• Journal of Power System Engineering
• /
• v.20 no.1
• /
• pp.36-41
• /
• 2016

Effects of austenite on the pitting corrosion in 202 stainless steel with two phase of austenite and martensite were investigated through the electrochemical polarization test. Two phases structures of martensite and austenite were obtained by reversed annealing treatment at the range of $500^{\circ}C-700^{\circ}C$ for 10min. in 70% cold-rolled 202 stainless steel. Volume fraction of reversed austenite has increased rapidly with an increase of annealing temperature. Pitting corrosion has arisen mainly on martensite phase in 202 stainless steel with two phases of austenite and martensite. Pitting current density has decreased with an increase of volume fraction of austenite. Consequently, pitting corrosion at martensite has occurred largely with an increase of volume fraction of austenite. Pitting corrosion was affected by volume fraction of austenite.

• Journal of the Korean Society for Heat Treatment
• /
• v.28 no.4
• /
• pp.200-205
• /
• 2015

Effects of austenite on the uniform corrosion in the solution of $1\;N\;H_2SO_4$ were investigated through the electrochemical polarization test. Two phases structures of martensite and austenite were obtained by annealing treatment at the range of $500^{\circ}C{\sim}700^{\circ}C$ for 10min. in 70% cold-rolled 202 stainless steel. Volume fraction of reversed austenite increased rapidly with an increase of annealing temperature. Uniform Corrosion was occur mainly on martensite phase in 202 austenitic stainless steel with two phase of austenite and martensite. Corrosion current density increased with an increase of volume fraction of austenite, therefore uniform corrosion was affected by volume fraction of austenite

• Proceedings of the KWS Conference
• /
• 1992.10a
• /
• pp.199-202
• /
• 1992

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.19 no.2
• /
• pp.171-178
• /
• 2023

For the phase boundary crack found in the gasket made of cast austenitic stainless steel in the nuclear power plant, the oxide layers were analyzed through SEM and TEM. The results showed that cracks initiated and propagated along the austenite/δ-ferrite phase boundary, the propagation path was changed to penetrate the inside of the phase. The oxide layer located at the periphery of the crack along the phase boundary was identified as a complex multi-layered spinel structure, and Cr-rich carbides were also detected in the oxide. The cracks that propagated inside the austenite matrix were attributed to the presence of high external stresses and impurities.

• Korean Journal of Metals and Materials
• /
• v.49 no.3
• /
• pp.197-202
• /
• 2011

This study was carried out to investigate the precipitation behavior of ${\chi}$ phase and effect of ${\chi}-phase$ which precipitated at the initial stage of aging on mechanical properties of 25%Cr-7%Ni-4%Mo-0.2%N super duplex stainless steel. ${\chi}-phase$ was precipitated mainly at the interface of ferrite / austenite phases and inside of the ferrite phase at the initial stage of aging, and it was transformed into ${\sigma}-phase$ with an increase of aging time. The ferrite phase was decomposed into new $austenite({\gamma}_2)phase$ and ${\sigma}-phase$ by aging treatment. The hardness and tensile strength of the initial stage of aging when ${\chi}-phase$ was precipitated did not changed considerably, while elongation rapidly decreased. Accordingly, it is considered that ${\chi}-phase$ didn't affect the hardness and strength significantly, but it affected the elongation.

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.17 no.1
• /
• pp.49-55
• /
• 2021

In this paper, an application example for fitness-for-service of material is shown. A kind of instrument valve is made of austenitic stainless steel fabricated by the cold working process. The tensile strength of the cold worked austenitic stainless steel has to be limited under 90 ksi to prevent the stress corrosion cracking in power plants. In industrial fields, tensile strengths of some materials were discovered to be over the regulation requirements in a certified material test report (CMTR). Owner's verification tests were performed to compare with that in a CMTR and to check the appropriateness. It is found that, in the case of verification test under the required test speed, valve materials could be used in the field. Although it is only one application sample of material check process in the power generation site, this case study could show an importance of basic experimental technology in academia and research circles.

