• Resources Recycling
• /
• v.17 no.5
• /
• pp.11-18
• /
• 2008

The purpose of this study was to evaluate the effects of blast-furnace slag on chemical attack and carbonation of latex-modified concrete (LMC) and ordinary portland cement concrete as slag contents. Main experimental variables were performed latex contents (0%, 15%) and slag contents (0%, 30%, 50%). The compressive strengths, chemical attacks resistance and carbonation depth were measured to analyze the characteristic of the developed LMC and BS-LMC(latex-modified concrete added blast-furnace slag) on hardened concrete. The test results showed that compressive strength of BS-LMC with blast-furnace slag content 30% was quite similar to it of OPC without slag content. The structural quality deterioration was concerned when blast slag content was up to 50%. However, carbonation restraint of BS-LMC with blast-furnace slag 30% was bigger then that of opc. Also, the effects of added latex on OPC and BS-LMC were increased on the carbonation restraint and chemical attacks resistance.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.22 no.6
• /
• pp.24-29
• /
• 2018

The properties of concrete with addition of microgel - containing hydrogel support were investigated. As a result of measuring the slump of the self - healing concrete, the target slump was satisfied in all the mixing conditions, but the slump was decreased as the mixing amount of the hydrogel support increased. The change of porosity due to incorporation of hydrogel support was minimal. As a result of the evaluation of the compressive strength of the self - healing concrete, the incorporation of the hydrogel support did not affect the strength. However, under the same mixing condition, the dispersion value of the specimens tended to increase with increasing hydrogel support contents. As a result of the permeability test of self-healing concrete according to the incorporation of hydrogel support, it was confirmed that the mixing ratio of hydrogel support was effective to decrease the permeability coefficient.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.31 no.2A
• /
• pp.105-113
• /
• 2011

This study evaluated the effects of fibers on the mechanical properties and chemical solution resistance of porous concrete with fiber type (jute, pulp, PVA and nylon fiber) and fiber volume fraction (0.0%, 0.1%, 0.2%, 0.3%). The tests that were carried out to analysis the properties of porous concrete included compressive strength, void ratio, pH value, and chemical solution exposure with varying type and volume fraction of fiber were conducted. The type and volume fraction of fiber also affected the void ratio, compressive strength, flexural strength and chemical solution exposure. Increased volume fractions of fiber resulted in improved properties of the compressive strength, flexural strength and void ratio. However, the difference between the measured pH value and chemical resistance of porous concrete with fiber type and volume fraction was not significant.

• Magazine of the Korea Concrete Institute
• /
• v.10 no.4
• /
• pp.125-133
• /
• 1998

In this study, an experiment in the field was performed to analyze the influence of steel fiber and silica fume on the rebound ratios of shotcrete. The experimental parameters which are the reinforcing methods(steel fiber, wire mesh), steel fiber contents(0.0%, 0.5%. 0.75%, 1.0%), silica fume contents(0.0%, 10.0%), and the three placing parts(side wall, shoulder, crown) were chosun. According to the results for the side wall in this test, the larger the fiber contents are in case of steel fiber reinforced shotcrete, the less the rebound ratios are within the range of 20~35%, compared to the wire mesh reinforced shotcrte. And also, the reduced rebound ratios were vary larger in using steel fiber reinforced shotcrete with silica fume content of 10%, and these results are true of the shoulder and the crown, respectively. In addition, the four-stage phenomenon for the rebound of the SFRS were estimated in the view of the co-action between steel fiber and coarse aggregate based upon the existing two-stage analysis method.

