• 대한기계학회논문집A
• /
• 제24권7호
• /
• pp.1673-1680
• /
• 2000

The degradation of a boiler header constructed by a material, 1Cr-0.5Mo steel in a fossil power plant is observed when the header is exposed for a long period to the high temperature and pressure. The present investigations are for evaluating the effect of the degradation on the material, such as its strength changes. Reheat-treated metal is used to compare the mechanical properties of the degraded and that of reheat-treated materials. Through the investigation, following results are obtained 1) the area ratio of ferrite in the reheat-treated material is larger than that of the degraded material, 2) the hardness and tensile strength of the degraded material are lower than that of the reheat-treated material, 3) the ductile-brittle transition temperature(DBTT) increased toward high temperature region, 4) the fatigue crack growth rate(FCGR) of the degraded material is higher than that of the reheat-treated material in the region of low ΔK value while FCGR of the both materials are similar in high ΔK region.

• 비파괴검사학회지
• /
• 제21권4호
• /
• pp.439-445
• /
• 2001

재료나 설비의 고온 장시간 사용으로 인하여 발생되는 재질열화 평가에는 파괴적인 방법이 널리 사용되고 있으며, 신뢰도가 높다. 그러나, 시험편의 채취가 어렵고 많은 경비와 시간이 소요된다. 전기저항법, 레프리카법, 바크하우젠 노이즈법, 전기화학적방법, 초음파법 등과 같은 비파괴적인 열화손상 평가 방법이 주목을 받고 있다. 본 연구에서는 2.25Cr-1Mo 강을 $630^{\circ}C$에서 장시간 등온열처리로 모의 열화시험편을 제작하고, 고온설비부재에서 발생되는 미세조직의 변화와 고주파 초음파의 전파특성(감쇠계수)과의 일대일 상관관계를 규명하여 초음파 비파괴평가에 의한 열화도 평가의 유용성 유모를 실험적으로 검증하였다. 그 결과 2.25Cr-1Mo 인공열화재의 경우 열화가 진행됨에 따라 탄화물의 석출 및 조대화가 일어나며 초음파 감쇠계수는 증가하는 경향을 나타내었으며, 그 정도는 침상의 탄화물이 거의 소멸되는 1,000시간 이후에 초음파 감쇠계수가 급격히 증가하는 매우 좋은 상관성을 나타내었다.

• 한국해양공학회지
• /
• 제12권2호통권28호
• /
• pp.65-70
• /
• 1998

In this report, the creep properties and creep life estimation by Larson-Miller Parameter(LMP) Method for 2.25Cr1Mo steel to be used as power plant tubes or other components were presented at the high temperatures of 500, 550, and $600^{\circ}C$. It was confirmed experimentally and quantitatively that a creep life estimation equation at such various high temperatures was well derived by LMP and could be used very effectively within the creep life of 10$^3$ hours, but very unreliable and even dangerous for design in a long term of creep life such as 10$^4$ or $10^5$ hours.

• 한국재료학회지
• /
• 제14권1호
• /
• pp.78-82
• /
• 2004

In this study, the degree of creep damages on the weldment accelerated creep degradation was nondestructively evaluated by replica method. The frequency of creep cavities occurrence has been observed highly at the intercritical HAZ. The life fraction of weldment damaged by creep has shown from 0.25(damage grade: 2) to 0.75(damage grade: 4) when it reptured. The degree of creep damages is considered to be evaluated by the metallographic replica method which is one of nondestructive evaluation methods.

• 한국압력기기공학회 논문집
• /
• 제10권1호
• /
• pp.64-69
• /
• 2014

Gr. 91 steel is used for the major structural components of Generation-IV reactor systems, such as a very high temperature reactor(VHTR) and sodium-cooled fast reactor(SFR). Since these structures are designed for up to 60 years at elevated temperatures, the prediction of long-term creep life is important for a design application of Gr. 91 steel. In this study, a number of creep rupture data were collected through world-wide literature surveys, and using these data, the long-term creep life was predicted in terms of three methods: the single-C method in Larson-Miller(L-M) parameter, multi-C constant method in the L-M parameter, and a modified method("sinh" equation) in the L-M parameter. The results of the creep-life prediction were compared using the standard deviation of error value, respectively. Modified method proposed by the "sinh" equation revealed better agreement in creep life prediction than the single-C L-M method.

