• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.456-456
• /
• 2009

Boron doping on an n-type Si wafer is requisite process for IBC (Interdigitated Back Contact) solar cells. Fiber laser annealing is one of boron doping methods. For the boron doping, uniformly coated or deposited film is highly required. Plasma enhanced chemical vapor deposition (PECVD) method provides a uniform dopant film or layer which can facilitate doping. Because amorphous silicon layer absorption range for the wavelength of fiber laser does not match well for the direct annealing. In this study, to enhance thermal affection on the existing p-a-Si:H layer, a ${\mu}c$-Si:H intrinsic layer was deposited on the p-a-Si:H layer additionally by PECVD. To improve heat transfer rate to the amorphous silicon layer, and as heating both sides and protecting boron eliminating from the amorphous silicon layer. For p-a-Si:H layer with the ratio of $SiH_4$ : $B_2H_6$ : $H_2$ = 30 : 30 : 120, at $200^{\circ}C$, 50 W, 0.2 Torr for 30 minutes, and for ${\mu}c$-Si:H intrinsic layer, $SiH_4$ : $H_2$ = 10 : 300, at $200^{\circ}C$, 30 W, 0.5 Torr for 60 minutes, 2 cm $\times$ 2 cm size wafers were used. In consequence of comparing the results of lifetime measurement and sheet resistance relation, the laser condition set of 20 ~ 27 % of power, 150 ~ 160 kHz, 20 ~ 50 mm/s of marking speed, and $10\;{\sim}\;50 {\mu}m$ spacing with continuous wave mode of scanner lens showed the correlation between lifetime and sheet resistance as $100\;{\Omega}/sq$ and $11.8\;{\mu}s$ vs. $17\;{\Omega}/sq$ and $8.2\;{\mu}s$. Comparing to the singly deposited p-a-Si:H layer case, the additional ${\mu}c$-Si:H layer for doping resulted in no trade-offs, but showed slight improvement of both lifetime and sheet resistance, however sheet resistance might be confined by the additional intrinsic layer. This might come from the ineffective crystallization of amorphous silicon layer. For the additional layer case, lifetime and sheet resistance were measured as $84.8\;{\Omega}/sq$ and $11.09\;{\mu}s$ vs. $79.8\;{\Omega}/sq$ and $11.93\;{\mu}s$. The co-existence of $n^+$layeronthesamesurfaceandeliminating the laser damage should be taken into account for an IBC solar cell structure. Heavily doped uniform boron layer by fiber laser brings not only basic and essential conditions for the beginning step of IBC solar cell fabrication processes, but also the controllable doping concentration and depth that can be established according to the deposition conditions of layers.

• Proceedings of the IEEK Conference
• /
• 2000.06b
• /
• pp.80-83
• /
• 2000

In this work we deposited Pentacene thin film by OMBD at the various substrate temperatures, deposition rate and the various annealing temperatures for the fabrication of organic TFT and investigated the electrical and film surface characteristics such as sheet resistance, contact resistance and conductance Film thickness were measured by $\alpha$-step and the sheet resistance, contact resistance and conductance were extracted from the relation between the distance of the contacts and the resistance. During the film deposition the substrate temperature was held at 3$0^{\circ}C$, 4$0^{\circ}C$, 5$0^{\circ}C$, 6$0^{\circ}C$, 8$0^{\circ}C$ and 10$0^{\circ}C$, respectively. After the film deposition, Au contact was deposited by thermal evaporation. For the effect of annealing, the thin film was annealed in the nitrogen environment at 10$0^{\circ}C$ and 14$0^{\circ}C$ for 10 seconds, respectively. Film surface characteristics at the vatious substrate temperatures were measured by AFM. The crystallization of thin film was improved as the substrate temperatures were increased and the maximum gram size was 4${\mu}{\textrm}{m}$. The conductivity of thin film was found to be 7.40 $\times$10$^{-7}$ ~ 7.78$\times$10$^{-6}$ S/cm and the minimum contact resistance was 2.5324 ㏁.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.4
• /
• pp.362-367
• /
• 2008

