• Journal of the Korean Institute of Gas
• /
• v.2 no.4
• /
• pp.42-46
• /
• 1998

Miniaturized specimen technology Permits mechanical behavior to be determined using a minimum volume of material. The technology is useful in case of not collecting a large amount of materials from industrial equipments. Five kinds of accelerated degradation materials were prepared by isothermal aging heat treatment at $630^{\circ}C$. Three kinds of specimens were prepared for impact testing. In order to increase plastic constraint of subsize specimen, side-groove was introduced. Results between subsize and full size impact testing were compared. Size effects correlations were developed for the impact properties of turbine rotor material. These correlations successfully predict the ductile brittle transition temperature (DBTT) of full size Charpy impact specimens based on subsize specimen data.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.22 no.1
• /
• pp.65-73
• /
• 2002

Artificial aging was performed to simulate the microstructural degradation in 2.25Cr-1Mo steel arising from long time exposure at $540^{\circ}C$. Microstructural analysis (mean equivalent size, number of carbides per unit area) and measurement of mechanical properties(UTS, Vickers hardness) and magnetic properties(coercivity, remanence) were performed. By comparing these results, the relationship between magnetic properties and microstructural changes with artificial aging was clarified. The carbides were classified as rod, globular and acicular type in terms of morphology. The fine acicular carbides were found to diminish drastically in the initial stage of aging. The magnetic coercivity and remanence were observed to decrease rapidly in the initial about 920 hours of aging time and then decrease slowly afterwards. Linear correlations between the mechanical properties and magnetic properties such as correlations remanence were found.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.28 no.6
• /
• pp.477-482
• /
• 2008

The influence of dislocation substructure of metallic materials on ultrasonic velocity has been experimentally investigated. The test materials of pure Cu, brass (Cu-35Zn), 2.25Cr-1Mo steel, and AISI 316 with different stacking fault energy (SFE) are plastically deformed in order to generate dislocation substructures. The longitudinal wave velocit $(C_L)$ decreases as a function of tensile strain in each material. The $C_L$ of Cu-35Zn and AISI 316 decreases monotonously with tensile strain, but $C_L$ of Cu and 2.25Cr-1Mo steel shows plateau phenomena due to the stable dislocation substructure. The variation of ultrasonic velocity with the extent of dislocation damping and dislocation substructures is discussed.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.132-137
• /
• 2008

A failure analysis of ammonia converter which suffered hydrogen attack in two years since its initial operating time was presented. It is constructed from 2.25 Cr.1 Mo steel. Analysis showed that the failure on closing seam weld joint was due to local improper post weld heat treatment (PWHT). Improper PWHT can introduce high residual stresses in thick-walled pressure vessel. High residual stress level in weld joint is very prone to hydrogen attack for any components which are operating in hydrogen gas environment. The repair procedures based on the principle to decrease the residual stress then proposed. The repair was controlled very carefully by applying several nondestructive tests in the each stage of repair. To assure the successful of the proposed repair, after one year since repair time, high temperature ultrasonic and TOFD methods were applied on-stream to this equipment in order to evaluate its post repair condition. The two methods showed good results on the repaired area.

• Journal of Ocean Engineering and Technology
• /
• v.10 no.2
• /
• pp.77-87
• /
• 1996

The estimation of the remaining life for the aged components in power plant as well as chemical and peroleum plants has been recently coberned. The raw materials used in this syudy are the 1Cr-1Mo-0.25V rotor steel which intensified P and S compositions along with the nominal compositions of ASTM A470 standard. Five kinds of specimens with the different degradation levels were prepared by isothermal aging teat treatment at $630^{\circ}C$ The mechanical properties and fatigue strength of virgin and aged 1Cr-1Mo-0.25V rotor steel have been inbestigated through the hardness, tensile, fatigue test, SEM fractograph and EDS analysis at room temperature. Thus, the data of aged specimens were compared with those of virgin specimen to evaluate the aging effects. The main results obtained in this study are as follows; The decrease of the hardness due to degradation was distinguished until 50, 000hrs simulated service time. And is was confirmed that the considerable amount of P, Mn, Cr and S was precipitated at the grain boundary of aged material through the SEM and EDS analysis. The fatigue strength of 25, 000, 50, 000, 75, 000 and 100, 000hrs aged material was decreased 29.5%, 24.4%, 28.6%, 35.7% than that of virgin material at $10^7$ cycles of room temperature. The major cracks of virgin and aged materials initiated at the inclusions including Si, P and Mn compositions which were located at the outer periphery of the specimen.