• 비파괴검사학회지
• /
• 제21권4호
• /
• pp.415-424
• /
• 2001

고온에서 장시간 사용으로 인하여 발생되는 경년열화 평가에는 파괴적인 방법이 신뢰성이 높지만 시험편 채취의 어려움이 있다. 그러므로 비파괴석인 방법에 의한 열화도 평가가 바람직하다. 본 연구에서는 2.23Cr-1Mo강에 대하여 장시간 등온열처리로 모의 열화시험편을 제작하여 고온설비부재에서 발생되는 탄화물의 석출 및 조대화, 분순물의 입계편석 등 금속학적 미세조직을 관찰하고, 미세조직의 변화와 유도 초음파의 전파특성과의 상관관계를 규명하고, 파괴시험치와 그 결과를 비교하여 초음파 비파괴평가에 의한 고온부재의 열화도 평가의 가능성을 실험적으로 검증하고자 한다.

• Journal of Welding and Joining
• /
• 제19권3호
• /
• pp.278-284
• /
• 2001

Both creep deformation and creep crack growth experiments have been conducted on 2.25Cr-1Mo steel weldment in order to provided an information on residual life prediction of structural component weldment containing a crack. The stress exponent of creep deformation equation for the base metal and weldment at 823k were found to be 10.2 and 7.3, respectively. These two values could be assumed that dislocation climb processes are controlling the creep deformation of both materials. The creep rate of the weldment was very low, compared with that of base metal under the same applied stress. Whereas the creep crack growth rate of the weldment was almost twice higher than that of base metal under the fixed value of $C^*$. This may indicate that the weldment is stronger than the base metal in view of creep deformation and is brittle during creep crack growth due to the intrinsic microstructure of banite and relatively higher and Mn contents.

• 대한치과기공학회지
• /
• 제36권3호
• /
• pp.149-158
• /
• 2014

Purpose: Dental casting Co-Cr-Mo based alloys of five kinds of ingot type and two kinds of shot type were analyzed the melting processes with heating time of high frequency induction centrifugal casting machine using infrared thermal image analyzer. Methods: When Co-Cr-Mo based alloys were put about 30g/charge in the ceramic crucible of high frequency induction centrifugal casting machine and heat, Infrared thermal image analyzer and IR thermometer indicated these alloys in the crucible were set and operated. Results: The melting temperatures of alloys measuring infrared thermal image analyzer were deviated ${\pm}10^{\circ}C$ compared to those of manufacturing company. On the other hand, the melting time of alloys were differently appeared with the shape of alloys(ingot and shot type). Conclusion: The melting temperatures of dental Co-Cr-Mo based alloys were measured the degree of $1,360{\sim}1410^{\circ}C$ and the heating time with the alloys of ingot and shot type were deviated ${\pm}10sec$.

• 비파괴검사학회지
• /
• 제21권1호
• /
• pp.32-38
• /
• 2001

재료의 손상을 평가하기 위하여 초음파법에 대한 많은 연구가 진행되었고 널리 사용되고 있으나 대부분 균열의 성장 또는 두께의 감소와 같은 문제에 집중되고 있다. 본 연구에서는 2.25Cr-1Mo 강을 이용하여 반복하중에 의해 재료내부에 발생하는 미시균열을 조기에 감지하고, 피로에 의한 파괴를 미연에 방지할 수 있도록 초음파 표면파의 감쇠와 속도변화를 이용하여 균열길이 측정의 정량적인 평가방법을 제시하였다. 중심주파수 5MHz의 탐촉자를 이용하여 파단수명비 약 60%, 균열길이 약 2mm 정도에서 표면파의 속도 및 감쇠 변화를 탐지할 수 있었다. 고주파 탐촉자를 이용함으로써 미시균열의 발생을 조기에 탐지할 수 있으며, 파단수명을 예측하는 기초자료로 활용할 수 있다.

• 비파괴검사학회지
• /
• 제22권1호
• /
• pp.65-73
• /
• 2002

2.25Cr-1M 강이 $540^{\circ}C$에서 장시간 노출되었을 때 일어나는 미세조직 변화를 모사하기 위해 인공 열화를 실시하였으며 이에 대해 미세조직(탄환화물의 평균등가크기 및 단위면 개수), 기계적 성질 (인장강도 및 경도), 자기적 성질(보자력 및 잔류자화)을 측정하였다. 이들 결과를 비교함으로써 열화에 따른 자기적 성질의 변화와 미세조직 사이의 상관관계률 규명하였다. 탄화물을 그 형장에 따라 막대상, 구상, 침상으로 분류하였으며 침상의 탄화물은 열화 초반부에 급격히 소멸되는 경향을 보였다. 또한 보자력과 잔류자화는 열화 초반부에 급격히 감소한 후 점차 완만히 감소하는 경향을 보였다. 기계적 성질과 보자력 및 잔류자화 사이에는 선형적 상관관계가 존재하였다.