We have Manufactured the low-k dielectric interlayer fabricated by plasma enhanced chemical vapor deposition (PECVD), The thin film of SiOCH is studied correlation between components and Dielectric constant. The precursor was evaporated and introduced with the flow rates from 16 sccm to 25 sccm by 1sccm step in the constant flow rate of 60 sccm $O_2$ in process chamber. The chemical characteristics of SiOCH were analyzed by measuring FT/IR absorption lines and obtained each dielectric constant measuring C-V. Then compare respectively. ILD of BTMSM/$O_2$ could have low dielectric constant about $k\sim2$, and react sensitively. Also dielectric constant could be decreased by the effects of decreasing $CH_3$ and growing Si-O-Si(C) after annealing process.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.11
• /
• pp.969-975
• /
• 2000

Laser direct writing of micro-patterned copper lines has been achieved by pyrolytic decomposition of copper formate films (Cu(HCOO)$_2$.4$H_2O$), as a metallo-organic precursor, using a focused CW Ar$^{+}$ laser beam (λ=514nm) on PCB boards and glass substrates. The linewidth and thickness of the lines wee investigated as a functin of laser power and scan speed. The profiles of the lines were measured by scanning electron microscope (SEM), surface profiler ($\alpha$-step) and atomic force measured by scanning electron microscope (SEM), surface profiler ($\alpha$-step) and atomic force microscopy (AFM). The electrical resistivities of the patterned lines were also investigated as a function of laser parameters using probe station and semiconductor analyzer. We compared resistivities of the patterned copper lines with these of the Cu bulk. Resistivities decreased due to changes in morphology and porosity of the deposit, which were about 3.8 $\mu$$\Omega$cm and 12$\mu$$\Omega$cm on PCB and glass substrates after annealing at 30$0^{\circ}C$ for 5 minutes.s.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.9
• /
• pp.739-745
• /
• 1998

The objective of this paper is to provide experimental data of Er(rare- earth)doped $SiO_2$thin film made by sputtering methods. The deposition rate of silica glass by sputtering method was 55$\AA$/min. In EDD measurements, the average Er concentration in the deposited film was 0.77(wt%). After annealing at $900^{\circ}C$, the Cl concentration decreased from 3.79(wt%) to 1.52(wt%). The refractive indices of the core $n_1$, cladding $n_2$ were 1.458, 1.558 respectively at 632.8 nm. The refractive index difference between core and cladding, $\Delta$n was 0.1. The refractive index profile of core and cladding interface shows step profile. In the study, $SiO_2$ glass films of Si wafer were successfully doped with active erbium. Therefore, this experimental data will be applicable for fabrications of Er doped planar integrated optical device.

• Journal of Magnetics
• /
• v.20 no.3
• /
• pp.211-214
• /
• 2015

$Cr_2O_3$ nanoparticles were prepared via one-step reactive laser ablation of Cr in oxygen. The metastable $CrO_2$ phase was obtained through the subsequent oxidation of $Cr_2O_3$ nanoparticles under $O_2$ with gas pressures of up to 40 MPa. The as-prepared $Cr_2O_3$ nanoparticles are spherical or rectangular in shape with sizes ranging from 20 nm to 50 nm. High oxygen pressure annealing is effective in producing meta-stable $CrO_2$ from as-dried $Cr_2O_3$ nanoparticles, and the $Cr_2O_3$ nanoparticles exhibit a weak ferromagnetic behavior with an exchange bias of up to 11 mT that can be ascribed to the interfacial exchange coupling between uncompensated surface spins and the antiferromagnetic core. The $Cr_2O_3/CrO_2$ nanoparticles exhibit an enhanced saturation magnetization and a reduced exchange bias with an increasing faction of $CrO_2$ due to the elimination of uncompensated surface spins over the $Cr_2O_3$ nanoparticles when exposed to a high pressure of $O_2$ and/or possible phase segregation that results in a smaller grain size for both $Cr_2O_3$ and $CrO_2$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.170-173
• /
• 2001

