded joints of austenitic stainless steels (AISI 304L and 316L) has addressed the differentiating solidification mode using three newly introduced filler wires with a flux-cored arc welding process (FCAW). The delta ferrite (${\delta}$-ferrite) content in the welded metals increased with an increasing equivalent weight ratio of chromium/nickel ($Cr_{eq}/Ni_{eq}$). Ductility dip cracking (DDC) was observed in the welded metal containing ferrite with none of AISI 304L and 0.1% of AISI 316L. The potentiodynamic anodic polarization results revealed that the $Cr_{eq}/Ni_{eq}$ ratio in a 3.5% NaCl solution didn't much affect the pitting potential ($E_{pit}$). The AISI 316L welded metals with ${\ddot{a}}$-ferrite content of over 10% had a superior $E_{pit}$ value. Though the AISI 316L welded metal with 0.1% ferrite had larger molybdenum contents than AISI 304L specimens, it showed a similar $E_{pit}$ value because the concentration of chloride ions and the corrosion product induced severe damage near the DDC.