• Korean Journal of Materials Research
• /
• v.3 no.1
• /
• pp.33-42
• /
• 1993

Abstract The increasing application of $Al_2$,$O_3$ and related ceramics as engineering materials is because of their attractive properties of fine ceramics. One solution to the wide variety of ceramic to metal combination lies in the effective joining. Active metal brazing of $Al_2$,$O_3$, to STS304 was investigated using Cu -Ti alloys. Titanium additive is chosen since it is good oxide former~. Brazing is performed under vacuum($10^{-3}$-$10^{-4}$ torr), a temperature between 1100 and 120$0^{\circ}C$ and time of 0.5-1.5hr. The microstructure of the brazed joints of $Al_2$,$O_3$ to STS304 with Cu-Ti insert metals were examined by using optical microscope and SEM and reaction products were analyzed by using EDX, WDX and XRD. Also interfacial reactions occuring during the brazing of $Al_2$,$O_3$/Cu-Ti/STS304 system are discussed. Experimental results showed formation of Titanium oxide T$i_2$$O_3$ which is attributable to the joining $Al_2$,$O_3$ to STS304 with Cu-Ti insert metal.

• Journal of Welding and Joining
• /
• v.30 no.3
• /
• pp.38-43
• /
• 2012

In this study, active metal brazing methods for $ZrO_2$ and Ti alloy were discussed. To get a successful metal-ceramic bonding, various factors (melting temperature, corrosion, sag resistance, thermal expansion coefficient etc. of base materilas and filler metal) should be considered. Moreover, in order to clarify bonding between the metal and ceramic, the mechanism of the interfacial structure of the joints should be identified. The driving force for the formation of metal and ceramic interfaces is the reduction of the free energy which occurs when their contact becomes complete. Interfacial bonding depends on the material combinations and the bonding processes. This study describes the bonding between ceramic and metal in an active metal brazing.

• Korean Journal of Materials Research
• /
• v.3 no.3
• /
• pp.282-291
• /
• 1993

Joining ${Al}_{2}{O}_{3}$ and STS 304 stainless steel by active metal brazing method with using CuI Owt % Ti and Cu -7 .5wt % Zr insert metal, their interfaces were analyzed and strength of the joint brazed with Cu-7.5wt % Zr insert metal also investigated with shear strength testing method. In brazing with Cu-lOwt% Ti insert metal, the single reaction layer was formed by the reaction with Ti and ${Al}_{2}{O}_{3}$ at the interface between ${Al}_{2}{O}_{3}$ and insert metal, but the double reaction layer was found in brazing with Cu-7.5wt % Zr insert metal because of the difference of their wettability on the surface of ${Al}_{2}{O}_{3}$. Fracture shear strength about 86MPa was obtained from ${Al}_{2}{O}_{3}$/Cu-7.5wt% Zr/STS 304 stainless steel joint and reasonable strength of the joints is attributed to the formation of double reaction layer at the interface.

• Korean Journal of Materials Research
• /
• v.9 no.10
• /
• pp.970-977
• /
• 1999

Effect of Mo interlayer on the relaxation of residual stress in AlN/Cu pint bonded by active-metal brazing method was investigated. The stress analyses by finite-element-method, the measurement of pint strength and the observation of fracture surface were carried out and their results were compared with each other. From the results of stress analysis it is confirmed that a Mo interlayer led to a shift of maximum stress concentration site from AlN/insert-metal interface$\rightarro$ insert-metal/Mo$\rightarro$Mo interlayer. Additionally, with increase of the Mo interlayer thickness the stress concentration with tensile component was separately built both at the interface of Cu/Mo and AlN/Mo. whereby the residual stress in the free surface of AlN close to the bonded interface was drastically reduced. The AlN/Mo/Cu pints with Mo interlayer thickness of above 400$\mu\textrm{m}$ showed the strengths higher than 200 MPa. upto max. 275 MPa, while the AlN/Cu pint only max. 52 MPa.

• Journal of Welding and Joining
• /
• v.10 no.3
• /
• pp.63-72
• /
• 1992

The joining methods of ceramics to metals which can be expected to obtain high temperature strength are mainly classified into the solid-state diffusion bonding method and the active brazing method. Between these two, the solid-state diffusion bonding method is given attentions as substituting method for active brazing method due to being capable of obtaining higher bonding strength at high temperature and accurate bonding. In this paper, the solid-state diffusion bonding of $Al_{2}$O$_{3}$ ceramics to Ni-Cr-Mo alloy steel (SNCM21) using insert metal was carried out. The insert metal employed in this study was experimentally home-made, Ag-Cu-Ti alloy. Influence of several bonding parameters of $Al_{2}$O$_{3}$SNCM21 joint was quantitatively evaluated by bonding strength test, and microstructural analyses at the interlayer were performed by SEM/EDX. From above experiments, the optimum bonding condition of the solid-state diffusion bonding of $Al_{2}$O$_{3}$/SNCM21 using Ag-Cu-Ti insert metal was determined. Futhermore, high temperature strength and thermal-shock properties of $Al_{2}$O$_{3}$/SNCM21 joint were also examined. The results obtained are as follows. 1. The maximum bonding strength was obtained at the temperature of 95% melting point of insert metal. 2. The high temperature strength of $Al_{2}$O$_{3}$/SNCM21 joint appeared to bemaximum value at test temperature 500.deg.C and the bonding strength with increasingtemperature showed parabolic curve. 3. The strength of thermal-shocked specimens was far deteriorated than those of as-bonded specimens. Especially, water-quenched specimen after heated up to 600.deg. C was directly fractured in quenching.