• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.5
• /
• pp.772-778
• /
• 2001

In this study, corrosion fatigue characteristics of 12Cr alloy steel were investigated in 3.5wt.% NaCl solution of 150$^{\circ}C$ and 4.5bar. Behavior of corrosion fatigue cracks was measured by the indirect compliance method and compared with the results in distilled water and in air. 1) 12Cr alloy steel was susceptible to temperature. Its susceptibility was increased as the temperature was increased. 2) The crack growth characteristics of 12Cr alloy steel in distilled water were similar to 3.5wt.% NaCl solution. 3) The temperature of solution affects to the crack growth characteristics of 12Cr alloy steel. In corrosion solutions of 4.5bar, 150$^{\circ}C$, fracture surfaces of corrosion fatigue crack growth at a/W=0.3 was showed the trans-granular fracture suface. As the crack grew up, it was changed to inter-granular type. In condition of high temperature, The crack growth behaviors of 12Cr alloy steel were remarkable.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.12
• /
• pp.2109-2115
• /
• 2001

Miniaturized specimen technology is useful to characterize the mechanical behavior when it is difficult to sample the material enough for the test. In this study, two kinds of miniaturized Charpy impact specimens(i.e., miniaturized specimen with side groove and without side groove) of aged 1Cr- lMo-0.25V steel were prepared and tested. The relationship between the extent of degradation in terms of ductile brittle transition temperature(DBTT) and the fracture stress of 1Cr-1Mo-0.25V steel was established. The fracture stress obtained from miniaturized specimen without side groove turned out to be linearly related with the DBTT of standard specimen. Therefore the fracture toughness of aged turbine rotor steel might be evaluated by the fracture stress. In addition, the correlation between DBTT of standard specimen and that of miniaturized specimen was investigated. As the results of normalizing DBTT by maximum elastic tensile stress, the normalized DBTT of miniaturized specimen without side groove allows one to estimate that of standard specimen.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.30 no.8 s.251
• /
• pp.965-975
• /
• 2006

High pressure turbine blades are one of the key components in fossil power plants operated at high temperature. The blade is usually made of 12Cr steel and its operating temperature is above $500^{\circ}C$. Long term service at this temperature causes material degradation accompanied by changes in microstructures and mechanical properties such as strength and toughness. Quantitative assessment of reduction of strength and toughness due to high temperature material degradation is required for residual life assessment of the blade components. Nondestructive technique is preferred. So far most of the research of this kind was conducted with low alloy steels such as carbon steel, 1.25Cr0.5Mo steel or 2.25Cr1Mo steel. High alloy steel was not investigated. In this study one of the high Cr steel, 12Cr steel, was selected for high temperature material degradation. Electrochemical polarization method was employed to measure degradation. Strength reduction of the 12Cr steel was represented by hardness and toughness reduction was represented by change of transition temperature, FATT. Empirical relationships between the electrochemical polarization parameter and significance of material degradation were established. These relationship can be used for assessing the strength and toughness on the aged high pressure blade components indirectly by using the electrochemical method.

• Journal of Ocean Engineering and Technology
• /
• v.3 no.2
• /
• pp.125-137
• /
• 1989

To check technical improvement in the soundness and strength of 12% Cr steel rotor, a 25 tons of rotor with 65 tons of ingot was made in real size and was cut to pieces to take test samples, and the various mechanical tests such as impact, tensile, creep, and fatigue were carried out. The strengths are compared with those of 1% Cr-Mo-V rotor of same size. Microstructures of the samples are examined and reviewed. The results can be summarized as follows. 1) Fracture appearance transition temperatures are 80.deg. C at the center part and 60.deg. C near surface of 12% Cr rotor, and 8.deg. C near surface of 1% Cr-Mo-V rotor. 2) Comparative rapid softening occurs at higher temperatures above 600.deg. C for 12% Cr steel and 550.deg. C for 1% Cr-Mo-V steel in tension tests. 3) Fatigue crack propagation rate of 12% Cr steel is almost same as that of 1% Cr-Mo-V steel at the same corresponding surface part of the rotors. The crack growth rate of center part of 12% Cr rotor is faster than near surface part of the rotor, and the crack growth rate at the load condition of R=0.04 is slower than that of the load condition of R=0.5 for both 12% Cr steel and 1% Cr-Mo-V steel. 4) Crack growth rate of radial direction near surface of 12% Cr rotor is faster than that of transverse direction at the same part because of the difference in residual stresses. 5) Both creep and fatigue strengths of 12% Cr steel are superior to those of 1% Cr-Mo-V steel and the difference is thought the effect of climb and glide controlled creep by solid solution of alloying elements and dispersion of carbides.

• Journal of Ocean Engineering and Technology
• /
• v.3 no.2
• /
• pp.625-625
• /
• 1989

