• 한국주조공학회지
• /
• 제27권2호
• /
• pp.88-94
• /
• 2007

General criteria for the risering design of steel castings and commercial codes for the flow and solidification analysis were used to design the optimized risering in V-process. Three type of specimens were chosen including thin plates and a thick disc. Sided riser installed in the front of a plate casting was effective to prevent the shrinkage defects and to increase the casting yield ratio. Exothennic sleeve and chill were also effective. It was possible to apply the general criteria for the risering design of steel castings to V-process. Temperature of a mold surface was expected to rise over $1,000^{\circ}C$ in the temperature calculation considering radiation effect of molten metal in the mold. Since weakening temperature of the vinyl used in V-process is about $70^{\circ}C$, it should be emphasized that a proper coating of the vinyl film is necessary to prevent the possibility of burning out of the vinyl by the molten metal.

• 한국주조공학회지
• /
• 제27권1호
• /
• pp.42-47
• /
• 2007

Vacuum molding process(V-process) has several benefits such as a lower total production cost and a high quality casting comparing to the conventional sand molding. Influence of the gating design on the molten metal flow was investigated in this study. General criteria for the gating design of the castings and commercial codes for the flow and solidification analysis were used to attain the optimized gating design in V-process. Though mold cavity was filled smoothly under the low initial velocity of molten metal, molten metal dashed against the upper part of the mold before the completion of the mold filling with higher initial molten metal velocity and fell soon. This phenomenon may affect collapsing the mold shape, however it is thought that the possibility of burning out of the vinyl by the molten metal is not so high because vinyl is coated with refractory material.

• Tribology and Lubricants
• /
• 제29권6호
• /
• pp.372-377
• /
• 2013

This study investigated the interface temperatures for the sliding friction of three types of pins fabricated with thermocouple wires by the suction casting method. Optical microscopy was used to examine the surrounding material state at the bonding interface with the thermocouple wires. Friction tests were performed under dry sliding conditions against stainless steel 304 at nominal stresses of 1.42-4.25 MPa and sliding speeds of 0.5-1.25 m/s. Tribological data were collected using a custom-made pin-on-disk apparatus that measured the interface temperature and corresponding friction coefficient. Static tests were performed to demonstrate the functionality and reliability of the thermocouple wires-combined temperature sensor (TCTS). Each TCTS showed good linearity and sensitivity and very similar response times for the thermocouple and critical temperature during sliding friction.