• Journal of the Korean Vacuum Society
• /
• v.14 no.1
• /
• pp.1-6
• /
• 2005

Getters are invariably covered with thin layers of oxides even in air. For the getter to function properly it is necessary to activate them by heating in vacuum during which the oxide layer is removed exposing clean surface. The so-called activation temperature is an important parameter along with gas sorption capacity since it determines the maximum temperature of a device in which a getter can be installed. Nevertheless, no standard method to measure activation temperature has been documented yet. In this study, a relatively simple method to measure the activation temperature based on the ultimate pressure measurement was suggested. The activation temperature of TiZrV alloy measured by the method was between 100℃～200℃.

• Journal of the Korean Vacuum Society
• /
• v.4 no.1
• /
• pp.104-108
• /
• 1995

Hall 효과 측정을 이용하여 As+이 주입된 다결정 실리콘의 열처리 조건에 따른 활성화 과정을 연구하였다. 주입된 이온의 농도 분포는 SIMS(Secondary Ion Mass Spectroscopy)와 SUPREMIV 모의 실험으로 조사하였다. 열처리 온도가 증가함에 따라 활성층의 전자 면 농도 증가가 뚜렷이 나타났으며, Hall 이동도의 온도 의존성 측정으로 주입된 도우즈에 따라 이온 주입층의 활성화에 필요한 열처리 온도가 달라져야함을 알 수 있었다. 그리고, 접합 손실전류의 감소는 $800^{\circ}C$(30분)의 열처리에서 현저하게 나타났다.

• Journal of the Korean Society of Safety
• /
• v.22 no.5
• /
• pp.77-83
• /
• 2007

This study is conducted on spontaneous ignition temperature and activation energy of Hydroxypropyl Methyl Cellulose(HMC) powder. HMC is a kind of cellulose derivative and used as additives for building material, surface coating, printing ink, adhesives, cosmetics and medical supplies. So this material has been widely used as important additive in the chemical industry fields and a mount of production has increased year by year. Therefore, it is very important to find out the thermal ignition characteristics of its danger and the critical ignition temperature. This study was performed by the Spontaneous Ignition Tester(SIT) and so on. Based on the data of the SIT-II, the critical ignition point of HMC is about $186^{\circ}C$ which is slightly lower than normal cellulose.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.376-376
• /
• 2012

본 연구는 Poly-Si에 이온 주입된 Boron의 Activation 거동을 연구하고자 SLS (Sequential Lateral Solidification) Poly-Si과 ELA (Excimer Laser Annealing) Poly-Si의 활성화 거동을 비교 분석하였다. SLS 및 ELA 결정화 방법으로 제조된 Poly-Si을 모재로 비 질량 분리 방식의 ISD (Ion Shower Doping) System을 사용하여 2.5~7.0 kV까지 이온주입 하였다. 이온주입 후 두 가지의 열처리 방법, 즉, FA 열처리(Furnace Annealing)와 RTA 열처리(Rapid Thermal Annealing)를 사용하여 도펀트 활성화 열처리를 수행하고 이온주입 조건 및 활성화 열처리 방법에 따른 결함 회복 및 도펀트 활성화 거동의 변화를 관찰하였다. TRIM-code Simulation 결과 가속 이온 에너지와 조사량이 증가 할수록 이온주입 시 발생하는 결함의 양이 증가하는 것을 정량적으로 계산하였다. 실험 결과 결함의 양이 증가 할수록 Activation이 잘되는 것을 관찰할 수 있었다. SLS Poly-Si에 비하여 ELA Poly-Si의 경우 도펀트 활성화 열처리 후 활성화 효율이 높게 나타났다. 본 결과는 Grain Boundary의 역할과 밀접한 관계가 있으며 간단한 정성적인 Model을 제시하였다. 활성화 효율의 경우 RTA 열처리 시편이 FA 시편에 비하여 높은 것이 관찰되었다. 본 결과는 열처리 온도 및 시간에 따라 변화하는 Boron의 특이한 활성화 거동인 Reverse Annealing 효과에 기인하는 것으로 규명되었다.

• Polymer(Korea)
• /
• v.36 no.6
• /
• pp.739-744
• /
• 2012

In this work, we prepared the carbons from synthesized styrene-acrylonitrile carbon precursor. The prepared carbons were chemically activated, and then the activated SAN-based carbons were named as A-SANs. The activations were carried out at different temperatures to investigate the effect of activation temperature on the surface and electrochemical properties of the activated SAN-based carbons for using as an electrode of electric double layer capacitors (EDLC). The characteristics of A-SAN were determined by X-ray diffraction (XRD), scanning electron microscopy (SEM), surface area and pore size analysis. Also, the electrochemical behaviors were observed by cyclic voltammetry and galvanostatic charge-discharge method. From the results, the A-SAN 700 showed excellent electrochemical property and the highest specific capacitance, but these properties decreased when the activation temperature was above $700^{\circ}C$. This is due to the fact that the activation at a temperature over $700^{\circ}C$ causes deformation of micropore structures.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2011.04a
• /
• pp.296-297
• /
• 2011

A series of thermogravimetric analysis tests were conducted to predict the lifetime of the PTFE electrical insulation material. The prepared PTFE samples were heated from $25^{\circ}C$ to $700^{\circ}C$ at different heating rates. The kinetic energy of the PTFE was calculated from the logarithmic heating rate versus reciprocal temperature curves at constant conversion levels. Also, the lifetime of the PTFE for a given operating temperature can be predicted using the relationship between the activation energy and the estimated lifetime proposed by Toop.