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.19 no.1
• /
• pp.11-19
• /
• 2023

Additive manufacturing technology, called as 3D printing, is one of fourth industrial revolution technologies that can drive innovation in the manufacturing process, and thus should be applied to nuclear industry for various purposes according to the manufacturing trend change in the future. In this paper, we performed tensile tests of 3D printed stainless steel 316L as-built specimens manufactured by two types of technology; DED (Directed Energy Deposition) and PBF (Powder Bed Fusion). Their mechanical properties (tensile strength, yield strength, elongation and reduction of area) were compared. As a result of comparison, the mechanical properties of the PBF specimens were slightly better than those of DED specimens. In the same additive type of specimens, the tensile and yield strength of specimens in the X and Y direction were higher than those in the Z direction, but the elongation and ROA were lower.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2000.04a
• /
• pp.202-205
• /
• 2000

The effect of two step cold rolling and intermediate annealing conditions on the microstructure and texture evolution in type 430 stainless steel has been investigated tin order to improve ridging characteristic and deep drawability. The rolling and recrystallization textures were examined by orientation distributionfunction(ODF) and electron backscattered diffraction(EBSD). The observation showed that the intensity of ${\gamma}$-fiber was increased with two-step cold rolling process and so ridging characteristic and deep drawability were considerably improved. The relation between these properties an texture evolution has been discussed.

• Journal of the Korean institute of surface engineering
• /
• v.52 no.4
• /
• pp.194-202
• /
• 2019

A systematic investigation was made on the influence of processing parameters such as gas composition and treatment temperature on the surface characteristics of hardened layers of low temperature plasma nitrided 316L Austenitic Stainless Steel. Various nitriding processes were conducted by changing temperature ($370^{\circ}C$ to $430^{\circ}C$) and changing $N_2$ percentage (10% to 25%) for 15 hours in the glow discharge environment of a gas mixture of $N_2$ and $H_2$ in a plasma nitriding system. In this process a constant pressure of 4 Torr was maintained. Increasing nitriding temperature from $370^{\circ}C$ to $430^{\circ}C$, increases the thickness of S phase layer and the surface hardness, and also makes an improvement in corrosion resistance, irrespective of nitrogen percent. On the other hand, increasing nitrogen percent from 10% to 25% at $430^{\circ}C$ decreases corrosion resistance although it increases the surface hardness and the thickness of S phase layer. Therefore, optimized condition was selected as nitriding temperature of $430^{\circ}C$ with 10% nitrogen, as at this condition, the treated sample showed better corrosion resistance. Moreover to further increase the thickness of S phase layer and surface hardness without compromising the corrosion behavior, further research was conducted by fixing the $N_2$ content at 10% with introducing various amount of $CH_4$ content from 0% to 5% in the nitriding atmosphere. The best treatment condition was determined as 10% $N_2$ and 5% $CH_4$ content at $430^{\circ}C$, where the thickness of S phase layer of about $17{\mu}m$ and a surface hardness of $980HV_{0.1}$ were obtained (before treatment $250HV_{0.1}$ hardness). This specimen also showed much higher pitting potential, i.e. better corrosion resistance, than specimens treated at different process conditions and the untreated one.

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.18 no.1
• /
• pp.26-35
• /
• 2022

When piping system in a nuclear power plant is subjected to a beyond design seismic condition, it is important to accurately determine possibility of crack initiation and, if initiation occurs, its location and time. From recent experimental works on elbow pipes, it was found that the crack initiation location and crack propagation direction of the SA403 WP316 stainless steel elbow pipe were affected by the pipe thickness. In this paper, the crack initiation location and crack propagation direction for SA403 WP316 stainless steel elbow pipes with different thickness were analyzed via elastic-plastic finite element analysis. Based on FE results, the effect of the pipe thickness on different crack initiation location and crack propagation direction was analyzed using ovality, stress and strain components. It was also confirmed that the presence of internal pressure had no effect on the crack initiation location and crack propagation direction.