Thin films of phase-pure perovskite (P $b_{0.72}$L $a_{0.28}$) $Ti_{0.93}$ $O_3$(PLT) were deposited in-situ onto Pt/Ti/ $SiO_2$/Si substrates by pulsed laser deposition. We have systematically investigated the variation of grain sizes depending on the process condition. Both in-situ annealing and ex-situ annealing treatments have been compared depending on the annealing time. Two-step process to grow (P $b_{0.72}$L $a_{0.28}$) $Ti_{0.93}$ $O_3$(PLT) films was adopted and verified to be useful to enlarge the grain size of the film and to enhance the leakage current characteristics. The grain sizes of PLT thin films were successfully controlled 260 to 350 nm by changing process parameters. Electrical properties including dielectric constant, ferroelectric characteristics, crystallization and leakage current of PLT thin films were shown to be strongly inf1uenced by grain size. Also PLT thin films on p-type(100) Si substrate will be fabricated by pulsed laser deposition technique using a Nd:YAG laser with different wavelengths of 355, 532 and 1064 nm. Effect of the variation of laser wavelength on dielectric properties will be discussed. Microstructural and electrical properties of the film were investigated by C-V measurement leakage current measurement and SEM.ent and SEM.

• Journal of the Korean Vacuum Society
• /
• v.13 no.3
• /
• pp.120-126
• /
• 2004

A damage-reduced trench was investigated in view of the defect distribution along trench sidewall and bottom using high resolution transmission electron microscopy, which was formed by HBr plasma and additive gases in magnetically enhanced reactive ion etching system. Adding $O_2$ and other additive gases into HBr plasma makes it possible to eliminate sidewall undercut and lower surface roughness by forming the passivation layer of lateral etching. To reduce the RIE induced damage and obtain the fine shape trench corner rounding, we investigated the hydrogen annealing effect after trench formation. Silicon atomic migration on trench surfaces using high temperature hydrogen annealing was observed with atomic scale view. Migrated atoms on crystal surfaces formed specific crystal planes such as (111), (113) low index planes, instead of fully rounded comers to reduce the overall surface energy. We could observe the buildup of migrated atoms against the oxide mask, which originated from the surface migration of silicon atoms. Using this hydrogen annealing, more uniform thermal oxide could be grown on trench surfaces, suitable for the improvement of oxide breakdown.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.48 no.9
• /
• pp.623-627
• /
• 1999

We report a new in-situ fluorine passivation method without in implantation by employing excimer laser annealing of $SiO_{x}F_{y}$/a-Si structure and its effects on p-channel poly-Si TFTs. The proposed method doesn't require any additional annealing step and is a low temperature process because fluorine passivation is simultaneous with excimer-laser-induced crystallization. A in-situ fluorine passivation by the proposed method was verified form XPS analysis and conductivity measurement. From experimental results, it has been shown that the proposed method is effective to improve the electrical characteristics, specially field-effect mobility, and the electrical stability of p-channel poly-Si TFTs. The improvement id due to fluorine passivation, which reduces the trap state density and forms the strong Si-F bonds in poly-Si channel and $SiO_2/poly-Si$ interface. From these results, the high performance poly-Si TFTs canbe obtained by employing the excimer-laser-induced fluorine passivation method.

• Applied Science and Convergence Technology
• /
• v.27 no.5
• /
• pp.105-108
• /
• 2018

Transparent $TiO_2$ nanotube arrays are successfully prepared by a two-step approach involving electrochemical anodization and RF magnetron sputtering. First, a Ti film is deposited on an FTO substrate by RF magnetron sputtering at room temperature. The morphologies of the Ti film are controlled by the working distance, Ar flow, and DC power. Second, an anodization treatment is electrochemically performed for the formation of nanotube arrays from the deposited Ti film, followed by post-annealing treatment in air for the formation of $TiO_2$ crystallization. The back side of the crystallized $TiO_2$ nanotube arrays is illuminated with solar light to characterize the photoelectrochemical reaction, and their photoelectrochemical properties are investigated. This work provides information on application of a thin film deposited by RF sputtering in the field of photoelectrochemical water splitting.