To check technical improvement in the soundness and strength of 12% Cr steel rotor, a 25 tons of rotor with 65 tons of ingot was made in real size and was cut to pieces to take test samples, and the various mechanical tests such as impact, tensile, creep, and fatigue were carried out. The strengths are compared with those of 1% Cr-Mo-V rotor of same size. Microstructures of the samples are examined and reviewed. The results can be summarized as follows. 1) Fracture appearance transition temperatures are 80.deg. C at the center part and 60.deg. C near surface of 12% Cr rotor, and 8.deg. C near surface of 1% Cr-Mo-V rotor. 2) Comparative rapid softening occurs at higher temperatures above 600.deg. C for 12% Cr steel and 550.deg. C for 1% Cr-Mo-V steel in tension tests. 3) Fatigue crack propagation rate of 12% Cr steel is almost same as that of 1% Cr-Mo-V steel at the same corresponding surface part of the rotors. The crack growth rate of center part of 12% Cr rotor is faster than near surface part of the rotor, and the crack growth rate at the load condition of R=0.04 is slower than that of the load condition of R=0.5 for both 12% Cr steel and 1% Cr-Mo-V steel. 4) Crack growth rate of radial direction near surface of 12% Cr rotor is faster than that of transverse direction at the same part because of the difference in residual stresses. 5) Both creep and fatigue strengths of 12% Cr steel are superior to those of 1% Cr-Mo-V steel and the difference is thought the effect of climb and glide controlled creep by solid solution of alloying elements and dispersion of carbides.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.28 no.2
• /
• pp.177-183
• /
• 2008

The typical heat-resisting rotor steels such as 2.25CrMo, 9CrMo and 12CrW steel were experimentally studied in order to understand their materials degradation under high temperature and pressure during the long-term service, and then use the basic studies for the structural health monitoring. In order to monitor the materials degradation, it was conducted by the isothermal aging for 2.25CrMo steel, creep-fatigue for 9CrMo steel and creep for 12Cr steel with the incremental step test. The ultrasonic wave properties, electrical resistivity and coercivity were interpreted in relation to microstructural changes at each material and showed strong sensitivity to the specific microstructural evolution.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.6
• /
• pp.965-971
• /
• 2001

To estimate the reliability of 12Cr alloy steel, the material of turbine blade in the steam power plant, Its corrosion susceptibility and fatigue characteristics in NaCl and Na$_2$SO$_4$solution with the difference of concentration and temperature was investigated. The polarization tests recommended in ASTM G5 standard for corrosion susceptibility in the various corrosive solutions was estimated. It showed that the higher temperature, the faster corrosion rates and corrosion rates were the fastest in 3.5 wt.% NaCl and 1M Na$_2$SO$_4$solution. From these results, the degradation conditions were determined in distilled water, 3.5 wt.% NaCl and 1M Na$_2$SO$_4$solution at room temperature, 60$\^{C}$ and 90$\^{C}$ during 3, 6 and 9 months. Its surface had a few pits for long duration. But, it was not susceptible in sulfide and chloride condition of several temperatures. If the degraded 12Cr alloy steel and non-degraded one were compared with fatigue characteristics, Any differences were not found regardless of temperature and degradation period.

• Journal of Power System Engineering
• /
• v.8 no.3
• /
• pp.18-22
• /
• 2004

Boiler is one of the most important utilities providing steam to turbine in order to supply mechanical energy in thermal power plant. It is composed of thousands of tubes for high efficient heat transfer. The material for boiler tubes is used in such high temperature and pressure condition as $540^{\circ}C$, 22MPa. The boiler tube material is required to resist creep damage, fatigue cracking, and corrosion damages. 2.25%Cr-1Mo steel is used for conventional boiler tubes, and austenitenite stainless steel is used for higher temperature boiler tubes. But the temperature and pressure of steam in power plant became higher for high plant efficiency. So, the property of boiler tube material must be upgaded to fit the plant property. Several boiler tube material was developed to fit such conditions. X20CrMoV12.1 steel is also developed in 1980's and used for superheater and reheater tubes in supercritical boilers. The material has martensite microstructures which is difficult to evaluate the degradation. In this thesis, degrade the X20CrMoV12.1 steel at high temperatures in electric furnace, and evaluate hardness with Vickers hardness tester and strengths with Indentation tester.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.12
• /
• pp.2116-2124
• /
• 2001

It's required mechanical properties of in-service facilities to maintain safety operation in power plants as well as chemical plants. In this studdy the four classes of the thermally aged 1Cr-lMo-0.25V specimens were prepared using an artificially accelerated aging method at 630$\^{C}$. Ultrasonic tests, tensile tests, K$\_$IC/ tests and hardness tests were performed in order to evaluate the degree of degradation of the material. The mechanical properties were decreased as degraded, but the attenuation coefficient and the harmonic generation level of a ultrasonic signal were increased. Expecially the nonlinear parameter derived from the harmonic generation level is sensitive and will be a good parameter to evaluate the material degradation.

• Proceedings of the KWS Conference
• /
• 2004.05a
• /
• pp.324-326
• /
• 2004

l2wt%Cr Steel has been applied on turbine bucket and nozzle partition material of power plant. Turbine bucket and nozzle get damaged by solid particle within steam, therefore they are protected by surface treatments such as ion nitriding, boriding and chrome carbide HVOF spray coating. In this study, solid particle erosion(SPE) characteristics after these surface treatments are examined at operating temperature 540$^{\circ}C$ and 590$^{\circ}C$ of fossil power plant and the mechanism of damage was studied. Erosion of 12wt%Cr steel is originated by micro cutting and that of boriding and chrome carbide HVOF spray is originated by these mechanism - repeating collision, crack initiation and propagation. As the results of SPE test at 540$^{\circ}C$ and 30$^{\circ}$ impact angle that is the most commonly occurred in power plant, Boriding had the best SPE -resistance property, Cr$_2$C$_3$-25(Ni20Cr) HVOF spayed and ion nitrided samples were also better than bare metals(l2wt%Cr Steels). At 590$^{\circ}C$ and 30$^{\circ}$ impact angle, Boriding had also the most superior characteristic and HVOF spay sample was better than bare metal.