• Journal of the Korean Society of Safety
• /
• v.15 no.4
• /
• pp.8-14
• /
• 2000

The remaining life estimation for the aged components in power plants as well as chemical plants are very important because mechanical properties of the components are degraded with time of service exposure in the high temperature. Since it is difficult to take specimens from the operating components to evaluate mechanical properties of components, accelerated aging technique are needed to estimate and analyse the material degradation. In the this study, test materials with 4 different degradation levels were prepared by isothermal aging heat treatment at $630^{\circ}C$. And tensile test, $k_{IC}$ test, hardness test and Scanning Electron Microscope analysis were performed in order to evaluate the degradation of 1Cr-1Mo-0.25V steels.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.132-137
• /
• 2001

Miniaturized specimen technology is useful to characterize the mechanical behavior using a minimum volume of material, because it is almost impossible to sample the conventional specimen for the fracture toughness test without damage to equipment. Test material was 1Cr-1Mo-0.25V steel which was widely used for turbine rotor material. Two kinds of miniaturized impact specimens were prepared, i.e., miniaturized specimen with side groove and without side groove. The correlation between ductile brittle transition temperature(DBTT) of full size impact specimen and that of miniaturized impact specimen was made. The characteristics of miniaturized impact specimens technique as well as fracture stress were discussed. Finally, we concluded that the characteristics of fracture stress change on aging time were similar to that of DBTT.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.109-109
• /
• 2018

Cr-Mo 합금강은 고온 환경 하에서 높은 크리이프 강도와 우수한 내식성 때문에 발전설비, 석유 화학, 그리고 해양산업과 같은 여러 산업분야에서 널리 사용되고 있다. 특히, Cr-Mo 강의 내식성은 합금 내 Cr 함량에 크게 의존한다. 이는 고온에서 Cr과 O가 화학적 반응을 일으킴에 따라 보호성의 Cr 산화스케일을 형성하기 때문이다. 그러나 화석연료를 사용하는 발전설비의 경우, $SO_2$가 포함된 강한 부식성의 연소 가스가 배출되며, 이에 노출된 금속의 표면에서는 산화와 황화가 동시에 발생한다. 황화스케일은 산화스케일에 비해 매우 빠르게 성장하며, 그 특성이 매우 취약하기 때문에 황화 환경에서 금속의 내식성 및 기계적 물성치는 보다 크게 저하된다. 따라서 본 연구에서는 화력 발전소의 증기발생용 튜브 재료인 9Cr-1MoVNb 강을 선정하였으며, $SO_2$ 가스 환경 하에서의 부식 및 기계적 물성치 저하 특성을 평가하고자 하였다. 본 연구에서 사용된 9Cr-1MoVNb강의 화학 성분 조성은 0.1 C, 0.38 Si, 0.46 Mn, 0.25 Ni, 8.38 Cr, 0.93 Mo, 0.18 V, 0.09 Nb, 그리고 나머지는 Fe이다. 부식시험은 가공된 미소시험편과 인장시험편을 전기열처리로에 장입한 후, $650^{\circ}C$에서 $N_2+O_2+O_2+SO_2$ 조성의 가스를 분당 50 CC로 흘려주었다. 제작된 시험편에 대한 부식거동은 무게 증가량, optical microscope, scanning electron microsope, 그리고 energy dispersive x-ray spectrum을 통해 평가하였다. 그리고 기계적 물성치 평가를 위한 인장시험은 분당 2mm 변위제어를 통해 실시하였다. 그 결과, 9Cr-1MoVNb 강은 $SO_2$ 가스 환경 하에서 비 보호적인 Fe-풍부상의 산화 스케일층이 두껍게 형성됨에 따라 열악한 내식성을 나타냈다. 그에 따라 기계적 물성치는 저하되는 경향을 나타내었다.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.7
• /
• pp.1262-1269
• /
• 2002

It is inevitable to evaluate the life of turbine rotor because the operating periods of power plants need to be extended. For the test, seven kinds of specimens with different degradation levels were prepared by the isothermal heat treatment at $630^{\circ}C$. Magnetic methods utilizing Barkhausen noise coercive force($BN_c$) were applied to detect the degradation caused by thermal aging. Magnetic property of material is related with domain dynamics and that is affected by the microstructure of material. Therefore $BN_c$ is very sensitive to the microstructure change of the material. With the increase of degradation, $BN_c$ was decreased and this phenomenon is considered due to precipitations and grain size. The result was compared with Vickers hardness($H_v$) and coercive force($H_c$) to detect the relative variation, and was related with $H_v$ and YS to estimate the change of the mechanical properties with the degradation.

