Copper nano particles have been considered as the materials for conductive ink due to its good thermal, electrical conductivity and low cost. However, copper nanoparticles oxidize easily, decreasing dispersion stability and electrical conductivity. Therefore, it is important to develop a method to minimize oxidation of copper nano particles to improve its dispersion stability property in copper nano ink. In this study, copper nano particles were coated with 1-Octanethiol VSAM(Vaporized Self Assembled Multilayers) to prevent oxidation and coated copper powders were dispersed in conductive ink successfully by studying its relationship of different chain length of solvents to 1-Octanethiol coating layer to fabricate nano ink. Various alcohol solvents, such as 1-Hexanol, 1-Octanol, and 1-Decanol were used. The coating layer was observed using FESEM and TEM. Furthermore, dispersion of copper nano particles in nano inks, was characterized using Turbiscan analyzer, viscometer, and contact angle measurement tool.

• Journal of Powder Materials
• /
• v.18 no.4
• /
• pp.322-326
• /
• 2011

Inkjet printing was successfully done using Cu nano powder ink after these Cu nano powders were dry-coated with 1-octanethiol for oxidation prevention. 1-octanethiol, which is Self-Assembled Multi-layers (SAMs), was coated approximately 10-nm thick on the surface of Cu nano powders. 1-Octanol, which has the same chain length as that for 1-octanethiol, was used as a solvent to make the ink for inkjet printing. As a result, the fabricated ink was dispersed for about 4 weeks, and after printing and heat treatment at $350^{\circ}C$ for 4 hours, the resistivity for the printed pattern was measured to be $1.15{\times}10^{-5}{\Omega}{\cdot}cm$.