• Journal of Sensor Science and Technology
• /
• v.6 no.4
• /
• pp.316-327
• /
• 1997

Polycrystalline $Sr_{2}Nb_{2}O_{7}$ and $La_{2}Ti_{2}O_{7}$ ceramics with very high Curie temperatures were synthesized by the chemical coprecipitation method (CCP). The powders synthesized were identified by XRD and their sintering behavior and physical properties were studied. The grain-orientation and electrical properties of sintered ceramics were investigated as a function of firing temperature. Single phase could be obtained by CCP method at temperature lower than that of the conventional method by 100 - $150^{\circ}C$. Strontium niobate, $Sr_{2}Nb_{2}O_{7}$, powder was Prepared by CCP method at temperatures as low as $800^{\circ}C$ via intermediate phase of $Sr_{5}Nb_{4}O_{15}$ formed at $700^{\circ}C$. The resulting CCP-derived powder was observed to have finer and more uniform particle size distribution than those obtained through the conventional or the molten salt synthesis method. Sintering of CCP-derived $Sr_{2}Nb_{2}O_{7}$ powder at $1500^{\circ}C$ yielded a highly dense ceramics with 97% theoretical density. Very high grain-orientation developed along the (0k0) direction was observed by SEM, which resulted in anisotropic dielectric properties of the sintered samples, with the dielectric constant values approaching those for single crystal.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.4
• /
• pp.274-280
• /
• 1998

Polycrystalline $Sr_2Nb_2O_7$ ceramics with very high Curie temperature were sintered using the powder derived by the chemical coprecipitation method (CCP). The phase evolution and grain-orientation of sintered samples were examined by XRD, while sintering behavior, dielectric properties and polarization were studied by SEM and ferroelectric tester. Extremely high degree of grain-orientation was observed along the (0k0) direction, which resulted in anisotropic dielectric properties of the sintered samples, with the dielectric constant values approaching those for single crystal. Thin film fabrication of $Sr_2Nb_2O_7$ in the pyroniobate family was also attempted on $SiO_2$/Si(100), Pt/$SiO_2$/Si(100), Pt/Ti/$SiO_2$/Si(100) and Pt/$ZrO_2/SiO_2/Si_2(100)$ substrates, using metalorganic decomposition (MOD) process. Neodecanoate precursor solution was prepared by mixing strontium neodecanoate with niobium neodecanoate synthesized from niobium ethoxide. It was found that $Sr_2Nb_2O_7$ single phase appeared in XRD patterns the samples annealed above $950^{\circ}C$. The effect of substrate type on film microstructure and dielectric properties was observed.