• Journal of Ocean Engineering and Technology
• /
• v.3 no.2
• /
• pp.125-137
• /
• 1989

To check technical improvement in the soundness and strength of 12% Cr steel rotor, a 25 tons of rotor with 65 tons of ingot was made in real size and was cut to pieces to take test samples, and the various mechanical tests such as impact, tensile, creep, and fatigue were carried out. The strengths are compared with those of 1% Cr-Mo-V rotor of same size. Microstructures of the samples are examined and reviewed. The results can be summarized as follows. 1) Fracture appearance transition temperatures are 80.deg. C at the center part and 60.deg. C near surface of 12% Cr rotor, and 8.deg. C near surface of 1% Cr-Mo-V rotor. 2) Comparative rapid softening occurs at higher temperatures above 600.deg. C for 12% Cr steel and 550.deg. C for 1% Cr-Mo-V steel in tension tests. 3) Fatigue crack propagation rate of 12% Cr steel is almost same as that of 1% Cr-Mo-V steel at the same corresponding surface part of the rotors. The crack growth rate of center part of 12% Cr rotor is faster than near surface part of the rotor, and the crack growth rate at the load condition of R=0.04 is slower than that of the load condition of R=0.5 for both 12% Cr steel and 1% Cr-Mo-V steel. 4) Crack growth rate of radial direction near surface of 12% Cr rotor is faster than that of transverse direction at the same part because of the difference in residual stresses. 5) Both creep and fatigue strengths of 12% Cr steel are superior to those of 1% Cr-Mo-V steel and the difference is thought the effect of climb and glide controlled creep by solid solution of alloying elements and dispersion of carbides.

• Journal of Ocean Engineering and Technology
• /
• v.3 no.2
• /
• pp.625-625
• /
• 1989

To check technical improvement in the soundness and strength of 12% Cr steel rotor, a 25 tons of rotor with 65 tons of ingot was made in real size and was cut to pieces to take test samples, and the various mechanical tests such as impact, tensile, creep, and fatigue were carried out. The strengths are compared with those of 1% Cr-Mo-V rotor of same size. Microstructures of the samples are examined and reviewed. The results can be summarized as follows. 1) Fracture appearance transition temperatures are 80.deg. C at the center part and 60.deg. C near surface of 12% Cr rotor, and 8.deg. C near surface of 1% Cr-Mo-V rotor. 2) Comparative rapid softening occurs at higher temperatures above 600.deg. C for 12% Cr steel and 550.deg. C for 1% Cr-Mo-V steel in tension tests. 3) Fatigue crack propagation rate of 12% Cr steel is almost same as that of 1% Cr-Mo-V steel at the same corresponding surface part of the rotors. The crack growth rate of center part of 12% Cr rotor is faster than near surface part of the rotor, and the crack growth rate at the load condition of R=0.04 is slower than that of the load condition of R=0.5 for both 12% Cr steel and 1% Cr-Mo-V steel. 4) Crack growth rate of radial direction near surface of 12% Cr rotor is faster than that of transverse direction at the same part because of the difference in residual stresses. 5) Both creep and fatigue strengths of 12% Cr steel are superior to those of 1% Cr-Mo-V steel and the difference is thought the effect of climb and glide controlled creep by solid solution of alloying elements and dispersion of carbides.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.9
• /
• pp.2819-2832
• /
• 1996