• Magazine of the Korea Concrete Institute
• /
• v.9 no.3
• /
• pp.189-197
• /
• 1997

This paper describes an experimental study on the seawater resistance of steel fiber reinforced concrete. The test methods adopted for this study are divided into long-term immersion test and acceleration test by wetting and drying. Tests were carried out to evaluate the procedures which were measured for nine months about reduction in dynamic modulus, length change and compressive strength. Resistance indicators are the water-cement ratio, the content of steel fiber, the content of fly ash, the immersion water(artificial seawater or freshwater) and the types of curing. The seawater resistance of the appropriate additions of steel fiber and fly ash have apparently increased.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.797-800
• /
• 2008

To decrease the usage of cement, the pozzolan reaction materials are used as a mineral admixture. Hwang Toh which is broadly deposited in Korea is well known as a environment friendly material and the activated Hwang Toh which has the property of pozzolan reaction is practically used as a mineral admixture of concrete. PET fiber which is made by recycled PET bottle controls micro crack in concrete. But the study about concrete mixed with reinforcing fiber is not enough and the property of Hwang Toh concrete mixed with PET fiber is more complicated case. So this study performed drying shrinkage experiment to analyse mechanical property of Hwang Toh concrete mixed with PET fiber.

• Journal of the Korea Concrete Institute
• /
• v.23 no.4
• /
• pp.461-469
• /
• 2011

In this study, the effect of polyvinyl alcohol (PVA) fiber volume fraction on the pullout behavior of structural synthetic fiber in hybrid structural synthetic fiber and PVA fiber cement composites are presented. Pullout behavior of the hybrid fiber cement composites and structural synthetic fiber were determined by dog-bone bond tests. Test results found that the addition of PVA fiber can effectively enhance the structural synthetic fiber cement based composites pullout behavior, especially in fiber interface toughness. Pullout test results of the structural synthetic fiber showed the interface toughness between structural synthetic fiber and PVA fiber reinforced cement composites increases with the volume fraction of PVA fiber. The microstructural observation confirms the incorporation of PVA fiber can effectively enhance the interface toughness mechanism of structural synthetic fiber and PVA fiber reinforced cement composites.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.697-700
• /
• 2008

Recently, high strength, flowability, and durability of concrete were required according to increase of large scale and high rise structure. However, cracks occurred easily on the high performance concrete. In this reason, using expansion agent for reducing shrinkage cracks were increased, but it did not consider on durability of high performance concrete. Accordingly, this study1 investigated the resistance of shrinkage and damage form salt by mixing CSA expansion agent on the blast-furnace slag cement and mixed cement for the low heat of hydration by three components. The cases that 8% of expansion agent was mixed and the proportion was OPC were expanded till 43.7 times compared with control concrete. For the resistance to the damage of salt, it was improved when mixing ratio was incresed and the maximum size of coarse aggregate growed bigger. In this study, the resistance to the damage of salt of the cases that 8% of expansion agent was mixed was improved about 16% compared with control concrete.

• Journal of the Korea Concrete Institute
• /
• v.28 no.1
• /
• pp.49-57
• /
• 2016

The aim of this study was to investigate the fundamental properties of pyroclastic flow deposit (PFD), and evaluate the fresh and strength properties of concrete mixed with PFD by indoor tests. The fresh properties, strength properties, shrinkage properties, and durability of the concrete mixed with PFD were also evaluated by outdoor plant tests. the harmful alkali-silica reaction did not occur by mixing concrete with PFD. ages. Moreover, no difficulty was found to be associated with concrete manufacture in the plant because no change in air contents and noticeable slump loss occurred by mixing concrete with PFD. The strength properties, shrinkage properties, and durability of the concrete mixed with PFD were also compared with those of normal concrete. With a suitable temperature control and curing method of concrete, the concrete mixed with PFD is considered to be useful in the construction material field.

• Journal of the Korea Concrete Institute
• /
• v.26 no.5
• /
• pp.607-614
• /
• 2014

The purpose of this dissertation was to investigate the effect of mineral admixtures, such as fly ash, blast furnace slag powder, meta kaolin and silica fume, on the basic properties and durability of crushed sand shotcrete, selecting a series of shotcrete mixtures with a variable admixture. Compressive strength increased as the content of mineral admixtures increased, specially it was the most effective when using meta kaolin both at sample specimen and core after shotcreting. Rapid chloride ion permeability test and sulfuric acid resistance test showed that both durability increased as the substitute rate of mineral admixture increased. In air void analysis with image analysis, the targeted the spacing factor and specific surface were not satisfied because air-entrained agent was not used.