• Journal of the Korean Vacuum Society
• /
• v.15 no.2
• /
• pp.168-172
• /
• 2006

GaN nucleation layers were grown by hydride vapor phase epitaxy (HVPE) and the effect of growth temperature on the structural properties of GaN nucleation layers for nanorods was investigated by synchrotron x-ray scattering and Atomic Force Microscopy (AFM). For the samples grown at different temperatures, two-component rocking profiles of (002) GaN Bragg peaks for the GaN nucleation layers were observed with one very sharp and the other broad. It was shown that the two-component rocking profile could be qualitatively explained by surface morphology, which was in good agreement with AFM result, from which we could conclude that relatively low temperature is favorable for GaN nanorods formation.

• Journal of the Korean Vacuum Society
• /
• v.16 no.6
• /
• pp.479-482
• /
• 2007

InN nanograins were directly grown on $0.3^{\circ}$-miscut (toward M-plane) c-plane sapphire substrates by hydride vapor phase epitaxy (HVPE) and their growth characteristics were investigated by utilizing x-ray scattering. Depending on the various growth parameters, the formation of InN was sensitively influenced. Six samples were grown by changing HCl flow rate, the substrate temperature and Ga/In source zone temperature. All the samples were grown on unintentionally $NH_3-pretreated$ sapphire substrates. By increasing the flow rate of HCl from 10 sccm to 20 sccm, the formation of GaN grains with different orientations was observed. On the other hand, when the substrate temperature was raised from $680^{\circ}C$ to $760^{\circ}C$, the increased substrate temperature dramatically suppressed the formation of InN. A similar behavior was observed for the samples grown with different source zone temperatures. By decreasing the source zone temperature from $460^{\circ}C$ to $420^{\circ}C$, a similar behavior was observed.