The estimation of the remaining life for the aged components in power plant as well as chemical and petroleum plants has been recently concerned. The raw materials used in this study are the 1Cr-1Mo-0.25V steel which intensified P and S compositions along with the nominal compositions of ASTM A 470 standard. Five kinds of specimens with the different degradation levels were prepared by isothermal aging heat treatment at 630.deg.C. The mechanical properties and rotated bending fatigue strength of virgin and aged 1Cr-1Mo-0.25V steel have been investigated through the hardness, tensile, fatigue test, SEM fractograph and EDS analysis at 538.deg.C and room temperature, respectively. Thus the data of aged specimens were compared with those of virgin specimen to evaluate the aging effects. The main results obtained in this study are as follows ; The decrease of the yield and tensile strength due to degradation was distinguished until 50, 000hrs simulated service time. And it was confirmed that the considerable amount of P, Mn, Cr and S was precipitated at the grain boundary of aged material through the SEM and EDS analysis. The rotated bendingd fatigue strength at 538.deg.C of virgin, 25, 000, 50, 000, 75, 000 and 100, 000 hrs aged material was decreased 44.6 %, 49.6 %, 51.5 %, 52.4% and 53.8% than that of virgin material at 10$_{7}$cycles of room temperature, respectively. The major cracks of virgin and aged materials mainly initiated at the inclusions including Si, P and Mn compositions which were located at the outer periphery of the specimen.n.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.22 no.1
• /
• pp.14-21
• /
• 2002

The development of a new experimental method is required to easily observe the growth behavior of fatigue cracks. To satisfy the requirement, an image processing technique was introduced to fatigue testing. The length of surface fatigue crack could be successfully measured by the image processing system. At first, the image data of cracks were stored into the computer while the cyclic loading was interrupted. After testing, crack length was determined using an image processing software which was developed by authors. Various image processing techniques like a block matching method was applied tc the detection of surface fatigue cracks. By comparing the data measured by the image processing system with those by the manual measurement with a microscope, the effectiveness of the image processing system was established. If the proposed method is used to monitor and observe the crack growth behavior automatically, the time and efforts for fatigue test could be dramatically reduced.

• Korean Journal of Materials Research
• /
• v.14 no.1
• /
• pp.78-82
• /
• 2004

In this study, the degree of creep damages on the weldment accelerated creep degradation was nondestructively evaluated by replica method. The frequency of creep cavities occurrence has been observed highly at the intercritical HAZ. The life fraction of weldment damaged by creep has shown from 0.25(damage grade: 2) to 0.75(damage grade: 4) when it reptured. The degree of creep damages is considered to be evaluated by the metallographic replica method which is one of nondestructive evaluation methods.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.111-111
• /
• 2018

ASTM A387-Gr.91 강은 우수한 고온 강도, 크리이프 저항성 그리고 내산화성 등으로 인해 화력 및 바이오매스 발전 시설과 같은 고온 설비의 구조재료로 널리 사용되고 있다. 고온 환경에서 높은 강도는 탄화물과 탄질화물에 의한 석출강화가 주 요인으로 작용한다. 열처리 과정에서 Mo, Cr, Mn, 그리고 Fe는 구-오스테나이트 및 마르텐사이트 라스 입계에 $M_{23}C_6$ 탄화물로 석출되며, V, Nb, 및 N은 조직 내부에 미세한 MX 탄질화물로 석출된다. 따라서 합금의 고온 강도는 조직 내 석출물의 개수밀도와 크기에 크게 의존한다. 그러나 적용 환경의 특성 상 고온 노출에 따른 2차상 석출 및 조대화의 조직열화 현상이 발생하며, 이는 재료의 강도를 저하시킨다. 본 연구에서는 ASTM A387-Gr.91 강의 미세조직 열화에 따른 강도저하 및 파괴 양상을 고찰하는데 그 목적을 두었다. 본 연구에서 사용된 ASTM A387-Gr.91 강의 화학성분(wt, %)은 0.1 C, 0.38 Si, 0.46 Mn, 0.25 Ni, 8.38 Cr, 0.93 Mo, 0.18 V, 0.09 Nb, 그리고 나머지는 Fe 이다. 조직열화 및 기계적 강도저하 특성을 평가하기 위한 등온열화는 $650^{\circ}C$의 대기 환경에서 최대 1000시간동안 실시하였다. 열화된 시험편의 미세조직 및 탄화물에 대한 분석은 SEM과 EDS를 이용하여 실시하였다. 그리고 기계적 강도 평가는 인장실험과 비커스 경도시험을 통해 실시하였다. 또한 열화 시간에 따른 파단양상의 변화를 관찰하기 위해 인장시험편의 파단면을 SEM과 EDS를 이용하여 분석하였다. 그 결과, 열화에 따른 마르텐사이트 라스의 소실, 탄화물의 조대화, 그리고 2차상 석출의 조직 열화현상이 나타났다. 또한 기계적 강도는 조직 열화에 따라 저하되는 경향을 나타냈다.