• Proceedings of the KWS Conference
• /
• 2003.05a
• /
• pp.251-253
• /
• 2003

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.17 no.6
• /
• pp.1321-1329
• /
• 1993

Long time creep strength and life prediction of 1% Cr-Mo-V and 12% Cr rotor steel were performed by using round-bar type specimens under static load at 500-600.deg. C TTP (time temperature parameter), MCM (minimum commitment method) and ISM (initial strain method newly devised) as life prediction methods were investigated, and the results could be summarized as follows. (1) The minimum parameter of SEE (standard error) by TTP was proved as LMP (larson-miller parameter), and the minimum parameter of RMS (root mean squares), by data less than 10$^{3}$hrs was MHP (manson-haferd parameter). (2) The parameters of the minimum and the maximum strength values predicted in $10^{5}$hrs creep life of 1% Cr-Mo-V steel by TTP were LMP and MSP, respectively. In case of 12% Cr steel above $550^{\circ}C$ OSDP (orr-sherby-dorn parameter) was minimum and MSP (manson-succop parameter) was maximum, but below $550^{\circ}C$, the inverse phenomena was observed. On the other hand the creep strengths before $10^{3}hrs$ life by MCM were similar to those by TTP, but the strengths after $10^{3}hrs$ life were 10-25% lower than those by TTP. (3) Creep strengths by ISM were maximum 5% lower than those by TTP. Because $10^{5}hrs$ strengths were similar to those of the lower band by TTP, the ISM was safer than the TTP.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2001.10a
• /
• pp.319-323
• /
• 2001

In significant number of energy-related facilities for like thermal power plant or petro-chemical industry, CrMo steels are widely used energy conversion industries. However, these materials undergo precipitation of carbides or intermetallic compounds into grain boundary and change of internal microstructure such as coarsening of precipitation, decrease of solute elements and impurity segregation under more severe service conditions, which results in deterioration of inherent superior material characteristics. In this study, it was verified experimentally the feasibility of the aging degradation evaluation for degraded 2.25Cr-lMo steel specimens prepared by isothermal aging heat treatment at 63$0^{\circ}C$ by high frequency longitudinal ultrasonic and surface SH wave investigating the change of attenuation coefficient analyzed by spectral analysis. Attenuation coefficient had a tendency to increase as degradation proceeded.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.21 no.1
• /
• pp.32-38
• /
• 2001

Although the ultrasonic method has been developed and used widely in the fields, it has been used only for measuring the defect size and thickness loss. In this study, the relationship between surface wave attenuation through micro-crack growth and variation of velocity under repeated cyclic loading has been investigated. The specimens are adopted from 2.25Cr-1Mo steel, which is used for power plant and pipeline system, and have dimensions of $200{\times}40{\times}4mm$. The results of ultrasonic test with a 5MHz transducer show that surface wave velocity gradually decreases from the point of 60% of fatigue life and the crack length of 2mm with the increasing fatigue cycles. From the results of this study, it is found that the technique using the ultrasonic velocity change is one of very useful methods to evaluate the fatigue life nondestructively.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.21 no.4
• /
• pp.439-445
• /
• 2001

The destructive method is reliable and widely used lot the estimation of material degradation but, it have time-consuming and a great difficulty in preparing specimens from in-service industrial facilities. Therefore, the estimation of degraded structural materials used at high temperature by nondestructive evaluation such as electric resistance method, replica method, Barkhausen noise method, electro-chemical method and ultrasonic method are strongly desired. Ultrasonic nondestructive evaluation technique has been reported good to attain efficiency of measurement, high sensitivity of measurement, and rapidity and reliability of result interpretation. In this study, it was verified experimentally the feasibility of the evaluation of degraded 2.25Cr-1Mo steel specimens which were prepared by the isothermal aging heat treatment at $630^{\circ}C$ by high frequency longitudinal wave method investigating the change of attenuation coefficient by FFT analysis and wavelet transform. Because of carbide precipitation increase and spheroidization near grain boundary of microstructure to aging degradation, attenuation coefficient had a tendency to increase as degradation proceeded. It was identified possibly to evaluate degradation using the characteristics of high-frequency ultrasonics. Frequency dependence of ultrasonic attenuation coefficient to aging degradation appeared large, which made sure that attenuation coefficient is an important parameter for evaluation of aging degradation.