• Transactions of the Korean hydrogen and new energy society
• /
• v.9 no.3
• /
• pp.127-133
• /
• 1998

This study was conducted to know to the effect of Pd film($180{\AA}$ thick) evaporation condition on the kinetics of hydrogen absorption-desorption. The activation energy of the forward reaction, the activation energy of the backward reaction, and the enthalpy were calculated by hydrogen absorption-desorption in ${\alpha}$-phase.($25{\sim}50^{\circ}C$ temperature) The activation energy of the forward reaction of Pd film, which is made at room temperature, is $6.4{\pm}0.4$ kcal/mol H and of the backward reaction $8.4{\pm}1.5$ kcal/mol H, which yields the reaction enthalpy -2kcal/mol H. The activation energy of forward reaction of Pd film, which is made at $300^{\circ}C$, is $-0.18{\pm}0.61$ kcal/mol H and of the backward reaction $-0.17{\pm}2.3$ kcal/mol H. The sample of $300^{\circ}C$ is more stable than the sample of room temperature in its struciural compactness and resistance value but standard error of result of $300^{\circ}C$ sample is higher than sample of room temperature do.

• Proceedings of the KAIS Fall Conference
• /
• 2011.12a
• /
• pp.266-268
• /
• 2011

본 논문은 폐타이어 열분해 잔류물인 char를 이용하여 수증기 활성화법으로 활성탄을 제조하였다. 활성화 온도가 증가할수록 비표면적은 증가하였으나 활성화 시간에 따른 비표면적은 3시간에서 최대를 보인 후 시간이 지속되면 비표면적은 감소하였다. 본 연구결과, 타이어열분해 잔류물 char를 이용한 활성탄 제조에 있어 최적의 실험조건은 활성화 온도 $850^{\circ}C$, 활성화 시간 3시간, 승온속도 $5^{\circ}C/min$이었으며 이 조건에서 제조한 활성탄의 비표면적은 $517.6m^2/g$으로 나타났다.

• Polymer(Korea)
• /
• v.24 no.1
• /
• pp.97-104
• /
• 2000

PAN-based activated carbon fibers/phenolic resin matrix composites (ACFCs) were manufactured via molding process with oxidized carbon fabrics (plain-type) and phenolic resin (resole-type) compounded by 70 : 30 wt%. The green body (as molded) was submitted to carbonization (at 100$0^{\circ}C$) in an inert environment and activation (at 700, 800, 900 and 100$0^{\circ}C$) in a $CO_2$ environment. In this work, the influence of activation temperatures was investigated in surface properties, such as pH, acid- and base-values by titration method, and in adsorption properties, i.e., specific surface area and pore structures by BET-method of the composites. Also, the pressure drops of the specimens were calibrated by ASTM. As a result, the activation temperature influenced the surface property of ACFCs. When the activation temperature was higher than 90$0^{\circ}C$, the surface was gradually developed in basic nature. And, the evolutions of specific surface area, total pore volume and pore size distribution of ACFCs could be easily confirmed the dependence on the activation temperature. Among them, well-developed pore structure from adsorption characteristics was changed of the ACFCs activated at 90$0^{\circ}C$. Also, the pressure drop was slightly decreased with increasing the temperature due to increasing the burn-off with heat treatment temperature of ACFCs.

• Resources Recycling
• /
• v.12 no.3
• /
• pp.13-24
• /
• 2003

The production characteristics of activated carbon from waste walnut shell have been investigated by taking activation temperature, activation time, amount of activating agent, and kind of activating agent as the major influential factors. The adsorption capacity of the activated carbon which was produced using phosphoric acid as the activating agent increased with activation temperature and showed its greatest value at about $550^{\circ}C$. Yield for activated carbon was observed to decrease continuously as the activation temperature was raised. The optimal activation time for the highest adsorption capacity was found to be about 2 hr, and as the activation time increased the yield for activated carbon was showed to decrease continuously. The increase in the amount of activating agent resulted in the increase of the yield for activated carbon, however, excessive amount of activating agent deteriorated its adsorption capacity reversely. The variations of the microstructure of activated carbon observed by SEM with several influential factors, correlated very well with its changes in the adsorbability with the same factors and the kind of activating agent was found to play an important role in the determination of the adsorption capacity of activated carbon. To investigate the adsorption characteristics of the produced activated carbon, the adsorption reactions of $Cu^{2+}$ ion were examined using the produced activated carbon as the adsorbent. In general, the kinetics of the adsorption of $Cu^{2+}$ ion was observed to follow a 2nd-order reaction and the rate constant for adsorption reaction increased as the initial concentration of adsorbate was diminished. The equilibrium adsorption of $Cu^{2+}$ was explained well with Freundlich model and its adsorption reaction was found to be endothermic. The activation energy for adsorption was calculated to be 13.07 kcal/mol, which implied that the adsorption reaction was very irreversible, and several thermodynamic parameters of adsorption reaction were estimated using van't. Hoff equation and thermodynamic relationships.